CN103835140A - 一种防紫外线织物面料 - Google Patents
一种防紫外线织物面料 Download PDFInfo
- Publication number
- CN103835140A CN103835140A CN201410092113.9A CN201410092113A CN103835140A CN 103835140 A CN103835140 A CN 103835140A CN 201410092113 A CN201410092113 A CN 201410092113A CN 103835140 A CN103835140 A CN 103835140A
- Authority
- CN
- China
- Prior art keywords
- ultraviolet
- fabric
- coffee powder
- fabric lining
- protection
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及一种防紫外线织物面料，包括织物面料和涂覆在织物面料里层的防紫外线层，所述的防紫外线层为咖啡粉体与聚酯的共混层，其中防紫外线层的厚度为0.05mm—0.3mm，咖啡粉体的粒径为0.5μm—5μm，咖啡粉体与聚酯的质量比为2:10—5:10。本发明的防紫外线织物面料可使其紫外防护系数(UPF)达到50以上，UVA的透过率<5%，且在使用过程中不会分解产生有毒物质对人体的健康造成影响；与此同时，因为咖啡粉体自身具有的抗菌除异味的特点，具有使面料在潮湿环境下使用而不产生异味等优点，适合做太阳伞伞面、汽车防晒防雨布等。
Description
技术领域
本发明涉及一种防紫外线织物面料，属于纺织技术领域。
背景技术
目前市场中常见的制作防紫外线面料的技术手段主要有两种：一种为在纺丝时混入防紫外线材料以达到防紫外线的效果；另一种为利用后整理的方法对织物进行防紫外线整理。后整理方法中最常见的为利用涂层技术在织物表面涂覆一层材料，涂覆材料一般为黑胶、银胶或其他具有防紫外线效果的材料。利用纺丝法制作防紫外线面料的技术手段对纤维原料有限制；利用涂层法制作的防紫外线面料在使用过程中，防紫外线层不可避免的被雨水腐蚀，容易出现防紫外线材料脱落、分解产生出对人体健康有害的化合物等问题。
公开杂志《印染》，公开日期2005年第15卷名称为《TiO 2 纳米材料防紫外线涂层整理》中提到了运用纳米二氧化钛作为防紫外线涂料对纺织品进行涂层整理，虽然它采用的方法使纺织面料的紫外防护系数达到国家要求水平。但是，其不足之处在于，由于二氧化钛具有光催化性，其作为防紫外线材料在光照的条件下可以将空气中的氧气和氮气转化为硝酸盐，加剧了日益严重的氮污染。
中国专利《一种抗紫外面料》授权公告号CN202592839U，授权公告日期2012年12月12日，公开了一种表面涂有一种防紫外线助剂的面料，这种面料可以达到国家防紫外标准，具有防紫外线的性能。但是，其不足之处在于，防紫外线助剂的化学性质不稳定，在使用过程中涂覆在织物外层的防紫外线助剂容易在光照和雨水的作用下腐蚀脱落，从而降低其防紫外线的效果。
发明内容
针对上述存在问题，本发明的目的在于提供一种防紫外线织物面料，为了实现上述目的，本发明的技术解决方案为：一种防紫外线织物面料，包括织物面料和涂覆在织物面料里层的防紫外线层，所述的防紫外线层为咖啡粉体与聚酯的共混层，其中防紫外线层的厚度为0.05mm—0.3mm，咖啡粉体的粒径为0.5μm—5μm，咖啡粉体与聚酯的质量比为2:10—5:10。
由于采用了上述技术方案，与现有制作防紫外线织物面料的技术相比，本发明具有以下优点：
本发明改变了现有防紫外线织物面料所用的防紫外线整理剂，利用咖啡粉体本身具有的防紫外线性能，将咖啡粉体运用到纺织技术领域；本发明的咖啡粉体属于天然防紫外线整理剂，咖啡粉体可以采用咖啡残渣制得，在节约能源的前提下，使织物面料在使用过程中不会分解产生有毒物质对人体的健康造成影响；与此同时，由于咖啡粉体本身还有抗菌除异味的特点，具有使面料在潮湿环境下使用而不产生异味等优点；本发明的防紫外线织物面料的紫外防护系数(UPF)可达到50以上，UVA的透过率<5%；本发明的防紫外线层位于织物面料里层，在保证防紫外线性能持久性的同时，不影响织物的表层美观性，适合做太阳伞伞面、汽车防晒防雨布等。
综合以上优点使得制成的织物面料在合理利用咖啡残渣的同时，既能保证防紫外性能的持久性，保证了织物的使用寿命，又不会产生不利人体健康的化合物。本发明的一种防紫外线织物面料防紫外线能力强，天然环保，取材容易，成本低。
附图说明
图1为本发明的结构示意图。
具体实施方式
下面结合附图和具体实施方式对本发明进行详细说明。
见附图。
一种防紫外线织物面料，包括织物面料1和涂覆在织物面料1里层的抗紫外线层2，所述的抗紫外线层2为咖啡粉体与聚酯的共混层，其中防紫外线层2的厚度为0.05mm—0.3mm，咖啡粉体的粒径为0.5μm—5μm，咖啡粉体与聚酯的质量比为2:10—5:10。
本发明的防紫外线织物面料的制备方法如下：
a在50℃—80℃油浴锅中将聚酯颗粒溶解于N-N二甲基甲酰胺溶剂中，搅拌均匀配制成质量比为1：5的聚酯溶液。
b在溶解并搅拌均匀之后，按照咖啡粉体与聚酯2:10—5:10的质量比称取咖啡粉体，并加入聚酯溶液中并搅拌使其均匀分布，其中咖啡粉体粒径为0.5μm—5μm。
c在将上述配置好的混合液均匀涂覆在织物面料1里层，形成0.05mm—0.3mm的防紫外线层2，静置烘干即得到防紫外线织物面料。
具体实施例1
按上述工艺步骤：分别准确称量10g聚酯颗粒和50gN-N二甲基甲酰胺溶剂，在50℃油浴锅中搅拌混合均匀后，加入5.0g粒径为0.5μm的咖啡粉体，搅拌均匀后直接涂覆在涤纶织物面料1里层制备形成厚度约为0.3mm的防紫外线层2，静置烘干后即得防紫外线织物面料。
将该防紫外线织物面料进行抗紫外线性能测试，得到其紫外线防护系数（UPF）为94.5，UVA的透过率为3.84%，尤其适合制作夏季太阳伞伞面。
具体实施例2
按上述工艺步骤：分别准确称量10g聚酯颗粒和50gN-N二甲基甲酰胺溶剂，在65℃油浴锅中搅拌混合均匀后，加入4.0g粒径为3.0μm的咖啡粉体，搅拌均匀后直接涂覆在涤纶织物面料1里层制备形成厚度约为0.2mm的防紫外线层2，静置烘干后即得防紫外线织物面料。
将该防紫外线织物面料进行抗紫外线性能测试，得到其紫外线防护系数（UPF）为71.6，UVA的透过率为4.35%，尤其适合制作汽车防晒防雨布。
具体实施例3
按上述工艺步骤：分别准确称量10g聚酯颗粒和50gN-N二甲基甲酰胺溶剂，在80℃油浴锅中搅拌混合均匀后，加入3.0g粒径为5.0μm的咖啡粉体，搅拌均匀后直接涂覆在涤纶织物面料1里层制备形成厚度约为0.05mm的防紫外线层2，静置烘干后即得防紫外线织物面料。
将该防紫外线织物面料进行抗紫外线性能测试，得到其紫外线防护系数（UPF）为57.7，UVA的透过率为4.54%，尤其适合制作夏季防晒衣。
Claims (1)
1.一种防紫外线织物面料，包括织物面料(1)和涂覆在织物面料(1)里层的防紫外线层(2)，其特征在于：所述的防紫外层(2)为咖啡粉体与聚酯的共混层，其中防紫外线层(2)的厚度为0.05mm—0.3mm，咖啡粉体的粒径为0.5μm—5μm，咖啡粉体与聚酯的质量比为2:10—5:10。