CN103468090A - 一种抗静电涂料的制备方法 - Google Patents
一种抗静电涂料的制备方法 Download PDFInfo
- Publication number
- CN103468090A CN103468090A CN 201310414929 CN201310414929A CN103468090A CN 103468090 A CN103468090 A CN 103468090A CN 201310414929 CN201310414929 CN 201310414929 CN 201310414929 A CN201310414929 A CN 201310414929A CN 103468090 A CN103468090 A CN 103468090A
- Authority
- CN
- China
- Prior art keywords
- coating
- antistatic coating
- mica
- preparation
- antistatic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种抗静电涂料的制备方法,其特征是由环氧树脂60-80g、纳米级石墨100-120g、聚甲基丙烯甲脂60-95g、云母40-60g和消泡剂20-25g配制成。本发明的优点在于:抗静性能好,涂层表面电阻对膜厚度不敏感,涂层厚度50-100μm之间。用本发明的材料涂敷的表面具有低的表面电阻。
Description
技术领域
本发明涉及一种涂料,具体一种抗静电性能好的涂料。用以制备具有抗静电性能的表面和制备涂敷基底。
背景技术
目前使用的热固性粉末涂料在很多领域得到应用,如作保护性和装饰用面漆。粉末涂料通过静电喷涂法涂覆于木制、金属等材料表面,并通过静电力粘结在待涂基材表面上,经加热,使涂料在基材表面形成一层膜。在实际应用中,在很多应用场合,要求涂覆的基材表面具有低电阻,高抗静电性能,甚至是导电性能。目前使用的涂料,是通过含有大量的导电性能的添加剂,如碳墨、金属粉末等来实现的。但抗静电性能仍满足不了实际应用的某些特定场合的需要,而且涂敷不够方便。
发明内容
本发明的目的,是提供一种抗静电涂料,能有效降低被涂敷基材表面的电阻,大幅度提高静电能力。
采用的技术方案是:
一种抗静电涂料,是由环氧树脂60-80g、纳米级石墨100-120g、聚甲基丙烯甲脂60-95g、云母40-60g和消泡剂20-25g配制成。
本发明的制备方法是:
一种抗静电涂料的制备方法是:
1、取环氧树脂60-80g、纳米级石墨100-120g、聚甲基丙烯甲脂60-95g、云母细粉40-60g和消泡剂20-25g放入混炼机内,在100-120℃温度下混炼均匀。
2、将步骤1制得的混合物用研磨机磨成30-50μm细粉,涂料为黑色。
本发明的优点在于:
抗静性能好,涂层表面电阻对膜厚度不敏感,涂层厚度50-100μm之间。
用本发明的材料涂敷的表面具有低的表面电阻。
具体实施方式
实施例一
一种抗静电涂料,是由环氧树脂60g、纳米级石墨100g、聚甲基丙烯甲脂60g、云母40g和消泡剂20g配制成。
实施例二
一种抗静电涂料,是由环氧树脂70g、纳米级石墨110g、聚甲基丙烯甲脂80g、云母50g和消泡剂23g配制成。
实施例三
一种抗静电涂料,是由环氧树脂80g、纳米级石墨120g、聚甲基丙烯甲脂95g、云母60g和消泡剂25g配制成。
实施例四
一种抗静电涂料的制备方法是:
1、取环氧树脂60-80g、纳米级石墨100-120g、聚甲基丙烯甲脂60-95g、云母细粉40-60g和消泡剂20-25g放入混炼机内,在100-120℃温度下混合均匀。
2、将步骤1制得的混合物用研磨机磨成30-50μm细粉,涂料为黑色。
Claims (5)
1.一种抗静电涂料,其特征是由环氧树脂60-80g、纳米级石墨100-120g、聚甲基丙烯甲脂60-95g、云母40-60g和消泡剂20-25g配制成。
2.根据权利要求1所述的一种抗静电涂料,其特征是由环氧树脂60g、纳米级石墨100g、聚甲基丙烯甲脂60g、云母40g和消泡剂20g配制成。
3.根据权利要求1所述的一种抗静电涂料,其特征是由环氧树脂70g、纳米级石墨110g、聚甲基丙烯甲脂80g、云母50g和消泡剂23g配制成。
4.根据权利要求1所述的一种抗静电涂料,其特征是由环氧树脂80g、纳米级石墨120g、聚甲基丙烯甲脂95g、云母60g和消泡剂25g配制成。
5.根据权利要求1所述的一种抗静电涂料的制备方法,其特征是:
1)、取环氧树脂60-80g、纳米级石墨100-120g、聚甲基丙烯甲脂60-95g、云母细粉40-60g和消泡剂20-25g放入混炼机内,在100-120℃温度下混合均匀;
2)、将步骤1制得的混合物用研磨机磨成30-50μm细粉,涂料为黑色。