CN103451663A - 一种稀土永磁材料表面处理的方法 - Google Patents
一种稀土永磁材料表面处理的方法 Download PDFInfo
- Publication number
- CN103451663A CN103451663A CN2013103599049A CN201310359904A CN103451663A CN 103451663 A CN103451663 A CN 103451663A CN 2013103599049 A CN2013103599049 A CN 2013103599049A CN 201310359904 A CN201310359904 A CN 201310359904A CN 103451663 A CN103451663 A CN 103451663A
- Authority
- CN
- China
- Prior art keywords
- rare earth
- earth permanent
- magnetic material
- ultrasonic
- temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及一种稀土永磁材料表面处理的方法,包括(1)稀土永磁材料的制备;(2)表面清洗;(3)喷丸处理;(4)活化处理;(5)表面镀膜处理;(6)二次镀膜处理;(7)钝化处理;(8)陈化处理。本发明的稀土永磁材料表面处理方法分层次、分步骤由内而外在基体表面镀覆一层均匀致密的、无孔隙的镀层,使基体表面镀覆一层均匀致密的、低孔隙的镀层,对基体起到阻断作用,而后,再进行钝化老化过程,使得镀层和基体结合更紧密,镀层更加致密,更好地起到对基体的防护作用。
Description
技术领域
本发明涉及一种稀土永磁材料表面处理方法。
背景技术
稀土金属基永磁体,例如,以Nd-Fe-B基永磁体为代表的R-Fe-B基永磁体,或者以Sm-Fe-N基永磁体等为代表的R-Fe-N基永磁体等利用的是资源丰富的廉价材料并具有优异的磁性能,并且特别是就上述两类永磁体而言,R-Fe-B基永磁体今天在各个领域得到应用。然而,由于稀土金属基永磁体含有反应性高的稀土金属,即:R,因此它们在大气环境中易于发生氧化和腐蚀,而且,当该永磁体未经任何表面处理使用时,在存在少量酸性或碱性物质或者水条件下腐蚀趋于从表面开始,从而产生锈蚀,这会引起磁性能的下降和波动。而且,当这种生锈的磁体嵌入在磁性回路和类似装置中时,锈蚀可能会四处扩展,从而对周边的元件造成污染。
因此,长期以来,人们就已公知在稀土金属基永磁体的表面上形成各种类型的耐蚀膜。另一方面,随着近来稀土金属基永磁体应用范围的扩大,要求在稀土金属基永磁体表面上形成的耐蚀膜具有优异的性能,其不仅耐蚀性高,而且,当用于温度变化的苛刻环境时还具有良好的耐热性。此外,还要同以在嵌入元件时使用的粘结剂为代表的有机树脂具有良好的粘结性能。而且,要求形成的耐蚀膜廉价。因此,本发明的目标是提供在表面上存在同时具有优异耐热性能和优异结合性能的廉价耐蚀膜的稀土金属基永磁体。
发明内容
本发明所要解决的技术问题是:本发明的目的是为粉未冶金材料及在酸碱溶液中易腐蚀材料提供一种镀层无孔隙、厚度均匀且耐蚀性强的表面方法。具体如下:包括以下步骤:
(1)稀土永磁材料的制备
稀土永磁材料为RE-Fe-M-B,其中RE是稀土元素中的至少一种,并且M是选自Ti、Nb、Al、V、Mn、Sn、Ca、Mg、Pb、Sb、Zn、Si、Zr、Cr、Ni、Cu、Ga、Mo、W和Ta中的至少一种元素,并且这些元素的含量在如下范围内:3at%≤RE≤15at%、75at%≤Fe≤88at%、0at%≤M≤3at%,0.2at%≤B≤8at%。
(2)表面清洗
a.采用机械滚磨倒角法,将稀土永磁材料与棕刚玉砂按体积比为1∶(2~3)置入密闭滚筒内,总量占滚筒总体积的4/5,然后加入浸润液浸没试样;启动滚筒,滚筒转速为10-20r/min,时间为80-100小时;b.将稀土永磁材料取出后置于含有4-6%NaOH、10-20%Na2CO3、1-4%Na3PO4的水溶液中超声波清洗;其中水溶液温度为85-100℃,超声波频率为85-100kHz、功率为50~500w,处理时间为20-40分钟;接着将稀土永磁材料置于浓度为1-2g·L-1的硬脂酸钠水溶液中,超声波清洗;c.最后在去离子水中超声波清洗;d.烘干;
(3)喷丸处理
在室温条件下采用碳化硅对稀土永磁材料表面施进行喷丸处理;所述碳化硅粒度为100-200目,喷丸机的压力为0.1~8MPa,喷丸角度为10度~90度;
(4)活化处理
采用含柠檬酸5~30g·L-1,氟化铵5~40g·L-1的活化溶液,在室温下活化时间为:1-3分钟;
(5)表面镀膜处理
电镀水溶液主要组成为:硫酸镍100-200g·L-1、NiC12·6H2O30~50g·L-1、H3BO350-100g·L-1、乙酸钠:12~24g·L-1、十二烷基硫酸钠0.1-1g·L-1,1,4-丁炔二醇0.3~0.5g·L-1、甘氨酸:1~10g·L-1,硫脲6~10ppm,纳米级TiO2颗粒30-60g·L-1;
其中纳米级TiO2颗粒在加入电镀水溶液前要进行预处理:即先在重量百分比浓度为1-9%的NaOH溶液中煮沸,然后用清水洗涤,再在稀酸溶液中清洗后又清水洗涤,最后缓慢加入电镀水溶液中,用超声波分散10-20分钟;电镀的频率19~80kHz,功率50~500W,pH为4-5,温度55-68℃,电镀中的电流密度为2-5A·dm-2,电镀60分钟,电镀过程中采用间歇式搅拌;电镀后膜厚度在0.5μm-30μm;
(6)二次镀膜处理
二次镀膜采用超声化学镀,镀液的配方如下:硫酸镍:35-40g·L-1;次亚磷酸钠:45-60g·L-1;乙酸钠:25-30g·L-1;;甘氨酸:11-15g·L-1;柠檬酸钠:5-10g·L-1;乳酸:20-25g·L-1;乙酸:15-30g·L-1;丁二酸:15-30g·L-1;乙酸铅:10-20ppm;硫脲:10-20ppm;超声化学镀工艺参数如下:频率90-100kHz,功率50~500W,pH6-8,温度95~100℃,时间1~15分钟,镀速为10-100μm/小时;
(7)钝化处理
采用CrO3进行处理,工艺参数:CrO3:1-20g·L-1、温度:90-110℃、时间:5-15分钟;
(8)陈化处理
将钝化处理后的稀土永磁材料置于氮气或氩气环境中,加热到300-400℃,保温10-20小时,然后降温到100℃,空冷到室温,所述加热速率为50-100℃/h,降温速率为50-100℃/h。
更进一步地,所述的稀土永磁材料为Nd8Pr3.2Fe81B7.8或Nd9Y1Fe78Ti2B10。
本发明的稀土永磁材料表面处理方法分层次、分步骤由内而外在基体表面镀覆一层均匀致密的、无孔隙的镀层,使基体表面镀覆一层均匀致密的、低孔隙的镀层,对基体起到阻断作用,而后,再进行钝化老化过程,使得镀层和基体结合更紧密,镀层更加致密,更好地起到对基体的防护作用。
本发明的有益效果如下:镀层无孔隙厚度均匀且基体孔洞均被镀覆,从而提高了稀土永磁材料的耐蚀性能,避免了因基体孔洞未被镀覆而造成镀层鼓包、起皮现象。通过使用本发明研制的镀液、钝化配方以及老化处理方法,更好地起到对基体的防护作用。
本发明实现工业应用简单易行,生产成本低,产品性价比高,能极大的满足国内稀土永磁材料生产企业的需求,比较好的解决实际生产上的问题。
具体实施方式
实施例1
一种稀土永磁材料表面处理的方法,包括以下步骤:
(1)稀土永磁材料的制备,制备通式为Nd8Pr3.2Fe81B7.8的稀土永磁材料;
(2)表面清洗,a.采用机械滚磨倒角法,将稀土永磁材料与棕刚玉砂按体积比为1∶2置入密闭滚筒内,总量占滚筒总体积的4/5,然后加入浸润液浸没试样;启动滚筒,滚筒转速为15r/min,时间为90小时;b.将稀土永磁材料取出后置于含有5%NaOH、12%Na2CO3、2%Na3PO4的水溶液中超声波清洗;其中水溶液温度为90℃,超声波频率为90kHz、功率为300w,处理时间为30分钟;接着将稀土永磁材料置于浓度为1g·L-1的硬脂酸钠水溶液中,超声波清洗;c.最后在去离子水中超声波清洗;d.烘干;
(3)喷丸处理
在室温条件下采用碳化硅对稀土永磁材料表面施进行喷丸处理;所述碳化硅粒度为150目,喷丸机的压力为0.5MPa,喷丸角度为80度;
(4)活化处理
采用含柠檬酸10g·L-1,氟化铵6g·L-1的活化溶液,在室温下活化时间为:2分钟;
(5)表面镀膜处理
电镀水溶液主要组成为:硫酸镍120g·L-1、NiCl2·6H2O30g·L-1、H3BO360g·L-1、乙酸钠:15g·L-1、十二烷基硫酸钠0.2g·L-1,1,4-丁炔二醇0.3g·L-1、甘氨酸:3g·L-1,硫脲7ppm,纳米级TiO2颗粒40g·L-1;
其中纳米级TiO2颗粒在加入电镀水溶液前要进行预处理:即先在重量百分比浓度为3%的NaOH溶液中煮沸,然后用清水洗涤,再在稀酸溶液中清洗后又清水洗涤,最后缓慢加入电镀水溶液中,用超声波分散15分钟;电镀的频率25kHz,功率300W,pH为4.5,温度60℃,电镀中的电流密度为3A·dm-2,电镀60分钟,电镀过程中采用间歇式搅拌;电镀后膜厚度在5μm;
(6)二次镀膜处理
二次镀膜采用超声化学镀,镀液的配方如下:硫酸镍:36g·L-1;次亚磷酸钠:50g·L-1;乙酸钠:26g·L-1;DL一苹果酸:33g·L-1;甘氨酸:12g·L-1;柠檬酸钠:7g·L-1;乳酸:23g·L-1;乙酸:18g·L-1;丁二酸:18g·L-1;乙酸铅:15ppm;硫脲:12ppm;
超声化学镀工艺参数如下:频率95kHz,功率200W,pH6.5,温度97℃,时间4分钟,镀速为20μm/小时;
(7)钝化处理
采用CrO3进行处理,工艺参数:CrO3:5g·L-1、温度:95℃、时间:6分钟;
(8)陈化处理
将钝化处理后的稀土永磁材料置于氮气或氩气环境中,加热到350℃,保温15小时,然后降温到100℃,空冷到室温,所述加热速率为80℃/h,降温速率为90℃/h。
实施例2
一种稀土永磁材料表面处理的方法,包括以下步骤:(1)稀土永磁材料的制备,制备通式为Nd9Y1Fe78Ti2B10的稀土永磁材料。其余步骤同实施例1。
将同样的稀土永磁材料使用单纯的酸性镀、碱性镀以及中性镀与本发明的实施例1、2进行实验比较,结果列于下表:
表面处理方法 | 盐雾实验 | 湿热实验 | 磁性损失率 | 外观 |
实施例1 | 320小时 | 1250小时 | 0.8% | 光亮 |
实施例2 | 315小时 | 1200小时 | 1% | 光亮 |
对比例1-酸性镀 | 90小时 | 200小时 | 19% | 灰暗 |
对比例2-碱性镀 | 100小时 | 400小时 | 15% | 灰暗 |
对比例3-中性镀 | 120小时 | 800小时 | 5% | 比较光亮 |
尽管上面已经示出和描述了本发明的实施例,可以理解的是,上述实施例是示例性的,不能理解为对本发明的限制,本领域的普通技术人员在不脱离本发明的原理和宗旨的情况下在本发明的范围内可以对上述实施例进行变化、修改、替换和变型。
Claims (2)
1.一种稀土永磁材料表面处理的方法,其特征在于:包括以下步骤:
(1)稀土永磁材料的制备
稀土永磁材料为RE-Fe-M-B,其中RE是稀土元素中的至少一种,并且M是选自Ti、Nb、Al、V、Mn、Sn、Ca、Mg、Pb、Sb、Zn、Si、Zr、Cr、Ni、Cu、Ga、Mo、W和Ta中的至少一种元素,并且这些元素的含量在如下范围内:3at%≤RE≤15at%、75at%≤Fe≤88at%、0at%≤M≤3at%,0.2at%≤B≤8at%。
(2)表面清洗
a.采用机械滚磨倒角法,将稀土永磁材料与棕刚玉砂按体积比为1∶(2~3)置入密闭滚筒内,总量占滚筒总体积的4/5,然后加入浸润液浸没试样;启动滚筒,滚筒转速为10-20r/min,时间为80-100小时;b.将稀土永磁材料取出后置于含有4-6%NaOH、10-20%Na2CO3、1-4%Na3PO4的水溶液中超声波清洗;其中水溶液温度为85-100℃,超声波频率为85-100kHz、功率为50~500w,处理时间为20-40分钟;接着将稀土永磁材料置于浓度为1-2g·L-1的硬脂酸钠水溶液中,超声波清洗;c.最后在去离子水中超声波清洗;d.烘干;
(3)喷丸处理
在室温条件下采用碳化硅对稀土永磁材料表面施进行喷丸处理;所述碳化硅粒度为100-200目,喷丸机的压力为0.1~8MPa,喷丸角度为10度~90度。
(4)活化处理
采用含柠檬酸5~30g·L-1,氟化铵5~40g·L-1的活化溶液,在室温下活化时间为:1-3分钟;
(5)表面镀膜处理
电镀水溶液主要组成为:硫酸镍100-200g·L-1、NiCl2·6H2O30~50g·L-1、HxBO350-100g·L-1、乙酸钠:12~24g·L-1、十二烷基硫酸钠0.1-1g·L-1,1,4-丁炔二醇0.3~0.5g·L-1、甘氨酸:1~10g·L-1,硫脲6~10ppm,纳米级TiO2颗粒30-60g·L-1;
其中纳米级TiO2颗粒在加入电镀水溶液前要进行预处理:即先在重量百分比浓度为1-9%的NaOH溶液中煮沸,然后用清水洗涤,再在稀酸溶液中清洗后又清水洗涤,最后缓慢加入电镀水溶液中,用超声波分散10-20分钟;电镀的频率19~80kHz,功率50~500W,pH为4-5,温度55-68℃,电镀中的电流密度为2-5A·dm-2,电镀60分钟,电镀过程中采用间歇式搅拌;电镀后膜厚度在0.5μm-30μm;
(6)二次镀膜处理
二次镀膜采用超声化学镀,镀液的配方如下:硫酸镍:35-40g·L-1;次亚磷酸钠:45-60g·L-1;乙酸钠:25-30g·L-1;甘氨酸:11-15g·L-1;柠檬酸钠:5-10g·L-1;乳酸:20-25g·L-1;乙酸:15-30g·L-1;丁二酸:15-30g·L-1;乙酸铅:10-20ppm;硫脲:10-20ppm。
超声化学镀工艺参数如下:频率90-100kHz,功率50~500W,pH6-8,温度95~100℃,时间1~15分钟,镀速为10-100μm/小时;
(7)钝化处理
采用CrO3进行处理,工艺参数:CrO3:1-20g·L-1、温度:90-110℃、时间:5-15分钟。
(8)陈化处理
将钝化处理后的稀土永磁材料置于氮气或氩气环境中,加热到300-400℃,保温10-20小时,然后降温到100℃,空冷到室温,所述加热速率为50-100℃/h,降温速率为50-100℃/h。
2.如权利要求1所述的稀土永磁材料表面处理的方法,其特征在于:所述的稀土永磁材料为Nd8Pr3.2Fe81B7.8或Nd9Y1Fe78Ti2B10。