CN103451923A - 一种以十溴二苯乙烷和三氧化二锑为原料的人造革基布阻燃剂的制造方法 - Google Patents

一种以十溴二苯乙烷和三氧化二锑为原料的人造革基布阻燃剂的制造方法 Download PDF

Info

Publication number
CN103451923A
CN103451923A CN201210176430XA CN201210176430A CN103451923A CN 103451923 A CN103451923 A CN 103451923A CN 201210176430X A CN201210176430X A CN 201210176430XA CN 201210176430 A CN201210176430 A CN 201210176430A CN 103451923 A CN103451923 A CN 103451923A
Authority
CN
China
Prior art keywords
fire retardant
antimonous oxide
base fabric
decabromodiphenylethane
leather base
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201210176430XA
Other languages
English (en)
Inventor
蔡建军
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SHANGHAI RIDUO HIGH POLYMER MATERIAL Co Ltd
Original Assignee
SHANGHAI RIDUO HIGH POLYMER MATERIAL Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SHANGHAI RIDUO HIGH POLYMER MATERIAL Co Ltd filed Critical SHANGHAI RIDUO HIGH POLYMER MATERIAL Co Ltd
Priority to CN201210176430XA priority Critical patent/CN103451923A/zh
Publication of CN103451923A publication Critical patent/CN103451923A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种以十溴二苯乙烷和三氧化二锑为原料的人造革基布阻燃剂的制备工艺方法。随着防火意识的增强，中国阻燃剂呈现出良好的市场前景和巨大的发展潜力。与此同时，国内外已经出台和即将出台的有关环保法规，在安全与环保方面对阻燃剂的使用，做出了越来越严格的限制。根据科学研究表示，卤素系阻燃剂已成为日常环境中到处扩散的污染物，且对于环境与人类的威胁日益升高。但因其不环保，含有重金属，对环境和人体有害的缺点在使用上受到限制。本发明是利用十溴二苯乙烷和三氧化二锑不同的作用机理，通过它们的互相补充，达到协同增效的结果，同时在阻燃剂中加入渗透剂和发泡剂，使阻燃剂渗入到合成革基布。利用本发明的阻燃剂制备成的合成革具有良好的阻燃功能，且对环境和人体无害，可应用于车辆座椅、内装饰、家具以及其他有较高阻燃要求的领域。

Description

一种以十溴二苯乙烷和三氧化二锑为原料的人造革基布阻燃剂的制造方法
本发明涉及一种以十溴二苯乙烷和三氧化二锑为原料的人造革基布阻燃剂的制备工艺方法。 
人造革基布主要分为三类：针织布、梭织布和无纺布。针织布是利用织针将纱线弯曲成圈并相互串套而形成的织物，具有质地柔软、吸湿透气、排汗保暖等特性，大多具有优良的弹性与延伸性。梭织布是将纱线由经纬两个方向相互垂直交织而成的布，没有弹性。无纺布又称不织布，是由定向的或随机的纤维构成，是新一代环保材料，具有防潮、透气、柔韧、质轻、不助燃等特点。 
随着防火意识和环保法规的增强，有些合成革的要求也从表面防火升级到了整体防火。因此，对阻燃剂在安全与环保方面的使用，也有了越来越严格的限制。在被用作溴系阻燃剂的70多个品种中，十溴二苯醚是生产工艺成熟、成本优势突出的传统品种，是世界上用量最大的阻燃剂品种之一，它是由溴与联苯醚在AlCl3作用下反应制得，其含溴量高达83.3％(质量分数)，具有阻燃效率高、适用面广、耐热性好、水解稳定性优异等特点，但是十溴二苯醚光解后会产生低溴代物，这无疑会增加十溴二苯醚的潜在危害。而十溴二苯乙烷由于与十溴二苯醚的溴含量、热稳定性和分子结构相似，阻燃效率和适用的树脂和工艺又和十溴二苯醚几乎相同，且燃烧不会产生致癌物质“二恶英”，加之原料易得，生产工艺要求不复杂、容易加工，性价比高，可回收利用而成为替代十溴二苯醚的首选。 
本发明的目的是解决十溴二苯醚阻燃剂对环境和人体的危害以及传统阻燃剂无法渗入到合成革基布的问题。本发明的原理是利用十溴二苯乙烷和三氧化二锑不同的作用机理，互相补充，达到阻燃的结果，同时在其载体树脂中加入发泡剂及渗透剂，使阻燃效果渗入到合成革基布。 
三氧化二锑是应用最早的阻燃剂，适用于环氧树脂、聚氨酯、聚氯乙稀、聚酯等，单独使用时用量要大，阻燃效果差，当与卤素化物并用时则有良好的协同效应，阻燃效果明显提高。 
本发明的以十溴二苯乙烷和三氧化二锑为原料的人造革基布阻燃剂的制备工艺如下： 
本发明的阻燃剂利用十溴二苯乙烷和三氧化二锑不同的作用机理，互相补充，达到协同增效的结果。具体配比见下表。 
  成分   份量   比例％
  十溴二苯乙烷   100   34.48
  三氧化二锑   50   17.25
  树脂   100   34.48
  硅油   30   10.35
  渗透剂   5   1.72
  发泡剂   5   1.72
  合计   290   100
本发明的阻燃剂的特征是：分子中同时兼有溴和三氧化二锑，在阻燃性能方面彼此起协同增效作用。分子中的溴含量较低，燃烧时放出H2O并生成熔点较低、能够气化的溴化锑，起到稀释可燃性气体的作用。它的相对密度较大，覆盖于高分子材料表面可以隔绝空气，促进炭化反应，降低燃烧系统的温度，能捕捉燃烧过程中气相里游离的HO.和H.，从而抑制燃烧。由于加入了渗透剂和发泡剂，使阻燃效果不只是发生在人造革基布表面，更能深入到基布，使人造革达到整体阻燃。 
用途：本发明的阻燃剂作用于合成革基布，采用本发明的阻燃剂制备成的合成革具有与常规合成革相同或相近的物理性能、外观和手感，并具有良好的阻燃功能，可应用于车辆座椅革、墙纸革、家具革、沙发革以及其他有较高阻燃要求的领域。 
举例： 
实施例1 
步骤一，含浸料的配制，在100份聚氨酯树脂中添加5％的阻燃剂和70的DMF，搅拌均匀。 
步骤二，将人造革基布放入含浸料中含浸充分，经过挤压辊挤压后，充分水洗，烘干。 
步骤三，将含浸过的人造革裁剪成300mm×80mm的尺寸垂直至于燃烧试验箱中，用规定的火源点燃12s，除去火源后测定试样的续燃时间。 
    添加5％阻燃剂的基布
[0017] 
  火苗熄灭及烟雾消失所用时间   10s
  积碳现象   无
实施例2 
步骤同实施例1，在100份聚氨酯树脂中添加10％的阻燃剂和70％的DMF。 
结果如下表： 
    添加10％阻燃剂的基布
  火苗熄灭及烟雾消失所用时间   5s
  积碳现象   无
实施例3 
步骤同实施例1，在100份聚氨酯树脂中添加15％的阻燃剂和70的DMF。 
结果如下表： 
    添加15％阻燃剂的基布
  火苗熄灭及烟雾消失所用时间   4s
  积碳现象   无
实施例1～3的结果比较如下： 
Figure BSA00000726573000021

Claims (1)

1.一种以十溴二苯乙烷和三氧化二锑为原料的人造革基布阻燃剂的制备方法，其特征是：它由十溴二苯乙烷和三氧化二锑，以树脂作为载体，加入硅油、渗透剂和发泡剂制成的。制成的阻燃剂能够深入到合成革基布，同时分子中兼有溴和三氧化二锑，，在阻燃性能方面彼此起协同增效的作用。 
CN201210176430XA 2012-05-31 2012-05-31 一种以十溴二苯乙烷和三氧化二锑为原料的人造革基布阻燃剂的制造方法 Pending CN103451923A (zh)