CN103526559A - 一种高透湿面料制备方法 - Google Patents
一种高透湿面料制备方法 Download PDFInfo
- Publication number
- CN103526559A CN103526559A CN201310529752.2A CN201310529752A CN103526559A CN 103526559 A CN103526559 A CN 103526559A CN 201310529752 A CN201310529752 A CN 201310529752A CN 103526559 A CN103526559 A CN 103526559A
- Authority
- CN
- China
- Prior art keywords
- glue
- moisture
- parts
- permeable
- shell fabric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种高透湿面料制备方法其步骤包括：第一选择基础材料，采用20D—50D的锦纶,涤纶或锦涤混纺织物面料作为基料层，并且纱线f数为17—48根，单位克重35—80克每平方米；第二备辅料透湿胶，透湿胶的配方是：透湿水压胶P023A 15-85质量份、交职剂AP-215 2-4质量份、促进剂AP-216 1-3质量份、丁酮溶剂5-8质量份、水5-10质量份；第三涂覆，取第二步制得的透湿胶50-90克每码，使用涂层机均匀涂一层于基料层面料的表面上，通风晾干；本发明制作的面料质量轻薄，抗撕裂，具有防风，保暖效果且透湿性良好；即维持了原有面料的手感风格，又有很好的透湿效果，同时具有防皱免烫功能，蓬松好，一道成膜达到透湿效果，改变了目前市场上要两道或三道涂层，有效地降低了成本，适合做风衣、羽绒服、小棉衣等。
Description
技术领域
本发明属于服装面料制作技术领域，具体涉及的是一种高透湿面料制备方法。
背景技术
现有的普通的涤纶，纯棉织物一般为单层面料，纯棉织物不具有抗皱性能，而涤纶虽有悬垂性好但有水压后透气性差具有穿着不舒适特点，并且其单层面料并不具有保暖及弹性，穿着时间长以后，面料不能及时将汗液排出体外；因此为了获得高效的透湿效果，现有的面料透湿度要达到8000-10000毫克每平方米每24小时，透湿胶的湿涂布量要达到160-230克每码布（1码=0.914米*1.52米），大大增加了面料的原材料使用成本。
发明内容
本发明的目的是针对现有技术的不足，提供一种高透湿面料制备方法，该方法制作合理简单，且面料透湿胶的湿涂布量只需要50-90克每码布就可以达到良好的透湿效果。
本发明是通过以下技术方案实现的：一种高透湿面料制备方法，其步骤包括：
第一，选择基础材料，采用20D—50D的锦纶,涤纶或锦涤混纺织物面料作为基料层，并且纱线f数为17—48根，单位克重35—80克每平方米；
第二，备辅料透湿胶，透湿胶的配方是：透湿水压胶P023A 15-85质量份、交职剂AP-215 2-4质量份、促进剂AP-216 1-3质量份、丁酮溶剂 5-8质量份、水 5-10质量份；制备透湿胶的温度25-35摄氏度，防止透湿胶蒸发或变质；水最后一步加入，其他制剂依次加入，依次加入一种，用搅拌机搅拌2-3分钟，最后一步加水的时候，需要缓慢加入，加水时同时搅拌，搅拌机要以2000-3000转每分钟的搅拌速度将透湿胶制剂打散；
第三，涂覆，取第二步制得的透湿胶50-90克每码，使用涂层机均匀涂一层于基料层面料的表面上，通风晾干。
所述基料层纱线为20D-50D，f数17-48根，单位克重为35—80克每平方米，基料层为锦纶和涤纶复合层或锦涤混纺面料构成。
本发明的有益效果体现在于：与现有技术相比，本发明方法制备的面料质量轻薄，抗撕裂，具有防风，保暖效果且透湿性良好；即维持了原有面料的手感风格，又有很好的透湿效果，同时具有防皱免烫功能，蓬松好，一道成膜达到透湿效果，改变了目前市场上要两道或三道涂层，有效地降低了成本，适合做风衣、羽绒服、小棉衣等。
具体实施方式
实施例一，一种高透湿面料制备方法，具体包括以下步骤：
第一，选择基础材料，采用20--50D的锦纶,涤纶或锦涤混纺织物面料作为基料层；
第二，备辅料透湿胶，透湿胶的配方是：透湿水压胶P023A 80质量份、交职剂AP-215 3质量份、促进剂AP-216 2质量份、丁酮溶剂 7质量份、水 8质量份；制备透湿胶的温度25-35摄氏度，防止透湿胶蒸发变质；水最后一步加入，其他制剂依次加入，依次加入一种，用搅拌机搅拌3分钟，最后一步加水的时候，需要缓慢加入，加水时同时搅拌，搅拌机要以2000-3000转每分钟的搅拌速度将透湿胶制剂打散；
第三，涂覆，取第二步制得的透湿胶70克每码，使用涂层机均匀涂一层于基料层面料的表面上，通风晾干。
本发明的面料基料层要求是20D—50D的锦纶，涤纶或锦涤混纺面料构成，其纱线f数为17—48根，单位克重：35—80克每平方米纺织而成；本发明既维持了原有面料的手感风格，又有很好的透湿效果，也有很好的防风，防绒效果，具有防皱免烫功能，蓬松好，一道成膜达到透湿效果，改变了目前市场上要两道或三道涂层，有效地降低了成本，适合做风衣，羽绒服或小棉衣等。
Claims (3)
1.一种高透湿面料制备方法，其特征在于：
第一，选择基础材料基料层；
第二，备辅料透湿胶，透湿胶的配方是：透湿水压胶P023A 15-85质量份、交职剂AP-215 2-4质量份、促进剂AP-216 1-3质量份、丁酮溶剂 5-8质量份、水 5-10质量份；制备透湿胶的温度25-35摄氏度，防止透湿胶蒸发或变质；水最后一步加入，其他制剂依次加入，依次加入一种，用搅拌机搅拌2-3分钟，最后一步加水的时候，需要缓慢加入，加水时同时搅拌，搅拌机要以2000-3000转每分钟的搅拌速度将透湿胶制剂打散；
第三，涂覆，取第二步制得的透湿胶50-90克每码，使用涂层机均匀涂一层于基料层面料的表面上，通风晾干。
2.根据权利要求1所述的一种高透湿面料制备方法，其特征在于：第一步所述的基料层为锦纶,涤纶或锦涤混纺织物层构成。
3.根据权利要求1所述的一种高透湿面料制备方法，其特征在于：第一步所述的基料层内纱线为20D-50D，f数17-48根，单位克重为35—80克每平方米。