CN103613956B - 机械力化学改性硅微粉的制备方法 - Google Patents

机械力化学改性硅微粉的制备方法 Download PDF

Info

Publication number
CN103613956B
CN103613956B CN201310599168.4A CN201310599168A CN103613956B CN 103613956 B CN103613956 B CN 103613956B CN 201310599168 A CN201310599168 A CN 201310599168A CN 103613956 B CN103613956 B CN 103613956B
Authority
CN
China
Prior art keywords
hexamethyldisilazane
ball mill
mechanical
preparation
chemical modification
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201310599168.4A
Other languages
English (en)
Other versions
CN103613956A (zh
Inventor
张建平
姜兵
王敏
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JIANGSU LIANRUI NEW MATERIAL Co Ltd
Original Assignee
JIANGSU LIANRUI NEW MATERIAL Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JIANGSU LIANRUI NEW MATERIAL Co Ltd filed Critical JIANGSU LIANRUI NEW MATERIAL Co Ltd
Priority to CN201310599168.4A priority Critical patent/CN103613956B/zh
Publication of CN103613956A publication Critical patent/CN103613956A/zh
Application granted granted Critical
Publication of CN103613956B publication Critical patent/CN103613956B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明是一种机械力化学改性硅微粉的制备方法，其步骤如下：将氧化铝球装入球磨机中；将4~16目石英砂和改性剂六甲基二硅胺烷同时加入球磨机中，六甲基二硅胺烷用量为石英砂质量的0.1‰~2‰，在30~50rpm的转速下，研磨0.5h~4h出料，筛分，利用不同孔径的筛网得到区别粒径的改性硅微粉。本发明方法减少了生产阶段，简化了工艺流程，提高了生产效率；不涉及溶剂的使用及熔炼，减少了环境的污染；可以获得用传统工艺很难或不能获得的产品；改性效果好，改性剂在矿物表面吸附牢固；自动化生产程度高，产品稳定性和一致性好。

Description

机械力化学改性硅微粉的制备方法
技术领域
本发明涉及一种硅微粉的制备方法，特别是一种机械力化学改性硅微粉的制备方法。
背景技术
物料在机械力作用下，产生各种物理及化学现象，其内部结构、物理化学性质以及化学反应性也相应地产生一系列变化。物料在强的机械力作用下受到剧烈的冲击，在晶体结构被破坏的同时，局部还会产生等离子体过程，降低体系反应的温度和活化能，从而诱发物质间的反应。
粉体与表面改性剂的作用机理和界面结合的方式，主要包括吸附或化学反应的类型、作用力或键合的强弱、热力学性质的变化等。目前粉体的表面改性方法很多。根据改性的具体实施工艺可分为：湿法、干法；根据改性的原理可分为：物理改性、化学改性，物理改性有：表面涂覆、表面活性剂改性、高能表面改性、胶囊化处理，化学改性有：表面沉积法、化学包覆、机械力化学、单体吸附包裹后聚合等。表面改性剂种类很多，如硅烷、钛酸酯、铝酸酯、有机铬等各种偶联剂，各类表面活性剂，不饱和有机酸，水溶性有机高聚物等。
在使用无机填料的时候，由于无机粉体填料与有机高聚物的表面或界面性质不同，相容性较差，因而难以在基质中均匀分散。故而必须对无机粉体填料表面进行改性，以改善其表面的物理化学特性，增强其与有机高聚物或树脂等的相容性和在有机基质中的分散性，以提高材料的机械强度及综合性能。
传统改性方法及其缺陷主要体现在：物理改性法，改性效果差，改性剂在粉体表面吸附不牢固；颗粒分散性不好，易团聚；化学改性法，能耗高，不环保，劳动强度大，生产周期长，自动化程度低。
发明内容
本发明所要解决的技术问题是针对现有技术的不足，提供一种新的、方法设计简单合理、提高了生产效率、改性效果好的机械力化学改性硅微粉的制备方法。
本发明所要解决的技术问题是通过以下的技术方案来实现的。本发明是一种机械力化学改性硅微粉的制备方法，其特点是，其步骤如下：将氧化铝球装入球磨机中；将4~16目石英砂和改性剂六甲基二硅胺烷同时加入球磨机中，六甲基二硅胺烷用量为石英砂质量的0.1‰~2‰，在30~50rpm的转速下，研磨0.5h~4h出料，筛分，利用不同孔径的筛网得到区别粒径的改性硅微粉。
本发明所要解决的技术问题是通过以下的技术方案来实现的。以上所述的机械力化学改性硅微粉的制备方法中：六甲基二硅胺烷用量优选为石英砂质量的1‰~2‰。研磨时间优选为3h~4h出料。
与现有技术相比，本发明方法及其制得的改性硅微粉的优点如下：
1、它减少了生产阶段，简化了工艺流程，提高了生产效率；
2、该方法不涉及到溶剂的使用及熔炼，减少了环境的污染；
3、该方法可以获得用传统工艺很难或不能获得的产品；
4、该方法改性效果好，改性剂在矿物表面吸附牢固；
5、该方法自动化生产程度高，产品稳定性和一致性好。
具体实施方式
以下进一步描述本发明的具体技术方案，以便于本领域的技术人员进一步地理解本发明，而不构成对其权利的限制。
实施例1，一种机械力化学改性硅微粉的制备方法，其步骤如下：将氧化铝球装入球磨机中；将4~16目石英砂和改性剂六甲基二硅胺烷同时加入球磨机中，六甲基二硅胺烷用量为石英砂质量的0.1‰，在30rpm的转速下，研磨0.5h出料，筛分，利用不同孔径的筛网得到区别粒径的改性硅微粉。
实施例2，一种机械力化学改性硅微粉的制备方法，其步骤如下：将氧化铝球装入球磨机中；将4~16目石英砂和改性剂六甲基二硅胺烷同时加入球磨机中，六甲基二硅胺烷用量为石英砂质量的2‰，在50rpm的转速下，研磨4h出料，筛分，利用不同孔径的筛网得到区别粒径的改性硅微粉。
实施例3，一种机械力化学改性硅微粉的制备方法，其步骤如下：将氧化铝球装入球磨机中；将4~16目石英砂和改性剂六甲基二硅胺烷同时加入球磨机中，六甲基二硅胺烷用量为石英砂质量的1‰，在35rpm的转速下，研磨3h出料，筛分，利用不同孔径的筛网得到区别粒径的改性硅微粉。
实施例4，一种机械力化学改性硅微粉的制备方法，其步骤如下：将氧化铝球装入球磨机中；将4~16目石英砂和改性剂六甲基二硅胺烷同时加入球磨机中，六甲基二硅胺烷用量为石英砂质量的0.5‰，在45rpm的转速下，研磨2h出料，筛分，利用不同孔径的筛网得到区别粒径的改性硅微粉。
实施例5，一种机械力化学改性硅微粉的制备方法，其步骤如下：将氧化铝球装入球磨机中；将4~16目石英砂和改性剂六甲基二硅胺烷同时加入球磨机中，六甲基二硅胺烷用量为石英砂质量的1.5‰，在40rpm的转速下，研磨1h出料，筛分，利用不同孔径的筛网得到区别粒径的改性硅微粉。
实施例6，本发明产品性能评价实验。按照实施例1所述的方法，区别参数进行改性制得改性硅微粉，与未改性的硅微粉相比，产品性能参见下述：
（1）相似粒度，改性和未改性活化率、吸油值、粘度对比数据：
（2）研磨3h后，改性剂用量对活化率的影响见下表：
（3）改性剂用量为石英砂质量的1‰，研磨时间对活化率的影响，见下表：
。

Claims (1)

1.一种机械力化学改性硅微粉的制备方法，其特征在于，其步骤如下：将氧化铝球装入球磨机中；将4～16目石英砂和改性剂六甲基二硅胺烷同时加入球磨机中，六甲基二硅胺烷用量为石英砂质量的1‰，在35rpm的转速下，研磨3h出料，筛分，利用不同孔径的筛网得到区别粒径的改性硅微粉。
CN201310599168.4A 2013-11-25 2013-11-25 机械力化学改性硅微粉的制备方法 Active CN103613956B (zh)