CN103613275B - 一种低羟基黄色石英管及其制备方法 - Google Patents

一种低羟基黄色石英管及其制备方法 Download PDF

Info

Publication number
CN103613275B
CN103613275B CN201310651353.3A CN201310651353A CN103613275B CN 103613275 B CN103613275 B CN 103613275B CN 201310651353 A CN201310651353 A CN 201310651353A CN 103613275 B CN103613275 B CN 103613275B
Authority
CN
China
Prior art keywords
nitrate
quartz ampoule
low hydroxyl
yellow quartz
hydroxyl yellow
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201310651353.3A
Other languages
English (en)
Other versions
CN103613275A (zh
Inventor
陶明顿
濮阳坤
庞海涛
张尧
张超
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
FUDONG LIGHTING LLC
Original Assignee
FUDONG LIGHTING LLC
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by FUDONG LIGHTING LLC filed Critical FUDONG LIGHTING LLC
Priority to CN201310651353.3A priority Critical patent/CN103613275B/zh
Publication of CN103613275A publication Critical patent/CN103613275A/zh
Application granted granted Critical
Publication of CN103613275B publication Critical patent/CN103613275B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种低羟基黄色石英管技术方案中,各原料的优选重量百分比组成为:重量百分含量SiO2 ≥ 98%、高纯石英砂98%、硝酸钴 0.1%、硝酸铈0.5%、硝酸铕0.7%、硝酸铝0.3%、三氯化钛0.2%、硝酸钾0.1%、硝酸钠0.1%;本发明低羟基黄色石英管除了具有普通滤紫外石英玻璃管的优点外,还具有配方配比更为合理的优点,由于加入了多种金属氧化物及稀土元素,经常规方法测试,其抗压强度大大提高,也大大降低了汽车灯具对烤漆的损害,同时提高了其安全性能。本发明方法设计合理,可操作性强,有效保证了低羟基黄色石英管的质量与性能。

Description

一种低羟基黄色石英管及其制备方法
技术领域
本发明涉及一种石英管,特别是一种低羟基黄色石英管;本发明还涉及该低羟基黄色色石英管的一种制备方法。
背景技术
由于目前的普通滤紫外石英玻璃管在200-320NM的透过率不能完全滤除,在做成灯时,不能滤除的一部分紫外线还会对人体有伤害和加速汽车烤漆老化的不足。
发明内容
本发明所要解决的技术问题是针对现有技术的不足,提供一种配方配比更为合理、将320NM以下有害紫外线完全滤除的石英管。
本发明所要解决的另一个技术问题是提供了上述低羟基黄色石英管的一种制备方法。
本发明所要解决的技术问题是通过以下的技术方案来实现的。本发明是一种低羟基黄色石英管,它包括以下比重量百分比的原料制成:
本发明所述的一种低羟基黄色石英管技术方案中,各原料的优选重量百分比组成为:重量百分含量SiO2 ≥ 98%、高纯石英砂98%、硝酸钴 0.1%、硝酸铈0.5% 、硝酸铕0.7%、硝酸铝0.3%、三氯化钛0.2%、硝酸钾0.1%、硝酸钠0.1%。
本发明所要解决的技术问题还可以通过以下的技术方案来进一步实现。
步骤如下:先称量一定量的硝酸钴、硝酸铈、硝酸铕、硝酸铝、三氯化钛、硝酸钾、硝酸钠溶于一定量的水中,然后再将溶液添加到100公斤高纯石英砂中,然后在搅拌器中搅拌均匀;将搅拌均匀的石英砂进行800度,烤砂结束后冷却至常温,再投入连熔炉中,在1800-2200℃下熔炼,拉制成黄色石英管,最后在脱羟炉内进行高温脱羟,脱羟温度为800-900℃,时间为4-6 个小时,将石英管的羟基含量降低到5ppm,得成品低羟基黄色石英管。
本发明低羟基黄色石英管除了具有普通滤紫外石英玻璃管的优点外,还具有配方配比更为合理的优点,由于加入了多种金属氧化物及稀土元素,经常规方法测试,其抗压强度大大提高,也大大降低了汽车灯具对烤漆的损害,同时提高了其安全性能。本发明方法设计合理,可操作性强,有效保证了低羟基黄色石英管的质量与性能。
具体实施方式
以下进一步描述本发明的具体技术方案,以便于本领域的技术人员进一步地理解本发明,而不构成对其权利的限制。
实施例,一种低羟基黄色石英管,它由以下比重量百分比的原料制成:
重量百分含量SiO2 ≥ 98%、高纯石英砂98%、硝酸钴 0.1%、硝酸铈0.5% 、硝酸铕0.7%、硝酸铝0.3%、三氯化钛0.2%、硝酸钾0.1%、硝酸钠0.1%。
其制备方法步骤如下:先称量一定量的硝酸钴、硝酸铈、硝酸铕、硝酸铝、三氯化钛、硝酸钾、硝酸钠溶于一定量的水中,然后再将溶液添加到100公斤高纯石英砂中,然后在搅拌器中搅拌均匀;将搅拌均匀的石英砂进行800度,烤砂结束后冷却至常温,再投入连熔炉中,在1800-2200℃下熔炼,拉制成黄色石英管,最后在脱羟炉内进行高温脱羟,脱羟温度为800-900℃,时间为4-6 个小时,将石英管的羟基含量降低到5ppm,得成品低羟基黄色石英管。

Claims (3)

1.一种低羟基黄色石英管,其特征在于,它包括以下比重量百分比的原料制成:重量百分含量SiO2 ≥ 98%、高纯石英砂97~99.89%、硝酸钴0.01 ~ 0.5%、硝酸铈0.01 ~ 2% 、硝酸铕0.01 ~ 0.5% 、硝酸铝0.01 ~ 0.5% 、三氯化钛0.01 ~ 0.5%、硝酸钾0.01 ~ 0.5%、硝酸钠0.01~ 0.5%。
2.根据权利要求1 所述的一种低羟基黄色石英管,其特征在于,它包括以下比重百分比的原料制成:重量百分含量SiO2 ≥ 98%、高纯石英砂98%、硝酸钴 0.1%、硝酸铈0.5% 、硝酸铕0.7%、硝酸铝0.3%、三氯化钛0.2%、硝酸钾0.1%、硝酸钠0.1%。
3.根据权利要求1 或2 所述的低羟基黄色石英管的制备方法,其特征在于,其步骤如下:先称量一定量的硝酸钴、硝酸铈、硝酸铕、硝酸铝、三氯化钛、硝酸钾、硝酸钠溶于一定量的水中,然后再将溶液添加到100公斤高纯石英砂中,然后在搅拌器中搅拌均匀;烤砂结束后冷却至常温,再投入连熔炉中,在1800-2200℃下熔炼,拉制成黄色石英管,最后在脱羟炉内进行高温脱羟,脱羟温度为800-900℃,时间为4-6 个小时,将石英管的羟基含量降低到5ppm,得成品低羟基黄色石英管。
CN201310651353.3A 2013-12-03 2013-12-03 一种低羟基黄色石英管及其制备方法 Active CN103613275B (zh)