CN103526602A - 牛奶蛋白纤维的活性染料染色工艺 - Google Patents

牛奶蛋白纤维的活性染料染色工艺 Download PDF

Info

Publication number
CN103526602A
CN103526602A CN201310454245.7A CN201310454245A CN103526602A CN 103526602 A CN103526602 A CN 103526602A CN 201310454245 A CN201310454245 A CN 201310454245A CN 103526602 A CN103526602 A CN 103526602A
Authority
CN
China
Prior art keywords
dyeing
value
temperature
milk protein
dye
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310454245.7A
Other languages
English (en)
Inventor
梁菊明
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Kunshan Pei Xin Clothes Co Ltd
Original Assignee
Kunshan Pei Xin Clothes Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Kunshan Pei Xin Clothes Co Ltd filed Critical Kunshan Pei Xin Clothes Co Ltd
Priority to CN201310454245.7A priority Critical patent/CN103526602A/zh
Publication of CN103526602A publication Critical patent/CN103526602A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种牛奶蛋白纤维的活性染料染色工艺,其工艺步骤为:(1)FeSO4用量20%(o.w.f),温度70℃,pH值4~5,预处理35min;(2)双氧水25g/L,硅酸钠4g/L,渗透剂JFC2g/L,pH值8~9,浴比1∶50,80℃处理60min;(3)浴比1∶40,匀染剂Albegal B1%,染料1.5%(o.w.f),调pH值,40℃始染,染10min后加入元明粉,再升至规定温度,染色60min;(4)将染液降至70℃左右,加入少量的氨水调节pH值至8~8.5处理15min。本发明的有益效果是:工艺简单,操作方便,染色牢度高,耐洗牢度高,固色率高、色泽鲜艳、耐晒和湿牢度好。

Description

牛奶蛋白纤维的活性染料染色工艺
技术领域
[0001] 本发明属于纺织染整技术领域,具体涉及一种牛奶蛋白纤维的活性染料染色工艺。
背景技术
[0002] 牛奶蛋白纤维是以牛奶为原料,经分离、提纯后得到蛋白质,再与聚乙烯醇缩甲醛接枝共聚而成,属蛋白质纤维。牛奶蛋白纤维集天然纤维(棉、麻、毛、蚕丝)和化学纤维的优点于一体,不仅具有化学纤维强度高、收缩小、防霉和防蛀的性能,又具有天然纤维柔软、亲肤、吸湿和透气等优点。蛋白质与聚乙烯醇缩甲醛聚合后固化,失去了原有的可溶性,在高温环境中,其分子结构紧密,水中软化点高而不溶于水。由于蛋白质分子多肽链之间以氢键相结合,分子中含有大量易与水结合的氨基、羟基、羧基等基团,从而使纤维具有良好的吸湿性和透气性。另外,牛奶蛋白纤维含有多种人体必需的氨基酸,与人体皮肤的亲和性好,具有良好的保健性。
[0003] 正如上述牛奶蛋白纤维具有很多优点,非常适合用于纺织业,因此,其染色工艺也成为研究重点。
发明内容
[0004] 本发明提供一种牛奶蛋白纤维的活性染料染色工艺,以得到染色效率高,固色均匀的牛奶蛋白纤维织物。
[0005] 一种牛奶蛋白纤维的活性染料染色工艺,其工艺步骤为:
[0006] (I)预处理=FeSO4 用量 20%(0.w.f),温度 70°C,pH 值 4 〜5,预处理 35min ;
[0007] (2)氧化漂白:双氧水25g/L,硅酸钠4g/L,渗透剂JFC2g/L,pH值8〜9,浴比I: 50,80°C处理 60min ;
[0008] (3)染色:采用浸染方式,浴比I: 40,匀染剂Albegal Bl%,染料1.5%(0.w.f),用醋酸调pH值,40°C始染,染IOmin后加入元明粉,再将染浴温度升至规定温度,染色60min ;
[0009] (4)水洗:将染液降至70°C左右,加入少量的氨水调节pH值至8〜8.5处理15min,以去除未吸附在纤维上的染料。
[0010] 进一步地,所述元明粉的用量为30g/L〜40g/L ;
[0011] 进一步地,所述染色pH值为3〜6 ;
[0012] 进一步地,所述染色规定温度为80°C〜90°C。
[0013] 本发明具有的有益效果是:本发明工艺简单,操作方便,在保证牛奶蛋白纤维原来优点的前提下,还具有染色牢度高,耐洗牢度高,反应性高、固色率高、色泽鲜艳、耐晒和湿牢度好的特点。
具体实施方式
[0014] 为了进一步理解本发明的优点,下面通过具体的实施例来说明本发明的功效。[0015] 实施例一:
[0016] 一种牛奶蛋白纤维的活性染料染色工艺,其工艺步骤为:
[0017] (I)预处理:FeS04 用量 20%(0.w.f),温度 70°C,pH 值 4,预处理 35min ;
[0018] (2)氧化漂白:双氧水25g/L,硅酸钠4g/L,渗透剂JFC2g/L,pH值9,浴比I: 50,80°C 处理 60min ;
[0019] (3)染色:采用浸染方式,浴比I: 40,匀染剂Albegal Bl%,染料1.5%(0.w.f),用醋酸调pH值为3,40°C始染,染IOmin后加入40g/L的元明粉,再将染浴温度升至80°C,染色 60min ;
[0020] (4)水洗:将染液降至70°C左右,加入少量的氨水调节pH值至8.5处理15min,以去除未吸附在纤维上的染料。
[0021] 实施例二:
[0022] 一种牛奶蛋白纤维的活性染料染色工艺,其工艺步骤为:
[0023] (I)预处理:FeS04 用量 20% (0.w.f),温度 70°C,pH 值 5,预处理 35min ;
[0024] (2)氧化漂白:双氧水25g/L,硅酸钠4g/L,渗透剂JFC2g/L,pH值8,浴比I: 50,80°C 处理 60min ;
[0025] (3)染色:采用浸染方式,浴比I: 40,匀染剂Albegal Bl%,染料1.5%(0.w.f),用醋酸调PH值为6,40°C始染,染IOmin后加入30g/L的元明粉,再将染浴温度升至90°C,染色 60min ;
[0026] (4)水洗:将染液降至70°C左右,加入少量的氨水调节pH值至8处理15min,以去除未吸附在纤维上的染料。
[0027] 实施例三:
[0028] 一种牛奶蛋白纤维的活性染料染色工艺,其工艺步骤为:
[0029] (I)预处理:FeS04 用量 20%(0.w.f),温度 70°C,pH 值 4.5,预处理3511^11 ;
[0030] (2)氧化漂白:双氧水25g/L,硅酸钠4g/L,渗透剂JFC2g/L,pH值8.5,浴比1: 50,80°C 处理 60min ;
[0031] (3)染色:采用浸染方式,浴比I: 40,匀染剂Albegal Bl%,染料1.5%(0.w.f),用醋酸调pH值为5,40°C始染,染IOmin后加入35g/L的元明粉,再将染浴温度升至85°C,染色 60min ;
[0032] (4)水洗:将染液降至70°C左右,加入少量的氨水调节pH值至8.5处理15min,以去除未吸附在纤维上的染料。
[0033] 牛奶蛋白纤维特别细,皮层结构紧密,且在制造过程中吸附了大量的表面活性剂。为便于染色时染料的吸附和扩散,可在温度70°C、pH值4~5的条件下,加洗涤剂处理35min,以洗除纤维表面粘附的表面活性剂,膨润纤维表面皮层。
[0034]由于牛奶蛋白纤维本身含有米黄色色素,在染浅色时,需先漂白,以获得较好的染色鲜艳度。对牛奶蛋白纤维进行亚铁盐预处理和双氧水氧化漂白两步法处理,以获得良好的漂白效果。
[0035] 综上所述,以上实施例仅用以说明本发明而并非限制本发明所描述的技术方案;因此,尽管本说明书参照上述的各个实施例对本发明已进行了详细的说明,但是,本领域的普通技术人员应当理解,仍然可以对本发明进行修改或等同替换;而一切不脱离本发明的精神和范围的技术方案及其改进,其均应涵盖在本发明的权利要求范围中。

Claims (4)

1.一种牛奶蛋白纤维的活性染料染色工艺,其特征在于,其工艺步骤为: (1)预处理:FeS04用量20%(0.w.f),温度70°C,pH值4〜5,预处理35min ; (2)氧化漂白:双氧水25g/L,硅酸钠4g/L,渗透剂JFC2g/L,pH值8〜9,浴比I: 50,80°C 处理 60min ; (3)染色:采用浸染方式,浴比I: 40,匀染剂Albegal Bl%,染料1.5%(0.w.f),用醋酸调pH值,40°C始染,染IOmin后加入元明粉,再将染浴温度升至规定温度,染色60min ; (4)水洗:将染液降至70°C,加入氨水调节pH值至8〜8.5处理15min。
2.根据权利要求1所述的牛奶蛋白纤维的活性染料染色工艺,其特征在于,所述元明粉的用量为30g/L〜40g/L。
3.根据权利要求1所述的牛奶蛋白纤维的活性染料染色工艺,其特征在于,所述染色pH值为3〜6。
4.根据权利要求3所述的牛奶蛋白纤维的活性染料染色工艺,其特征在于,所述染色规定温度为80°C〜90°C。
CN201310454245.7A 2013-09-27 2013-09-27 牛奶蛋白纤维的活性染料染色工艺 Pending CN103526602A (zh)