CN103666052A - 一种环保型紫外光固化印铁油墨及其制备方法 - Google Patents
一种环保型紫外光固化印铁油墨及其制备方法 Download PDFInfo
- Publication number
- CN103666052A CN103666052A CN201310600754.6A CN201310600754A CN103666052A CN 103666052 A CN103666052 A CN 103666052A CN 201310600754 A CN201310600754 A CN 201310600754A CN 103666052 A CN103666052 A CN 103666052A
- Authority
- CN
- China
- Prior art keywords
- parts
- printing ink
- friendly
- environment
- tin printing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种环保型紫外光固化印铁油墨,其特征在于,由下列重量份的原料制备制成:有机颜料1-2、氢氧化镧1-2、柠檬酸钙2-3、二缩三丙二醇二丙烯酸酯9-12、氧化锆1-2、三聚氰胺1-2、12-羟基硬脂酸1-2、防老剂MB1-2、2-硫醇基苯骈咪唑1-2、甲基三甲氧基硅烷1-3、醋酸乙烯酯7-9、丙酸乙烯酯4-6、促进剂CZ1-2、三丁基三氯化锡1-2、2959光引发剂4-6、助剂4-5;本发明助剂提高了油墨的韧性,使油墨分散均匀,并且维持了油墨的稳定性;本发明紫外光固化印铁油墨更能降低生产成本,节约能源,加快印刷速度,提高生产效率,操作简单,而且无溶剂排放,对环境友好。
Description
技术领域
本发明涉及一种油墨及其制备方法,特别是一种环保型紫外光固化印铁油墨及其制备方法。
背景技术
印铁油墨广泛应用于食品、饮料罐、保温瓶壳、玩具、化妆品盒等的印刷。应用于凸版胶印机和湿式胶印方式印刷铁皮(马口铁)和处理钢板、铝板等金属用油墨的总称。印铁油墨主要特性是对金属片的黏附强,耐蒸煮、耐烤烘、耐溶剂、耐光及加工性好(成型、冲切、接缝等)。干燥形式有烘烤型和紫外光固化型。目前国内对普通印铁油墨的固化采用的是加热烘烤,需要使用大量的天然气,石油液化气,或电能。而且印铁生产线后置烘炉一般长21-30米,占用场地空间;而且普通印铁油墨含有大量的挥发性,不够环保。采用紫外光(UV)固化方式,完全颠覆了传统的印铁方式,能为企业大幅降低生产成本,提高生产效率,降低了生产成本。
发明内容
本发明的目的是提供一种环保型紫外光固化印铁油墨及其制备方法。
为了实现本发明的目的,本发明通过以下方案实施:
一种环保型紫外光固化印铁油墨,由下列重量份的原料制备制成:有机颜料1-2、氢氧化镧1-2、柠檬酸钙2-3、二缩三丙二醇二丙烯酸酯9-12、氧化锆1-2、三聚氰胺1-2、12-羟基硬脂酸1-2、防老剂MB 1-2、2-硫醇基苯骈咪唑1-2、甲基三甲氧基硅烷1-3、醋酸乙烯酯7-9、丙酸乙烯酯4-6、促进剂CZ1-2、三丁基三氯化锡1-2、2959光引发剂4-6、助剂4-5;
所述助剂由下列重量份的原料制备而成:纳米硅藻土粉0.2-0.3、纳米云母粉0.2-0.3、硅烷偶联剂KH-550 2-3、茶多酚2-3、新戊二醇5-7、对叔丁基苯甲酸1-2、抗氧剂1035 1-2、2-丁氧基-乙醇3-4、交联剂TAC2-3、乙氧基化三羟甲基丙烷三丙烯酸酯10-12、没食子酸丙酯2-3、薏仁油1-2;其制备方法是将各物料混合,加热至60-70℃,搅拌反应30-40分钟,即得。
本发明所述环保型紫外光固化印铁油墨,由以下具体步骤制成:首先加入有机颜料、氢氧化镧、柠檬酸钙、二缩三丙二醇二丙烯酸酯、氧化锆、三聚氰胺、12-羟基硬脂酸、防老剂MB、2-硫醇基苯骈咪唑、甲基三甲氧基硅烷搅拌混匀,加热至80-90℃,搅拌25-35分钟;然后加入除2959光引发剂之外的其余剩余成分,搅拌反应3-5小时;最后降温至60-70℃,加入2959光引发剂,搅拌反应40-50分钟,冷却后,研磨得到20-40μm浆料,即得。
本发明的有益效果是:本发明助剂提高了油墨的韧性,使油墨分散均匀,并且维持了油墨的稳定性;本发明紫外光固化印铁油墨更能降低生产成本,节约能源,加快印刷速度,提高生产效率,操作简单,而且无溶剂排放,对环境友好。
具体实施方案
下面通过具体实例对本发明进行详细说明。
一种环保型紫外光固化印铁油墨,由下列重量份(公斤)的原料制备制成:有机颜料1、氢氧化镧1、柠檬酸钙2、二缩三丙二醇二丙烯酸酯9、氧化锆1、三聚氰胺1、12-羟基硬脂酸1、防老剂MB 1、2-硫醇基苯骈咪唑1、甲基三甲氧基硅烷1、醋酸乙烯酯7、丙酸乙烯酯4、促进剂CZ1、三丁基三氯化锡1、2959光引发剂4、助剂4;
所述助剂由下列重量份(公斤)的原料制备而成:纳米硅藻土粉0.2、纳米云母粉0.2、硅烷偶联剂KH-550 2、茶多酚2、新戊二醇5、对叔丁基苯甲酸1、抗氧剂1035 1、2-丁氧基-乙醇3、交联剂TAC 2、乙氧基化三羟甲基丙烷三丙烯酸酯10、没食子酸丙酯2、薏仁油1;其制备方法是将各物料混合,加热至60-70℃,搅拌反应30-40分钟,即得。
本发明所述环保型紫外光固化印铁油墨,由以下具体步骤制成:首先加入有机颜料、氢氧化镧、柠檬酸钙、二缩三丙二醇二丙烯酸酯、氧化锆、三聚氰胺、12-羟基硬脂酸、防老剂MB、2-硫醇基苯骈咪唑、甲基三甲氧基硅烷搅拌混匀,加热至80-90℃,搅拌25-35分钟;然后加入除2959光引发剂之外的其余剩余成分,搅拌反应3-5小时;最后降温至60-70℃,加入2959光引发剂,搅拌反应40-50分钟,冷却后,研磨得到20-40μm浆料,即得。
所得的油墨,使用划格法牛皮胶带剥离,划格间距1mm,100%附着;使用浸有酒精的棉球,300克压力擦拭50次,无异状;浸泡于色拉油中(常温)8小时,无异状;使用浸有盐水的棉球,300克压力擦拭50次,无异状。
Claims (2)
1.一种环保型紫外光固化印铁油墨,其特征在于,由下列重量份的原料制备制成:有机颜料1-2、氢氧化镧1-2、柠檬酸钙2-3、二缩三丙二醇二丙烯酸酯9-12、氧化锆1-2、三聚氰胺1-2、12-羟基硬脂酸1-2、防老剂MB 1-2、2-硫醇基苯骈咪唑1-2、甲基三甲氧基硅烷1-3、醋酸乙烯酯7-9、丙酸乙烯酯4-6、促进剂CZ1-2、三丁基三氯化锡1-2、2959光引发剂4-6、助剂4-5;
所述助剂由下列重量份的原料制备而成:纳米硅藻土粉0.2-0.3、纳米云母粉0.2-0.3、硅烷偶联剂KH-550 2-3、茶多酚2-3、新戊二醇5-7、对叔丁基苯甲酸1-2、抗氧剂1035 1-2、2-丁氧基-乙醇3-4、交联剂TAC2-3、乙氧基化三羟甲基丙烷三丙烯酸酯10-12、没食子酸丙酯2-3、薏仁油1-2;其制备方法是将各物料混合,加热至60-70℃,搅拌反应30-40分钟,即得。
2.根据权利要求1所述环保型紫外光固化印铁油墨,其特征在于,由以下具体步骤制成:首先加入有机颜料、氢氧化镧、柠檬酸钙、二缩三丙二醇二丙烯酸酯、氧化锆、三聚氰胺、12-羟基硬脂酸、防老剂MB、2-硫醇基苯骈咪唑、甲基三甲氧基硅烷搅拌混匀,加热至80-90℃,搅拌25-35分钟;然后加入除2959光引发剂之外的其余剩余成分,搅拌反应3-5小时;最后降温至60-70℃,加入2959光引发剂,搅拌反应40-50分钟,冷却后,研磨得到20-40μm浆料,即得。