CN103613712A - 一种高亲水性聚氯乙烯及其制备方法 - Google Patents

一种高亲水性聚氯乙烯及其制备方法 Download PDF

Info

Publication number
CN103613712A
CN103613712A CN201310596897.4A CN201310596897A CN103613712A CN 103613712 A CN103613712 A CN 103613712A CN 201310596897 A CN201310596897 A CN 201310596897A CN 103613712 A CN103613712 A CN 103613712A
Authority
CN
China
Prior art keywords
polyvinyl chloride
initiator
lubricant
parts
methacrylic acid
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201310596897.4A
Other languages
English (en)
Other versions
CN103613712B (zh
Inventor
张建康
邰锡峰
蒋周山
姚建强
储旭超
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JIANGSU HENGFENG CABLE CO Ltd
Original Assignee
JIANGSU HENGFENG CABLE CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JIANGSU HENGFENG CABLE CO Ltd filed Critical JIANGSU HENGFENG CABLE CO Ltd
Priority to CN201310596897.4A priority Critical patent/CN103613712B/zh
Publication of CN103613712A publication Critical patent/CN103613712A/zh
Application granted granted Critical
Publication of CN103613712B publication Critical patent/CN103613712B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种高亲水性聚氯乙烯及其制备方法，该聚氯乙烯是由以下重量份的组分制成：PVC90-110份，稳定剂3～3.8份，引发剂0.4-1份，润滑剂0.5-1.0份，邻苯二甲酸二辛酯24-30份，甲基丙烯酸2.4-3.0份。本发明高亲水性聚氯乙烯具有优异的力学机械性能和亲水性，可用于制备电缆绝缘、护套等电缆产品。

Description

一种高亲水性聚氯乙烯及其制备方法
技术领域：
本发明属于化工技术领域，具体涉及一种高亲水性聚氯乙烯及其制备方法。
背景技术：
聚氯乙烯，简称PVC由氯乙烯在引发剂作用下聚合而成的热塑性树脂。是氯乙烯的均聚物。氯乙烯均聚物和氯乙烯共聚物统称为氯乙烯树脂。PVC为无定形结构的白色粉末，支化度较小。工业生产的PVC分子量一般在5万～12万范围内，具有较大的多分散性，分子量随聚合温度的降低而增加；无固定熔点，80～85℃开始软化，130℃变为粘弹态，160～180℃开始转变为粘流态；有较好的机械性能，抗张强度60MPa左右，冲击强度5～10kJ/m2；有优异的介电性能。，是一种性能优良的通用塑料，由于其可改变配方而得到从软度邵氏20A到邵氏90D的各种产品，大量使用制造输血袋和输液管。PVC很坚硬，溶解性也很差，只能溶于环己酮、二氯乙烷和四氢呋喃等少数溶剂中，对有机和无机酸、碱、盐均稳定，化学稳定性随使用温度的升高而降低。由于PVC具有憎水性，其使用范围受到很大的限制。
发明内容：
本发明的目的是克服上述不足之处提供一种高亲水性聚氯乙烯。
本发明的另一目的是提供上述高亲水性聚氯乙烯的制备方法。
本发明的目的是通过以下方式实现的：
一种高亲水性聚氯乙烯，该聚氯乙烯是由以下重量份的组分制成：PVC90-110份，稳定剂3～3.8份，引发剂0.4-1份，润滑剂0.5-1.0份，邻苯二甲酸二辛酯（DOP）24-30份，甲基丙烯酸2.4-3.0份。
上述高亲水性聚氯乙烯优选由以下重量份的组分制成：PVC100份，稳定剂3.2～3.6份，引发剂0.4-0.6份，润滑剂0.8-1.0份，DOP24-28份，甲基丙烯酸2.4-2.8份。
所述的稳定剂为钙锌复合稳定剂。
所述的引发剂为双2-5（硅橡胶硫化剂）。本发明原料中加入了甲基丙烯酸，可将双2-5作为引发剂使用具有优异的引发聚合效果。
所述的润滑剂优选为硬脂酸。
上述低吸水率尼龙66的制备方法包括以下步骤：
将PVC，稳定剂，引发剂，润滑剂，邻苯二甲酸二辛酯和甲基丙烯酸在高速混合机中搅拌至100℃，加入双螺杆挤出机中挤出造粒，挤出造粒时采用的螺杆转速是80-100转∕分钟；双螺杆挤出机温度设置如下表所示：
Figure BDA0000420126100000021
与现有技术比较本发明的有益效果：由于PVC具有憎水性，本发明是通过反应性挤出，在大分子链上接枝了甲基丙烯酸，使亲水性有很大的提高。PVC接枝甲基丙烯酸后，亲水性明显改善，接触角由原来的96度减小到64度。与此同时，又通过增加适当的辅助材料保证得到的材料具有优异的机械性能。该产品可用于制备对力学性能及与亲水性要求较高的湿热带电线，船用电缆及浮水电缆，电缆绝缘、护套等电缆产品，以满足市场多样化的需求。
具体实施方式
下面结合具体实施例来详细说明本发明，在此本发明的示意性实施例以及说明用来解释本发明，但并不作为对本发明的限定。双2-5由上海硕津贸易有限公司生产。
实施例1
试验配方：
配方材料 剂量（重量份）
PVC（医用级） 100
钙锌复合稳定剂 3.3
双2-5（引发剂） 0.4-0.6
润滑剂硬脂酸 0.8-1.0
DOP(医用级) 24
甲基丙烯酸 2.4
将PVC，稳定剂，引发剂，润滑剂，DOP和甲基丙烯酸在高速混合机中搅拌至100℃，加入双螺杆挤出机中挤出造粒，挤出造粒时采用的螺杆转速是80-100转/分钟；双螺杆挤出机温度设置如下表所示：
Figure BDA0000420126100000031
得到的高亲水性聚氯乙烯经测量仪器测试接触角为96°，而现有市售的PVC接触角仅有64°，而且本发明PVC亲水性显著升高的同时，其他机械性能均不变或略高于现有普通PVC。
实施例2
试验配方：
配方材料 剂量（重量份）
PVC（医用级） 95
钙锌复合稳定剂 3.6
双2-5（引发剂） 0.4-0.6
润滑剂硬脂酸 0.8-1.0
DOP(医用级) 28
甲基丙烯酸 2.8
将PVC，稳定剂，引发剂，润滑剂，DOP和甲基丙烯酸在高速混合机中搅拌至100℃，加入双螺杆挤出机中挤出造粒，挤出造粒时采用的螺杆转速是80-100转/分钟；双螺杆挤出机温度设置如下表所示：
Figure BDA0000420126100000032
得到的高亲水性聚氯乙烯经测量仪器测试接触角为95°，而现有市售的PVC接触角仅有64°，而且本发明PVC亲水性显著升高的同时，其他机械性能均不变或略高于现有普通PVC。

Claims (6)

1.一种高亲水性聚氯乙烯，其特征在于该聚氯乙烯是由以下重量份的组分制成：PVC90-110份，稳定剂3～3.8份，引发剂0.4-1份，润滑剂0.5-1.0份，邻苯二甲酸二辛酯24-30份，甲基丙烯酸2.4-3.0份。
2.根据权利要求1所述的高亲水性聚氯乙烯，其特征在于该聚氯乙烯是由以下重量份的组分制成：PVC100份，稳定剂3.2～3.6份，引发剂0.4-0.6份，润滑剂0.8-1.0份，邻苯二甲酸二辛酯24-28份，甲基丙烯酸2.4-2.8份。
3.根据权利要求1或2所述的高亲水性聚氯乙烯，其特征在于所述的稳定剂为钙锌复合稳定剂。
4.根据权利要求1或2所述的高亲水性聚氯乙烯，其特征在于所述的引发剂为双2-5。
5.根据权利要求1或2所述的高亲水性聚氯乙烯，其特征在于所述的润滑剂为硬脂酸。
6.一种权利要求1或2所述的高亲水性聚氯乙烯的制备方法，其特征在于所述的方法包括以下步骤：将PVC，稳定剂，引发剂，润滑剂，邻苯二甲酸二辛酯和甲基丙烯酸在高速混合机中搅拌至100℃，加入双螺杆挤出机中挤出造粒，挤出造粒时采用的螺杆转速是80-100转/分钟；双螺杆挤出机温度设置如下表所示：
Figure FDA0000420126090000011
CN201310596897.4A 2013-11-22 2013-11-22 一种高亲水性聚氯乙烯及其制备方法 Active CN103613712B (zh)