CN103418310A - 一种立方氮化硼合成方法 - Google Patents
一种立方氮化硼合成方法 Download PDFInfo
- Publication number
- CN103418310A CN103418310A CN2012101474186A CN201210147418A CN103418310A CN 103418310 A CN103418310 A CN 103418310A CN 2012101474186 A CN2012101474186 A CN 2012101474186A CN 201210147418 A CN201210147418 A CN 201210147418A CN 103418310 A CN103418310 A CN 103418310A
- Authority
- CN
- China
- Prior art keywords
- boron nitride
- cubic boron
- catalyst
- synthetic method
- temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种立方氮化硼合成方法，将六方氮化硼和触媒混合均匀，在一定压力和温度下转化为立方氮化硼，所述触媒粒度为80~100目。进一步，所述温度为1673~2173K，所述压力为4~6GPa。进一步，所述触媒为镁基合金，触媒浓度为5~8wt%。本发明单产可提高8~12克拉/块，产品质量稳定，设备利用率和原材料转化率也得到了提高。
Description
技术领域
本发明涉及一种立方氮化硼合成方法。
背景技术
立方氮化硼是由六方氮化硼和触媒在高温高压下合成的，是继人造金刚石问世后出现的又一种新型高新技术产品。它具有很高的硬度、热稳定性和化学惰性，以及良好的透红外形和较宽的禁带宽度等优异性能，它的硬度仅次于金钢石，但热稳定性远高于金钢石，对铁系金属元素有较大的化学稳定性。
目前，公开的立方氮化硼合成工艺单产比较低，产品质量不稳定，设备利用率和原材料转化率比较低。
发明内容
针对现有技术中的问题，本发明所要解决的问题是提供一种单产较高的立方氮化硼合成方法。
本发明的技术方案是：一种立方氮化硼合成方法，将六方氮化硼和触媒混合均匀，在一定压力和温度下转化为立方氮化硼，所述触媒粒度为80~100目。
进一步，所述温度为1673~2173K，所述压力为4~6GPa。
进一步，所述触媒为镁基合金，触媒浓度为5~8wt%。
本发明单产可提高8~12克拉/块，产品质量稳定，设备利用率和原材料转化率也得到了提高。
具体实施方式
下面结合实施例对本发明做进一步说明。
实施例1
将六方氮化硼和镁基合金混合均匀，镁基合金的浓度为5wt%，然后在温度为1673K，压力为4GPa的条件下转化为立方氮化硼。
实施例2
将六方氮化硼和镁基合金混合均匀，镁基合金的浓度为8wt%，然后在温度为2173K，压力为6GPa的条件下转化为立方氮化硼。
实施例3
将六方氮化硼和镁基合金混合均匀，镁基合金的浓度为6wt%，然后在温度为1873K，压力为5GPa的条件下转化为立方氮化硼。
实施例4
将六方氮化硼和镁基合金混合均匀，镁基合金的浓度为7wt%，然后在温度为2073K，压力为5GPa的条件下转化为立方氮化硼。
Claims (3)
1.一种立方氮化硼合成方法，将六方氮化硼和触媒混合均匀，在一定压力和温度下转化为立方氮化硼，其特征在于，所述触媒粒度为80~100目。
2.根据权利要求1所述的一种立方氮化硼合成方法，其特征在于，所述温度为1673~2173K，所述压力为4~6GPa。
3.根据权利要求1或2所述的一种立方氮化硼合成方法，其特征在于，所述触媒为镁基合金，触媒浓度为5~8wt%。