CN103802588B - A kind of manufacture method of interlayer safe and colour glass mirror - Google Patents
A kind of manufacture method of interlayer safe and colour glass mirror Download PDFInfo
- Publication number
- CN103802588B CN103802588B CN201310751821.4A CN201310751821A CN103802588B CN 103802588 B CN103802588 B CN 103802588B CN 201310751821 A CN201310751821 A CN 201310751821A CN 103802588 B CN103802588 B CN 103802588B
- Authority
- CN
- China
- Prior art keywords
- glass
- glass mirror
- mirror
- dry
- film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The manufacture method that the present invention relates to a kind of interlayer safe and colour glass mirror, belongs to glass applications technical field. Its manufacture process comprises the steps: that (1) carry out feeding, edging, cleaning, dry to glass mirror; (2) EVA film, dried flower, hay are carried out to feeding, cutting, splicing, dry; (3) plate glass is carried out to feeding, edging, cleaning, dry; (4) glass mirror, EVA film or dried flower, hay and plate glass are superposeed neatly, again the semi-finished product stained glass mirror having superposeed is entered to stove, regulating stove controller is progressively warming up to 60 DEG C～135 DEG C, make softening plate glass and the glass mirror inner surface of being fitted in of EVA film, insulation 10min～55min, naturally cooling 10min～30min, to normal temperature, comes out of the stove; (5) colored mirror is carried out to edging. The interlayer safe and colour glass mirror that method of the present invention produces, when glass is broken, fragment can not splash, not only attractive in appearance but also safety, change color were various, of many uses.
Description
Technical field
The manufacture method that the present invention relates to a kind of interlayer safe and colour glass mirror, belongs to glass applicationsTechnical field.
Background technology
Stained glass mirror is because its color is sparkling and crystal-clear reflective bright and belong to safety glass scope and obtainTo liking of people, purposes is also more and more extensive, and particularly people adopt interlayer safe and colour glassGlass mirror is as ornament, dining table, tea table or building curtain wall etc. Along with carrying of people's living standardHeight, more and more higher to aesthetic requirement, the utilization rate of interlayer safe and colour glass mirror strengthens thereupon.And simple glass mirror dull coloring, Colour selection scope is few, cannot meet people and produce colorful manyThe decoration demand of appearance. And single-glass mirror is frangible, the simple and easy wound of Sui Hou Workflow, is absolutely unsafe.
Summary of the invention
The object of the present invention is to provide a kind of not only attractive in appearance but also safe interlayer safe and colour glassThe manufacture method of mirror.
To achieve these goals, the present invention is by the following technical solutions:
A manufacture method for interlayer safe and colour glass mirror, its manufacture process comprises following stepRapid:
(1) glass mirror is carried out to feeding, edging, cleaning, dry;
(2) to redness, yellow, cyan, green, light blue, lilac, lilac look,Brown, blue, golden yellow, orange, champagne, emerald green, micro-purple, black tea look, ashBlue, micro-grey or colourless EVA film, dried flower, hay etc. carry out feeding, cutting, splicing,Dry;
(3) plate glass is carried out to feeding, edging, cleaning, dry;
(4) glass mirror, EVA film, dried flower or hay and plate glass are superposeed neatly,Again the semi-finished product stained glass mirror having superposeed is entered to stove, regulating stove controller is progressively warming up to 60DEG C～135 DEG C, make softening plate glass and the glass mirror inner surface of being fitted in of EVA film, insulation10min～55min, naturally cooling 10min～30min, to normal temperature, comes out of the stove.
(5) colored mirror is carried out to edging.
That described plate glass, colored EVA film, glass mirror will keep in laminating is smooth, tableFace clean dried, the area of colored EVA film is greater than and equals plate glass and glass mirror area.
The interlayer safe and colour glass mirror that method of the present invention produces, when glass is brokenFragment can not splash, not only attractive in appearance but also safety, makes simply, and change color is various, does not fade notAging, environmental protection, color or pattern can keep for a long time, purposes in family property decoration and daily lifeExtensively.
Brief description of the drawings
Fig. 1 is structural representation of the present invention;
In figure: glass mirror 1, EVA film 2, plate glass 3.
Detailed description of the invention
Embodiment 1: a kind of manufacture method of interlayer safe and colour glass mirror, its manufacture process comprises
Following steps:
(1) glass mirror 1 is carried out to feeding, edging, cleaning, dry; Described glass mirror is silverMirror, gray out or tawny glasses etc.
(2) to redness, yellow, cyan, green, light blue, lilac, lilac look,Brown, blue, golden yellow, orange, champagne, emerald green, micro-purple, black tea look, ashBlue, micro-grey or colourless EVA film 2 carry out feeding, cutting, splicing, dry;
(3) plate glass 3 is carried out to feeding, edging, cleaning, dry;
(4) glass mirror, EVA film and plate glass are superposeed neatly, then will superposeGood semi-finished product stained glass mirror enters stove, and regulating stove controller is progressively warming up to 60 DEG C～135 DEG C,Make softening plate glass and the glass mirror inner surface of being fitted in of EVA film, insulation 10min～55min, naturally cooling 10min～30min, to normal temperature, comes out of the stove.
(5) colored mirror is carried out to edging.
That described plate glass, colored EVA film, glass mirror will keep in laminating is smooth, tableFace clean dried, the area of colored EVA film is greater than and equals plate glass and glass-mirrorLong-pending.
Embodiment 2: a kind of manufacture method of interlayer safe and colour glass mirror, its manufacture process comprises
Following steps:
(1) glass mirror 1 is carried out to feeding, edging, cleaning, dry; Described glass mirror is silverMirror, gray out or tawny glasses etc.
(2) to redness, yellow, cyan, green, light blue, lilac, lilac look,Brown, blue, golden yellow, orange, champagne, emerald green, micro-purple, black tea look, ashBlue, micro-grey or colourless EVA film 2, dried flower, hay carry out feeding, cutting, splicing,Dry;
(3) plate glass 3 is carried out to feeding, edging, cleaning, dry;
(4) one deck glass mirror, two layers of colourful transparent EVA film or one deck EVA is thoroughly coloredThe high clear, colorless film of gelatin foil and one deck EVA and dried flower, hay or pattern and plate glass enterRow stack is neat, shown in dried flower, hay or pattern between two layers of EVA film, ensure glueThe stickup of shape of the pattern increasing, dried flower or hay being remained unchanged after sheet is softening is combined in dull and stereotyped glassIn glass and glass mirror, firmly stick into entirety, then the semi-finished product stained glass mirror having superposeed entered to stove,Regulating stove controller is progressively warming up to 60 DEG C～135 DEG C, makes the softening flat board that is fitted in of EVA filmGlass and glass mirror inner surface, insulation 10min～55min, naturally cooling 10min～30minTo normal temperature, come out of the stove;
(5) safe and colour glass mirror is carried out to edging.
That described plate glass, colored EVA film, glass mirror will keep in laminating is smooth, tableFace clean dried, the area of colored EVA film is greater than and equals plate glass and glass-mirrorLong-pending. In process of production, plate glass, color film, glass mirror will keep flat in laminatingWhole, surperficial clean dried, the area of color film is greater than or equals plate glass and glass mirrorArea, guarantees that the softening rear plate glass of color film, color film and glass mirror are tight after intensificationClose bonding. Laminating plate glass, film, various dried flower or hay and various pattern, glassWhen mirror, various dried flowers or hay and various pattern are laid between plate glass or glass mirror pressesThickness after tight is less than the gross thickness of plate glass and glass mirror interlayer.
Claims (2)
1. a manufacture method for interlayer safe and colour glass mirror, is characterized in that: its manufacture process comprise asLower step:
(1) glass mirror (1) is carried out to feeding, edging, cleaning, dry; Described glass mirror is silver mirror, ashMirror or tawny glasses;
(2) to redness, yellow, cyan, green, light blue, lilac, lilac look, brown, blue,Golden yellow, orange, champagne, emerald green, micro-purple, black tea look, dusty blue, micro-grey or colourless EVAFilm (2), dried flower, hay carry out feeding, cutting, splicing, dry;
(3) plate glass (3) is carried out to feeding, edging, cleaning, dry;
(4) by one deck glass mirror, two layers of colourful transparent EVA film or one deck EVA colourful transparent film and oneThe layer high clear, colorless film of EVA and dried flower, hay or pattern and plate glass superpose neatly, described dryFlower, hay or pattern, between two layers of EVA film, ensure that film can be by the pattern increasing, dry after softeningThe remain unchanged stickup of shape of flower or hay is combined in plate glass and glass mirror, firmly sticks into entirety, then will foldThe semi-finished product stained glass mirror having added enters stove, and regulating stove controller is progressively warming up to 60 DEG C～135 DEG C, makes EVASoftening plate glass and the glass mirror inner surface of being fitted in of film, insulation 10min～55min, naturally cooling10min～30min, to normal temperature, comes out of the stove;
(5) safe and colour glass mirror is carried out to edging.
2. the manufacture method of interlayer safe and colour glass mirror according to claim 1, is characterized in that:Described plate glass, colored EVA film, glass mirror will keep smooth, surperficial clean dried in laminating,The area of colored EVA film is greater than and equals plate glass and glass mirror area.