CN103641947A - 织物三防整理剂的制备方法 - Google Patents
织物三防整理剂的制备方法 Download PDFInfo
- Publication number
- CN103641947A CN103641947A CN201310625479.3A CN201310625479A CN103641947A CN 103641947 A CN103641947 A CN 103641947A CN 201310625479 A CN201310625479 A CN 201310625479A CN 103641947 A CN103641947 A CN 103641947A
- Authority
- CN
- China
- Prior art keywords
- mass parts
- proofing
- finishing agent
- mixed
- emulsion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种织物三防整理剂的制备方法,包括如下步骤:1)取丙酮、水组成的混合溶剂;2)将混合溶剂与甲基丙烯酸羟乙酯、甲基丙烯酸全氟壬烯氧基乙酯、甲基丙烯酸缩水甘油酯、甲基丙烯酸十八酯、聚乙二醇双硬脂酸酯、十二烷基三甲基氯化铵、十六烷基三甲基氯化铵、脂肪醇聚氧乙烯醚混合均匀,形成混合液;3)将混合液搅拌混合后倒入均质机内均质,得乳白色预乳液;4)然后在40-45℃下向预乳液中滴加1-2质量份偶氮二异丁酸二甲酯、1-2质量份聚丙烯酸钠、2-3质量份偶氮二异丁咪唑盐酸盐;5)滴加完毕,保温反应11-12小时,冷却至室温并过滤,即得产品。本发明制备的织物三防整理剂不含PFOS,避免PFOS对环境的影响。
Description
技术领域
本发明涉及织物三防整理剂的制备方法。
背景技术
目前常用的织物三防整理剂含全氟辛烷磺酰基化合物PFOS,PFOS是一种非常持久、生物积累和有毒的化学品,不但会造成呼吸系统伤害、导致新生儿死亡,并且分布在血液和肝脏内,很难通过新陈代谢而分解。
发明内容
本发明的目的在于提供一种织物三防整理剂的制备方法,其制备的织物三防整理剂不含PFOS,避免PFOS对环境的影响。
为实现上述目的,本发明的技术方案是设计一种织物三防整理剂的制备方法,包括如下步骤:
1)取12-32质量份丙酮、300-600质量份水组成的混合溶剂;
2)将混合溶剂与15-20质量份甲基丙烯酸羟乙酯、30-40质量份甲基丙烯酸全氟壬烯氧基乙酯、8-9质量份甲基丙烯酸缩水甘油酯、60-70质量份甲基丙烯酸十八酯、1-2质量份聚乙二醇双硬脂酸酯、1-2质量份十二烷基三甲基氯化铵、2-3质量份十六烷基三甲基氯化铵、5-6质量份脂肪醇聚氧乙烯醚混合均匀,形成混合液;
3)将混合液搅拌混合后倒入均质机内均质,得乳白色预乳液;
4)然后在40-45℃下向预乳液中滴加1-2质量份偶氮二异丁酸二甲酯、1-2质量份聚丙烯酸钠、2-3质量份偶氮二异丁咪唑盐酸盐;
5)滴加完毕,保温反应11-12小时,冷却至室温并过滤,即得产品。
本发明的优点和有益效果在于:提供一种织物三防整理剂的制备方法,其制备的织物三防整理剂不含PFOS,避免PFOS对环境的影响。
具体实施方式
下面结合实施例,对本发明的具体实施方式作进一步描述。以下实施例仅用于更加清楚地说明本发明的技术方案,而不能以此来限制本发明的保护范围。
本发明具体实施的技术方案是:
实施例1
一种织物三防整理剂的制备方法,包括如下步骤:
1)取32质量份丙酮、600质量份水组成的混合溶剂;
2)将混合溶剂与20质量份甲基丙烯酸羟乙酯、40质量份甲基丙烯酸全氟壬烯氧基乙酯、9质量份甲基丙烯酸缩水甘油酯、70质量份甲基丙烯酸十八酯、2质量份聚乙二醇双硬脂酸酯、2质量份十二烷基三甲基氯化铵、3质量份十六烷基三甲基氯化铵、6质量份脂肪醇聚氧乙烯醚混合均匀,形成混合液;
3)将混合液搅拌混合后倒入均质机内均质,得乳白色预乳液;
4)然后在45℃下向预乳液中滴加2质量份偶氮二异丁酸二甲酯、2质量份聚丙烯酸钠、3质量份偶氮二异丁咪唑盐酸盐;
5)滴加完毕,保温反应12小时,冷却至室温并过滤,即得产品。
实施例2
一种织物三防整理剂的制备方法,包括如下步骤:
1)取12质量份丙酮、300质量份水组成的混合溶剂;
2)将混合溶剂与15质量份甲基丙烯酸羟乙酯、30质量份甲基丙烯酸全氟壬烯氧基乙酯、8质量份甲基丙烯酸缩水甘油酯、60质量份甲基丙烯酸十八酯、1质量份聚乙二醇双硬脂酸酯、1质量份十二烷基三甲基氯化铵、2质量份十六烷基三甲基氯化铵、5质量份脂肪醇聚氧乙烯醚混合均匀,形成混合液;
3)将混合液搅拌混合后倒入均质机内均质,得乳白色预乳液;
4)然后在40℃下向预乳液中滴加1质量份偶氮二异丁酸二甲酯、1质量份聚丙烯酸钠、2质量份偶氮二异丁咪唑盐酸盐;
5)滴加完毕,保温反应11小时,冷却至室温并过滤,即得产品。
实施例3
一种织物三防整理剂的制备方法,包括如下步骤:
1)取22质量份丙酮、400质量份水组成的混合溶剂;
2)将混合溶剂与18质量份甲基丙烯酸羟乙酯、35质量份甲基丙烯酸全氟壬烯氧基乙酯、8.9质量份甲基丙烯酸缩水甘油酯、66质量份甲基丙烯酸十八酯、1.2质量份聚乙二醇双硬脂酸酯、1.2质量份十二烷基三甲基氯化铵、2.3质量份十六烷基三甲基氯化铵、5.6质量份脂肪醇聚氧乙烯醚混合均匀,形成混合液;
3)将混合液搅拌混合后倒入均质机内均质,得乳白色预乳液;
4)然后在43℃下向预乳液中滴加1.2质量份偶氮二异丁酸二甲酯、1.2质量份聚丙烯酸钠、2.3质量份偶氮二异丁咪唑盐酸盐;
5)滴加完毕,保温反应11.5小时,冷却至室温并过滤,即得产品。
以上所述仅是本发明的优选实施方式,应当指出,对于本技术领域的普通技术人员来说,在不脱离本发明技术原理的前提下,还可以做出若干改进和润饰,这些改进和润饰也应视为本发明的保护范围。
Claims (1)
1.织物三防整理剂的制备方法,其特征在于,包括如下步骤:
1)取12-32质量份丙酮、300-600质量份水组成的混合溶剂;
2)将混合溶剂与15-20质量份甲基丙烯酸羟乙酯、30-40质量份甲基丙烯酸全氟壬烯氧基乙酯、8-9质量份甲基丙烯酸缩水甘油酯、60-70质量份甲基丙烯酸十八酯、1-2质量份聚乙二醇双硬脂酸酯、1-2质量份十二烷基三甲基氯化铵、2-3质量份十六烷基三甲基氯化铵、5-6质量份脂肪醇聚氧乙烯醚混合均匀,形成混合液;
3)将混合液搅拌混合后倒入均质机内均质,得乳白色预乳液;
4)然后在40-45℃下向预乳液中滴加1-2质量份偶氮二异丁酸二甲酯、1-2质量份聚丙烯酸钠、2-3质量份偶氮二异丁咪唑盐酸盐;
5)滴加完毕,保温反应11-12小时,冷却至室温并过滤,即得产品。