CN107651948A - 一种负离子瓷砖及其生产工艺 - Google Patents

一种负离子瓷砖及其生产工艺 Download PDF

Info

Publication number
CN107651948A
CN107651948A CN201710811679.6A CN201710811679A CN107651948A CN 107651948 A CN107651948 A CN 107651948A CN 201710811679 A CN201710811679 A CN 201710811679A CN 107651948 A CN107651948 A CN 107651948A
Authority
CN
China
Prior art keywords
parts
hours
ball milling
feldspar
mesh
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710811679.6A
Other languages
English (en)
Inventor
林柱权
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
FOSHAN CITY GAOMING DISTRICT XINYUEFENG BUILDING MATERIAL Co Ltd
Original Assignee
FOSHAN CITY GAOMING DISTRICT XINYUEFENG BUILDING MATERIAL Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by FOSHAN CITY GAOMING DISTRICT XINYUEFENG BUILDING MATERIAL Co Ltd filed Critical FOSHAN CITY GAOMING DISTRICT XINYUEFENG BUILDING MATERIAL Co Ltd
Priority to CN201710811679.6A priority Critical patent/CN107651948A/zh
Publication of CN107651948A publication Critical patent/CN107651948A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种负离子瓷砖及其生产工艺，制作的负离子瓷砖不仅能够提升室内空气负离子的浓度，避免产生臭氧、正离子或静电，更加安全环保；而且能长期持续大量产生空气负离子，且负离子衰减率低，有效与空气中漂浮的烟雾、灰尘及杂质结合，增加其比重，使其沉降，中和静电、电波、电脑、电视等产生的辐射，达到清新空气、降低辐射的效果。同时使用特殊制作工艺，使陶瓷具有更好的抗腐蚀、抗氧化、耐磨损性能，表面还具有宝石般的光泽，具有保健功能。

Description

一种负离子瓷砖及其生产工艺
技术领域
本发明属于釉面砖技术领域，具体涉及一种负离子瓷砖及其生产工艺。
背景技术
瓷砖，又称磁砖，是以耐火的金属氧化物及半金属氧化物，经由研磨、混合、压制、施釉、烧结之过程，而形成的一种耐酸碱的瓷质或石质等，建筑或装饰材料，称之为瓷砖。其原材料多由粘土、石英砂等等混合而成。
负离子是空气中一种带负电荷的气体离子，具有抑菌杀菌、除尘除臭、提高身体免疫力、改善心脏功能、中和正电荷的功能：能与空气中漂浮的烟雾、灰尘及杂质结合，增加其比重，使其沉降，中和静电、电波、电脑、电视等产生的辐射，达到清新空气、降低辐射的效果。
随着人们生活水平不断提高，对于健康的要求也不断上升，目前市面上的保健瓷砖产品十分匮乏，仍有很大市场待发掘。
发明内容
为了解决上述问题，本发明提供了一种负离子瓷砖及其生产工艺。
本发明通过以下技术方案实现：
一种负离子瓷砖，按质量份数计，由如下组分制得:矽藻土100-120份、长石30-40份、黏土35-40份、石墨烯10-15份、石英20-25份、硅酸钠15-20份、氧化镁1-2份、氧化锂1-1.5份、氧化钾1-1.5份、氧化钙1-1.5份、氧化钠2-2.5份、釉料30-50份；
所述釉料，由如下组分制得:石英15-20份、长石15-18份、大理石5-10份、微晶材料8-12份、负离子粉4-6份；
所述负离子粉，由如下组分制得:矽藻土5-8份、高铝泥2-5份、水洗泥1-3份、麦饭石5-10份、贝壳1-2份、电气石3-5份、膨润土3-8份、铝矾土2-4份、珊瑚化石2-6份。
一种负离子瓷砖，其生产工艺，具体为如下步骤:
(1)制作瓷砖胚体；
A将所述矽藻土、长石、黏土均化后，加水球磨2-3小时后过筛20目，得初浆；
B将所述初浆与所述石墨烯、石英、硅酸钠混合后继续球磨8-10小时，得二次浆；
C将氧化镁、氧化锂、氧化钾、氧化钙、氧化钠先用水清洗干净，然后烘干至含水量0.5％以下，再置于-10℃冷库中冷冻处理6-8小时，最后与所述二次浆混合后球磨3-5小时，得泥浆；
D将所述泥浆过筛40目，除铁后入陈腐池陈腐20-24小时后，喷雾干燥至含水量5-5.5％，得粉料；
E将所述粉料过筛80目后入仓，陈腐10-12小时，待用；
(2)釉料的制备
将所述石英、长石、大理石、微晶材料、负离子粉按比例混合后，加水球磨2-4小时后，使用25-35kHz超声波乳化15-20分钟，然后继续球磨3小时，过筛50目，陈腐18-22小时后待用；
(3)将步骤(1)处理好的粉料压制成型后喷釉，烧结得成品。
本发明的有益效果：本发明在釉料中添加了负离子粉，使瓷砖不仅能够提升室内空气负离子的浓度，避免产生臭氧、正离子或静电，更加安全环保；而且能长期持续大量产生空气负离子，且负离子衰减率低，有效与空气中漂浮的烟雾、灰尘及杂质结合，增加其比重，使其沉降，中和静电、电波、电脑、电视等产生的辐射，达到清新空气、降低辐射的效果。同时使用特殊制作工艺，使陶瓷具有更好的抗腐蚀、抗氧化、耐磨损性能，表面还具有宝石般的光泽，具有保健功能。
具体实施方式
实施例1
一种负离子瓷砖，按质量份数计，由如下组分制得:矽藻土100份、长石30份、黏土35份、石墨烯10份、石英20份、硅酸钠15份、氧化镁1份、氧化锂1份、氧化钾1份、氧化钙1份、氧化钠2份、釉料30份；
所述釉料，由如下组分制得:石英15份、长石15份、大理石5份、微晶材料8份、负离子粉4份；
所述负离子粉，由如下组分制得:矽藻土5份、高铝泥2份、水洗泥1份、麦饭石5份、贝壳1份、电气石3份、膨润土3份、铝矾土2份、珊瑚化石2份。
一种负离子瓷砖，其生产工艺，具体为如下步骤:
(1)制作瓷砖胚体；
A将所述矽藻土、长石、黏土均化后，加水球磨2小时后过筛20目，得初浆；
B将所述初浆与所述石墨烯、石英、硅酸钠混合后继续球磨8小时，得二次浆；
C将氧化镁、氧化锂、氧化钾、氧化钙、氧化钠先用水清洗干净，然后烘干至含水量0.5％以下，再置于-10℃冷库中冷冻处理6小时，最后与所述二次浆混合后球磨3小时，得泥浆；
D将所述泥浆过筛40目，除铁后入陈腐池陈腐20小时后，喷雾干燥至含水量5-5.5％，得粉料；
E将所述粉料过筛80目后入仓，陈腐10-12小时，待用；
(2)釉料的制备
将所述石英、长石、大理石、微晶材料、负离子粉按比例混合后，加水球磨2小时后，使用25-35kHz超声波乳化15分钟，然后继续球磨3小时，过筛50目，陈腐18小时后待用；
(3)将步骤(1)处理好的粉料压制成型后喷釉，烧结得成品。
实施例2
一种负离子瓷砖，按质量份数计，由如下组分制得:矽藻土120份、长石40份、黏土40份、石墨烯15份、石英25份、硅酸钠20份、氧化镁2份、氧化锂1.5份、氧化钾1.5份、氧化钙1.5份、氧化钠2.5份、釉料50份；
所述釉料，由如下组分制得:石英20份、长石18份、大理石10份、微晶材料12份、负离子粉6份；
所述负离子粉，由如下组分制得:矽藻土8份、高铝泥5份、水洗泥3份、麦饭石10份、贝壳2份、电气石5份、膨润土8份、铝矾土4份、珊瑚化石6份。
一种负离子瓷砖，其生产工艺，具体为如下步骤:
(1)制作瓷砖胚体；
A将所述矽藻土、长石、黏土均化后，加水球磨3小时后过筛20目，得初浆；
B将所述初浆与所述石墨烯、石英、硅酸钠混合后继续球磨10小时，得二次浆；
C将氧化镁、氧化锂、氧化钾、氧化钙、氧化钠先用水清洗干净，然后烘干至含水量0.5％以下，再置于-10℃冷库中冷冻处理8小时，最后与所述二次浆混合后球磨5小时，得泥浆；
D将所述泥浆过筛40目，除铁后入陈腐池陈腐24小时后，喷雾干燥至含水量5-5.5％，得粉料；
E将所述粉料过筛80目后入仓，陈腐12小时，待用；
(2)釉料的制备
将所述石英、长石、大理石、微晶材料、负离子粉按比例混合后，加水球磨4小时后，使用25-35kHz超声波乳化20分钟，然后继续球磨3小时，过筛50目，陈腐22小时后待用；
(3)将步骤(1)处理好的粉料压制成型后喷釉，烧结得成品。
实施例3
一种负离子瓷砖，按质量份数计，由如下组分制得:矽藻土110份、长石35份、黏土38份、石墨烯12份、石英23份、硅酸钠18份、氧化镁1.5份、氧化锂1.2份、氧化钾1.3份、氧化钙1.3份、氧化钠2.4份、釉料40份；
所述釉料，由如下组分制得:石英18份、长石16份、大理石8份、微晶材料10份、负离子粉5份；
所述负离子粉，由如下组分制得:矽藻土7份、高铝泥3份、水洗泥2份、麦饭石8份、贝壳1.5份、电气石4份、膨润土6份、铝矾土3份、珊瑚化石5份。
一种负离子瓷砖，其生产工艺，具体为如下步骤:
(1)制作瓷砖胚体；
A将所述矽藻土、长石、黏土均化后，加水球磨2.5小时后过筛20目，得初浆；
B将所述初浆与所述石墨烯、石英、硅酸钠混合后继续球磨9小时，得二次浆；
C将氧化镁、氧化锂、氧化钾、氧化钙、氧化钠先用水清洗干净，然后烘干至含水量0.5％以下，再置于-10℃冷库中冷冻处理7小时，最后与所述二次浆混合后球磨4小时，得泥浆；
D将所述泥浆过筛40目，除铁后入陈腐池陈腐22小时后，喷雾干燥至含水量5-5.5％，得粉料；
E将所述粉料过筛80目后入仓，陈腐11小时，待用；
(2)釉料的制备
将所述石英、长石、大理石、微晶材料、负离子粉按比例混合后，加水球磨3小时后，使用25-35kHz超声波乳化18分钟，然后继续球磨3小时，过筛50目，陈腐20小时后待用；
(3)将步骤(1)处理好的粉料压制成型后喷釉，烧结得成品。
对比例
市售负离子瓷砖。
经过实验，本发明通过改善负离子瓷砖的原料组分配比和制作工艺，使瓷砖不仅能够提升室内空气负离子的浓度，避免产生臭氧、正离子或静电，更加安全环保；而且能长期持续大量产生空气负离子，且负离子衰减率低，有效与空气中漂浮的烟雾、灰尘及杂质结合，增加其比重，使其沉降，中和静电、电波、电脑、电视等产生的辐射，达到清新空气、降低辐射的效果。同时还具有更好的抗腐蚀、抗氧化、耐磨损性能，表面还具有宝石般的光泽，具有保健功能。相比于市售同类产品市场竞争力更强，制得大力推广。
最后应说明的是：以上仅为本发明的优选实施例而已，并不用于限制本发明，尽管参照实施例对本发明进行了详细的说明，对于本领域的技术人员来说，其依然可以对前述各实施例所记载的技术方案进行修改，或者对其中部分技术特征进行等同替换，但是凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。

Claims (7)

1.一种负离子瓷砖，其特征在于，按质量份数计，由如下组分制得:矽藻土100-120份、长石30-40份、黏土35-40份、石墨烯10-15份、石英20-25份、硅酸钠15-20份、氧化镁1-2份、氧化锂1-1.5份、氧化钾1-1.5份、氧化钙1-1.5份、氧化钠2-2.5份、釉料30-50份；
所述釉料，由如下组分制得:石英15-20份、长石15-18份、大理石5-10份、微晶材料8-12份、负离子粉4-6份；
所述负离子粉，由如下组分制得:矽藻土5-8份、高铝泥2-5份、水洗泥1-3份、麦饭石5-10份、贝壳1-2份、电气石3-5份、膨润土3-8份、铝矾土2-4份、珊瑚化石2-6份。
2.一种负离子瓷砖的生产工艺，其特征在于，具体为如下步骤:
(1)制作瓷砖胚体；
A将所述矽藻土、长石、黏土均化后，加水球磨2-3小时后过筛20目，得初浆；
B将所述初浆与所述石墨烯、石英、硅酸钠混合后继续球磨8-10小时，得二次浆；
C将氧化镁、氧化锂、氧化钾、氧化钙、氧化钠先用水清洗干净，然后烘干至含水量0.5％以下，再置于-10℃冷库中冷冻处理6-8小时，最后与所述二次浆混合后球磨3-5小时，得泥浆；
D将所述泥浆过筛40目，除铁后入陈腐池陈腐20-24小时后，喷雾干燥至含水量5-5.5％，得粉料；
E将所述粉料过筛80目后入仓，陈腐10-12小时，待用；
(2)釉料的制备
将所述石英、长石、大理石、微晶材料、负离子粉按比例混合后，加水球磨2-4小时后，使用25-35kHz超声波乳化15-20分钟，然后继续球磨3小时，过筛50目，陈腐18-22小时后待用；
(3)将步骤(1)处理好的粉料压制成型后喷釉，烧结得成品。
3.根据权利要求1所述的一种负离子瓷砖，其特征在于，按质量份数计，由如下组分制得:矽藻土110份、长石35份、黏土38份、石墨烯12份、石英23份、硅酸钠18份、氧化镁1.5份、氧化锂1.2份、氧化钾1.3份、氧化钙1.3份、氧化钠2.4份、釉料40份。
4.根据权利要求1或3所述的一种负离子瓷砖，其特征在于，所述釉料，由如下组分制得:石英18份、长石16份、大理石8份、微晶材料10份、负离子粉5份。
5.根据权利要求1或4所述的一种负离子瓷砖，其特征在于，所述负离子粉，由如下组分制得:矽藻土7份、高铝泥3份、水洗泥2份、麦饭石8份、贝壳1.5份、电气石4份、膨润土6份、铝矾土3份、珊瑚化石5份。
6.根据权利要求2所述的一种负离子瓷砖的生产工艺，其特征在于，步骤(1)所述制作瓷砖胚体，具体方法为:
A将所述矽藻土、长石、黏土均化后，加水球磨2.5小时后过筛20目，得初浆；
B将所述初浆与所述石墨烯、石英、硅酸钠混合后继续球磨9小时，得二次浆；
C将氧化镁、氧化锂、氧化钾、氧化钙、氧化钠先用水清洗干净，然后烘干至含水量0.5％以下，再置于-10℃冷库中冷冻处理7小时，最后与所述二次浆混合后球磨4小时，得泥浆；
D将所述泥浆过筛40目，除铁后入陈腐池陈腐22小时后，喷雾干燥至含水量5-5.5％，得粉料；
E将所述粉料过筛80目后入仓，陈腐11小时，待用。
7.根据权利要求2所述的一种负离子瓷砖的生产工艺，其特征在于，步骤(2)所述釉料的制备，具体方法为:将所述石英、长石、大理石、微晶材料、负离子粉按比例混合后，加水球磨3小时后，使用25-35kHz超声波乳化18分钟，然后继续球磨3小时，过筛50目，陈腐20小时后待用。
CN201710811679.6A 2017-09-11 2017-09-11 一种负离子瓷砖及其生产工艺 Pending CN107651948A (zh)