CN101396223B - Manufacture method of laminated glass decorative dish - Google Patents
Manufacture method of laminated glass decorative dish Download PDFInfo
- Publication number
- CN101396223B CN101396223B CN2008101233003A CN200810123300A CN101396223B CN 101396223 B CN101396223 B CN 101396223B CN 2008101233003 A CN2008101233003 A CN 2008101233003A CN 200810123300 A CN200810123300 A CN 200810123300A CN 101396223 B CN101396223 B CN 101396223B
- Authority
- CN
- China
- Prior art keywords
- glass
- plate
- manufacture method
- laminated glass
- decorative dish
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention provides a method for manufacturing a laminated glass ornamental plate which has beautiful appearance and is not decolored. First, plate glass is taken, ground and washed, material layer which form patterns are placed between two layers of plate glass, and then the material layer and the plate glass are integrally placed on a special die of the ornamental plate, sent to a kiln for heating to 800-870 DEG C for 25-35 minutes, and naturally cooled to normal temperature for demolding, and then the plate body is ground and polished. The laminated glass ornamental plate manufactured by the method is characterized in that: the patterns can be preserved for a long time, and the internal wall and external wall of the plate body do not contain pigment or heavy metal, and the plate can be used for multiple purposes, such as candle plates, dinner plates, fruit dishes, and the like.
Description
Technical field
The present invention relates to a kind of manufacture method of glassware, relate in particular to a kind of manufacture method of laminated glass decorative dish.
Background technology
Glassware enters daily life just more and more owing to its glittering and translucent texture obtains liking of people, purposes also more and more widely, people adopt glassware to be used as ornament, or splendid attire food, fruit etc.Raising along with people's living standard, more and more higher to aesthetic requirement, the utilization rate of colour glassware strengthens thereupon, owing to often contain harmful materials such as heavy metal in the stained glass, should not be used as service plate and use, the inwall colored drawing at disk body also will pollute food, and the painted adhesive force of glass is very poor, and often cleaning makes the glass decolouring easily and influences attractive in appearance.
Summary of the invention
The technical problem to be solved in the present invention provides the manufacture method of the laminated glass decorative dish of a kind of not only attractive in appearance but also nondiscoloration.
For solving above technical problem, the manufacture method of laminated glass decorative dish of the present invention comprises following manufacturing step:
(1) plate glass is got material, edging, cleaning;
(2) material layers that will constitute pattern is placed between the two-layer plate glass, whole again being placed on the particular manufacturing craft of decorated disk, and lower floor's plate glass is provided with air-vent;
(3) mould is sent into together with plate glass progressively be warming up to 800 ℃～870 ℃ in the kiln, make the softening molten stream of glass be fitted in the inner surface of mould, under this temperature, kept 25～35 minutes, cool off 30～40 minutes naturally, carry out the demoulding to normal temperature;
(4) disk body is carried out sanding and polishing.
The laminated glass decorative dish that this method manufacturing forms, pattern can keep for a long time, and the disk body inside and outside wall does not all contain pigment or heavy metal, can also be used as multiple uses such as candle dish, service plate, fruit dish.
Lower floor's plate glass is provided with air-vent.Flow through the air that is in the journey between the layer glass and can discharge smoothly softening molten like this, and do not influence the smooth of disk body inwall.
Plate glass is placed on the temperature that heats up in the kiln can be 840 ℃, and the time that keeps under this temperature can be 30 minutes.
The material layers that constitutes pattern can comprise thousand flower sheets, stainless steel wire, colored cullet or high temp glass pigment.
Description of drawings
Below in conjunction with the drawings and specific embodiments, the present invention is described in further detail.
Fig. 1 is the front view of a kind of embodiment of laminated glass decorative dish;
Fig. 2 is the vertical view of a kind of embodiment of laminated glass decorative dish;
Among the figure: 1 disk body, 2 internal layers, 3 material layers, 4 skins.
The specific embodiment
As shown in Figures 1 and 2, laminated glass decorative dish of the present invention comprises disk body, and disk body comprises internal layer, skin and material layers, and material layers is positioned at the disk body bottom, is clipped between the ectonexine, and its manufacture method comprises the steps:
(1) plate glass is got material, edging, cleaning;
(2) material layers that will constitute pattern is placed between the two-layer plate glass, whole again being placed on the particular manufacturing craft of decorated disk, and lower floor's plate glass is provided with air-vent, brushes releasing agent on the mould;
(3) plate glass and mould are sent in the stainless steel tunnel cave, progressively heated up while advance, according to the material of plate glass and the difference of thickness, be warming up to 800 ℃～870 ℃, for example be warming up to 840 ℃, make the softening molten stream of glass be fitted in the inner surface of particular manufacturing craft, under this temperature, kept 25～35 minutes, it for example is 30 minutes, then, carry out the nature cooling when moving on, cool off 30～40 minutes to normal temperature, carry out the demoulding after coming out of the stove, obtain the base dish;
(4) disk body is carried out sanding and polishing, obtain finished disk.
Claims (5)
1. the manufacture method of a laminated glass decorative dish is characterized in that its manufacture process comprises the steps:
(1) plate glass is got material, edging, cleaning;
(2) material layers that will constitute pattern is placed between the two-layer plate glass, whole again being placed on the particular manufacturing craft of decorated disk, and lower floor's plate glass is provided with air-vent;
(3) mould is placed on together with plate glass progressively is warming up to 800 ℃～870 ℃ in the kiln, make the softening inner surface that is fitted in mould of glass, under this temperature, kept 25～35 minutes, cool off 30～40 minutes naturally, carry out the demoulding to normal temperature;
(4) disk body is carried out sanding and polishing.
2. the manufacture method of laminated glass decorative dish according to claim 1 is characterized in that it is 840 ℃ that plate glass is placed on the temperature that heats up in the kiln, keeps 30 minutes under this temperature.
3. the manufacture method of laminated glass decorative dish according to claim 1 is characterized in that described material layers comprises thousand flower sheets.
4. the manufacture method of laminated glass decorative dish according to claim 1 is characterized in that described material layers comprises stainless steel wire.
5. the manufacture method of laminated glass decorative dish according to claim 1 is characterized in that described material layers comprises colored cullet or high temp glass pigment.