CN103860087B - 一种耐久性易吸水柔软毛巾的生产工艺 - Google Patents

一种耐久性易吸水柔软毛巾的生产工艺 Download PDF

Info

Publication number
CN103860087B
CN103860087B CN201210535894.5A CN201210535894A CN103860087B CN 103860087 B CN103860087 B CN 103860087B CN 201210535894 A CN201210535894 A CN 201210535894A CN 103860087 B CN103860087 B CN 103860087B
Authority
CN
China
Prior art keywords
temperature
caustic soda
adopt
production technology
dyeing
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201210535894.5A
Other languages
English (en)
Other versions
CN103860087A (zh
Inventor
张华�
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangsu sdefu new materials Co., Ltd
Original Assignee
NANTONG SIDEFU TEXTILE DECORATION CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by NANTONG SIDEFU TEXTILE DECORATION CO Ltd filed Critical NANTONG SIDEFU TEXTILE DECORATION CO Ltd
Priority to CN201210535894.5A priority Critical patent/CN103860087B/zh
Publication of CN103860087A publication Critical patent/CN103860087A/zh
Application granted granted Critical
Publication of CN103860087B publication Critical patent/CN103860087B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种耐久性易吸水柔软毛巾的生产工艺，包括纺纱、织造和染整加工等步骤：其中染整加工步骤为：首先退浆：在温度为85℃-95℃的热水中进行退浆，采用100%烧碱3-5g/l，时间为25-35min；然后煮练：在温度为90-100℃的热水中进行煮练，采用100%烧碱3-5g/l，时间为25-35min；然后漂白：在温度为98-100℃、含量为30%双氧水5-8g/l，100%烧碱3-5g/l的漂白液中进行漂白，PH值为10.5-11，漂白时间为55-65min；染色：将漂白过的织物采用活性染料进行染色，温度为30-35℃；最后进行清洗烘干。采用本发明的耐久性易吸水柔软毛巾的生产工艺制作出来的毛巾显著改善了产品的柔软性能，并兼具易吸水性等特点，本发明实用性强，适合行业内的广泛使用。

Description

一种耐久性易吸水柔软毛巾的生产工艺
技术领域
本发明涉及一种酒店用床上用品，特别是涉及一种耐久性易吸水柔软毛巾的生产工艺。
背景技术
公知的全棉毛巾类产品，使用过程中，为了保持其柔软的手感，一般采用添加柔软剂整理的方法来完成，但这种柔软性是非耐久性的，会随着使用次数的增加而逐渐减弱，直至消失，所以，要保持毛巾具有耐久性的柔软手感，可以采用周期性添加柔软剂整理方法。但添加柔软剂整理的方法，会因纤维拒水性增强而导致吸水性下降，及纤维之间摩擦力的减小，洗涤过程中所导致的起球现象，最终，降低了全棉毛巾的使用效果，不能满足使用者的使用需求。
发明内容
发明目的：本发明解决了现有技术的不足，提供了一种柔软性能和吸水性都优异的耐久性易吸水柔软毛巾的生产工艺。
技术方案：为达到上述目的，本发明采用如下技术方案：
一种耐久性易吸水柔软毛巾的生产工艺，包括如下步骤：
（1）纺纱：选用1.5D，中空率为15-20%的中空亲水型涤纶纤维与纤维长度大于35mm的长绒棉纤维混纺成16s及20s纱，其配比为65-70%：30-35%；
（2）织造：将步骤（1）中的混纺出来的纱织成底经纱*底纬纱*圈经纱20s/2*20s/1*16s/1，124*290*124根/10cm；
（3）染整加工，工艺步骤为：
退浆：在温度为85℃-95℃的热水中进行退浆，此处理过程中采用100%烧碱3-5g/l，时间为25-35min；
煮练：在温度为90-100℃的热水中进行煮练，此处理过程中采用100%烧碱3-5g/l，时间为25-35min；
漂白：在温度为98-100℃、含量为30%双氧水5-8g/l，100%烧碱3-5g/l的漂白液中进行漂白，PH值为10.5-11，漂白时间为55-65min；
染色：将漂白过的织物采用活性染料进行染色，温度为30-35℃；
清洗：PH值小于8.5；
烘干：门幅加工系数小于92-94%。
进一步的，所述步骤（2）中织造出来织物的的规格为35cm*77cm*120g。
有益效果：采用本发明的耐久性易吸水柔软毛巾的生产工艺制作出来的毛巾显著改善了产品的柔软性能，并兼具易吸水性等特点，在整理过程中无需加入亲水剂以及柔软助剂，不会随着使用次数的增加而逐渐减弱柔软性能，增加了毛巾的使用寿命，同时也不会出现起球现象，保证了毛巾的使用效果，本发明实用性强，适合行业内的广泛使用。
具体实施方式
下面通过具体实施例对本发明进行详细阐述：
实施例1：
一种耐久性易吸水柔软毛巾的生产工艺，包括如下步骤：
（1）纺纱：选用1.5D，中空率为17.5%的中空亲水型涤纶纤维与纤维长度大于35mm的长绒棉纤维混纺成16s及20s纱，其配比为67.5%：32.5%；
（2）织造：将步骤（1）中的混纺出来的纱织成底经纱*底纬纱*圈经纱20s/2*20s/1*16s/1，124*290*124根/10cm，规格为35cm*77cm*120g；
（3）染整加工，工艺步骤为：
退浆：在温度为90℃的热水中进行退浆，此处理过程中采用100%烧碱4g/l，时间为30min；
煮练：在温度为95℃的热水中进行煮练，此处理过程中采用100%烧碱4g/l，时间为30min；
漂白：在温度为99℃、含量为30%双氧水6.5g/l，100%烧碱4g/l的漂白液中进行漂白，PH值为10.75，漂白时间为60min；
染色：将漂白过的织物采用活性染料进行染色，温度为32.5℃；
清洗：PH值小于8.5；
烘干：门幅加工系数小于93%。
实施例2：
一种耐久性易吸水柔软毛巾的生产工艺，包括如下步骤：
（1）纺纱：选用1.5D，中空率为15%的中空亲水型涤纶纤维与纤维长度大于35mm的长绒棉纤维混纺成16s及20s纱，其配比为65%：30%；
（2）织造：将步骤（1）中的混纺出来的纱织成底经纱*底纬纱*圈经纱20s/2*20s/1*16s/1，124*290*124根/10cm，规格为35cm*77cm*120g。；
（3）染整加工，工艺步骤为：
退浆：在温度为85℃的热水中进行退浆，此处理过程中采用100%烧碱3g/l，时间为25min；
煮练：在温度为90℃的热水中进行煮练，此处理过程中采用100%烧碱3g/l，时间为25min；
漂白：在温度为98℃、含量为30%双氧水5-8g/l，100%烧碱3g/l的漂白液中进行漂白，PH值为10.5，漂白时间为55min；
染色：将漂白过的织物采用活性染料进行染色，温度为30℃；
清洗：PH值小于8.5；
烘干：门幅加工系数小于92%。
实施例3：
一种耐久性易吸水柔软毛巾的生产工艺，包括如下步骤：
（1）纺纱：选用1.5D，中空率为15-20%的中空亲水型涤纶纤维与纤维长度大于35mm的长绒棉纤维混纺成16s及20s纱，其配比为70%：35%；
（2）织造：将步骤（1）中的混纺出来的纱织成底经纱*底纬纱*圈经纱20s/2*20s/1*16s/1，124*290*124根/10cm，规格为35cm*77cm*120g；
（3）染整加工，工艺步骤为：
退浆：在温度为95℃的热水中进行退浆，此处理过程中采用100%烧碱5g/l，时间为35min；
煮练：在温度为100℃的热水中进行煮练，此处理过程中采用100%烧碱5g/l，时间为35min；
漂白：在温度为100℃、含量为30%双氧水8g/l，100%烧碱5g/l的漂白液中进行漂白，PH值为11，漂白时间为65min；
染色：将漂白过的织物采用活性染料进行染色，温度为35℃；
清洗：PH值小于8.5；
烘干：门幅加工系数小于94%。
附表：纯棉毛巾与本发明生产出来的毛巾的性能指标对比

Claims (2)

1.一种耐久性易吸水柔软毛巾的生产工艺，其特征在于：包括如下步骤：
步骤1、纺纱：选用1.5D，中空率为15-20％的中空亲水型涤纶纤维与纤维长度大于35mm的长绒棉纤维混纺成16s及20s纱，中空亲水型涤纶纤维与长绒棉纤维的配比为65-70％：30-35％；
步骤2、织造：将步骤1、中的混纺出来的纱织成底经纱*底纬纱*圈经纱20s/2*20s/1*16s/1，124*290*124根/10cm；
步骤3、染整加工，工艺步骤为：
退浆：在温度为85℃-95℃的热水中进行退浆，此处理过程中采用100％烧碱3-5g/l，时间为25-35min；
煮练：在温度为90-100℃的热水中进行煮练，此处理过程中采用100％烧碱3-5g/l，时间为25-35min；
漂白：在温度为98-100℃、含量为30％双氧水5-8g/l，100％烧碱3-5g/l的漂白液中进行漂白，PH值为10.5-11，漂白时间为55-65min；
染色：将漂白过的织物采用活性染料进行染色，温度为30-35℃；
清洗：PH值小于8.5；
烘干：门幅加工系数小于92-94％。
2.根据权利要求1所述的一种耐久性易吸水柔软毛巾的生产工艺，其特征在于：所述步骤2、中织造出来织物的的规格为35cm*77cm*120g。
CN201210535894.5A 2012-12-13 2012-12-13 一种耐久性易吸水柔软毛巾的生产工艺 Active CN103860087B (zh)