CN111877601A - 一种便于施工的建筑用砌块砖 - Google Patents

一种便于施工的建筑用砌块砖 Download PDF

Info

Publication number
CN111877601A
CN111877601A CN202010737698.0A CN202010737698A CN111877601A CN 111877601 A CN111877601 A CN 111877601A CN 202010737698 A CN202010737698 A CN 202010737698A CN 111877601 A CN111877601 A CN 111877601A
Authority
CN
China
Prior art keywords
brick body
brick
concrete
building block
mould
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN202010737698.0A
Other languages
English (en)
Inventor
倪敬国
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Hengchuang Environmental Protection Building Materials Co ltd
Original Assignee
Anhui Hengchuang Environmental Protection Building Materials Co ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Hengchuang Environmental Protection Building Materials Co ltd filed Critical Anhui Hengchuang Environmental Protection Building Materials Co ltd
Priority to CN202010737698.0A priority Critical patent/CN111877601A/zh
Publication of CN111877601A publication Critical patent/CN111877601A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种便于施工的建筑用砌块砖，其技术方案是：包括砖体，所述砖体上开设有两个通槽，两个所述通槽均贯穿砖体，所述砖体上开设有两个方槽，两个所述方槽均贯穿箱体，所述砖体顶部固定设有加强板，所述加强板设于两个通槽之间，所述加强板延伸入砖体内部，所述砖体顶部开设有滑槽，所述砖体底部固定设有滑块，所述加强板由酚醛板制成，本发明的有益效果是：通过滑槽和滑块的设计，使得砖体在使用时只需将其中一个砖体的滑块放置于另一个砖体的滑槽内部，可以初步的对砖体进行定位，使得使用者在使用时更加的方便，同时通过通槽和方槽的设计，使得砖体在使用时有一定的隔热和隔音的效果。

Description

一种便于施工的建筑用砌块砖
技术领域
本发明涉及砌块砖技术领域，具体涉及一种便于施工的建筑用砌块砖。
背景技术
砌筑工程又叫砌体工程，是指在建筑工程中使用普通黏土砖、承重黏土空心砖、蒸压灰砂砖、粉煤灰砖、各种中小型砌块和石材等材料进行砌筑的工程，包括砌砖、石、砌块及轻质墙板等内容，砌砖、砌石、砌块砖砌体对砌筑材料的要求，组砌工艺，质量要求以及质量通病的防治措施，在砌筑工程中，经常需要使用到砌块砖。
现有技术存在以下不足：现有技术中的砌块砖在使用时，由于砌块砖大多都是方形，导致砌块砖在使用时，需要对砌块砖进行严格的定位，防止砌块砖砌成的墙面歪曲，同时现有技术中的砌块砖的保温隔热和隔音效果较差，使得由砌块砖砌成的墙面的保温隔热和隔音效果较差。
因此，发明一种便于施工的建筑用砌块砖很有必要。
发明内容
为此，本发明提供一种便于施工的建筑用砌块砖，通过滑槽和滑块的设计，使得砖体在使用时只需将其中一个砖体的滑块放置于另一个砖体的滑槽内部，可以初步的对砖体进行定位，使得使用者在使用时更加的方便，同时通过通槽和方槽的设计，使得砖体在使用时有一定的隔热和隔音的效果，同时在制作时，也节省了原料，以解决导致砌块砖在使用时，需要对砌块砖进行严格的定位的问题。
为了实现上述目的，本发明提供如下技术方案：一种便于施工的建筑用砌块砖，包括砖体，所述砖体上开设有两个通槽，两个所述通槽均贯穿砖体，所述砖体上开设有两个方槽，两个所述方槽均贯穿箱体，所述砖体顶部固定设有加强板，所述加强板设于两个通槽之间，所述加强板延伸入砖体内部，所述砖体顶部开设有滑槽，所述砖体底部固定设有滑块。
优选的，所述加强板由酚醛板制成，所述酚醛板截面形状设为T形。
一种便于施工的建筑用砌块砖，包括混凝土、聚氨酯泡沫、灰砂和陶粒，其中各成分质量份数为：
混凝土30-50份；
聚氨酯泡沫10-20份；
灰砂10-15份；
陶粒10-15份。
一种便于施工的建筑用砌块砖，还包括砌块砖的制备方法：
S1制作模具：首先制作一个倒凸字形的模具，再准备两个方杆，将两个方杆插入模具内部，同时在模具的底部通过焊接固定两个竖板。
S2涂粉：将模具内部及方杆和竖板上涂上滑石粉。
S3配料：将混凝土、聚氨酯泡沫、灰砂和陶粒放入到搅拌机内部混合。
S4注模：将混合好的混凝土放置于模具内部，通过振动棒给模具内部混凝土进行振动。
S5插板：将加强板插入到混凝土内部，加强板插入的位置处于两个竖板之间。
S6盖模具：再将一个倒凸字形的模盖盖在模具上方。
S7烘干：然后将模具放置于烘干箱内部烘干。
S8水冷：将模具内部的混凝土烘干成型后，将模具放置冷水内部。
S9取模：经水冷后，将模具拿出砖体内部。
优选的，在所述步骤S3中，先将混凝土放置于搅拌机内部，再依次放入聚氨酯泡沫、灰砂和陶粒。
优选的，在所述步骤S3中，搅拌机混合时长为10-20min。
优选的，在所述步骤S4中，振动棒振动频率为5000-8000次/min，振动时长为3-6min。
优选的，在所述步骤S6中，通过小型液压机对模具进行挤压。
优选的，在所述步骤S7中，烘干时长为30-50min。
优选的，在所述步骤S8中，水冷时长为15-25min。
本发明的有益效果是：
1、本发明通过滑槽和滑块的设计，使得砖体在使用时只需将其中一个砖体的滑块放置于另一个砖体的滑槽内部，可以初步的对砖体进行定位，使得使用者在使用时更加的方便，同时通过通槽和方槽的设计，使得砖体在使用时有一定的隔热和隔音的效果，同时在制作时，也节省了原料，通过加强板的设计，因为酚醛板具有轻质、防火、隔音、遇明火不燃烧、无烟、无毒、无滴落等性质，使用温度范围广等优点，因此通过酚醛板可加强砖体的防火和隔音的特性；
2、本发明通过混凝土的设计，因为混凝土具有抗压强度高，耐久性好，强度等级范围宽等特点，所以通过混凝土的设计可增强砖体的强度和耐久度，聚氨酯泡沫是一种具有保温与防水功能的新型合成材料，通过聚氨酯泡沫的设计可增强砖体的保温性和防水性，通过灰砂的设计，可增强砖体的硬度，因为陶粒具有保温、隔热、耐火性优异、抗震性好、抗冻性能和耐久性能好等优点，所以通过陶粒的设计，可增强砖体的保温、隔热、耐火性、抗震性、抗冻性能和耐久性能等。
附图说明
图1为本发明提供的整体结构示意图；
图2为本发明提供的俯视图；
图3为本发明提供的正视图；
图4为本发明提供的剖视图；
图中：1砖体、2通槽、3方槽、4加强板、5滑槽、6滑块。
具体实施方式
以下结合附图对本发明的优选实施例进行说明，应当理解，此处所描述的优选实施例仅用于说明和解释本发明，并不用于限定本发明。
实施例1：
参照附图1-4，本发明提供的一种便于施工的建筑用砌块砖，包括砖体1，所述砖体1上开设有两个通槽2，两个所述通槽2均贯穿砖体1，所述砖体1上开设有两个方槽3，两个所述方槽3均贯穿箱体，所述砖体1顶部固定设有加强板4，所述加强板4设于两个通槽2之间，所述加强板4延伸入砖体1内部，所述砖体1顶部开设有滑槽5，所述砖体1底部固定设有滑块6。
进一步地，所述加强板4由酚醛板制成，所述酚醛板截面形状设为T形。
一种便于施工的建筑用砌块砖，包括混凝土、聚氨酯泡沫、灰砂和陶粒，其中各成分质量份数为：
混凝土30份，因为混凝土具有抗压强度高，耐久性好，强度等级范围宽等特点，所以通过混凝土的设计可增强砖体1的强度和耐久度；
聚氨酯泡沫10份，聚氨酯泡沫是一种具有保温与防水功能的新型合成材料，通过聚氨酯泡沫的设计可增强砖体1的保温性和防水性；
灰砂10份，通过灰砂的设计，可增强砖体1的硬度；
陶粒10份，因为陶粒具有保温、隔热、耐火性优异、抗震性好、抗冻性能和耐久性能好等优点，所以通过陶粒的设计，可增强砖体1的保温、隔热、耐火性、抗震性、抗冻性能和耐久性能等。
一种便于施工的建筑用砌块砖，还包括砌块砖的制备方法：
S1制作模具：首先制作一个倒凸字形的模具，再准备两个方杆，将两个方杆插入模具内部，同时在模具的底部通过焊接固定两个竖板。
S2涂粉：将模具内部及方杆和竖板上涂上滑石粉。
S3配料：将混凝土、聚氨酯泡沫、灰砂和陶粒放入到搅拌机内部混合，先将混凝土放置于搅拌机内部，再依次放入聚氨酯泡沫、灰砂和陶粒，搅拌机混合时长为10min。
S4注模：将混合好的混凝土放置于模具内部，通过振动棒给模具内部混凝土进行振动，振动棒振动频率为5000次/min，振动时长为3min。
S5插板：将加强板4插入到混凝土内部，加强板4插入的位置处于两个竖板之间。
S6盖模具：再将一个倒凸字形的模盖盖在模具上方，通过小型液压机对模具进行挤压。
S7烘干：然后将模具放置于烘干箱内部烘干，烘干时长为30min。
S8水冷：将模具内部的混凝土烘干成型后，将模具放置冷水内部，水冷时长为15min。
S9取模：经水冷后，将模具拿出砖体1内部。
实施例2：
本发明提供的一种便于施工的建筑用砌块砖，包括混凝土、聚氨酯泡沫、灰砂和陶粒，其中各成分质量份数为：
混凝土35份，因为混凝土具有抗压强度高，耐久性好，强度等级范围宽等特点，所以通过混凝土的设计可增强砖体1的强度和耐久度；
聚氨酯泡沫12份，聚氨酯泡沫是一种具有保温与防水功能的新型合成材料，通过聚氨酯泡沫的设计可增强砖体1的保温性和防水性；
灰砂12份，通过灰砂的设计，可增强砖体1的硬度；
陶粒13份，因为陶粒具有保温、隔热、耐火性优异、抗震性好、抗冻性能和耐久性能好等优点，所以通过陶粒的设计，可增强砖体1的保温、隔热、耐火性、抗震性、抗冻性能和耐久性能等。
一种便于施工的建筑用砌块砖，还包括砌块砖的制备方法：
S1制作模具：首先制作一个倒凸字形的模具，再准备两个方杆，将两个方杆插入模具内部，同时在模具的底部通过焊接固定两个竖板。
S2涂粉：将模具内部及方杆和竖板上涂上滑石粉。
S3配料：将混凝土、聚氨酯泡沫、灰砂和陶粒放入到搅拌机内部混合，先将混凝土放置于搅拌机内部，再依次放入聚氨酯泡沫、灰砂和陶粒，搅拌机混合时长为13min。
S4注模：将混合好的混凝土放置于模具内部，通过振动棒给模具内部混凝土进行振动，振动棒振动频率为6000次/min，振动时长为3min。
S5插板：将加强板4插入到混凝土内部，加强板4插入的位置处于两个竖板之间。
S6盖模具：再将一个倒凸字形的模盖盖在模具上方，通过小型液压机对模具进行挤压。
S7烘干：然后将模具放置于烘干箱内部烘干，烘干时长为35min。
S8水冷：将模具内部的混凝土烘干成型后，将模具放置冷水内部，水冷时长为18min。
S9取模：经水冷后，将模具拿出砖体1内部。
实施例3：
本发明提供的一种便于施工的建筑用砌块砖，包括混凝土、聚氨酯泡沫、灰砂和陶粒，其中各成分质量份数为：
混凝土45份，因为混凝土具有抗压强度高，耐久性好，强度等级范围宽等特点，所以通过混凝土的设计可增强砖体1的强度和耐久度；
聚氨酯泡沫18份，聚氨酯泡沫是一种具有保温与防水功能的新型合成材料，通过聚氨酯泡沫的设计可增强砖体1的保温性和防水性；
灰砂14份，通过灰砂的设计，可增强砖体1的硬度；
陶粒14份，因为陶粒具有保温、隔热、耐火性优异、抗震性好、抗冻性能和耐久性能好等优点，所以通过陶粒的设计，可增强砖体1的保温、隔热、耐火性、抗震性、抗冻性能和耐久性能等。
一种便于施工的建筑用砌块砖，还包括砌块砖的制备方法：
S1制作模具：首先制作一个倒凸字形的模具，再准备两个方杆，将两个方杆插入模具内部，同时在模具的底部通过焊接固定两个竖板。
S2涂粉：将模具内部及方杆和竖板上涂上滑石粉。
S3配料：将混凝土、聚氨酯泡沫、灰砂和陶粒放入到搅拌机内部混合，先将混凝土放置于搅拌机内部，再依次放入聚氨酯泡沫、灰砂和陶粒，搅拌机混合时长为18min。
S4注模：将混合好的混凝土放置于模具内部，通过振动棒给模具内部混凝土进行振动，振动棒振动频率为7000次/min，振动时长为6min。
S5插板：将加强板4插入到混凝土内部，加强板4插入的位置处于两个竖板之间。
S6盖模具：再将一个倒凸字形的模盖盖在模具上方，通过小型液压机对模具进行挤压。
S7烘干：然后将模具放置于烘干箱内部烘干，烘干时长为45min。
S8水冷：将模具内部的混凝土烘干成型后，将模具放置冷水内部，水冷时长为23min。
S9取模：经水冷后，将模具拿出砖体1内部。
实施例4：
本发明提供的一种便于施工的建筑用砌块砖，包括混凝土、聚氨酯泡沫、灰砂和陶粒，其中各成分质量份数为：
混凝土50份，因为混凝土具有抗压强度高，耐久性好，强度等级范围宽等特点，所以通过混凝土的设计可增强砖体1的强度和耐久度；
聚氨酯泡沫20份，聚氨酯泡沫是一种具有保温与防水功能的新型合成材料，通过聚氨酯泡沫的设计可增强砖体1的保温性和防水性；
灰砂15份，通过灰砂的设计，可增强砖体1的硬度；
陶粒15份，因为陶粒具有保温、隔热、耐火性优异、抗震性好、抗冻性能和耐久性能好等优点，所以通过陶粒的设计，可增强砖体1的保温、隔热、耐火性、抗震性、抗冻性能和耐久性能等。
一种便于施工的建筑用砌块砖，还包括砌块砖的制备方法：
S1制作模具：首先制作一个倒凸字形的模具，再准备两个方杆，将两个方杆插入模具内部，同时在模具的底部通过焊接固定两个竖板。
S2涂粉：将模具内部及方杆和竖板上涂上滑石粉。
S3配料：将混凝土、聚氨酯泡沫、灰砂和陶粒放入到搅拌机内部混合，先将混凝土放置于搅拌机内部，再依次放入聚氨酯泡沫、灰砂和陶粒，搅拌机混合时长为20min。
S4注模：将混合好的混凝土放置于模具内部，通过振动棒给模具内部混凝土进行振动，振动棒振动频率为8000次/min，振动时长为6min。
S5插板：将加强板4插入到混凝土内部，加强板4插入的位置处于两个竖板之间。
S6盖模具：再将一个倒凸字形的模盖盖在模具上方，通过小型液压机对模具进行挤压。
S7烘干：然后将模具放置于烘干箱内部烘干，烘干时长为50min。
S8水冷：将模具内部的混凝土烘干成型后，将模具放置冷水内部，水冷时长为25min。
S9取模：经水冷后，将模具拿出砖体1内部。
实施例5：
分别取上述实施例1-4的方法，在四个相同面积的模具内部制作40次砖块，每10个分为一组，成型后检测砖体1的隔热性，得到以下数据：
Figure BDA0002605566020000091
Figure BDA0002605566020000101
由上表可知，实施例4中方法适宜，通过混凝土的设计，因为混凝土具有抗压强度高，耐久性好，强度等级范围宽等特点，所以通过混凝土的设计可增强砖体1的强度和耐久度，聚氨酯泡沫是一种具有保温与防水功能的新型合成材料，通过聚氨酯泡沫的设计可增强砖体1的保温性和防水性，通过灰砂的设计，可增强砖体1的硬度，因为陶粒具有保温、隔热、耐火性优异、抗震性好、抗冻性能和耐久性能好等优点，所以通过陶粒的设计，可增强砖体1的保温、隔热、耐火性、抗震性、抗冻性能和耐久性能等。
以上所述，仅是本发明的较佳实施例，任何熟悉本领域的技术人员均可能利用上述阐述的技术方案对本发明加以修改或将其修改为等同的技术方案。因此，依据本发明的技术方案所进行的任何简单修改或等同置换，尽属于本发明要求保护的范围。

Claims (10)

1.一种便于施工的建筑用砌块砖，包括砖体(1)，其特征在于：所述砖体(1)上开设有两个通槽(2)，两个所述通槽(2)均贯穿砖体(1)，所述砖体(1)上开设有两个方槽(3)，两个所述方槽(3)均贯穿砖体(1)，所述砖体(1)顶部固定设有加强板(4)，所述加强板(4)设于两个通槽(2)之间，所述加强板(4)延伸入砖体(1)内部，所述砖体(1)顶部开设有滑槽(5)，所述砖体(1)底部固定设有滑块(6)。
2.根据权利要求1所述的一种便于施工的建筑用砌块砖，其特征在于：所述加强板(4)由酚醛板制成，所述酚醛板截面形状设为T形。
3.根据权利要求1所述的一种便于施工的建筑用砌块砖，其特征在于：包括混凝土、聚氨酯泡沫、灰砂和陶粒，其中各成分质量份数为：
混凝土30-50份；
聚氨酯泡沫10-20份；
灰砂10-15份；
陶粒10-15份。
4.根据权利要求3所述的一种便于施工的建筑用砌块砖，其特征在于：还包括砌块砖的制备方法：
S1制作模具：首先制作一个倒凸字形的模具，再准备两个方杆，将两个方杆插入模具内部，同时在模具的底部通过焊接固定两个竖板。
S2涂粉：将模具内部及方杆和竖板上涂上滑石粉。
S3配料：将混凝土、聚氨酯泡沫、灰砂和陶粒放入到搅拌机内部混合。
S4注模：将混合好的混凝土放置于模具内部，通过振动棒给模具内部混凝土进行振动。
S5插板：将加强板(4)插入到混凝土内部，加强板(4)插入的位置处于两个竖板之间。
S6盖模具：再将一个倒凸字形的模盖盖在模具上方。
S7烘干：然后将模具放置于烘干箱内部烘干。
S8水冷：将模具内部的混凝土烘干成型后，将模具放置冷水内部。
S9取模：经水冷后，将模具拿出砖体(1)内部。
5.根据权利要求4所述的一种便于施工的建筑用砌块砖，其特征在于：在所述步骤S3中，先将混凝土放置于搅拌机内部，再依次放入聚氨酯泡沫、灰砂和陶粒。
6.根据权利要求4所述的一种便于施工的建筑用砌块砖，其特征在于：在所述步骤S3中，搅拌机混合时长为10-20min。
7.根据权利要求4所述的一种便于施工的建筑用砌块砖，其特征在于：在所述步骤S4中，振动棒振动频率为5000-8000次/min，振动时长为3-6min。
8.根据权利要求4所述的一种便于施工的建筑用砌块砖，其特征在于：在所述步骤S6中，通过小型液压机对模具进行挤压。
9.根据权利要求4所述的一种便于施工的建筑用砌块砖，其特征在于：在所述步骤S7中，烘干时长为30-50min。
10.根据权利要求4所述的一种便于施工的建筑用砌块砖，其特征在于：在所述步骤S8中，水冷时长为15-25min。
CN202010737698.0A 2020-07-28 2020-07-28 一种便于施工的建筑用砌块砖 Pending CN111877601A (zh)