CN103802588A - Method for manufacturing interlayer safe colored glass mirror - Google Patents
Method for manufacturing interlayer safe colored glass mirror Download PDFInfo
- Publication number
- CN103802588A CN103802588A CN201310751821.4A CN201310751821A CN103802588A CN 103802588 A CN103802588 A CN 103802588A CN 201310751821 A CN201310751821 A CN 201310751821A CN 103802588 A CN103802588 A CN 103802588A
- Authority
- CN
- China
- Prior art keywords
- glass
- mirror
- glass mirror
- edging
- eva film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a method for manufacturing an interlayer safe colored glass mirror, and belongs to the technical field of glass application. The manufacturing process comprises the following steps: (1) selecting a glass mirror, edging, washing and drying; (2) selecting a EVA (ethylene-vinyl acetate) film, a dried flower and hay, cutting, splicing and drying; (3) selecting a piece of plate glass, edging, washing and drying; (4) tidily overlapping the glass mirror and the EVA film or the dried flower, the hay and the plate glass, feeding overlapped semi-finished product colored glass into a furnace, adjusting a furnace controller to gradually raise the temperature to be 60-135 DEG C so as to soften the EVA film and adhere to the inner surfaces of the plate glass and the glass mirror, keeping the temperature for 10-55 minutes, naturally cooling for 10-30 minutes to the normal temperature, and discharging outside the furnace; and (5) edging the colored mirror. When the glass of the interlayer safe colored glass mirror manufactured by adopting the method is broken, the debris does not fly and splash, and the mirror is attractive in appearance, safe, diversified in color and wide in application.
Description
Technical field
The manufacture method that the present invention relates to a kind of interlayer safe and colour glass mirror, belongs to glass applications technical field.
Background technology
Stained glass mirror is because its color is sparkling and crystal-clear reflective bright and belong to safety glass scope and obtain liking of people, and purposes is also more and more extensive, and particularly people adopt interlayer safe and colour glass mirror as ornament, dining table, tea table or building curtain wall etc.Along with the raising of people's living standard, more and more higher to aesthetic requirement, the utilization rate of interlayer safe and colour glass mirror strengthens thereupon.And simple glass mirror dull coloring, Colour selection scope is few, cannot meet people and produce well-rounded decoration demand.And single-glass mirror is frangible, the simple and easy wound of Sui Hou Workflow, is absolutely unsafe.
Summary of the invention
The object of the present invention is to provide the manufacture method of a kind of not only attractive in appearance but also safe interlayer safe and colour glass mirror.
To achieve these goals, the present invention is by the following technical solutions:
A manufacture method for interlayer safe and colour glass mirror, its manufacture process comprises the steps:
(1) glass mirror is carried out to feeding, edging, cleaning, dry;
(2) redness, yellow, cyan, green, light blue, lilac, lilac look, brown, blue, golden yellow, orange, champagne, emerald green, micro-purple, black tea look, dusty blue, micro-grey or colourless EVA film, dried flower, hay etc. are carried out to feeding, cutting, splicing, dry;
(3) plate glass is carried out to feeding, edging, cleaning, dry;
(4) glass mirror, EVA film, dried flower or hay and plate glass are superposeed neatly, again the semi-finished product stained glass mirror having superposeed is entered to stove, regulating stove controller is progressively warming up to 60 ℃～135 ℃, make softening plate glass and the glass mirror inner surface of being fitted in of EVA film, insulation 10min～55min, naturally cooling 10min～30min, to normal temperature, comes out of the stove.
(5) colored mirror is carried out to edging.
Described plate glass, colored EVA film, glass mirror will keep smooth, surperficial clean dried in laminating, and the area of colored EVA film is greater than and equals plate glass and glass mirror area.
The interlayer safe and colour glass mirror that method of the present invention produces, when glass is broken fragment can not splash, not only attractive in appearance but also safety, make simple, change color is various, do not fade not aging, and environmental protection, color or pattern can keep for a long time, and in family property decoration and daily life, purposes is wide.
Accompanying drawing explanation
Fig. 1 is structural representation of the present invention;
In figure: glass mirror 1, EVA film 2, plate glass 3.
The specific embodiment
Embodiment 1: a kind of manufacture method of interlayer safe and colour glass mirror, its manufacture process comprises
Following steps:
(1) glass mirror 1 is carried out to feeding, edging, cleaning, dry; Described glass mirror is silver mirror, gray out or tawny glasses etc.
(2) redness, yellow, cyan, green, light blue, lilac, lilac look, brown, blue, golden yellow, orange, champagne, emerald green, micro-purple, black tea look, dusty blue, micro-grey or colourless EVA film 2 are carried out to feeding, cutting, splicing, dry;
(3) plate glass 3 is carried out to feeding, edging, cleaning, dry;
(4) glass mirror, EVA film and plate glass are superposeed neatly, again the semi-finished product stained glass mirror having superposeed is entered to stove, regulating stove controller is progressively warming up to 60 ℃～135 ℃, make softening plate glass and the glass mirror inner surface of being fitted in of EVA film, insulation 10min～55min, naturally cooling 10min～30min, to normal temperature, comes out of the stove.
(5) colored mirror is carried out to edging.
Described plate glass, colored EVA film, glass mirror will keep smooth, surperficial clean dried in laminating, and the area of colored EVA film is greater than and equals plate glass and glass mirror area.
Embodiment 2: a kind of manufacture method of interlayer safe and colour glass mirror, its manufacture process comprises
Following steps:
(1) glass mirror 1 is carried out to feeding, edging, cleaning, dry; Described glass mirror is silver mirror, gray out or tawny glasses etc.
(2) redness, yellow, cyan, green, light blue, lilac, lilac look, brown, blue, golden yellow, orange, champagne, emerald green, micro-purple, black tea look, dusty blue, micro-grey or colourless EVA film 2, dried flower, hay are carried out to feeding, cutting, splicing, dry;
(3) plate glass 3 is carried out to feeding, edging, cleaning, dry;
(4) by one deck glass mirror, two layers of colourful transparent EVA film or one deck EVA colourful transparent film and the high clear, colorless film of one deck EVA and dried flower, hay or pattern and plate glass superpose neatly, shown in dried flower, hay or pattern are between two layers of EVA film, guarantee that film can be by the pattern increasing after softening, the remain unchanged stickup of shape of dried flower or hay is combined in plate glass and glass mirror, firmly stick into entirety, again the semi-finished product stained glass mirror having superposeed is entered to stove, regulating stove controller is progressively warming up to 60 ℃～135 ℃, make softening plate glass and the glass mirror inner surface of being fitted in of EVA film, insulation 10min～55min, naturally cooling 10min～30min is to normal temperature, come out of the stove,
(5) safe and colour glass mirror is carried out to edging.
Described plate glass, colored EVA film, glass mirror will keep smooth, surperficial clean dried in laminating, and the area of colored EVA film is greater than and equals plate glass and glass mirror area.In process of production, plate glass, color film, glass mirror will keep smooth, surperficial clean dried in laminating, the area of color film is greater than or equals plate glass and glass mirror area, guarantees softening rear plate glass, color film and glass mirror close adhesion of color film after intensification.When laminating plate glass, film, various dried flower or hay and various pattern, glass mirror, the thickness after various dried flowers or hay and various pattern are laid in and compress between plate glass or glass mirror is less than the gross thickness of plate glass and glass mirror interlayer.
Claims (2)
1. a manufacture method for interlayer safe and colour glass mirror, is characterized in that: its manufacture process comprises the steps:
(1) glass mirror (1) is carried out to feeding, edging, cleaning, dry;
(2) redness, yellow, cyan, green, light blue, lilac, lilac look, brown, blue, golden yellow, orange, champagne, emerald green, micro-purple, black tea look, dusty blue, micro-grey or colourless EVA film (2), dried flower, hay are carried out to feeding, cutting, splicing, dry;
(3) plate glass (3) is carried out to feeding, edging, cleaning, dry;
(4) glass mirror, EVA film or dried flower, hay are superposeed neatly, again the semi-finished product stained glass mirror having superposeed is entered to stove, regulating stove controller is progressively warming up to 60 ℃～135 ℃, make softening plate glass and the glass mirror inner surface of being fitted in of EVA film, insulation 10min～55min, naturally cooling 10min～30min, to normal temperature, comes out of the stove.
(5) colored mirror is carried out to edging.
2. the manufacture method of interlayer safe and colour glass mirror according to claim 1, it is characterized in that: described plate glass, colored EVA film, glass mirror will keep smooth, surperficial clean dried in laminating, the area of colored EVA film is greater than and equals plate glass and glass mirror area.