CN104442167B - Art glass and its manufacturing method - Google Patents
Art glass and its manufacturing method Download PDFInfo
- Publication number
- CN104442167B CN104442167B CN201410619687.7A CN201410619687A CN104442167B CN 104442167 B CN104442167 B CN 104442167B CN 201410619687 A CN201410619687 A CN 201410619687A CN 104442167 B CN104442167 B CN 104442167B
- Authority
- CN
- China
- Prior art keywords
- glass
- art
- manufacturing
- skin
- doubling
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention relates to a kind of art glass and its manufacturing method, wherein, the art glass includes：Skin glass, laminated glass and bottom glass；The laminated glass is set between the skin glass and bottom glass, and is passed through doubling layer and fixed with the skin glass and bottom glass；The skin glass includes the glass unit that polylith mutually splices.In art glass provided by the invention and its manufacturing method, triplex glass doubling ruggedized construction is used to improve the intensity of the art glass, simultaneously, the skin glass of the art glass is formed by multiple pieces of glass unit spliced, therefore it is not only able to that big module finished product is made, and the art glass is enabled to be heated evenly in sintering procedure, it prevents from bursting.
Description
Technical field
The present invention relates to glassmaking art, more particularly to a kind of art glass and its manufacturing method.
Background technology
Art glass is a kind of using glass as carrier, embodies design concept and the glassware of art of expression effect.Art
Glass it is with a long history, technical matters level is also increasingly mature.As people are to the attention of indoor decorative effect and sense organ body
The promotion tested, art glass are widely used, and charming and noble visual effect is favored by more and more people.
Traditional art glass processing technology is divided into two kinds：Heat processing technique and cold machining process.Cold machining process be
Various surface effect is formed, then 593 DEG C are not higher than with temperature by grinding the modes such as quarter, sandblasting, artificial colored drawing under normal temperature environment
Kiln heated, cooling after obtain finished product.Heat processing technique be under 593 DEG C or more of hot environment by blowing,
The modes such as thermoplastic, doubling are processed glass baseplate, and finished product is obtained after cooling.
Wherein, the manufacture craft of artistic color glass generally uses high temperature colored glaze color or colored drawing on the glass surface, such as
Colored glaze color glass, colored glaze colored drawing etc..In order to reach the requirement of permeability, traditional artistic color glass is usually using single-glass system
Into.High using artistic color glass brittleness made of single-glass, intensity is low, also extremely fragile during transport and use.
Moreover, traditional artistic color glass easily bursts when carrying out high-temperature firing, easily fade after high-temperature firing, influence its effect
Fruit.The manufacture craft of artistic doubling glass is usually the marble paper using figured cloth, colored glued membrane, woven wire material as sandwich of layers,
Its form is although various, but relatively simple compared in effect for stained glass, and artistic feeling is not strong.
For traditional art glass processing technology due to the limitation of technique, the finished product module of various art glasses is all smaller,
And in the case where pattern requirement is higher, need by manually drawing a design, not only process time is longer, and difficult to realize
Produce in enormous quantities.
Invention content
The purpose of the present invention is to provide a kind of art glass and its manufacturing method, to solve adding for existing art glass
It is long between working hour, it easily bursts in sintering procedure, the problem of finished product module is small and frangible.
In order to solve the above technical problems, the present invention provides a kind of art glass, the art glass includes：Skin glass,
Laminated glass and bottom glass；The laminated glass is set between the skin glass and bottom glass, and passes through doubling layer
It is fixed with the skin glass and bottom glass；The skin glass includes the glass unit that polylith mutually splices.
Optionally, in the art glass, the raw material of the skin glass, laminated glass and the bottom glass
Select ultra-clear glasses.
Optionally, in the art glass, the ultra-clear glasses are self-cleaning coat nanometer sand glass.
Optionally, in the art glass, the skin glass is etching glass, and the laminated glass is dyeing glass
Glass.
Optionally, in the art glass, the thickness range of the skin glass is between 3mm to 8mm, the folder
The thickness range of layer glass is between 6mm to 10mm, and the thickness range of the bottom glass is between 8mm to 15mm, the folder
The thickness range of glue-line is between 0.5mm to 2mm.
Optionally, in the art glass, the thickness of the skin glass is 5mm, the thickness of the laminated glass
For 8mm, the thickness of the bottom glass is 10mm, and the thickness of the doubling layer is 1.14mm.
Correspondingly, the present invention also provides a kind of manufacturing method of art glass, the manufacturing method of the art glass includes：
Skin glass, laminated glass and bottom glass are made respectively, and the skin glass includes the glass that polylith mutually splices
Glass unit；
The skin glass, laminated glass and bottom glass progress doubling are fixed；And
Semi-finished product after doubling is fixed are put into autoclave and form by a firing.
Optionally, in the manufacturing method of the art glass, the manufacturing process of the glass unit includes：
Make ground glass；
Surface sense organ processing is carried out to the ground glass；
A bonding silica gel treatment is carried out to the ground glass；
Surface etching processing is carried out to the ground glass；
Remove the silica gel of the ground glass remained on surface.
Optionally, in the manufacturing method of the art glass, the process for making ground glass includes：
Paraffin liquid is coated with as protective layer by ultra-clear glasses horizontal, and on its surface；
Required word or pattern are carved out on paraffin layer after hardening；
By hydrofluoric acid drop on the word or pattern, and according to the depth control corrosion rate time of required decorative pattern；
Deparaffnize and hydrofluoric acid is washed with water.
Optionally, in the manufacturing method of the art glass, the surface sense organ processing includes：By the frosted glass
Glass puts into the liquid carry out immersion treatment.
Optionally, in the manufacturing method of the art glass, described bonding silica gel treatment includes：With point or sheet
Silica gel arrangement is bonded on the surface of the ground glass by the form of distribution.
Optionally, in the manufacturing method of the art glass, before doubling fixation is carried out, in the glass unit
After completing, further include：To the glass unit into driving edge polishing.
Optionally, in the manufacturing method of the art glass, the manufacturing process of the laminated glass is included at air brushing
Reason, the air brushing processing is using Digital printing technology.
Optionally, in the manufacturing method of the art glass, by the skin glass, laminated glass and bottom glass
Before glass carries out doubling fixation, after the multiple pieces of glass unit completes, using fissure of displacement connecting method by the polylith
Glass unit is layed on the laminated glass.
Optionally, in the manufacturing method of the art glass, the startup voltage of the autoclave is arrived at 300 kilowatts
Between 400 kilowatts, operating voltage between 250 kilowatts to 300 kilowatts, temperature in the autoclave 120 DEG C to 160 DEG C it
Between, the firing time is between 5 hours to 10 hours.
Optionally, in the manufacturing method of the art glass, the startup voltage of the autoclave is 350 kilowatts, work
It is 280 kilowatts to make voltage, and the temperature in the autoclave is kept for 140 DEG C, and the firing time is 7 hours.
In art glass provided in an embodiment of the present invention and its manufacturing method, use triplex glass doubling ruggedized construction with
Improve the intensity of the art glass, meanwhile, the skin glass of the art glass by multiple pieces of glass unit spliced and
Into, therefore be not only able to big module finished product be made, and the art glass is enabled to be heated evenly in sintering procedure, prevent
Only burst.
Description of the drawings
Fig. 1 is the sectional view of the art glass of the embodiment of the present invention；
Fig. 2 is the fragmentary elevational view of the art glass of the embodiment of the present invention；
Fig. 3 is the flow diagram of the manufacturing method of the art glass of the embodiment of the present invention.
Specific embodiment
Art glass proposed by the present invention and its manufacturing method are made below in conjunction with the drawings and specific embodiments further detailed
It describes in detail bright.According to following explanation and claims, advantages and features of the invention will become apparent from.It should be noted that attached drawing is equal
Using very simplified form and using non-accurate ratio, only to convenience, the embodiment of the present invention is lucidly aided in illustrating
Purpose.
It please refers to Fig.1, is the sectional view of the art glass of the embodiment of the present invention.As shown in Figure 1, the art glass 10
Including：Skin glass 11, laminated glass 12 and bottom glass 13；The laminated glass 12 is set to the skin glass 11 and bottom
Between layer glass 13, and pass through doubling layer 14 and fixed with the skin glass 11 and bottom glass 13；The skin glass 11 is wrapped
Include the glass unit 11a that polylith mutually splices.
Specifically, the characteristics of in view of Glass breadks easily, the art glass 10 uses triplex glass doubling ruggedized construction, with
Increase its integral strength.As shown in Figure 1, the laminated glass 12 is set between the skin glass 11 and bottom glass 13,
Transparent folder is both provided between the skin glass 11 and laminated glass 12, between the laminated glass 12 and bottom glass 13
Glue-line 14, the laminated glass 12 are solid with the skin glass 11 and bottom glass 13 respectively by the transparent doubling layer 14
Fixed connection.
It please refers to Fig.2, is the fragmentary elevational view of the art glass of the embodiment of the present invention.As shown in Fig. 2, the surface layer glass
Glass 11 includes the glass unit 11a that polylith mutually splices.The multiple pieces of glass unit 11a is mutual in a manner that the fissure of displacement splices (misspelled)
Combination, forms the skin glass 11.Wherein, the shape of the glass unit 11a is polygon, such as triangle, rectangle, water chestnut
Shape, pentagon etc., the concrete shape of the glass unit 11a, size and number are according to the product design of the art glass 10
Depending on, it does not limit herein.
In the present embodiment, the skin glass 11 for etching glass, the laminated glass 12 be stained glass, the bottom
Glass 13 is ultra-clear glasses.The art glass 10 by the etching glass, stained glass and ultra-clear glasses through heat pressure adhesive and
Into.
Wherein, the laminated glass 12 be a monoblock stained glass, the bottom glass 13 be a monoblock ultra-clear glasses, institute
It states skin glass 11 and includes the glass unit 11a that polylith mutually splices, it is (wrong that the multiple pieces of glass unit 11a uses the fissure of displacement to splice
Spell) mode is combined with each other to form the etching glass.The stained glass is set between the etching glass and ultra-clear glasses,
It is more easy to that it is protected to be in bright colors.Etching glass positioned at surface layer can effectively protect positioned at intermediate stained glass color and luster and
Coloring, using it is described etching glass translucency, can perfection show its artistic effect.The ultra-clear glasses can improve
The intensity of the art glass 10 so that the art glass 10 is not easily broken during transport, use, so as to reduce loss
Rate.
In order to ensure the translucency of the art glass 10, the ingredient requirement of the stained glass uses permeability good and oneself
The low specific glass of quick-fried rate.In the present embodiment, the raw material of the stained glass is using ultra-clear glasses, and the stained glass is by ultrawhite
Glass is process by dyeing.Ultra-clear glasses (English name：Ultra Clear Glass, Super Clear
Glass, Super White Glass or low iron glass) it is a kind of super transparent low iron glass, also referred to as low iron glass, height
Transparent glass, light transmittance is more than 91.5%.For ultra-clear glasses after chemical treatment, surface still can keep nothing
Folding line, not coarse smoothness, are not easy to burst in high-temperature firing, and with good permeability, therefore are applicable in very much
In the making of stained glass.Base material of the ultra-clear glasses as the stained glass is selected, not only can have the stained glass
Excellent translucency, and can ensure to dye the real embodiment of texture.The stained glass is not only bright and lustrous, it is prolonged not
Become, and the light of transmission can be made to become soft, avoid dazzle, and effectively absorb the ultraviolet light of the sun, prevent to interior
The colour fading and metamorphism of article.
In the present embodiment, in order to avoid because during machine-shaping glass surface there are marks such as hand fat, greases, lead to light
Line reflects and influences perception effect, and the ultra-clear glasses are using self-cleaning coat nanometer sand glass made of nanometer technology, glass
Surface be formed with a nano thin-film so that dust, greasy dirt etc. are difficult to adhere to.The self-cleaning coat nanometer sand glass is not only kept
The characteristic of ultra-clear glasses, and with more excellent hydrophily, there is self-cleaning function.
The raw material of the etching glass also using ultra-clear glasses, forms the glass unit 11a of the etching glass by super
White glass is process by etch process, i.e., corrodes the glass unit 11a scribed using etchant (such as hydrofluoric acid), make
The surface of glass unit 11a forms word, pattern or its arbitrary combination.Moreover, the surface of the glass unit 11a is by special
Liquid processing, not only gloss is uniformly but also hand touches impulse- free robustness sense on surface.
The thickness of the etching glass, stained glass and ultra-clear glasses is generally depending on the shape of product and requirement.It is excellent
Choosing, the thickness range of the etching glass between 3mm to 8mm, the thickness range of the stained glass 6mm to 10mm it
Between, the thickness range of the ultra-clear glasses is between 8mm to 15mm.Preferably, it is described etching glass and stained glass between, institute
The thickness of the doubling layer 14 between stained glass and ultra-clear glasses is stated between 0.5mm to 2mm.For example, the etching glass,
Stained glass and the thickness of ultra-clear glasses are respectively 5mm, 8mm and 10mm, between the etching glass and stained glass, described
The thickness of doubling layer 14 between stained glass and ultra-clear glasses is 1.14mm.
In the present embodiment, the art glass 10 uses triplex glass doubling ruggedized construction, and intensity is better than traditional
Art glass, moreover, the skin glass 11 of the art glass 10 by multiple pieces of glass unit 11a with fissure of displacement connecting method combines and
Into so that by gap evenly into the laminated glass 12 inside the skin glass 11, the laminated glass 12 exists thermal energy
In sintering procedure also can thermally equivalent, shrink synchronize, so as to prevent explosion.So as to which big module finished product be made.Further,
The surface of the art glass 10 is handled by special process, the smooth no mark in surface, easy cleaning, easy to use and bear dirty.
Wherein, the skin glass 11 can also make mosaic glass (damascene, English edge by other process
Embedding, conventional damascene etc.), engraved glass, sand blasting glass, paste glass, the forms such as embossment, so as to allow the shape of the art glass 10
Formula is more abundant.
Correspondingly, the present embodiment additionally provides a kind of manufacturing method of art glass.It is described incorporated by reference to referring to figs. 1 to Fig. 3
The manufacturing method of art glass includes the following steps：
S10：Skin glass 11, laminated glass 12 and bottom glass 13 are made respectively, and the skin glass 11 includes polylith
The glass unit 11a mutually spliced；
S11：The skin glass 11, laminated glass 12 and bottom glass 13 are carried out doubling to fix；
S12：Semi-finished product after doubling is fixed are put into autoclave and form by a firing.
Specifically, first, the ultra-clear glasses of different-thickness are selected according to the shape of the art glass 10 and requirement, and right
It is cleaned and is dried, dirt, grease, filth etc. to be prevented to be shown on the surface of art glass 10.It cleans after drying, point
It Zhi Zuo not skin glass 11, laminated glass 12 and bottom glass 13.
In the present embodiment, the raw material of the skin glass 11, laminated glass 12 and bottom glass 13 selects the thickness to be respectively
The ultra-clear glasses of 5mm, 8mm and 10mm.The ultra-clear glasses are using self-cleaning coat nanometer sand glass, energy made of nanometer technology
It enough avoids, because there are the marks such as hand fat, grease for glass surface during machine-shaping, light being caused to reflect and influence perception effect.
Wherein, the bottom glass 13 is directly cut by the ultra-clear glasses that thickness is 10mm, the laminated glass 12
It is made of thickness of the ultra-clear glasses of 8mm by dyeing, dye process includes air brushing processing, using pigment in glass
Glass surface forms printing pattern, and the spraying painting pigment that the air brushing processing uses can make different color lumps at rugged interface
Naturally it is soft excessive and non-discolouring, colour-fast in high-temperature firing.The printing pattern is by computer design and makes.
After air brushing processing, required word or pattern are formd on the surface of the laminated glass 12.
In the present embodiment, the air brushing processing can realize that DIY is designed using Digital printing technology, make individual character
Change printing pattern, the technology for needing not rely on drawing teacher carrys out finishing patterns drafting.Using Digital printing technology, not only precision is high, imitates
Fruit is good, with reference to threedimensional model deduction more can show perspective, three-dimensional stereo effect decorative pattern and pattern, magnificent mansion.By
In the effect with regard to that can see works before air brushing processing is carried out, convenient for making modification in time, finished product is made to be needed closer in client
It asks, so as to reduce rework rate.Moreover, processing efficiency can be greatly improved conducive to Digital printing technology, shorten the process-cycle
2/3。
The skin glass 11 misspelled is formed by the glass unit 11a that polylith thickness is 5mm.The glass unit 11a's
Making step includes：Make ground glass；Surface sense organ processing is carried out to the ground glass；The ground glass is carried out a little
Bonding silica gel treatment；Surface etching processing is carried out to the ground glass.
Wherein, the manufacturing process of the ground glass includes：First, by thickness for the ultra-clear glasses horizontal of 5mm and at it
The paraffin liquid that coating gasoline dissolves on surface is as protective layer；Then, it is carved out on paraffin layer after hardening required
Word or pattern, when engraving, must carve paraffin layer, expose the ultra-clear glasses；Then, hydrofluoric acid is dripped described super in exposing
On the word or pattern of white glass, according to the depth control corrosion rate time of required decorative pattern；Hereafter, deparaffnize and hydrogen fluorine is washed with water
Acid, you can the ground glass with beautiful decorative pattern is made.
The process that surface sense organ processing is carried out to the ground glass includes the ground glass putting into the liquid progress
Immersion treatment.After liquid immersion treatment, not only gloss is uniformly but also hand touches impulse- free robustness sense on the surface of the glass unit 11a,
So the clarity and stereovision of 10 surface texture of art glass can be not only ensured, but also solve traditional art glass surface not
It is smooth, difficult cleaning of problem.
A process for bonding silica gel treatment is carried out to the ground glass to include silica gel in the form of point or sheet are distributed
Arrangement is bonded on the surface of the ground glass, to show the artistic skin texture of glass surface and need the specific region etched.
Ground glass progress surface etching processing is referred to carry out the ground glass after a bonding silica gel treatment whole
Body immerses, balanced flowing, part sprinkle and the etch process such as wash, equivalent to be formed on its surface frosted, ripples, irregular grain
Fruit.After surface etching treatment process is completed, the silica gel of remained on surface is removed, so as to obtain the glass unit 11a.
Wherein, according to the modeling requirement of art glass, putting bonding silica gel treatment and surface etching processing can be repeated as many times,
Silica gel is repeatedly utilized to fill and lead up the hollow that surface etching processing corrodes out in glass surface, it will to meet different light transmission directions
It asks, multiple process superposition is so as to complete whole etching design.
After the glass unit 11a is made, it is also necessary to it into driving edge polishing, make its edge more smooth.It is pressing from both sides
Before glue pellet, the multiple pieces of glass unit 11a after vehicle edge polishing is layed in fissure of displacement arrangement mode on the laminated glass 12,
Form skin glass 11.Since the edge of the glass unit 11a is by polishing, splicing edge is very smooth, after the completion of splicing
Skin glass 11 will not influence its surface smoothness and aesthetics because of misspelled, can also prevent refraction effect.
Later, it carries out doubling to the skin glass 11, laminated glass 12 and bottom glass 13 to fix, realizes that superposition is closed
Piece.After doubling is fixed, between the bottom glass 13 and laminated glass 12, between the laminated glass 12 and skin glass 11
Be respectively formed transparent doubling layer 14, the doubling layer 14 so that the laminated glass 12 respectively with the bottom glass 13 and table
Layer glass 11 is closely adhered to together.As shown in Figure 1, a surface of the stained glass passes through doubling layer 14 and the polylith
The etching glass that glass unit 11a is spliced is fixed, and another surface of the stained glass is surpassed by doubling layer 14 with described
White glass is fixed, and the ultra-clear glasses, stained glass and etching glass realize that piece is closed in superposition, are integrally formed.
Finally, the semi-finished product after doubling is fixed, which are put into autoclave, to be heated, and is formed by a firing.In sintering procedure
In, due to etching glass be by fritter glass unit 11a it is misspelled form, there are gap between glass unit 11a, therefore heat
It can be by gap evenly into the stained glass of interlayer so that stained glass thermally equivalent shrinks and synchronizes, so as to avoid half
Explosion problem occurs due to uneven heating for finished product.Moreover, the gap between the glass unit 11a is slowly closed when thermal energy inputs
Hold together, pressing molding, so as to increase globality in the case where not affecting the appearance.The art glass 10 after cold treatment by
High-temperature firing is not only able to improve its globality and intensity, can also reinforce the compactness of color and will not fade, so as to complete
Beauteously requirement and aesthetics are combined together.
Autoclave has heat transfer unit (HTU) and a controller, temperature-visualized, controllable, therefore inside being controlled in sintering procedure
Pressure, temperature, heated situation, ensure the balanced temperature adjustment of sintering procedure.The actual temp of heat treatment and time are according to glass object
Kind, thickness and processing graphic pattern and determine, the art glass 10 after the process conditions requirement of heat treatment is heated meets it and sets
The artistic effect of meter and using security intensity.In the present embodiment, the startup voltage of autoclave is 350 kilowatts, and rank is fired in constant temperature
The operating voltage of section is controlled at 280 kilowatts, and the temperature in autoclave is kept for 140 DEG C, and the firing time was controlled at 7 hours.
After firing, the art glass 10 is formd.
The side for using the manufacturing method of the art glass that can splice the pieces of glass of various geometries with the fissure of displacement
Formula combines the art glass 10 to form big module, in process using the principle expanded with heat and contract with cold, does not influence product beauty effect
It being capable of effectively protective glass under the premise of fruit.The finished product module of the art glass 10 is big, is carried on the back suitable for wall, art
Large glass product, the application fields such as scape, facing decoration, lamp box, furniture, indoor and outdoor window are more extensive.Moreover, the art
The surface of glass 10 is handled by special process, and texture is apparent, the smooth no mark in surface, easy cleaning, easy to use and bear dirty.
The manufacturing method of art glass provided in this embodiment breaches traditional handicraft, and cold working is melted with heat processing technique
It is combined into the novel forming technology of a set of completion so that translucency, aesthetics and the intensity of the art glass 10 are obtained for greatly
The earth is promoted, meanwhile, using the artificial colored drawing of colored drawing technical substitution is digitized, realize personalized, high-precision and high image quality, not only can
Enough ensure final product quality, be conducive to the quality management and control of batch production, and significantly shorten the process-cycle.
To sum up, in art glass provided in an embodiment of the present invention and its manufacturing method, the art glass uses three layers
Glass laminating ruggedized construction prevents from crushing to improve its intensity.Moreover, the skin glass of the art glass is by multiple pieces of glass list
Member is spliced, therefore is not only able to that big module finished product is made, and enable to the art glass in sintering procedure by
Heat is more uniform, prevents from bursting.
Foregoing description is only the description to present pre-ferred embodiments, not to any restriction of the scope of the invention, this hair
Any change, the modification that the those of ordinary skill in bright field does according to the disclosure above content, belong to the protection of claims
Range.
Claims (8)
1. a kind of manufacturing method of art glass, which is characterized in that including：
Skin glass, laminated glass and bottom glass are made respectively, and the skin glass is to use the fissure of displacement by multiple pieces of glass unit
Connecting method is combined with each other the etching glass to be formed, and the laminated glass is a monoblock stained glass, and the bottom glass is one
Monoblock ultra-clear glasses；
The skin glass, laminated glass and bottom glass progress doubling are fixed；And
Semi-finished product after doubling is fixed are put into autoclave and form by a firing；
Wherein, the manufacturing process of the glass unit includes：Make ground glass；The ground glass is carried out at the sense organ of surface
Reason；A bonding silica gel treatment is carried out to the ground glass；Surface etching processing is carried out to the ground glass；Remove the mill
The silica gel of sand glass remained on surface；
Wherein, the process for making ground glass includes：By ultra-clear glasses horizontal, and in its surface coating paraffin liquid as protection
Layer；Required word or pattern are carved out on paraffin layer after hardening；By hydrofluoric acid drop on the word or pattern, and
According to the depth control corrosion rate time of required decorative pattern；Deparaffnize and hydrofluoric acid is washed with water.
2. the manufacturing method of art glass as described in claim 1, which is characterized in that the surface sense organ processing includes：It will
The ground glass puts into the liquid carry out immersion treatment.
3. the manufacturing method of art glass as described in claim 1, which is characterized in that described bonding silica gel treatment includes：
Silica gel arrangement is bonded on the surface of the ground glass in the form of point or sheet are distributed.
4. the manufacturing method of art glass as described in claim 1, which is characterized in that before doubling fixation is carried out, in institute
It states after glass unit completes, further includes：To the glass unit into driving edge polishing.
5. the manufacturing method of art glass as described in claim 1, which is characterized in that the manufacturing process packet of the laminated glass
Air brushing processing is included, the air brushing processing is using Digital printing technology.
6. the manufacturing method of art glass as described in claim 1, which is characterized in that by the skin glass, interlayer glass
Before glass and bottom glass carry out doubling fixation, after the multiple pieces of glass unit completes, using fissure of displacement connecting method
The multiple pieces of glass unit is layed on the laminated glass.
7. such as the manufacturing method of art glass according to any one of claims 1 to 6, which is characterized in that the autoclave
Start voltage between 300 kilowatts to 400 kilowatts, operating voltage is between 250 kilowatts to 300 kilowatts, in the autoclave
Temperature is between 120 DEG C to 160 DEG C, and the firing time is between 5 hours to 10 hours.
8. the manufacturing method of art glass as claimed in claim 7, which is characterized in that the startup voltage of the autoclave is
350 kilowatts, operating voltage is 280 kilowatts, and the temperature in the autoclave is kept for 140 DEG C, and the firing time is 7 hours.