CN103589380A - 一种改进型环氧树脂胶粘剂 - Google Patents

一种改进型环氧树脂胶粘剂 Download PDF

Info

Publication number
CN103589380A
CN103589380A CN201310508106.8A CN201310508106A CN103589380A CN 103589380 A CN103589380 A CN 103589380A CN 201310508106 A CN201310508106 A CN 201310508106A CN 103589380 A CN103589380 A CN 103589380A
Authority
CN
China
Prior art keywords
parts
modified version
epoxy resin
epoxyn
resin adhesive
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310508106.8A
Other languages
English (en)
Inventor
孙加元
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
VIS FILM TECHNOLOGY Co Ltd
Original Assignee
VIS FILM TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by VIS FILM TECHNOLOGY Co Ltd filed Critical VIS FILM TECHNOLOGY Co Ltd
Priority to CN201310508106.8A priority Critical patent/CN103589380A/zh
Publication of CN103589380A publication Critical patent/CN103589380A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种改进型环氧树脂胶粘剂,以重量份计包括如下组分：环氧树脂65～85份、芳香胺类固化剂20～30份、咪唑类固化促进剂5～15份、丁腈橡胶25～35份、偶联剂1～2.5份、稀释剂15～25份、磷系阻燃剂10～20份、柔韧剂5～10份、碳酸钙填料10～15份及有机溶剂适量。本发明加入端羟基丁腈橡胶能够提高环氧树脂胶粘剂的韧性。含磷阻燃剂能够影响溢胶量和储存期，提高组合物的阻燃性，柔韧剂增加的韧度。因此得到的环氧树脂胶粘剂具有良好的阻燃和韧度以及较高的粘性。

Description

一种改进型环氧树脂胶粘剂
技术领域：
本发明涉及一种环氧树脂组合物，尤其是涉及一种环氧树脂胶粘剂。
背景技术：
随着汽车、电子等产业的迅速发展，用于汽车、电子行业的环氧树脂材料的选择显得尤为重要。目前，很多树脂和固化剂的组合物要求具有阻燃的性能，而粘性和耐热性又很难得到协调，因此为了满足市场的考虑，目前需要提供一种环氧树脂树胶粘剂，其具有良好的阻燃、耐热和粘性等特性。
发明内容：
本发明的目的在于提供一种改进型环氧树脂胶粘剂，该胶粘剂韧度、阻燃性、耐热性和粘性都良好。
为实现上述目的，本发明的一种改进型环氧树脂胶粘剂以重量份计包括如下组分：环氧树脂65～85份、芳香胺类固化剂20～30份、咪唑类固化促进剂5～15份、丁腈橡胶25～35份、偶联剂1～2.5份、稀释剂15～25份、磷系阻燃剂10～20份、柔韧剂5～10份、碳酸钙填料10～15份及有机溶剂适量。
作为上述技术方案的优选，所述的丁腈橡胶为端羟基丁腈橡胶。
作为上述技术方案的优选，所述的芳香胺类固化剂为二氨基二苯甲烷(DDM)、二氨基二苯砜(DDS)、3,3-二氯-4,4-二氨基二苯甲烷(MOCA)中的一种或几种组合物。
作为上述技术方案的优选，所述的咪唑类固化促进剂为2-甲基咪唑、2-乙基-4-甲基咪唑、2-苯基咪唑、2-苯基-4-甲基咪唑中的一种或几种组合物。
作为上述技术方案的优选，所述的含磷阻燃剂为聚磷酸胺或磷酸三甲苯酯。
作为上述技术方案的优选，所述的偶联剂包括γ-缩水甘油醚氧丙基三甲氧基硅烷。
作为上述技术方案的优选，所述的柔韧及为壬基酚。
作为上述技术方案的优选，所述的有机溶剂为乙醇、乙酸乙酯、丙酮等中的一种或几种组合物。
本发明的有益效果在于：其加入端羟基丁腈橡胶能够提高环氧树脂胶粘剂的韧性。含磷阻燃剂能够影响溢胶量和储存期，提高组合物的阻燃性，柔韧剂增加的韧度。因此得到的环氧树脂胶粘剂具有良好的阻燃和韧度以及较高的粘性。
具体实施方式：
实施例一：
一种改进型环氧树脂胶粘剂，以重量份计包括如下组分：环氧树脂65份、芳香胺类固化剂20份、咪唑类固化促进剂5份、丁腈橡胶25份、偶联剂1份、稀释剂15份、磷系阻燃剂10份、柔韧剂5份、碳酸钙填料10份及有机溶剂适量。
丁腈橡胶为端羟基丁腈橡胶。
芳香胺类固化剂为二氨基二苯甲烷(DDM)。
咪唑类固化促进剂为2-甲基咪唑。
含磷阻燃剂为聚磷酸胺。
偶联剂包括γ-缩水甘油醚氧丙基三甲氧基硅烷。
柔韧及为壬基酚。
有机溶剂为乙醇。
实施例二：
一种改进型环氧树脂胶粘剂，以重量份计包括如下组分：环氧树脂75份、芳香胺类固化剂25份、咪唑类固化促进剂10份、丁腈橡胶30份、偶联剂1.5份、稀释剂20份、磷系阻燃剂15份、柔韧剂8份、碳酸钙填料12份及有机溶剂适量。
丁腈橡胶为端羟基丁腈橡胶。
芳香胺类固化剂为二氨基二苯砜(DDS)。
咪唑类固化促进剂为2-乙基-4-甲基咪唑和2-苯基咪唑。
含磷阻燃剂为磷酸三甲苯酯。
偶联剂包括γ-缩水甘油醚氧丙基三甲氧基硅烷。
柔韧及为壬基酚。
有机溶剂为丙酮。
实施例三：
一种改进型环氧树脂胶粘剂，以重量份计包括如下组分：环氧树脂85份、芳香胺类固化剂30份、咪唑类固化促进剂15份、丁腈橡胶35份、偶联剂2.5份、稀释剂25份、磷系阻燃剂20份、柔韧剂10份、碳酸钙填料15份及有机溶剂适量。
丁腈橡胶为端羟基丁腈橡胶。
芳香胺类固化剂为3,3-二氯-4,4-二氨基二苯甲烷(MOCA)。
咪唑类固化促进剂为2-苯基咪唑和2-苯基-4-甲基咪唑。
含磷阻燃剂为聚磷酸胺。
偶联剂包括γ-缩水甘油醚氧丙基三甲氧基硅烷。
柔韧及为壬基酚。
有机溶剂为乙酸乙酯。
以上实施例，并非对本发明的组合物的含量作任何限制，凡是依据本发明的技术实质或组合物成份或含量对以上实施例所作的任何细微修改、等同变化与修饰，均仍属于本发明技术方案的范围内。

Claims (8)

1.一种改进型环氧树脂胶粘剂，其特征在于：以重量份计包括如下组分：环氧树脂65～85份、芳香胺类固化剂20～30份、咪唑类固化促进剂5～15份、丁腈橡胶25～35份、偶联剂1～2.5份、稀释剂15～25份、磷系阻燃剂10～20份、柔韧剂5～10份、碳酸钙填料10～15份及有机溶剂适量。
2.根据权利要求1所述的改进型环氧树脂胶粘剂，其特征在于：所述的丁腈橡胶为端羟基丁腈橡胶。
3.根据权利要求1所述的改进型环氧树脂胶粘剂，其特征在于：所述的芳香胺类固化剂为二氨基二苯甲烷(DDM)、二氨基二苯砜(DDS)、3,3-二氯-4,4-二氨基二苯甲烷(MOCA)中的一种或几种组合物。
4.根据权利要求1所述的改进型环氧树脂胶粘剂，其特征在于：所述的咪唑类固化促进剂为2-甲基咪唑、2-乙基-4-甲基咪唑、2-苯基咪唑、2-苯基-4-甲基咪唑中的一种或几种组合物。
5.根据权利要求1所述的改进型环氧树脂胶粘剂，其特征在于：所述的含磷阻燃剂为聚磷酸胺或磷酸三甲苯酯。
6.根据权利要求1所述的改进型环氧树脂胶粘剂，其特征在于：所述的偶联剂包括γ-缩水甘油醚氧丙基三甲氧基硅烷。
7.根据权利要求1所述的改进型环氧树脂胶粘剂，其特征在于：所述的柔韧及为壬基酚。
8.根据权利要求1所述的改进型环氧树脂胶粘剂，其特征在于：所述的有机溶剂为乙醇、乙酸乙酯、丙酮等中的一种或几种组合物。
CN201310508106.8A 2013-10-24 2013-10-24 一种改进型环氧树脂胶粘剂 Pending CN103589380A (zh)