CN101633286B - Sandwich painting reinforced flat plate art glass and preparation method thereof - Google Patents
Sandwich painting reinforced flat plate art glass and preparation method thereof Download PDFInfo
- Publication number
- CN101633286B CN101633286B CN200910181969A CN200910181969A CN101633286B CN 101633286 B CN101633286 B CN 101633286B CN 200910181969 A CN200910181969 A CN 200910181969A CN 200910181969 A CN200910181969 A CN 200910181969A CN 101633286 B CN101633286 B CN 101633286B
- Authority
- CN
- China
- Prior art keywords
- glass
- painting
- sandwich
- flat plate
- art glass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention provides sandwich painting reinforced flat plate art glass and a preparation method thereof. A solid glue layer and a painting layer are arranged between two glass plate layers, the layers are mutually bonded and stacked to form the art glass. The preparation method comprises the following steps: sequentially stacking a plurality of layer surfaces as a workpiece, arranging one or a plurality of workpieces between an upper siliceous skin piece and a lower siliceous skin piece, sealing the siliceous skin pieces, vacuumizing and pushing into a high-temperature reinforcing furnace, and controlling a temperature range between 105 DEGC and 120 DEG C at constant temperature for 40-50 minutes; and when the temperature in the furnace is reduced below 100 DEG C, taking the siliceous skin pieces out, vacuumizing for several minutes and cooling to room temperature to obtain finished products. The surface of the sandwich painting reinforced flat plate art glass resists wear and sharp scratches, and the sandwich painting is bright as new in a long period. The sandwich painting reinforced flat plate art glass can be used as an ornament, has high intensity and high explosion-proof level, is safe and reliable, can be manufactured into art glass with various characteristics and can be selected and used by different crowds.
Description
Technical field
The present invention relates to the suitability for industrialized production technology of art glass, particularly a kind of sandwich painting reinforced flat plate art glass and preparation method thereof.
Background technology
Along with the raising of The development in society and economy, national life level, everybody also begins to pursue fine cultural life when enjoying material life.Advocate culture and arts and become current fashion.People economic is well-to-do, just buys new house, indoor decoration is got splendid, is full of cultural spirit and artistic atmosphere, almost is a kind of trend.In house decoraton, generally all adopt the glass plies that has various beautiful pictures sliding door as balcony, or in order to some cupboard door in the make-up room.So not only light transmission is good, and compares more vivaciously colorfully with the wooden type door cabinet of sedate dullness, is rich in poetic and pictorial splendor.At present, the described various art glass plate bodys that have different pictures are on the monolithic glass plate body, adopt the solid film to paste selected picture, place then and strengthen stove heating and molding acquisition product; Or, adopt the ultraviolet light heating and molding then pasting selected picture with liquid glue on the monolithic glass plate body.The art glass of this monolithic is attractive in appearance, has also built certain cultural atmosphere, but the picture abrasion resistance that also exists set poster is relatively poor relatively, not the cut of anti-sharp weapon; Thin monolithic glass body intensity is lower, receives collision with stronger dynamics, also possibly meet with defectives such as shot fragmentation.
Summary of the invention
The present invention is directed to above-mentioned existing problems, proposed a kind of sandwich painting reinforced flat plate art glass and preparation method thereof, purpose is to make the picture of the sandwich picture that receives the double-sided glass protection more clear permanent; Have the intensity that increases sandwich picture art glass, improve the effects such as anti-explosion grade of dull and stereotyped art glass.
Technical solution of the present invention:
The alleged sandwich painting reinforced flat plate art glass of the present invention comprises a plurality of aspects, promptly is between two glass plies, to be provided with solid glue-line and picture frame layer, and each layer fitted each other to superpose and constituted.Described overlay order is followed successively by first glass plies, the first solid glue-line, transparency surface layer, the second solid glue-line, second glass plies, is five layers altogether; Or be followed successively by first glass plies, the first solid glue-line, the first opaque picture frame layer, the 3rd solid glue-line, the second opaque picture frame layer, the second solid glue-line, second glass plies.Said two glass plies gross thickness are 4-6mm.
Sandwich painting reinforced flat plate art glass preparation method's of the present invention concrete steps are:
(1) on the operation platen; Add a plurality of aspects as a workpiece by the technique scheme order stack, the stack of one or more workpiece be placed on the siliceous skin sheet (market is buied), get another siliceous skin sheet cover on the workpiece that superposes; The siliceous skin sheet seals up and down, and vacuumizes;
(2) will operate the siliceous skin bag that workpiece is housed on the platen, and keep a vacuum state in the bag, push the High-Temperature Strengthening stove, the control temperature range is between 105 ℃-120 ℃, constant temperature 40-50 minute, stops to heat; And in stove, naturally cool to below 100 ℃;
(3) the siliceous skin bag is withdrawed from the High-Temperature Strengthening stove, continue again to add and vacuumize 8-10 minute, naturally cool to room temperature, then process the sandwich painting reinforced flat plate art glass finished product.
Beneficial effect of the present invention
(1) the present invention accompanies artistic pictures among the two-sided strengthened glass, and tempered glass surface abrasion resistance, the cut of anti-sharp weapon can " be remained youthful forever " folded artistic pictures, for a long time can both be as before vivid, and the utmost point has ornamental value;
(2) the present invention is two-sided strengthened glass, as sliding door or cupboard door intensity big, anti-explosion grade can be increased to I level or superfine, safety coefficient is high;
(3) artistic pictures in the tempered glass interlayer of the present invention; Can process the art glass that transparent sandwich formula, shadow film sandwich, the sandwich pair of picture, spun silk sandwich etc. differ from one another, can satisfy different hobby of people and different consumer groups' thereof selection and use.
Description of drawings
Accompanying drawing 1 is the structural representation of the embodiment of the invention one;
Accompanying drawing 2 is the structural representation of the embodiment of the invention two;
Accompanying drawing 3 is the structural representation of the embodiment of the invention three;
Accompanying drawing 4 is the structural representation of the embodiment of the invention four.
The specific embodiment
Embodiment one, as shown in Figure 1,
Preparation transparent sandwich painting reinforced flat plate art glass finished product:
(1) prepares two siliceous skin sheets, two 2mm glass, two solid gums and a slice transparency;
(2) on the operation platen from bottom to top order put first glass plies 1, the superpose first solid glue-line 2, transparency layer 3, the second solid glue-line 4, second glass plies 5 again; Totally five layers compound as a workpiece; Or by above-mentioned same order or make 2-6 workpiece again, one or 2-7 workpiece stack are placed on the siliceous skin sheet, get another siliceous skin sheet cover on the workpiece that superposes; The siliceous skin sheet seals up and down, and vacuumizes;
(3) will operate the siliceous skin bag that workpiece is housed on the platen, and keep a vacuum state in the bag, push the High-Temperature Strengthening stove, and the control temperature range is 105 ℃, constant temperature 40 minutes (wherein constant temperature time needs according to advancing the adjustment of furnaceman's number of packages appropriateness), stop to heat; And in stove, naturally cool to 90 ℃;
(4) the siliceous skin bag is withdrawed from the High-Temperature Strengthening stove, continue again to add and vacuumize minutes about 8, naturally cool to room temperature, then process the bright sandwich painting reinforced flat plate art glass finished product of full impregnated.This finished product entire body is transparent, and the two sides of glass all has sight, mar-proof, explosive-proof grade is the I level.
Embodiment two, as shown in Figure 2,
Preparation shadow film sandwich painting reinforced flat plate art glass finished product:
(1) prepares two siliceous skin sheets, get a slice 2.5mm glass (or float glass), the beautiful sand glass of a slice 2.5mm (or the beautiful sand glass of float glass process), two solid gums (or EVA solid gum) and a slice transparency (or transparency description picture);
(2) on the operation platen from bottom to top order put first glass plies (or beautiful sand glass) 1, the superpose first solid glue-line 2, transparency 3, the second solid glue-line 4, beautiful sand glass flaggy (or second glass plies) 51 again; Totally five layers compound as a workpiece; Or make 2-6 workpiece equally in order or again by above-mentioned, one or 2-7 workpiece stack are placed on the siliceous skin sheet, get another siliceous skin sheet cover on the workpiece that superposes; The siliceous skin sheet seals up and down, and vacuumizes;
(3) will operate the siliceous skin bag that workpiece is housed on the platen, and keep a vacuum state in the bag, push the High-Temperature Strengthening stove, and the control temperature range is 110 ℃, constant temperature 45 minutes (wherein constant temperature time needs according to advancing the adjustment of furnaceman's number of packages appropriateness), stop to heat; And in stove, naturally cool to 80 ℃;
(4) the siliceous skin bag is withdrawed from the High-Temperature Strengthening stove, continue again to add and vacuumize about 9 minutes, naturally cool to room temperature, then process shadow film sandwich painting reinforced flat plate art glass finished product.The glass two sides of this finished product all has sight, and printing opacity is and opaque, and suitable especially some consumer groups do not hope that penetrating decoration is used, and it is mar-proof, explosive-proof grade is the I level.
Embodiment three, as shown in Figure 3,
Preparation spun silk sandwich painting reinforced flat plate art glass finished product:
(1) prepares two siliceous skin sheets, get two 3mm glass, two solid gums and a slice spun silk and draw;
(2) order is put first glass plies 1 from bottom to top on the operation platen, the superpose first solid glue-line 2, transparent spun silk drawn 31, the second solid glue-line 4, second glass plies 5 again; Totally five layers compound as a workpiece; Or by above-mentioned same order or make 2-6 workpiece again, one or 2-7 workpiece stack are placed on the siliceous skin sheet, get another siliceous skin sheet cover on the workpiece that superposes; The siliceous skin sheet seals up and down, and vacuumizes;
(3) will operate the siliceous skin bag that workpiece is housed on the platen, and keep a vacuum state in the bag, push the High-Temperature Strengthening stove, and the control temperature range is 120 ℃, constant temperature 45 minutes (wherein constant temperature time needs according to advancing the adjustment of furnaceman's number of packages appropriateness), stop to heat; And in stove, naturally cool to 90 ℃;
(4) the siliceous skin bag is withdrawed from the High-Temperature Strengthening stove, continue again to add and vacuumize about 9 minutes, naturally cool to room temperature, then process spun silk sandwich painting reinforced flat plate art glass finished product.This finished product can be made into transparent or opaque two kinds of printing opacity as required.Its ornamental value is higher and high-grade because the sandwich picture of spun silk is fine and smooth, is fit to and the hard-cover coupling of luxurious house, and it is mar-proof, explosive-proof grade is the I level.
Embodiment four, as shown in Figure 4,
Prepare sandwich pair of picture reinforced flat plate art glass finished product:
(1) prepares two siliceous skin sheets, get the opaque picture (or the hard sheet of PVC is drawn) that a slice 2mm glass, a slice 3mm glass, two solid gums and two draftings have different pictures;
(2) on the operation platen from bottom to top order put first glass plies 1, superpose that (picture is towards glass plies for the first solid glue-line, 2, first opaque picture layers 32 again; So expression among the figure), opaque the pictures layer 33 of the 3rd solid glue-line 6, second (picture towards with first opaque the pictures layer picture towards on the contrary), the second solid glue-line 4, second glass plies 5; Totally seven layers compound as a workpiece; Or make 2-6 workpiece equally in order or again by above-mentioned, one or 2-7 workpiece stack are placed on the siliceous skin sheet, get another siliceous skin sheet cover on the workpiece that superposes; The siliceous skin sheet seals up and down, and vacuumizes;
(3) will operate the siliceous skin bag that workpiece is housed on the platen, and keep a vacuum state in the bag, push the High-Temperature Strengthening stove, and the control temperature range is 120 ℃, constant temperature 50 minutes (wherein constant temperature time needs according to advancing the adjustment of furnaceman's number of packages appropriateness), stop to heat; In stove, naturally cool to 90 ℃
(4) the siliceous skin bag is withdrawed from the High-Temperature Strengthening stove, continue again to add and vacuumize about 10 minutes, naturally cool to room temperature, then process shadow film sandwich painting reinforced flat plate art glass finished product.The glass two sides of this finished product has the different pictures sight, and light transmission, transparency are lower, does not also suitablely especially hope that penetrating decoration is used, and it is mar-proof, explosive-proof grade be superfine.
Glass of the present invention or be float glass; Described solid gum or be the EVA solid gum; Described opaque picture or be that opaque hard sheet is drawn.
To sum up, the present invention can reach the goal of the invention of expection.
Claims (4)
1. the preparation method of a sandwich painting reinforced flat plate art glass, it is characterized in that: said sandwich painting reinforced flat plate art glass comprises a plurality of aspects, promptly is between two glass plies, to be provided with solid glue-line and picture frame layer, and the stack of fitting each other is prepared from; Said preparation method's concrete steps are:
(1) on the operation platen, order stack adds a plurality of aspects as a workpiece, and the stack of one or more workpiece is placed on the siliceous skin sheet, gets another siliceous skin sheet and covers on institute's workpiece that superpose, and the siliceous skin sheet seals about the general, and vacuumizes;
(2) will operate the siliceous skin bag that workpiece is housed on the platen, and keep a vacuum state in the bag, push the High-Temperature Strengthening stove, and the control temperature range is between 105 ℃-120 ℃, constant temperature 40-50 minute, stop to heat; And in stove, naturally cool to below 100 ℃;
(3) the siliceous skin bag is withdrawed from the High-Temperature Strengthening stove, continue to add again and vacuumize 8-10 minute, the cold naturally room temperature that retreats to is then processed the sandwich painting reinforced flat plate art glass finished product.
2. the preparation method of a kind of sandwich painting reinforced flat plate art glass according to claim 1; It is characterized in that: a plurality of aspects of said order stack are followed successively by first glass plies, the first solid glue-line, picture frame layer, the second solid glue-line, second glass plies, are five layers altogether.
3. the preparation method of a kind of sandwich painting reinforced flat plate art glass according to claim 1; It is characterized in that: a plurality of aspect glass plies of said order stack are followed successively by first glass plies, the first solid glue-line, the first opaque picture frame layer, the 3rd solid glue-line, the second opaque picture frame layer, the second solid glue-line, second glass plies, are seven layers altogether.
4. the preparation method of a kind of sandwich painting reinforced flat plate art glass according to claim 1 and 2, it is characterized in that: in the said glass plies, it is beautiful sand glass flaggy that one deck is arranged; Said picture frame layer is the transparency surface layer, constitutes shadow film sandwich painting reinforced flat plate art glass finished product.