CN103643229A - 金属紧固件用磷化液 - Google Patents
金属紧固件用磷化液 Download PDFInfo
- Publication number
- CN103643229A CN103643229A CN201310605015.6A CN201310605015A CN103643229A CN 103643229 A CN103643229 A CN 103643229A CN 201310605015 A CN201310605015 A CN 201310605015A CN 103643229 A CN103643229 A CN 103643229A
- Authority
- CN
- China
- Prior art keywords
- mass parts
- mass
- parts
- zinc
- phosphating solution
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种金属紧固件用磷化液,由10-12质量份磷酸二氢盐、11-15质量份磷酸、1-2质量份乙二胺四乙酸、8-9质量份磷酸锌、2-3质量份氧化锌、3-4质量份硝酸、2-4质量份碳酸锰、1-2质量份过硼酸钠、7-9质量份硝酸镍、20-25质量份硫酸锌、11-13质量份酒石酸、3-4质量份硝酸锌、4-6质量份硫酸镍、6-8质量份碳酸钠、3-5质量份柠檬酸、2-4质量份氯酸钾和60-70质量份水混合均匀制得。本发明提供的金属紧固件用磷化液,稳定性好,处理时间短,形成的磷化膜层强度大,附着力好,耐腐蚀性强。
Description
技术领域
本发明涉及金属紧固件用磷化液。
背景技术
金属紧固件表面需要喷漆或者喷塑处理,从而防止金属紧固件被腐蚀。为了提高面漆或喷塑的附着力,金属紧固件在进行表面喷塑或者喷漆之前,需要用磷化液进行前处理。但传统使用的磷化液使用温度高,耗能大,处理时间长,而且成本高,处理时间过长。
发明内容
本发明的目的在于提供一种金属紧固件用磷化液,其稳定性好,处理时间短,形成的磷化膜层强度大,附着力好,耐腐蚀性强。
为实现上述目的,本发明的技术方案是设计一种金属紧固件用磷化液,由10-12质量份磷酸二氢盐、11-15质量份磷酸、1-2质量份乙二胺四乙酸、8-9质量份磷酸锌、2-3质量份氧化锌、3-4质量份硝酸、2-4质量份碳酸锰、1-2质量份过硼酸钠、7-9质量份硝酸镍、20-25质量份硫酸锌、11-13质量份酒石酸、3-4质量份硝酸锌、4-6质量份硫酸镍、6-8质量份碳酸钠、3-5质量份柠檬酸、2-4质量份氯酸钾和60-70质量份水混合均匀制得。
本发明的优点和有益效果在于:提供一种金属紧固件用磷化液,其稳定性好,处理时间短,形成的磷化膜层强度大,附着力好,耐腐蚀性强。
具体实施方式
下面结合实施例,对本发明的具体实施方式作进一步描述。以下实施例仅用于更加清楚地说明本发明的技术方案,而不能以此来限制本发明的保护范围。
本发明具体实施的技术方案是:
实施例1
一种金属紧固件用磷化液,由10质量份磷酸二氢盐、11质量份磷酸、1质量份乙二胺四乙酸、8质量份磷酸锌、2质量份氧化锌、3质量份硝酸、2质量份碳酸锰、1质量份过硼酸钠、7质量份硝酸镍、20质量份硫酸锌、11质量份酒石酸、3质量份硝酸锌、4质量份硫酸镍、6质量份碳酸钠、3质量份柠檬酸、2质量份氯酸钾和60质量份水混合均匀制得。
实施例2
一种金属紧固件用磷化液,由11质量份磷酸二氢盐、13质量份磷酸、1.5质量份乙二胺四乙酸、8.7质量份磷酸锌、2.3质量份氧化锌、3.4质量份硝酸、2.4质量份碳酸锰、1.2质量份过硼酸钠、7.9质量份硝酸镍、23质量份硫酸锌、12质量份酒石酸、3.4质量份硝酸锌、4.6质量份硫酸镍、6.8质量份碳酸钠、3.5质量份柠檬酸、2.4质量份氯酸钾和64质量份水混合均匀制得。
实施例3
一种金属紧固件用磷化液,由2质量份磷酸二氢盐、15质量份磷酸、2质量份乙二胺四乙酸、9质量份磷酸锌、3质量份氧化锌、4质量份硝酸、4质量份碳酸锰、2质量份过硼酸钠、9质量份硝酸镍、25质量份硫酸锌、13质量份酒石酸、4质量份硝酸锌、6质量份硫酸镍、8质量份碳酸钠、5质量份柠檬酸、4质量份氯酸钾和70质量份水混合均匀制得。
以上所述仅是本发明的优选实施方式,应当指出,对于本技术领域的普通技术人员来说,在不脱离本发明技术原理的前提下,还可以做出若干改进和润饰,这些改进和润饰也应视为本发明的保护范围。
Claims (1)
1.金属紧固件用磷化液,其特征在于,由10-12质量份磷酸二氢盐、11-15质量份磷酸、1-2质量份乙二胺四乙酸、8-9质量份磷酸锌、2-3质量份氧化锌、3-4质量份硝酸、2-4质量份碳酸锰、1-2质量份过硼酸钠、7-9质量份硝酸镍、20-25质量份硫酸锌、11-13质量份酒石酸、3-4质量份硝酸锌、4-6质量份硫酸镍、6-8质量份碳酸钠、3-5质量份柠檬酸、2-4质量份氯酸钾和60-70质量份水混合均匀制得。