CN103643267A - 金属紧固件的电镀工艺 - Google Patents

金属紧固件的电镀工艺 Download PDF

Info

Publication number
CN103643267A
CN103643267A CN201310605144.5A CN201310605144A CN103643267A CN 103643267 A CN103643267 A CN 103643267A CN 201310605144 A CN201310605144 A CN 201310605144A CN 103643267 A CN103643267 A CN 103643267A
Authority
CN
China
Prior art keywords
electroplating
acid
sodium
anode
solution
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310605144.5A
Other languages
English (en)
Inventor
查希炜
查清源
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Changshu Foch Machinery Spare Parts Manufacturing Co Ltd
Original Assignee
Changshu Foch Machinery Spare Parts Manufacturing Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Changshu Foch Machinery Spare Parts Manufacturing Co Ltd filed Critical Changshu Foch Machinery Spare Parts Manufacturing Co Ltd
Priority to CN201310605144.5A priority Critical patent/CN103643267A/zh
Publication of CN103643267A publication Critical patent/CN103643267A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种金属紧固件的电镀工艺，包括如下步骤：1）先电镀铜；2）再电镀镍；3）最后电镀锌。本发明提供的金属紧固件的电镀工艺，其能避免氢脆现象的发生，使电镀层结合牢固，使电镀沉积速度加快。

Description

金属紧固件的电镀工艺
技术领域
本发明涉及金属紧固件的电镀工艺。
背景技术
 金属紧固件防锈蚀一般是在表面镀锌，但容易产生氢脆。氢脆会导致金属紧固件锁付后经过一段时间放置后或在锁付后振动出现断裂。一般有两种热处理方法来改善镀锌金属紧固件的氢脆现象：
第一种方法是降低热处理时的强度，来降低金属紧固件镀锌时本身对氢的敏感性；此方法常常会达不到金属紧固件使用时的强度，度很难掌握。
第二种方法是在电镀锌时除氢工艺中必须把温度控制在190-210℃的恒温箱中退氢4小时。
上述两种方法不能够完全杜绝氢脆现象，只能在一定程度降低氢脆现象。
发明内容
本发明的目的在于提供一种金属紧固件的电镀工艺，其能避免氢脆现象的发生，使电镀层结合牢固，使电镀沉积速度加快。
为实现上述目的，本发明的技术方案是设计一种金属紧固件的电镀工艺，包括如下步骤：
 1）先电镀铜：电镀溶液由200-250mg/L的硫酸铜、80-90mg/L的柠檬酸钾、80-90mg/L的环烷酸铜、40-50mg/L的葡萄糖、100-120mg/L的柠檬酸、200-250mg/L的柠檬酸铜、50-55mg/L的次磷酸钠和30-40mg/L的苹果酸组成；溶液温度为30-35℃，电镀电流密度为4-5安培/平方分米，电镀时间为20-30min，阳极为4‰的含磷铜板，阳极与阴极的面积比1.5:1；
 2）再电镀镍：电镀溶液由150-160mg/L的氢氧化钠、80-90mg/L的硼酸、40-55mg/L的氯化镍、10-15mg/L的丁二酸、2-4mg/L的十二烷基苯磺酸钠、20-25mg/L的氯化钠、60-70g/L的氨基磺酸镍、200-250g/L的黑镍盐、20-30mg/L的亚磷酸和40-50mg/L的羟甲基丙烯酸组成；溶液温度为40-45℃，电镀电流密度为1-1.5安培/平方分米，电镀时间为45-50min，阳极为不锈钢；
3）最后电镀锌：电镀溶液由200-220mg/L的氢氧化钠、5-10mg/L的乙二胺、25-30mg/L的三乙醇胺、150-160mg/L的氯化铵、10-15mg/L的氧化锌、60-70mg/L的苯甲酸钠、40-50mg/L的亚磷酸、60-70mg/L的琥珀酸二异辛酯磺酸钠和50-70mg/L的氯化钠组成；溶液温度为35-40℃，电镀电流密度为4-5安培/平方分米，电镀时间为5-7min，阳极为不锈钢或纯锌板。 
本发明的优点和有益效果在于：提供一种金属紧固件的电镀工艺，其能避免氢脆现象的发生，使电镀层结合牢固，使电镀沉积速度加快。
具体实施方式
下面结合实施例，对本发明的具体实施方式作进一步描述。以下实施例仅用于更加清楚地说明本发明的技术方案，而不能以此来限制本发明的保护范围。
本发明具体实施的技术方案是：
实施例1
一种金属紧固件的电镀工艺，包括如下步骤：
 1）先电镀铜：电镀溶液由250mg/L的硫酸铜、90mg/L的柠檬酸钾、90mg/L的环烷酸铜、50mg/L的葡萄糖、120mg/L的柠檬酸、250mg/L的柠檬酸铜、55mg/L的次磷酸钠和40mg/L的苹果酸组成；溶液温度为35℃，电镀电流密度为5安培/平方分米，电镀时间为30min，阳极为4‰的含磷铜板，阳极与阴极的面积比1.5:1；
 2）再电镀镍：电镀溶液由160mg/L的氢氧化钠、90mg/L的硼酸、55mg/L的氯化镍、15mg/L的丁二酸、4mg/L的十二烷基苯磺酸钠、25mg/L的氯化钠、70g/L的氨基磺酸镍、250g/L的黑镍盐、30mg/L的亚磷酸和50mg/L的羟甲基丙烯酸组成；溶液温度为45℃，电镀电流密度为1.5安培/平方分米，电镀时间为50min，阳极为不锈钢；
3）最后电镀锌：电镀溶液由220mg/L的氢氧化钠、10mg/L的乙二胺、30mg/L的三乙醇胺、160mg/L的氯化铵、15mg/L的氧化锌、70mg/L的苯甲酸钠、50mg/L的亚磷酸、70mg/L的琥珀酸二异辛酯磺酸钠和70mg/L的氯化钠组成；溶液温度为40℃，电镀电流密度为5安培/平方分米，电镀时间为7min，阳极为不锈钢或纯锌板。
实施例2
一种金属紧固件的电镀工艺，包括如下步骤：
 1）先电镀铜：电镀溶液由230mg/L的硫酸铜、84mg/L的柠檬酸钾、86mg/L的环烷酸铜、43mg/L的葡萄糖、110mg/L的柠檬酸、220mg/L的柠檬酸铜、52mg/L的次磷酸钠和36mg/L的苹果酸组成；溶液温度为32℃，电镀电流密度为4.5安培/平方分米，电镀时间为23min，阳极为4‰的含磷铜板，阳极与阴极的面积比1.5:1；
 2）再电镀镍：电镀溶液由157mg/L的氢氧化钠、87mg/L的硼酸、45mg/L的氯化镍、13mg/L的丁二酸、3mg/L的十二烷基苯磺酸钠、22mg/L的氯化钠、64g/L的氨基磺酸镍、231g/L的黑镍盐、25mg/L的亚磷酸和48mg/L的羟甲基丙烯酸组成；溶液温度为44℃，电镀电流密度为1.4安培/平方分米，电镀时间为47min，阳极为不锈钢；
3）最后电镀锌：电镀溶液由213mg/L的氢氧化钠、7mg/L的乙二胺、28mg/L的三乙醇胺、154mg/L的氯化铵、12mg/L的氧化锌、68mg/L的苯甲酸钠、42mg/L的亚磷酸、61mg/L的琥珀酸二异辛酯磺酸钠和59mg/L的氯化钠组成；溶液温度为38℃，电镀电流密度为4.5安培/平方分米，电镀时间为6min，阳极为不锈钢或纯锌板。
实施例3
一种金属紧固件的电镀工艺，包括如下步骤：
 1）先电镀铜：电镀溶液由200mg/L的硫酸铜、80mg/L的柠檬酸钾、80mg/L的环烷酸铜、40mg/L的葡萄糖、100mg/L的柠檬酸、200mg/L的柠檬酸铜、50mg/L的次磷酸钠和30mg/L的苹果酸组成；溶液温度为30℃，电镀电流密度为4安培/平方分米，电镀时间为20min，阳极为4‰的含磷铜板，阳极与阴极的面积比1.5:1；
 2）再电镀镍：电镀溶液由150mg/L的氢氧化钠、80mg/L的硼酸、40mg/L的氯化镍、10mg/L的丁二酸、2mg/L的十二烷基苯磺酸钠、20mg/L的氯化钠、60g/L的氨基磺酸镍、200g/L的黑镍盐、20mg/L的亚磷酸和40mg/L的羟甲基丙烯酸组成；溶液温度为40℃，电镀电流密度为1安培/平方分米，电镀时间为45min，阳极为不锈钢；
 3）最后电镀锌：电镀溶液由200mg/L的氢氧化钠、5mg/L的乙二胺、25mg/L的三乙醇胺、150mg/L的氯化铵、10mg/L的氧化锌、60mg/L的苯甲酸钠、40mg/L的亚磷酸、60mg/L的琥珀酸二异辛酯磺酸钠和50mg/L的氯化钠组成；溶液温度为35℃，电镀电流密度为4安培/平方分米，电镀时间为5min，阳极为不锈钢或纯锌板。
以上所述仅是本发明的优选实施方式，应当指出，对于本技术领域的普通技术人员来说，在不脱离本发明技术原理的前提下，还可以做出若干改进和润饰，这些改进和润饰也应视为本发明的保护范围。

Claims (1)

1.金属紧固件的电镀工艺，其特征在于，包括如下步骤：
先电镀铜：电镀溶液由200-250mg/L的硫酸铜、80-90mg/L的柠檬酸钾、80-90mg/L的环烷酸铜、40-50mg/L的葡萄糖、100-120mg/L的柠檬酸、200-250mg/L的柠檬酸铜、50-55mg/L的次磷酸钠和30-40mg/L的苹果酸组成；溶液温度为30-35℃，电镀电流密度为4-5安培/平方分米，电镀时间为20-30min，阳极为4‰的含磷铜板，阳极与阴极的面积比1.5:1；
 2）再电镀镍：电镀溶液由150-160mg/L的氢氧化钠、80-90mg/L的硼酸、40-55mg/L的氯化镍、10-15mg/L的丁二酸、2-4mg/L的十二烷基苯磺酸钠、20-25mg/L的氯化钠、60-70g/L的氨基磺酸镍、200-250g/L的黑镍盐、20-30mg/L的亚磷酸和40-50mg/L的羟甲基丙烯酸组成；溶液温度为40-45℃，电镀电流密度为1-1.5安培/平方分米，电镀时间为45-50min，阳极为不锈钢；
3）最后电镀锌：电镀溶液由200-220mg/L的氢氧化钠、5-10mg/L的乙二胺、25-30mg/L的三乙醇胺、150-160mg/L的氯化铵、10-15mg/L的氧化锌、60-70mg/L的苯甲酸钠、40-50mg/L的亚磷酸、60-70mg/L的琥珀酸二异辛酯磺酸钠和50-70mg/L的氯化钠组成；溶液温度为35-40℃，电镀电流密度为4-5安培/平方分米，电镀时间为5-7min，阳极为不锈钢或纯锌板。
CN201310605144.5A 2013-11-26 2013-11-26 金属紧固件的电镀工艺 Pending CN103643267A (zh)