CN103483507A - 一种软性亲水接触镜材料及其制备方法 - Google Patents
一种软性亲水接触镜材料及其制备方法 Download PDFInfo
- Publication number
- CN103483507A CN103483507A CN201310479737.1A CN201310479737A CN103483507A CN 103483507 A CN103483507 A CN 103483507A CN 201310479737 A CN201310479737 A CN 201310479737A CN 103483507 A CN103483507 A CN 103483507A
- Authority
- CN
- China
- Prior art keywords
- lens material
- polydimethylsiloxane
- soft hydrophilic
- initiator
- methacryloxy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种软性亲水接触镜材料及其制备方法，由甲基丙烯酰氧基聚二甲基硅氧烷、亲水性单体、交联剂、引发剂、染料组成，以质量份计，其特征在于：其组分为：甲基丙烯酰氧基聚二甲基硅氧烷30-70份、甲基丙烯酸缩水甘油酯15-40份、甲基丙烯酸甲酯0-10份、N-乙烯吡咯烷酮占8-20份、交联剂0.1-2份、引发剂0.1-1份、染料0.01-0.1份。本发明选用的甲基丙烯酰氧基聚二甲基硅氧烷，可提高软性亲水接触镜的透氧率，减少镜片佩戴时的并发症。
Description
技术领域
本发明涉及软性亲水接触镜，特别是涉及含甲基丙烯酰氧基聚二甲基硅氧烷的软性亲水接触镜及其制备方法。
背景技术
软性角膜接触镜是一种含水隐形眼镜,由于其材料含有一定的水分,因此材料本身含有一定的空隙。一般地,含水量越高,则空隙越大。软性角膜接触镜的发展经历2个阶段:非亲水性阶段和亲水性阶段。以硅胶材料制造的非亲水性软性角膜接触镜可满足角膜正常生理代谢的需要,但与人眼的匹配性较差,戴后不舒服;而亲水性角膜接触镜是一种水凝胶材料,水分含量大,柔软舒适,可随眼球转动,并可防止角膜干燥,对氧气、钠离子等的通透性较好,是目前普遍使用的角膜接触镜材料。
硅氧烷水凝胶是目前最有前途的角膜接触镜材料。采用硅氧烷材料制备的硅氧烷水凝胶软性非亲水性角膜接触镜具有很高的透氧性,但由于不具有亲水性,佩戴舒适度不高。为了结合硅氧烷材料高透氧性以及水凝胶材料佩戴舒适性的优点,一些研究人员将含有甲基丙烯酸酯或乙烯基的聚二甲基硅氧烷与亲水性单体共聚制备硅氧烷水凝胶。硅氧烷水凝胶可以形成具有不同含水量和透氧性能的一系列结构,其透氧机理与一般水凝胶不同,其透氧性能主要由硅氧烷部分决定,而水凝胶部分只赋予材料良好的佩戴舒适性。
聚二甲基硅氧烷（Polydimethylsiloxane，PDMS)，作为一种高分子有机硅化合物，通常被称为有机硅。具有光学透明，且在一般情况下，被认为是惰性，无毒，不易燃。聚二甲基硅氧烷是最广泛使用的硅为基础的有机聚合物材料。
发明内容
本发明的目的是提供一种含甲基丙烯酰氧基聚二甲基硅氧烷的软性亲水接触镜及其制备方法，是以甲基丙烯酰氧基聚二甲基硅氧烷为原料，经紫外光照射或加热引发聚合反应而成，是一种新型的角膜接触镜材料。
本发明的技术方案通过以下方式实现：一种软性亲水接触镜材料，由甲基丙烯酰氧基聚二甲基硅氧烷、亲水性单体、交联剂、引发剂、染料组成，以质量份计，其特征在于：其组分为：甲基丙烯酰氧基聚二甲基硅氧烷30-70份、甲基丙烯酸缩水甘油酯15-40份、甲基丙烯酸甲酯0-10份、N-乙烯吡咯烷酮占8-20份、交联剂0.1-2份、引发剂0.1-1份、染料0.01-0.1份。
上述的交联剂是二甲基丙烯酸乙二醇酯、甲基丙烯酸烯丙基酯中的至少一种。
上述的引发剂是过氧化苯甲酰、偶氮二异丁腈、偶氮二异庚腈、安息香甲醚、2-羟基-2-甲基-1-苯基丙酮中的至少一种。
上述的染料是活性蓝、活性黄中的至少一种。
本发明的软性亲水接触镜的制备方法是：将上述的甲基丙烯酰氧基聚二甲基硅氧烷、甲基丙烯酸缩水甘油酯、甲基丙烯酸甲酯、N-乙烯吡咯烷酮、交联剂、引发剂、染料混合均匀，注入模具中，经紫外光照射或加热引发聚合反应，制成镜片，将镜片脱模具后，进行放入缓冲磷酸盐生理盐水中进行和水化，去除未反应的单体，得到软性亲水接触镜。
所述的加热是将染料混合物在60-65℃下保持120分钟，再在100℃下保持60分钟，自然冷却到室温。
所述的紫外光照射时间是20分钟到1小时。
本发明，具有高透氧、舒适性、抗蛋白沉淀，减少镜片佩戴时的并发症。
具体实施方式
实施例1：
取：甲基丙烯酰氧基聚二甲基硅氧烷65g，甲基丙烯酸缩水甘油酯20g，甲基丙烯酸甲酯5g，N-乙烯吡咯烷酮14g，二甲基丙烯酸乙二醇酯0.2g，偶氮二异丁腈0.23g，活性蓝4号0.05g。上述原料混合均匀，注入模具中，在65℃下保持120分钟，再在100℃下保持60分钟，自然冷却到室温，取出材料，浸泡入磷酸盐生理盐水中水化，萃取，得镜片。镜片可见光透过率大于92%，材料的延伸率大于100%。
实施例2：
取：甲基丙烯酰氧基聚二甲基硅氧烷65g，甲基丙烯酸缩水甘油酯20g，甲基丙烯酸甲酯5g，N-乙烯吡咯烷酮占到单体总质量14g，甲基丙烯酸烯丙基酯0.2g，偶氮二异丁腈0.23g,活性蓝4号0.05g，活性黄86号0.03g。上述原料混合均匀，注入模具中，在65℃下保持120分钟，再在100℃下保持60分钟，自然冷却到室温，取出材料，浸泡入磷酸盐生理盐水中水化，萃取，得镜片。镜片可见光透过率大于92%，材料的延伸率大于100%。
实施例3：
取：甲基丙烯酰氧基聚二甲基硅氧烷54g，甲基丙烯酸缩水甘油酯25g，甲基丙烯酸甲酯5g，N-乙烯吡咯烷酮占到单体总质量12g，二甲基丙烯酸乙二醇酯0.37g，安息香甲醚0.3g，活性蓝4号0.05g，活性黄86号0.03g。上述原料混合均匀，注入模具中，经紫外光照射20分钟到1小时，取出材料，浸泡入磷酸盐生理盐水中水化，萃取，得镜片。镜片可见光透过率大于92%，材料的延伸率大于100%。
实施例4：
取：甲基丙烯酰氧基聚二甲基硅氧烷54g，甲基丙烯酸缩水甘油酯25g，甲基丙烯酸甲酯5g，N-乙烯吡咯烷酮占到单体总质量12g，二甲基丙烯酸乙二醇酯0.37g，2-羟基-2-甲基-1-苯基丙酮0.18g，活性蓝4号0.05g。上述原料混合均匀，注入模具中，经紫外光照射20分钟到1小时，取出材料，浸泡入磷酸盐生理盐水中水化，萃取，得镜片。镜片可见光透过率大于92%，材料的延伸率大于100%。
实施例5：
取：甲基丙烯酰氧基聚二甲基硅氧烷54g，甲基丙烯酸缩水甘油酯25g，甲基丙烯酸甲酯5g，N-乙烯吡咯烷酮占到单体总质量12g，二甲基丙烯酸乙二醇酯0.37g，2-羟基-2-甲基-1-苯基丙酮0.18g，活性蓝4号0.05g，活性黄86号0.03g。上述原料混合均匀，注入模具中，经紫外光照射20分钟到1小时，取出材料，浸泡入磷酸盐生理盐水中水化，萃取，得镜片。镜片可见光透过率大于92%，材料的延伸率大于100%。
实施例6：
取：甲基丙烯酰氧基聚二甲基硅氧烷38g，甲基丙烯酸缩水甘油酯28g，甲基丙烯酸甲酯8g，N-乙烯吡咯烷酮16g，二甲基丙烯酸乙二醇酯0.32g，安息香甲醚0.3g，活性蓝4号0.05g，活性黄86号0.03g。上述原料混合均匀，注入模具中，经紫外光照射20分钟到1小时，取出材料，浸泡入磷酸盐生理盐水中水化，萃取，得镜片。镜片可见光透过率大于92%，材料的延伸率大于100%。
实施例7：
取：甲基丙烯酰氧基聚二甲基硅氧烷38g，甲基丙烯酸缩水甘油酯36g，甲基丙烯酸甲酯8g，N-乙烯吡咯烷酮16g，二甲基丙烯酸乙二醇酯0.32g，过氧化苯甲酰0.5g，活性蓝4号0.05g。上述原料混合均匀，注入模具中，在65℃下保持120分钟，再在100℃下保持60分钟，自然冷却到室温，取出材料，浸泡入磷酸盐生理盐水中水化，萃取，得镜片。镜片可见光透过率大于92%，材料的延伸率大于100%。
实施例8：
取：甲基丙烯酰氧基聚二甲基硅氧烷38g，甲基丙烯酸缩水甘油酯36g，甲基丙烯酸甲酯8g，N-乙烯吡咯烷酮16g，二甲基丙烯酸乙二醇酯0.32g，过氧化苯甲酰0.3g，偶氮二异丁腈0.2g，活性蓝4号0.05g。上述原料混合均匀，注入模具中，在65℃下保持120分钟，再在100℃下保持60分钟，自然冷却到室温，取出材料，浸泡入磷酸盐生理盐水中水化，萃取，得镜片。镜片可见光透过率大于92%，材料的延伸率大于100%。
Claims (7)
1.一种软性亲水接触镜材料，由甲基丙烯酰氧基聚二甲基硅氧烷、亲水性单体、交联剂、引发剂、染料组成，以质量份计，其特征在于：其组分为：甲基丙烯酰氧基聚二甲基硅氧烷30-70份、甲基丙烯酸缩水甘油酯15-40份、甲基丙烯酸甲酯0-10份、N-乙烯吡咯烷酮占8-20份、交联剂0.1-2份、引发剂0.1-1份、染料0.01-0.1份。
2.根据权利要求1所述一种软性亲水接触镜材料，其特征在于：所述的交联剂是二甲基丙烯酸乙二醇酯、甲基丙烯酸烯丙基酯中的至少一种。
3.根据权利要求1所述一种软性亲水接触镜材料，其特征在于：所述的引发剂是过氧化苯甲酰、偶氮二异丁腈、偶氮二异庚腈、安息香甲醚、2-羟基-2-甲基-1-苯基丙酮中的至少一种。
4.根据权利要求1所述一种软性亲水接触镜材料，其特征在于：所述的染料是活性蓝、活性黄中的至少一种。
5.一种制备权利要求1所述的软性亲水接触镜材料的方法，其特征在于：将甲基丙烯酰氧基聚二甲基硅氧烷30-70份、甲基丙烯酸缩水甘油酯15-40份、甲基丙烯酸甲酯0-10份、N-乙烯吡咯烷酮占8-20份、交联剂0.1-2份、引发剂0.1-1份、染料0.01-0.1份混合均匀，注入模具中，经紫外光照射或加热引发聚合反应，制成镜片，镜片脱模具后，进行放入缓冲磷酸盐生理盐水中进行和水化，去除未反应的单体，得到软性亲水接触镜。
6.根据权利要求5所述制备方法，其特征在于：所述的加热是将染料混合物在60-65℃下保持120分钟，再在100℃下保持60分钟，自然冷却到室温。
7.根据权利要求5所述制备方法，其特征在于：所述的紫外光照射的时间是20分钟到1小时。