CN103739246A - 一种保温混凝土 - Google Patents

一种保温混凝土 Download PDF

Info

Publication number
CN103739246A
CN103739246A CN201310702603.1A CN201310702603A CN103739246A CN 103739246 A CN103739246 A CN 103739246A CN 201310702603 A CN201310702603 A CN 201310702603A CN 103739246 A CN103739246 A CN 103739246A
Authority
CN
China
Prior art keywords
insulation concrete
parts
water
thermal insulation
whipping agent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310702603.1A
Other languages
English (en)
Inventor
唐萍
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Liuzhou Zhengling Group Co Ltd
Original Assignee
Liuzhou Zhengling Group Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Liuzhou Zhengling Group Co Ltd filed Critical Liuzhou Zhengling Group Co Ltd
Priority to CN201310702603.1A priority Critical patent/CN103739246A/zh
Publication of CN103739246A publication Critical patent/CN103739246A/zh
Pending legal-status Critical Current

Abstract

本发明提供一种保温混凝土，包括以下质量份数的各组分：水泥800-850份、粉煤灰100-120份、硬脂酸钙20-25份、聚氨酯颗粒35-40份、陶粒10-15份、发泡剂15-20份、萘系高效减水剂0.6-0.8份、水800-850份。由于聚氨酯具有非常优异的隔热性能，陶粒也是一种很好的隔热材料，本发明的保温混凝土将两者很好的结合在一起，具有优异的隔热性能。经测定，本发明的保温混凝土的抗压强度为1.03-1.09MPa，导热系数为0.05-0.06w/（m·k）。

Description

一种保温混凝土
技术领域
本发明属于建筑材料技术领域，具体涉及一种保温混凝土。
背景技术
目前，我国现有房屋建筑外墙墙体材料，主要有粘土实心砖、粘土空心砖、多孔砖、页岩砖、混凝土砌块、免烧水泥砖等，以上的外墙墙体材料普遍存在导热系数高、隔热性能差，不能满足国家对房屋建筑节能的要求，使用以上材料还需在墙体外表面或内表面做保温隔热层才能满足相关规范要求，而且仍然存在保温隔热效果不好、重量大等缺陷。
发明内容
本发明提供了一种保温混凝土，保温效果好，干燥速度快。
    本发明提供一种保温混凝土，包括以下质量份数的各组分：水泥800-850份、粉煤灰100-120份、硬脂酸钙20-25份、聚氨酯颗粒35-40份、陶粒10-15份、发泡剂15-20份、萘系高效减水剂0.6-0.8份、水800-850份。
    优选地，所述发泡剂为FA-1发泡剂和/或KC-20发泡剂。
    本发明还提供上述保温混凝土的制备方法，是将发泡剂加入水中，制成发泡剂水溶液，水和发泡剂的重量比为35-40:1；将粉煤灰、硬脂酸钙、聚氨酯颗粒、陶粒、水泥、萘系高效减水剂和剩余的水混合均匀；再将上述两者混合均匀，经养护、浇注、成型得到本发明的保温混凝土。
由于聚氨酯具有非常优异的隔热性能，陶粒也是一种很好的隔热材料，本发明的保温混凝土将两者很好的结合在一起，具有优异的隔热性能。经测定，本发明的保温混凝土的抗压强度为1.03-1.09MPa，导热系数为0.05-0.06w/（m·k）。
具体实施方式
    以下的实施例便于更好地理解本发明，但并不限定本发明。下述实施例中的实验方法，如无特殊说明，均为常规方法。
实施例1
本发明的保温混凝土的配方如下：
水泥740kg、粉煤灰110kg、硬脂酸钙22kg、聚氨酯颗粒38kg、陶粒9kg、发泡剂18kg、萘系高效减水剂0.7kg、水780kg。
其中，发泡剂为FA-1发泡剂。
本发明的保温混凝土的制备方法为：     将18kg发泡剂加入720kg水中，制成发泡剂水溶液；将110kg粉煤灰、22kg硬脂酸钙、38kg聚氨酯颗粒、9kg陶粒、740kg水泥、0.7kg萘系高效减水剂和60kg水混合均匀；再将上述两者混合均匀，经养护、浇注、成型得到本发明的保温混凝土。
实施例2
本发明的保温混凝土的配方如下：
水泥720kg、粉煤灰120kg、硬脂酸钙20kg、聚氨酯颗粒35kg、陶粒8kg、发泡剂15kg、萘系高效减水剂0.8kg、水760kg。
其中，发泡剂为KC-20发泡剂。
本发明的保温混凝土的制备方法为：     将15kg发泡剂加入600kg水中，制成发泡剂水溶液；将120kg粉煤灰、20kg硬脂酸钙、35kg聚氨酯颗粒、8kg陶粒、720kg水泥、0.8kg萘系高效减水剂和160kg水混合均匀；再将上述两者混合均匀，经养护、浇注、成型得到本发明的保温混凝土。
实施例3
本发明的保温混凝土的配方如下：
水泥760kg、粉煤灰100kg、硬脂酸钙25kg、聚氨酯颗粒40kg、陶粒10kg、发泡剂20kg、萘系高效减水剂0.6kg、水800kg。
其中，发泡剂为FA-1发泡剂。
本发明的保温混凝土的制备方法为：     将20kg发泡剂加入600kg水中，制成发泡剂水溶液；将100kg粉煤灰、25kg硬脂酸钙、40kg聚氨酯颗粒、10kg陶粒、760kg水泥、0.6kg萘系高效减水剂和200kg水混合均匀；再将上述两者混合均匀，经养护、浇注、成型得到本发明的保温混凝土。
 
最后应说明的是：以上所述仅为本发明的优选实施例而已，并不用于限制本发明，尽管参照前述实施例对本发明进行了详细的说明，对于本领域的技术人员来说，其依然可以对前述各实施例所记载的技术方案进行修改，或者对其中部分技术特征进行等同替换。凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。

Claims (3)

1.一种保温混凝土，其特征在于：包括以下质量份数的各组分：水泥720-760份、粉煤灰100-120份、硬脂酸钙20-25份、聚氨酯颗粒35-40份、陶粒8-10份、发泡剂15-20份、萘系高效减水剂0.6-0.8份、水760-800份。
2.根据权利要求1所述的保温混凝土，其特征在于：所述发泡剂为FA-1发泡剂和/或KC-20发泡剂。
3.权利要求1或2所述的保温混凝土的制备方法，是将发泡剂加入水中，制成发泡剂水溶液，水和发泡剂的重量比为35-40:1；将粉煤灰、硬脂酸钙、聚氨酯颗粒、陶粒、水泥、萘系高效减水剂和剩余的水混合均匀；再将上述两者混合均匀，经养护、浇注、成型得到本发明的保温混凝土。
CN201310702603.1A 2013-12-19 2013-12-19 一种保温混凝土 Pending CN103739246A (zh)