CN103694595A - 一种环保填充电缆料 - Google Patents

一种环保填充电缆料 Download PDF

Info

Publication number
CN103694595A
CN103694595A CN201310652136.6A CN201310652136A CN103694595A CN 103694595 A CN103694595 A CN 103694595A CN 201310652136 A CN201310652136 A CN 201310652136A CN 103694595 A CN103694595 A CN 103694595A
Authority
CN
China
Prior art keywords
powder
kaolinite
parts
oxide
minute
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201310652136.6A
Other languages
English (en)
Other versions
CN103694595B (zh
Inventor
魏善恒
王磊
王国云
何立群
王小宝
郭守恒
肖本国
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Guodian Cable Group Co Ltd
Original Assignee
Anhui Guodian Cable Group Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Guodian Cable Group Co Ltd filed Critical Anhui Guodian Cable Group Co Ltd
Priority to CN201310652136.6A priority Critical patent/CN103694595B/zh
Publication of CN103694595A publication Critical patent/CN103694595A/zh
Application granted granted Critical
Publication of CN103694595B publication Critical patent/CN103694595B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种环保填充电缆料，其是由下述重量份的原料制得：PVC树脂粉90-110、CPE5-8、三氧化二锑5-7、硬脂酸钡2-3、邻苯二甲酸二辛酯2.3-3.5、氧化镝0.1-0.3、氮化硼2-3、抗氧剂3000.3-0.5、抗氧剂626 0.1-0.2、硅酸镁1.4-2.4、环氧丙烷甘油聚醚0.2-0.4、改性纳米高岭石粉10-18，复合填料30-40，偏苯三酸三辛酯0.2-0.4。

Description

一种环保填充电缆料
技术领域
本发明涉及电缆料领域，确切地说是一种环保填充电缆料。
背景技术
聚氯乙烯电缆料即PVC电缆料品质的优劣，根本上是由PVC电缆料配方以及所选用的原料来决定的。随着PVC的各种助剂和填充物的不断更新和发展，也使得PVC电缆料的配方不断完善和提高。
发明内容
本发明的目的在于提供一种环保填充电缆料
上述目的通过以下方案实现：
一种环保填充电缆料，其特征在于：其是由下述重量份的原料制得：PVC树脂粉90-110、CPE5-8、三氧化二锑5-7、硬脂酸钡2-3、邻苯二甲酸二辛酯2.3-3.5、氧化镝0.1-0.3、氮化硼2-3、抗氧剂3000.3-0.5、抗氧剂6260.1-0.2、硅酸镁1.4-2.4、环氧丙烷甘油聚醚0.2-0.4、改性纳米高岭石粉10-18，复合填料30-40，偏苯三酸三辛酯0.2-0.4；
改性纳米高岭石粉的制备方法为：
(1)取高岭石破碎后，在闪烧窑中750-800℃闪烧15-20秒，再于去离子水中于80-90℃下搅拌2-4小时，干燥，再向高岭石中倒入相当于高岭石重量6-9倍的浓度1-3mol/L的盐酸溶液,于35-45℃下，搅拌10-20分钟，再浸泡3-5h，1900-2800r/min离心处理10-19min、去离子水洗涤、烘干，粉碎，过60-100目筛；
（2）在步骤（1）处理后的高岭石中加入相当于其重量1-2%的氯化石蜡、1.5-2.5%的烷基糖苷搅拌均匀后，装入反应釜，然后升温至90-95℃时,保温4-8分钟,再加入相当于高岭石重量1-2%的硬脂酸铝、0.4-0.9%的丙烯酸甲酯，升温至120-130℃,保温8-15分钟,冷却至55-65℃,保温5-7分钟,研磨成纳米粉末后即得；
复合填料由下列重量份的原料制成：
膨润土15-18、黄土5-7、轻质碳酸钙1-2、水镁石粉1-2，重质碳酸钙1-2，氧化镁1-2、硬脂酸钙1-2、氯化石蜡1-2、柠檬酸三丁酯2-3、氢氧化铝4-6；
复合填料的制备方法是将膨润土、黄土在500-550℃下煅烧4-5小时，然后，取出，与氢氧化铝一并加入适量水中研磨，加10-15%盐酸溶液调PH为4.4-5.5，研磨浆料至400-500目后，再加氢氧化钠调为中性，喷雾干燥，得粉末；将所得粉末与其它剩余成分混合，研磨混合均匀即得。
所述的一种环保填充电缆料，其特征在于：
制备方法为：
（1）取PVC树脂粉、CPE、三氧化二锑、硬脂酸钡、邻苯二甲酸二辛酯、氧化镝、氮化硼按重量份混匀，于捏合机中140-150℃下捏合5-10分钟后，取出冷却；
（2）将步骤（1）所得冷却后的胶料与剩余各原料混匀，于双螺杆挤出机中混炼、造粒，控制温度165-170℃，得到成品。
本发明的有益效果为：本发明所得的电缆料环保、阻燃性能好、耐高温、低烟、易剥离，制备工艺简单易行,便于工业化生产,产品质量稳定。
具体实施方式
一种环保填充电缆料，其是由下述重量份（kg)的原料制得：PVC树脂粉102、CPE8、三氧化二锑7、硬脂酸钡3、邻苯二甲酸二辛酯3.1、氧化镝0.3、氮化硼2.3、抗氧剂3000.4、抗氧剂6260.2、硅酸镁2.4、环氧丙烷甘油聚醚0.2、改性纳米高岭石粉18，复合填料40，偏苯三酸三辛酯0.4；
改性纳米高岭石粉的制备方法为：
(1)取高岭石破碎后，在闪烧窑中800℃闪烧20秒，再于去离子水中于90℃下搅拌4小时，干燥，再向高岭石中倒入相当于高岭石重量9倍的浓度3mol/L的盐酸溶液,于45℃下，搅拌20分钟，再浸泡5h，2300r/min离心处理15min、去离子水洗涤、烘干，粉碎，100目筛；
（2）在步骤（1）处理后的高岭石中加入相当于其重量1.3%的氯化石蜡、1.8%的烷基糖苷搅拌均匀后，装入反应釜，然后升温至93℃时,保温5分钟,再加入相当于高岭石重量1%的硬脂酸铝、0.9%的丙烯酸甲酯，升温至125℃,保温10分钟,冷却至60℃,保温6分钟,研磨成纳米粉末后即得；
复合填料由下列重量份（kg)的原料制成：
膨润土16、黄土6、轻质碳酸钙2、水镁石粉1，重质碳酸钙1，氧化镁2、硬脂酸钙2、氯化石蜡1、柠檬酸三丁酯3、氢氧化铝6；
复合填料的制备方法是将膨润土、黄土在550℃下煅烧4小时，然后，取出，与氢氧化铝一并加入适量水中研磨，加15%盐酸溶液调PH为4.9，研磨浆料至400目后，再加氢氧化钠调为中性，喷雾干燥，得粉末；将所得粉末与其它剩余成分混合，研磨混合均匀即得。
所述的一种环保填充电缆料，
制备方法为：
（1）取PVC树脂粉、CPE、三氧化二锑、硬脂酸钡、邻苯二甲酸二辛酯、氧化镝、氮化硼按重量份混匀，于捏合机中150℃下捏合5分钟后，取出冷却；
（2）将步骤（1）所得冷却后的胶料与剩余各原料混匀，于双螺杆挤出机中混炼、造粒，控制温度165℃，得到成品。
将本实施例进行性能测试，所得数据如下：
Figure BDA0000431181100000031
Figure BDA0000431181100000041
从本实施例测试结果可见，本发明的产品经过100℃×168h的老化和80℃×6h高温压力试验，其机械物理性能变化符合相应标注要求，具有良好的物理机械性能，满足不同温度环境变化的需求。

Claims (2)

1.一种环保填充电缆料，其特征在于：其是由下述重量份的原料制得：PVC树脂粉90-110、CPE 5-8、三氧化二锑5-7、硬脂酸钡2-3、邻苯二甲酸二辛酯2.3-3.5、氧化镝0.1-0.3、氮化硼2-3、抗氧剂300 0.3-0.5、抗氧剂626  0.1-0.2、硅酸镁1.4-2.4、环氧丙烷甘油聚醚0.2-0.4、改性纳米高岭石粉10-18，复合填料30-40，偏苯三酸三辛酯0.2-0.4；
   改性纳米高岭石粉的制备方法为：
　　(1)取高岭石破碎后，在闪烧窑中750-800℃闪烧15-20秒，再于去离子水中于80-90℃下搅拌2-4小时，干燥，再向高岭石中倒入相当于高岭石重量6-9倍的浓度1-3mol/L的盐酸溶液,于35-45℃下，搅拌10-20分钟，再浸泡3-5h，1900-2800r/min离心处理10-19min、去离子水洗涤、烘干，粉碎，过60-100目筛；
（2）在步骤（1）处理后的高岭石中加入相当于其重量1-2%的氯化石蜡、1.5-2.5%的烷基糖苷搅拌均匀后，装入反应釜，然后升温至90-95℃时,保温4-8分钟,再加入相当于高岭石重量1-2%的硬脂酸铝、0.4-0.9%的丙烯酸甲酯，升温至120-130℃,保温8-15分钟,冷却至55-65℃,保温5-7分钟,研磨成纳米粉末后即得；
复合填料由下列重量份的原料制成：
膨润土15-18、黄土5-7、轻质碳酸钙1-2、水镁石粉1-2，重质碳酸钙1-2，氧化镁1-2、硬脂酸钙1-2、氯化石蜡1-2、柠檬酸三丁酯2-3、氢氧化铝4-6；
复合填料的制备方法是将膨润土、黄土在500-550℃下煅烧4-5小时，然后，取出，与氢氧化铝一并加入适量水中研磨，加10-15%盐酸溶液调PH为4.4-5.5，研磨浆料至400-500目后，再加氢氧化钠调为中性，喷雾干燥，得粉末；将所得粉末与其它剩余成分混合，研磨混合均匀即得。
2.根据权利要求1所述的一种环保填充电缆料，其特征在于：
  制备方法为：
　　（1）取PVC树脂粉、CPE、三氧化二锑、硬脂酸钡、邻苯二甲酸二辛酯、氧化镝、氮化硼按重量份混匀，于捏合机中140-150℃下捏合5-10分钟后，取出冷却；
　　（2）将步骤（1）所得冷却后的胶料与剩余各原料混匀，于双螺杆挤出机中混炼、造粒，控制温度165-170℃，得到成品。
CN201310652136.6A 2013-12-03 2013-12-03 一种环保填充电缆料 Active CN103694595B (zh)