CN103481519A - 一种绝缘橡胶片的加工工艺 - Google Patents

一种绝缘橡胶片的加工工艺 Download PDF

Info

Publication number
CN103481519A
CN103481519A CN201310430623.8A CN201310430623A CN103481519A CN 103481519 A CN103481519 A CN 103481519A CN 201310430623 A CN201310430623 A CN 201310430623A CN 103481519 A CN103481519 A CN 103481519A
Authority
CN
China
Prior art keywords
electro
parts
insulating rubber
insulating
rubber
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201310430623.8A
Other languages
English (en)
Inventor
周建
颜玉荣
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Suzhou Xiangyuan Special Fine Chemical Co Ltd
Original Assignee
Suzhou Xiangyuan Special Fine Chemical Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Suzhou Xiangyuan Special Fine Chemical Co Ltd filed Critical Suzhou Xiangyuan Special Fine Chemical Co Ltd
Priority to CN201310430623.8A priority Critical patent/CN103481519A/zh
Publication of CN103481519A publication Critical patent/CN103481519A/zh
Withdrawn legal-status Critical Current

Abstract

本发明公开的是一种绝缘橡胶片的加工工艺，包括以下几个步骤：A.配料：所述配料是指将三元乙丙橡胶22份、炭黑5份、白炭黑18份、促进剂2份、增粘树脂3份、软化剂8份、微晶蜡0.01份、防老剂0.01份，以质量份计混合在一起，形成绝缘橡胶混合物，所述绝缘橡胶混合物的温度控制在50～90℃；B.切割；C.压延；D.拉伸；E.贴合；F.硫化处理；G.压合。本发明的加工工艺，无需利用粘合剂进行粘着，从而避免了粘合剂仓储与劣化所可能引起的种种因素，而提升了整个生产流程的系统化；另外，加工的绝缘橡胶片耐热性能好，使用寿命长。

Description

一种绝缘橡胶片的加工工艺
 技术领域：
本发明涉及一种加工工艺，具体涉及一种绝缘橡胶片的加工工艺，属于橡胶技术领域。
 背景技术：
随着科学技术进步的要求 , 目前，绝缘橡胶不仅要求较高的绝缘性能，而且同时要具有好的耐臭氧特性及耐热老化性能，确保产品的使用寿命，降低生产成本，同时，要保证此类橡胶的环保性能，避免由于与人体的直接接触造成皮肤过敏或其它疾病的产生等；因此，传统的橡胶制品单纯具有良好的绝缘性能，已经远远满足不了现代社会的要求。另外，绝缘橡胶可以模压或挤出成形，有片装或其他的冲切形状可供选择。
但是，目前绝缘橡胶片的加工工艺是利用界面活性剂，直接将橡胶与酚醛树脂积层板两种不同极性的材料粘合，而形成制品。从而整个工艺多了一道粘合工段，且需额外的界面活性剂。因此，造成工艺繁琐，再者，粘着状态也易受到界面活性剂劣化而受到影响，而使得绝缘橡胶片具有耐热性差、寿命短等缺点。
 发明内容：
本发明目的是，用来弥补现有技术的不足，而提供一种工艺简单的绝缘橡胶片的加工工艺，加工的绝缘橡胶片耐热性能好，使用寿命长。
为了实现上述目的，本发明的技术方案如下：
本发明包括以下几个步骤：
A、配料：配料是指将三元乙丙橡胶22份、炭黑5份、白炭黑18份、促进剂2份、增粘树脂3份、软化剂 8份、微晶蜡 0.01份、防老剂0.01份，以质量份计混合在一起，形成绝缘橡胶混合物，绝缘橡胶混合物的温度控制在50～90℃；
B、切割：将绝缘橡胶混合物切割成块状绝缘橡胶混合物；
C、压延：将块状绝缘橡胶混合物放入压延机中压延，得到绝缘橡胶膜，绝缘橡胶膜的厚度控制在1～3mm，压延机的罗拉温度控制在60～100℃；
D、拉伸：利用拉伸机对压延机压出的绝缘橡胶膜进行拉薄、拉宽及裁剪，得到所需厚度和宽度的绝缘橡胶膜；
E、贴合：将步骤D得到的绝缘橡胶膜通过压延机贴合在一表面经拔水处理的纱布上，以形成一绝缘橡胶布；
F、硫化处理：对绝缘橡胶布通过加硫机进行硫化处理，硫化处理时温度控制在120℃，维持10分钟，随后剥离纱布，剩下一经硫化处理的绝缘橡胶膜；
G、压合：将步骤F得到的绝缘橡胶膜通过模压机与一酚醛树脂基层板进行压合，即得成品。
上述模压机是以150℃将橡胶胶膜与酚醛树脂基层板进行压合。
上述步骤C中绝缘橡胶膜的厚度控制在3mm。
上述步骤C中压延机为三辊压延机。
本发明的绝缘橡胶，具备良好的绝缘性能，耐臭氧特性及耐热老化性能较强，使用寿命较长，生产使用成本较低，环保性能好等优点；另外，本发明的加工工艺，无需利用粘合剂进行粘着，从而避免了粘合剂仓储与劣化所可能引起的种种因素，而提升了整个生产流程的系统化；另外，加工的绝缘橡胶片耐热性能好，使用寿命长。
具体实施方式：
为了使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解，进一步阐述本发明。
实施例1
一种绝缘橡胶片的加工工艺，包括以下几个步骤：
A、配料：配料是指将三元乙丙橡胶22份、炭黑5份、白炭黑18份、促进剂2份、增粘树脂3份、软化剂 8份、微晶蜡 0.01份、防老剂0.01份，以质量份计混合在一起，形成绝缘橡胶混合物，绝缘橡胶混合物的温度控制在90℃；
B、切割：将绝缘橡胶混合物切割成块状绝缘橡胶混合物；
C、压延：将块状绝缘橡胶混合物放入三辊压延机中压延，得到绝缘橡胶膜，绝缘橡胶膜的厚度控制在3mm，三辊压延机的罗拉温度控制在100℃；
D、拉伸：利用拉伸机对三辊压延机压出的绝缘橡胶膜进行拉薄、拉宽及裁剪，得到所需厚度和宽度的绝缘橡胶膜；
E、贴合：将步骤D得到的绝缘橡胶膜通过三辊压延机贴合在一表面经拔水处理的纱布上，以形成一绝缘橡胶布；
F、硫化处理：对绝缘橡胶布通过加硫机进行硫化处理，硫化处理时温度控制在120℃，维持10分钟，随后剥离纱布，剩下一经硫化处理的绝缘橡胶膜；
G、压合：将步骤F得到的绝缘橡胶膜通过模压机与一酚醛树脂基层板进行压合，即得成品，模压机是以150℃将橡胶胶膜与酚醛树脂基层板进行压合。
本发明的加工工艺，无需利用粘合剂进行粘着，从而避免了粘合剂仓储与劣化所可能引起的种种因素，而提升了整个生产流程的系统化，另外，加工的绝缘橡胶片耐热性能好，使用寿命长。
实施例2
一种绝缘橡胶片的加工工艺，包括以下几个步骤：
A、配料：配料是指将三元乙丙橡胶22份、炭黑5份、白炭黑18份、促进剂2份、增粘树脂3份、软化剂 8份、微晶蜡 0.01份、防老剂0.01份，以质量份计混合在一起，形成绝缘橡胶混合物，绝缘橡胶混合物的温度控制在50℃；
B、切割：将绝缘橡胶混合物切割成块状绝缘橡胶混合物；
C、压延：将块状绝缘橡胶混合物放入三辊压延机中压延，得到绝缘橡胶膜，绝缘橡胶膜的厚度控制在1mm，三辊压延机的罗拉温度控制在60℃；
D、拉伸：利用拉伸机对三辊压延机压出的绝缘橡胶膜进行拉薄、拉宽及裁剪，得到所需厚度和宽度的绝缘橡胶膜；
E、贴合：将步骤D得到的绝缘橡胶膜通过三辊压延机贴合在一表面经拔水处理的纱布上，以形成一绝缘橡胶布；
F、硫化处理：对绝缘橡胶布通过加硫机进行硫化处理，硫化处理时温度控制在120℃，维持10分钟，随后剥离纱布，剩下一经硫化处理的绝缘橡胶膜；
G、压合：将步骤F得到的绝缘橡胶膜通过模压机与一酚醛树脂基层板进行压合，即得成品，模压机是以150℃将橡胶胶膜与酚醛树脂基层板进行压合。
本发明的加工工艺，无需利用粘合剂进行粘着，从而避免了粘合剂仓储与劣化所可能引起的种种因素，而提升了整个生产流程的系统化，另外，加工的绝缘橡胶片耐热性能好，使用寿命长。
以上显示和描述了本发明的基本原理和主要特征和本发明的优点。本行业的技术人员应该了解，本发明不受上述实施例的限制，上述实施例和说明书中描述的只是说明本发明的原理，在不脱离本发明精神和范围的前提下，本发明还会有各种变化和改进，这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。

Claims (4)

1.一种绝缘橡胶片的加工工艺，其特征在于，包括以下几个步骤：
A、配料：所述配料是指将三元乙丙橡胶22份、炭黑5份、白炭黑18份、促进剂2份、增粘树脂3份、软化剂 8份、微晶蜡 0.01份、防老剂0.01份，以质量份计混合在一起，形成绝缘橡胶混合物，所述绝缘橡胶混合物的温度控制在50～90℃；
B、切割：将所述绝缘橡胶混合物切割成块状绝缘橡胶混合物；
C、压延：将所述块状绝缘橡胶混合物放入压延机中压延，得到绝缘橡胶膜，所述绝缘橡胶膜的厚度控制在1～3mm，所述压延机的罗拉温度控制在60～100℃；
D、拉伸：利用拉伸机对所述压延机压出的绝缘橡胶膜进行拉薄、拉宽及裁剪，得到所需厚度和宽度的绝缘橡胶膜；
E、贴合：将步骤D得到的所述绝缘橡胶膜通过所述压延机贴合在一表面经拔水处理的纱布上，以形成一绝缘橡胶布；
F、硫化处理：对所述绝缘橡胶布通过加硫机进行硫化处理，硫化处理时温度控制在120℃，维持10分钟，随后剥离所述纱布，剩下一经硫化处理的绝缘橡胶膜；
G、压合：将步骤F得到的所述绝缘橡胶膜通过模压机与一酚醛树脂基层板进行压合，即得成品。
2.根据权利要求1所述的绝缘橡胶片的加工工艺，其特征在于，所述模压机是以150℃将所述橡胶胶膜与酚醛树脂基层板进行压合。
3.根据权利要求1所述的绝缘橡胶片的加工工艺，其特征在于，
所述步骤C中绝缘橡胶膜的厚度控制在3mm。
4.根据权利要求1所述的绝缘橡胶片的加工工艺，其特征在于，
所述步骤C中压延机为三辊压延机。
CN201310430623.8A 2013-09-22 2013-09-22 一种绝缘橡胶片的加工工艺 Withdrawn CN103481519A (zh)