CN103771776B - 一种再生微粉混凝土及其制备方法 - Google Patents

一种再生微粉混凝土及其制备方法 Download PDF

Info

Publication number
CN103771776B
CN103771776B CN201310734414.2A CN201310734414A CN103771776B CN 103771776 B CN103771776 B CN 103771776B CN 201310734414 A CN201310734414 A CN 201310734414A CN 103771776 B CN103771776 B CN 103771776B
Authority
CN
China
Prior art keywords
concrete
micro powder
cement
regenerative micro
water
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201310734414.2A
Other languages
English (en)
Other versions
CN103771776A (zh
Inventor
耿欧
赵桂云
冯太
张圣彩
王海进
赵园园
孙韬
陈琳
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
China University of Mining and Technology CUMT
Original Assignee
China University of Mining and Technology CUMT
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by China University of Mining and Technology CUMT filed Critical China University of Mining and Technology CUMT
Priority to CN201310734414.2A priority Critical patent/CN103771776B/zh
Publication of CN103771776A publication Critical patent/CN103771776A/zh
Application granted granted Critical
Publication of CN103771776B publication Critical patent/CN103771776B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

<b>本发明涉及一种再生微粉混凝土及其制备方法，该再生微粉混凝土包括水泥、砂、石子、水、</b><b>再生</b><b>微粉、激发剂</b><b>Ca(OH)2</b><b>，</b><b>其制备步骤为：</b><b>1</b><b>）将废弃混凝土破碎为细骨料，再从中筛选出直径小于</b><b>0.16mm</b><b>的</b><b>再生</b><b>微粉；</b><b>2</b><b>）按照水灰比为</b><b>0.54</b><b>计算强度等级为</b><b>C30</b><b>的混凝土各材料用量，用再生微粉等质量取代</b><b>10%</b><b>的水泥，并加入再生微粉质量</b><b>3.5%</b><b>的激发剂</b><b>Ca(OH)2</b><b>；</b><b>3</b><b>）将水泥、再生微粉、激发剂</b><b>Ca(OH)2</b><b>称量后加入搅拌机进行搅拌，搅拌均匀后，加水进行搅拌，先后分别加入砂、石子进行搅拌即可。</b><b>采用该方法制备的再生微粉混凝土强度和抗碳化性均高于同配合比的普通混凝土，安全应用于实际工程中，提高废弃混凝土的利用率。</b>

Description

一种再生微粉混凝土及其制备方法
技术领域
本发明涉及一种建筑材料，尤其是一种再生微粉混凝土及其制备方法。
背景技术
在当今土木建筑行业中，混凝土材料依然作为主要的结构材料，但由于环境条件的影响和混凝土自身的缺陷，往往会降低结果的质量，产生危害，减少建筑物的寿命。
当前我国城市建设日益加快，建筑业发展迅速，在拆迁和新建过程中产生了大量的建筑垃圾。随着废弃混凝土不断增多，如何有效处理和循环利用成为了十分迫切的问题。传统的废弃混凝土的处理方法主要是将其运往郊外堆放或填埋，这不仅占用大量的耕地，而且造成环境污染。为此，一些工程将废弃混凝土破碎成骨料，用以取代天然骨料生产再生混凝土，使废弃混凝土得到了一些利用，但在破碎过程中产生的微粉未被利用，降低了废弃混凝土的利用率。
发明内容
为提高废弃混凝土的利用率，本发明提供一种再生微粉混凝土及其制备方法，采用该方法制备的再生微粉混凝土强度和抗碳化性均高于同配合比的普通混凝土，安全应用于实际工程中，提高废弃混凝土的利用率。
本发明解决其技术问题所采用的技术方案：本发明提供一种再生微粉混凝土及其制备方法，该再生微粉混凝土包括水泥、砂、石子、水、再生微粉、激发剂Ca(OH) 2 ，其制备步骤为：
1）将废弃混凝土破碎为细骨料，再从中筛选出直径小于0.16mm的再生微粉；
2）按照水灰比为0.54计算强度等级为C30的混凝土各材料用量，用再生微粉等质量取代10%的水泥，并加入再生微粉质量3.5%的激发剂Ca(OH) 2 ；
3）将水泥、再生微粉、激发剂Ca(OH) 2 称量后加入搅拌机进行搅拌，搅拌均匀后，加水进行搅拌，先后分别加入砂、石子进行搅拌即可。
所述水泥为巨龙牌425号复合硅酸盐水泥；所述水为普通自来水；所述砂为天然中砂；所述石子为最大粒径D max =20mm的碎石。
本发明的有益效果是，采用该方法制备的再生微粉混凝土强度和抗碳化性均高于同配合比的普通混凝土，安全应用于实际工程中，提高废弃混凝土的利用率。
具体实施方式
本发明提供一种再生微粉混凝土及其制备方法，该再生微粉混凝土包括水泥、砂、石子、水、再生微粉、激发剂Ca(OH) 2 ，其制备步骤为：
1）将废弃混凝土破碎为细骨料，再从中筛选出直径小于0.16mm的再生微粉；
2）按照水灰比为0.54计算强度等级为C30的混凝土各材料用量，用再生微粉等质量取代10%的水泥，并加入再生微粉质量3.5%的激发剂Ca(OH) 2 ，每立方米混凝土中各材料质量如下：
石子：1142kg；
砂：643kg；
水泥：360kg；
水：215kg；
再生微粉：40kg；
激发剂Ca(OH) 2 ：1.4kg；
3）将水泥、再生微粉、激发剂Ca(OH) 2 称量后加入搅拌机进行搅拌，搅拌均匀后，加水进行搅拌，再先后分别加入砂、石子进行搅拌即可。
所述水泥为巨龙牌425号复合硅酸盐水泥；所述水为普通自来水；所述砂为天然中砂；所述石子为最大粒径D max =20mm的碎石。
采用该方法制备的再生微粉混凝土强度比普通混凝土提高15%，碳化深度降低5%，可见采用该方法制备的再生微粉混凝土具有实用性。

Claims (1)

1.一种再生微粉混凝土的制备方法，该再生微粉混凝土包括水泥、砂、石子、水、再生微粉、激发剂Ca(OH)2，其特征在于，该再生微粉混凝土的制备步骤为：
（1）将废弃混凝土破碎为细骨料，再从中筛选出直径小于0.16mm的再生微粉；
（2）按照水灰比为0.54计算强度等级为C30的混凝土各材料用量，用再生微粉等质量取代10%的水泥，并加入再生微粉质量3.5%的激发剂Ca(OH)2；
（3）将水泥、再生微粉、激发剂Ca(OH)2称量后加入搅拌机进行搅拌，搅拌均匀后，加水进行搅拌，先后分别加入砂、石子进行搅拌即可；
所述水泥为巨龙牌425号复合硅酸盐水泥；所述水为普通自来水；所述砂为天然中砂；所述石子为最大粒径Dmax=20mm的碎石。
CN201310734414.2A 2013-12-27 2013-12-27 一种再生微粉混凝土及其制备方法 Expired - Fee Related CN103771776B (zh)