CN104442167A - Art glass and manufacturing method thereof - Google Patents
Art glass and manufacturing method thereof Download PDFInfo
- Publication number
- CN104442167A CN104442167A CN201410619687.7A CN201410619687A CN104442167A CN 104442167 A CN104442167 A CN 104442167A CN 201410619687 A CN201410619687 A CN 201410619687A CN 104442167 A CN104442167 A CN 104442167A
- Authority
- CN
- China
- Prior art keywords
- glass
- art
- skin
- manufacture method
- laminated
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to art glass and a manufacturing method thereof, wherein the art glass comprises surface-layer glass, sandwich glass and bottom-layer glass, the sandwich glass is arranged between the surface-layer glass and the bottom-layer glass and fixed together with the surface-layer glass and the bottom-layer glass by virtue of lined adhesive layers; the surface-layer glass comprises a plurality of glass units which are spliced with one another. In the art glass and the manufacturing method thereof, provided by the invention, a three-layer glass lined adhesive reinforcing structure is adopted to improve the strength of the art glass; meanwhile, the surface-layer glass of the art glass is formed by splicing the plurality of glass units, so that not only can large-module finished products be manufactured, but also the art glass can be uniformly heated in a firing process, so that the burst is prevented.
Description
Technical field
The present invention relates to glassmaking art, particularly a kind of art glass and manufacture method thereof.
Background technology
Art glass is a kind of is carrier with glass, embodies the glassware of design concept and art of expression effect.Art glass with a long history, its technical matters level is also increasingly mature.Along with the attention of people to indoor decorative effect and the lifting of sensory experience, art glass is widely used, and its charming and visual effect of noble quality is subject to the favor of more and more people.
Traditional art glass processing technology is divided into two kinds: heat processing technique and cold machining process.Cold machining process forms various surface effect by grinding the modes such as quarter, sandblasting, artificial colored drawing under normal temperature environment, then do not heat higher than the kiln of 593 DEG C by temperature, obtains finished product after cooling.Heat processing technique is processed glass baseplate by modes such as blowing, thermoplastic, doublings under the hot environment more than 593 DEG C, obtains finished product after cooling.
Wherein, the manufacture craft of artistic color glass generally uses high temperature colored glaze look or colored drawing on the glass surface, such as colored glaze look glass, colored glaze colored drawing etc.In order to reach the requirement of permeability, traditional artistic color glass uses single-glass to make usually.The artistic color glass fragility using single-glass to make is high, and intensity is low, also very frangible in transport and use procedure.And traditional artistic color glass easily bursts when carrying out high-temperature firing, very easily fades after high-temperature firing, affects its effect.The manufacture craft of art doubling glass is generally use figured cloth, and marble paper, colored glued membrane, woven wire material is as sandwich of layers, although its form is various, compare in stained glass effect more single, artistic feeling is not strong.
Traditional art glass processing technology is due to the restriction of technique, and the finished product module of various art glass is all smaller, and when pattern requirement is higher, need dependence manually to draw a design, not only process time is longer, and is difficult to realize producing in enormous quantities.
Summary of the invention
The object of the present invention is to provide a kind of art glass and manufacture method thereof, to solve the long processing time of existing art glass, easily burst in sintering procedure, the problem that finished product module is little and frangible.
For solving the problems of the technologies described above, the invention provides a kind of art glass, described art glass comprises: skin glass, laminated glass and bottom glass; Described laminated glass is arranged between described skin glass and bottom glass, and is fixed by doubling layer and described skin glass and bottom glass; Described skin glass comprises the glass unit that polylith splices mutually.
Optionally, in described art glass, the raw material of described skin glass, laminated glass and described bottom glass all select ultra-clear glasses.
Optionally, in described art glass, described ultra-clear glasses is self-cleaning coat nanometer sand glass.
Optionally, in described art glass, described skin glass is etching glass, and described laminated glass is stained glass.
Optionally, in described art glass, the thickness range of described skin glass is between 3mm to 8mm, and the thickness range of described laminated glass is between 6mm to 10mm, the thickness range of described bottom glass is between 8mm to 15mm, and the thickness range of described doubling layer is between 0.5mm to 2mm.
Optionally, in described art glass, the thickness of described skin glass is 5mm, and the thickness of described laminated glass is 8mm, and the thickness of described bottom glass is 10mm, and the thickness of described doubling layer is 1.14mm.
Accordingly, the present invention also provides a kind of manufacture method of art glass, and the manufacture method of described art glass comprises:
Make skin glass, laminated glass and bottom glass respectively, described skin glass comprises the glass unit that polylith splices mutually;
Described skin glass, laminated glass and bottom glass are carried out doubling fix; And
Semi-finished product after being fixed by doubling are put into autoclave and are formed by a firing.
Optionally, in the manufacture method of described art glass, the manufacturing process of described glass unit comprises:
Make ground glass;
Surperficial sense organ process is carried out to described ground glass;
A bonding silica gel treatment is carried out to described ground glass;
Surface etching process is carried out to described ground glass;
Remove the silica gel of described ground glass remained on surface.
Optionally, in the manufacture method of described art glass, the process making ground glass comprises:
By ultra-clear glasses horizontal, and at its surface coating paraffin liquid as protective layer;
Word on paraffin layer after hardening required for carve or pattern;
Hydrofluoric acid is dripped on described word or pattern, and according to depth control corrosion rate time of required decorative pattern;
Wash deparaffnize and hydrofluoric acid with water.
Optionally, in the manufacture method of described art glass, described surperficial sense organ process comprises: put by described ground glass and into the liquidly carry out immersion treatment.
Optionally, in the manufacture method of described art glass, described some bonding silica gel treatment comprises: silica gel layout be bonded on the surface of described ground glass with the form put or sheet distributes.
Optionally, in the manufacture method of described art glass, carry out doubling fixing before, after described glass unit completes, also comprise: car edge polishing is carried out to described glass unit.
Optionally, in the manufacture method of described art glass, the manufacturing process of described laminated glass comprises air brushing process, and described air brushing process adopts digital air brushing technology.
Optionally, in the manufacture method of described art glass, described skin glass, laminated glass and bottom glass are carried out doubling fixing before, after described multiple pieces of glass unit completes, adopt fissure of displacement connecting method to be layed on described laminated glass by described multiple pieces of glass unit.
Optionally, in the manufacture method of described art glass, the starting resistor of described autoclave is between 300 kilowatts to 400 kilowatts, and operating voltage is between 250 kilowatts to 300 kilowatts, temperature in described autoclave is between 120 DEG C to 160 DEG C, and the firing time is between 5 hours to 10 hours.
Optionally, in the manufacture method of described art glass, the starting resistor of described autoclave is 350 kilowatts, and operating voltage is 280 kilowatts, and the temperature in described autoclave keeps 140 DEG C, and the firing time is 7 hours.
In the art glass provided in the embodiment of the present invention and manufacture method thereof, adopt triplex glass doubling ruggedized construction to improve the intensity of described art glass, simultaneously, described art glass skin glass formed by multiple pieces of glass unit spliced, therefore large module finished product can not only be made, and described art glass can be made to be heated evenly in sintering procedure, prevent explosion.
Accompanying drawing explanation
Fig. 1 is the sectional view of the art glass of the embodiment of the present invention;
Fig. 2 is the fragmentary elevational view of the art glass of the embodiment of the present invention;
Fig. 3 is the schematic flow sheet of the manufacture method of the art glass of the embodiment of the present invention.
Detailed description of the invention
The art glass proposed the present invention below in conjunction with the drawings and specific embodiments and manufacture method thereof are described in further detail.According to the following describes and claims, advantages and features of the invention will be clearer.It should be noted that, accompanying drawing all adopts the form that simplifies very much and all uses non-ratio accurately, only in order to object that is convenient, the aid illustration embodiment of the present invention lucidly.
Please refer to Fig. 1, it is the sectional view of the art glass of the embodiment of the present invention.As shown in Figure 1, described art glass 10 comprises: skin glass 11, laminated glass 12 and bottom glass 13; Described laminated glass 12 is arranged between described skin glass 11 and bottom glass 13, and is fixed by doubling layer 14 and described skin glass 11 and bottom glass 13; Described skin glass 11 comprises the glass unit 11a that polylith splices mutually.
Concrete, consider the feature of Glass breadks easily, described art glass 10 adopts triplex glass doubling ruggedized construction, to increase its bulk strength.As shown in Figure 1, described laminated glass 12 is arranged between described skin glass 11 and bottom glass 13, be provided with transparent doubling layer 14 between described skin glass 11 and laminated glass 12, between described laminated glass 12 and bottom glass 13, described laminated glass 12 is fixedly connected with bottom glass 13 with described skin glass 11 respectively by described transparent doubling layer 14.
Please refer to Fig. 2, it is the fragmentary elevational view of the art glass of the embodiment of the present invention.As shown in Figure 2, described skin glass 11 comprises the glass unit 11a that polylith splices mutually.Described multiple pieces of glass unit 11a combines mutually in fissure of displacement splicing (misspelled) mode, forms described skin glass 11.Wherein, the shape of described glass unit 11a is polygon, such as triangle, rectangle, rhombus, pentagon etc., and the concrete shape of described glass unit 11a, size and quantity are determined according to the product design of described art glass 10, do not limit at this.
In the present embodiment, described skin glass 11 is etching glass, and described laminated glass 12 is stained glass, and described bottom glass 13 is ultra-clear glasses.Described art glass 10 is formed through heat pressure adhesive by described etching glass, stained glass and ultra-clear glasses.
Wherein, described laminated glass 12 is a monoblock stained glass, described bottom glass 13 is a monoblock ultra-clear glasses, described skin glass 11 comprises the glass unit 11a that polylith splices mutually, and described multiple pieces of glass unit 11a adopts fissure of displacement splicing (misspelled) mode to be mutually combined to form described etching glass.Described stained glass is arranged between described etching glass and ultra-clear glasses, more easily protects it to be in bright colors.The etching glass being positioned at top layer can protect the color and luster and Color that are positioned at middle stained glass effectively, utilizes the light transmission of described etching glass, perfection can represent its artistic effect.Described ultra-clear glasses can improve the intensity of described art glass 10, makes described art glass 10 not easily broken in transport, use procedure, thus the rate that reduces the wastage.
In order to ensure the light transmission of described art glass 10, the ingredient requirement of described stained glass adopts permeability good and the specific glass that self-destruction rate is low.In the present embodiment, the raw material of described stained glass adopts ultra-clear glasses, and described stained glass is processed through dyeing by ultra-clear glasses.Ultra-clear glasses (English name: UltraClear Glass, Super Clear Glass, Super White Glass or low iron glass) be a kind of super transparent low iron glass, also claim low iron glass, high-transparent glass, its light transmittance is more than 91.5%.Ultra-clear glasses is after chemical treatment, and its surface still can keep, without folding line, not coarse smoothness, also not easily bursting, and having good permeability, be therefore highly suitable for the making of stained glass when high-temperature firing.Select ultra-clear glasses as the base material of described stained glass, described stained glass not only can be made to possess excellent light transmission, and the real embodiment of dyeing texture can be ensured.Described stained glass is not only bright and lustrous, prolonged constant, and can make through light become soft, avoid dazzle, and effectively absorb the ultraviolet of the sun, prevent fading and metamorphism to indoor article.
In the present embodiment, in order to avoid leaving the impressions such as hand fat, grease because of glass surface in machine-shaping process, cause light refraction and affect perception effect, described ultra-clear glasses is the self-cleaning coat nanometer sand glass adopting nanometer technology to make, the surface of glass is formed with a nano thin-film, makes dust, greasy dirt etc. be difficult to attachment.Described self-cleaning coat nanometer sand glass not only keeps the characteristic of ultra-clear glasses, and has more excellent hydrophily, has self-cleaning function.
The raw material of described etching glass also adopts ultra-clear glasses, the glass unit 11a forming described etching glass processes through etch process by ultra-clear glasses, namely utilize etchant (such as hydrofluoric acid) to corrode the glass unit 11a scribed, make the surface of glass unit 11a form word, pattern or its any combination.And, the surface of described glass unit 11a through special liquid process, its surface not only gloss evenly and also hand touch impulse-free robustness sense.
The thickness of described etching glass, stained glass and ultra-clear glasses is generally determined according to the shape of goods and requirement.Preferably, the thickness range of described etching glass is between 3mm to 8mm, and the thickness range of described stained glass is between 6mm to 10mm, and the thickness range of described ultra-clear glasses is between 8mm to 15mm.Preferably, the thickness of the doubling layer 14 between described etching glass and stained glass, between described stained glass and ultra-clear glasses is all between 0.5mm to 2mm.Such as, the thickness of described etching glass, stained glass and ultra-clear glasses be respectively 5mm, 8mm and 10mm, the thickness of the doubling layer 14 between described etching glass and stained glass, between described stained glass and ultra-clear glasses is 1.14mm.
In the present embodiment, described art glass 10 adopts triplex glass doubling ruggedized construction, its intensity is better than traditional art glass, and, the skin glass 11 of described art glass 10 is combined with fissure of displacement connecting method by multiple pieces of glass unit 11a, makes heat energy enter the laminated glass 12 of described skin glass 11 inside equably by space, and described laminated glass 12 also can thermally equivalent in sintering procedure, shrink synchronous, thus prevent explosion.Thus make large module finished product.Further, the surface of described art glass 10 is through special process process, and smooth surface is without impression, easy cleaning, easy to use and bear dirty.
Wherein, described skin glass 11 also can make the form such as mosaic glass (damascene, Englishly to inlay, conventional damascene etc.), engraved glass, sand blasting glass, sticking glass, embossment through other PROCESS FOR TREATMENT, thus makes the form of described art glass 10 abundanter.
Accordingly, the present embodiment additionally provides a kind of manufacture method of art glass.Incorporated by reference to referring to figs. 1 to Fig. 3, the manufacture method of described art glass comprises the following steps:
S10: make skin glass 11, laminated glass 12 and bottom glass 13 respectively, described skin glass 11 comprises the glass unit 11a that polylith splices mutually;
S11: described skin glass 11, laminated glass 12 and bottom glass 13 is carried out doubling and fixes;
S12: the semi-finished product after being fixed by doubling are put into autoclave and formed by a firing.
Concrete, first, select the ultra-clear glasses of different-thickness according to shape and the requirement of described art glass 10, and it is cleaned and drying, be presented on the surface of art glass 10 to prevent dirt, grease, filth etc.Clean after drying, make skin glass 11, laminated glass 12 and bottom glass 13 respectively.
In the present embodiment, the raw material of described skin glass 11, laminated glass 12 and bottom glass 13 selects thickness to be the ultra-clear glasses of 5mm, 8mm and 10mm respectively.Described ultra-clear glasses is the self-cleaning coat nanometer sand glass adopting nanometer technology to make, and can avoid, because glass surface leaves the impressions such as hand fat, grease in machine-shaping process, causing light refraction and affecting perception effect.
Wherein, the ultra-clear glasses cutting that described bottom glass 13 is directly 10mm by thickness forms, the ultra-clear glasses that described laminated glass 12 is 8mm by thickness is made through dyeing, dye process comprises air brushing process, pigment is used to form printing pattern at glass surface, the spraying painting pigment that described air brushing process uses can make different color lumps at rugged interface naturally soft conjunction excessive, and the nondiscolouring when high-temperature firing, colour-fast.Described printing pattern is by computer design and making.After air brushing process, the surface of described laminated glass 12 defines required word or pattern.
In the present embodiment, described air brushing process adopts digital air brushing technology, therefore can realize DIY design, make personalized printing pattern, does not need to rely on the technology of drawing teacher to carry out finishing patterns and draws.Not only precision is high, effective to utilize digital air brushing technology, and the deduction in conjunction with threedimensional model more can show perspective, the decorative pattern of three-dimensional stereo effect and pattern, magnificent mansion.Due to the effect of works just can be seen before carrying out air brushing process, be convenient to make amendment in time, make finished product more be close to customer demand, thus reduce rework rate.And being beneficial to digital air brushing technology can improve working (machining) efficiency greatly, the process-cycle is made to shorten 2/3.
To be that the glass unit 11a of 5mm is misspelled by polylith thickness form described skin glass 11.The making step of described glass unit 11a comprises: make ground glass; Surperficial sense organ process is carried out to described ground glass; A bonding silica gel treatment is carried out to described ground glass; Surface etching process is carried out to described ground glass.
Wherein, the manufacturing process of described ground glass comprises: first, using thickness be 5mm ultra-clear glasses horizontal and in its surface the paraffin liquid that dissolves of coating gasoline as protective layer; Then, the word on paraffin layer after hardening required for carve or pattern, must carve paraffin layer during engraving, exposes described ultra-clear glasses; Then, hydrofluoric acid is dripped on the word exposing described ultra-clear glasses or pattern, according to the depth control corrosion rate time of required decorative pattern; After this, wash deparaffnize and hydrofluoric acid with water, the ground glass with beautiful decorative pattern can be obtained.
The process of carrying out surperficial sense organ process to described ground glass comprises described ground glass to put into the liquidly carries out immersion treatment.After liquid immersion treatment, the surface of described glass unit 11a not only gloss evenly and also hand touch impulse-free robustness sense, so both can ensure definition and the stereovision of described art glass 10 superficial makings, solve again the out-of-flatness of traditional art glass surface, not the problem of easy cleaning.
Carry out a process of bonding silica gel treatment to described ground glass to comprise putting or silica gel to be arranged and is bonded on the surface of described ground glass, to show the artistic skin texture of glass surface and to need the specific region of etching by the form of sheet distribution.
Described ground glass is carried out that surface etching process refers to that the ground glass after to a bonding silica gel treatment carries out that entirety immerses, balanced flowing, local sprinkle etch process such as washing, to form the effects such as frosted, ripples, irregular grain on its surface.After surface etching treatment process completes, remove the silica gel of remained on surface, thus obtain described glass unit 11a.
Wherein, according to the modeling requirement of art glass, point bonding silica gel treatment and surface etching process can be repeatedly, namely the hollow repeatedly utilizing silica gel to fill and lead up surface etching process to corrode out at glass surface, to meet different printing opacity direction requirements, repeatedly operation superposes thus completes overall etching design.
After described glass unit 11a makes, also need to carry out car edge polishing to it, make its edge more smooth.Before folder glue pellet, the multiple pieces of glass unit 11a after car edge polishing is layed on described laminated glass 12 with fissure of displacement arrangement mode, forms skin glass 11.Because the edge of described glass unit 11a is through polishing, splicing edge unusual light, the skin glass 11 after having spliced can not affect its surface smoothness and aesthetics because of misspelled, also can prevent refraction effect.
Afterwards, doubling is carried out to described skin glass 11, laminated glass 12 and bottom glass 13 and fixes, realize superposition and close sheet.After doubling is fixing, all define transparent doubling layer 14 between described bottom glass 13 and laminated glass 12, between described laminated glass 12 and skin glass 11, described doubling layer 14 makes described laminated glass 12 closely be bonded together with described bottom glass 13 and skin glass 11 respectively.As shown in Figure 1, one surface of described stained glass is fixed by doubling layer 14 and the etching glass that described multiple pieces of glass unit 11a is spliced, another surface of described stained glass is fixed by doubling layer 14 and described ultra-clear glasses, described ultra-clear glasses, stained glass and etching glass realize superposition and close sheet, and one-tenth is integrated.
Finally, the semi-finished product after being fixed by doubling are put into autoclave and are heated, and form by a firing.In sintering procedure, because etching glass is misspelled by the glass unit 11a of fritter, space is left between glass unit 11a, therefore heat energy is entered in the stained glass of interlayer equably by space, make stained glass thermally equivalent, shrink synchronous, thus avoid semi-finished product that explosion problem occurs because being heated inequality.And the space between described glass unit 11a slowly closes up when heat energy inputs, and compresses shaping, thus adds globality when not affecting the appearance.Described art glass 10 through high-temperature firing, not only can improve its globality and intensity after cold treatment, also can reinforce the laminating degree of color and can not fade, thus ideally instructions for use and aesthetics being combined together.
Autoclave has heat transfer unit (HTU) and controller, temperature-visualized, controlled, therefore, it is possible in sintering procedure, control internal pressure, temperature, situation of being heated, ensure the balanced temperature adjustment of sintering procedure.The actual temp heated and time are determined according to glass kind, thickness and processing graphic pattern, and the process conditions of heating require that the art glass 10 after heating meets artistic effect and the application safety intensity of its design.In the present embodiment, the starting resistor of autoclave is 350 kilowatts, and the operating voltage firing the stage at constant temperature controls at 280 kilowatts, and the temperature in autoclave keeps 140 DEG C, and the firing time controlled at 7 hours.
After firing end, define described art glass 10.
Adopt the manufacture method of described art glass the pieces of glass of various geometry can be combined to form the art glass 10 of large module in the mode that the fissure of displacement splices; in process, utilize the principle of expanding with heat and contract with cold, not affecting under the prerequisite of product aesthetic can cover glass effectively.The finished product module of described art glass 10 is large, and be applicable to the large glass goods such as wall, artistic background, facing decoration, lamp box, furniture, indoor and outdoor window, application is more extensive.And the surface of described art glass 10 is through special process process, and texture is more clear, smooth surface is without impression, easy cleaning, easy to use and bear dirty.
The manufacture method of the art glass that the present embodiment provides breaches traditional handicraft, cold working and heat processing technique are fused to a set of novel forming technology completed, the light transmission of described art glass 10, aesthetics and intensity are obtained for promote widely, simultaneously, utilize the artificial colored drawing of digitlization colored drawing technical substitution, realize personalization, high accuracy and high image quality, not only can ensure end product quality, be conducive to the quality management and control of producing in batches, and shorten the process-cycle widely.
To sum up, in the art glass provided in the embodiment of the present invention and manufacture method thereof, described art glass adopts triplex glass doubling ruggedized construction to improve its intensity, prevents fragmentation.And the skin glass of described art glass is formed by multiple pieces of glass unit spliced, therefore not only can make large module finished product, and it is more even that described art glass can be made to be heated in sintering procedure, prevents explosion.
Foregoing description is only the description to present pre-ferred embodiments, any restriction not to the scope of the invention, and any change that the those of ordinary skill in field of the present invention does according to above-mentioned disclosure, modification, all belong to the protection domain of claims.
Claims (16)
1. an art glass, is characterized in that, comprising: skin glass, laminated glass and bottom glass; Described laminated glass is arranged between described skin glass and bottom glass, and is fixed by doubling layer and described skin glass and bottom glass; Described skin glass comprises the glass unit that polylith splices mutually.
2. art glass as claimed in claim 1, it is characterized in that, the raw material of described skin glass, laminated glass and described bottom glass all select ultra-clear glasses.
3. art glass as claimed in claim 2, it is characterized in that, described ultra-clear glasses is self-cleaning coat nanometer sand glass.
4. art glass as claimed any one in claims 1 to 3, it is characterized in that, described skin glass is etching glass, and described laminated glass is stained glass.
5. art glass as claimed in claim 1, it is characterized in that, the thickness range of described skin glass is between 3mm to 8mm, the thickness range of described laminated glass is between 6mm to 10mm, the thickness range of described bottom glass is between 8mm to 15mm, and the thickness range of described doubling layer is between 0.5mm to 2mm.
6. art glass as claimed in claim 5, it is characterized in that, the thickness of described skin glass is 5mm, and the thickness of described laminated glass is 8mm, and the thickness of described bottom glass is 10mm, and the thickness of described doubling layer is 1.14mm.
7. a manufacture method for art glass, is characterized in that, comprising:
Make skin glass, laminated glass and bottom glass respectively, described skin glass comprises the glass unit that polylith splices mutually;
Described skin glass, laminated glass and bottom glass are carried out doubling fix; And
Semi-finished product after being fixed by doubling are put into autoclave and are formed by a firing.
8. the manufacture method of art glass as claimed in claim 7, it is characterized in that, the manufacturing process of described glass unit comprises:
Make ground glass;
Surperficial sense organ process is carried out to described ground glass;
A bonding silica gel treatment is carried out to described ground glass;
Surface etching process is carried out to described ground glass;
Remove the silica gel of described ground glass remained on surface.
9. the manufacture method of art glass as claimed in claim 8, is characterized in that, the process making ground glass comprises:
By ultra-clear glasses horizontal, and at its surface coating paraffin liquid as protective layer;
Word on paraffin layer after hardening required for carve or pattern;
Hydrofluoric acid is dripped on described word or pattern, and according to depth control corrosion rate time of required decorative pattern;
Wash deparaffnize and hydrofluoric acid with water.
10. the manufacture method of art glass as claimed in claim 8, it is characterized in that, described surperficial sense organ process comprises: put by described ground glass and into the liquidly carry out immersion treatment.
The manufacture method of 11. art glasses as claimed in claim 8, it is characterized in that, described some bonding silica gel treatment comprises: silica gel layout be bonded on the surface of described ground glass with the form put or sheet distributes.
The manufacture method of 12. art glasses as claimed in claim 8, is characterized in that, carry out doubling fixing before, after described glass unit completes, also comprise: car edge polishing is carried out to described glass unit.
The manufacture method of 13. art glasses as claimed in claim 7, it is characterized in that, the manufacturing process of described laminated glass comprises air brushing process, and described air brushing process adopts digital air brushing technology.
The manufacture method of 14. art glasses as claimed in claim 7, it is characterized in that, described skin glass, laminated glass and bottom glass are carried out doubling fixing before, after described multiple pieces of glass unit completes, fissure of displacement connecting method is adopted to be layed on described laminated glass by described multiple pieces of glass unit.
The manufacture method of 15. art glasses according to any one of claim 7 to 14, it is characterized in that, the starting resistor of described autoclave is between 300 kilowatts to 400 kilowatts, operating voltage is between 250 kilowatts to 300 kilowatts, temperature in described autoclave is between 120 DEG C to 160 DEG C, and the firing time is between 5 hours to 10 hours.
The manufacture method of 16. art glasses as claimed in claim 15, is characterized in that, the starting resistor of described autoclave is 350 kilowatts, and operating voltage is 280 kilowatts, and the temperature in described autoclave keeps 140 DEG C, and the firing time is 7 hours.