CN103382331A - 汽车用水性耐碎落涂料 - Google Patents
汽车用水性耐碎落涂料 Download PDFInfo
- Publication number
- CN103382331A CN103382331A CN2013102830337A CN201310283033A CN103382331A CN 103382331 A CN103382331 A CN 103382331A CN 2013102830337 A CN2013102830337 A CN 2013102830337A CN 201310283033 A CN201310283033 A CN 201310283033A CN 103382331 A CN103382331 A CN 103382331A
- Authority
- CN
- China
- Prior art keywords
- water
- portions
- resistant coating
- chipping resistant
- ethylhexyl
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
汽车用水性耐碎落涂料，包括按照质量份数计的如下原料：苯乙烯-丙烯酸-2-乙基己酯-丙烯酸聚合物180-190份、重质碳酸钙9-12份、碳化硅微粉10-15份、六偏磷酸钠0.9-1.8份、2-丁氧基乙醇10-15份、二甲氨基乙醇1-5份、三聚磷酸铝30-38份、辛基酚聚氧乙烯醚0.5-1份、去离子水18-25份，所述苯乙烯-丙烯酸-2-乙基己酯-丙烯酸聚合物的固含量为45-50%，所述碳化硅微粉的粒径为1200目。本发明涂料对金属附着力强，30℃和-30℃时附着力为1级；涂层耐碎落性能良好，耐碎等级为1级；本发明涂层外观为2级；本发明可用于汽车外金属板、挡泥板和前挡板等处，适于空气喷涂。
Description
技术领域
本发明属于涂料领域，具体涉及一种汽车用水性耐碎落涂料。
背景技术
当路面环境比较恶劣时，汽车行驶时容易受到飞石或杂物冲击，此时车身涂装的涂料可保护其免受外物冲击而损坏，但是一般的涂料在使用一段时间后，会因冲击而损坏剥落。
综上所述，如何克服现有技术的不足已成为涂料领域亟待解决的问题。
发明内容
本发明的目的是克服现有技术的不足而提出一种汽车用水性耐碎落涂料，本发明耐碎落效果佳、对金属附着力好、防锈性能优良、漆膜外观优良。
本发明的技术方案如下：
汽车用水性耐碎落涂料，包括按照质量份数计的如下原料：苯乙烯-丙烯酸-2-乙基己酯-丙烯酸聚合物180-190份、重质碳酸钙9-12份、碳化硅微粉10-15份、六偏磷酸钠0.9-1.8份、2-丁氧基乙醇10-15份、二甲氨基乙醇1-5份、三聚磷酸铝30-38份、辛基酚聚氧乙烯醚0.5-1份、去离子水18-25份。
所述苯乙烯-丙烯酸-2-乙基己酯-丙烯酸聚合物的固含量为45-50%。
所述碳化硅微粉的粒径为1200目。
本发明制备方法：按照质量配比，将苯乙烯-丙烯酸-2-乙基己酯-丙烯酸聚合物、重质碳酸钙、碳化硅微粉、三聚磷酸铝和六偏磷酸钠依次加入分散罐中，搅拌30min后混合均匀得混合物料A，再将2-丁氧基乙醇、二甲氨基乙醇、辛基酚聚氧乙烯醚和去离子水依次加入上述混合物料A中，搅拌均匀，即可得本发明成品。
有益效果：本发明涂料对金属附着力强，30℃和-30℃时附着力为1级；涂层耐碎落性能良好，耐碎等级为1级；本发明涂层外观为2级；本发明可用于汽车外金属板、挡泥板和前挡板等处，适于空气喷涂。
具体实施方式
本发明所述苯乙烯-丙烯酸-2-乙基己酯-丙烯酸聚合物的固含量为45-50%，所述碳化硅微粉的粒径为1200目。
下面结合具体实施方式对本发明作进一步详细说明。
实施例1
汽车用水性耐碎落涂料，包括按照质量份数计的如下原料：苯乙烯-丙烯酸-2-乙基己酯-丙烯酸聚合物180份、重质碳酸钙9份、碳化硅微粉10份、六偏磷酸钠0.9份、2-丁氧基乙醇10份、二甲氨基乙醇1份、三聚磷酸铝30份、辛基酚聚氧乙烯醚0.5份、去离子水18份。
本发明制备方法：按照上述质量配比，将苯乙烯-丙烯酸-2-乙基己酯-丙烯酸聚合物、重质碳酸钙、碳化硅微粉、三聚磷酸铝和六偏磷酸钠依次加入分散罐中，搅拌30min后混合均匀得混合物料A，再将2-丁氧基乙醇、二甲氨基乙醇、辛基酚聚氧乙烯醚和去离子水依次加入上述混合物料A中，搅拌均匀，即可得本发明成品。将该成品进行性能检测，检测结果见表1。
实施例2
汽车用水性耐碎落涂料，包括按照质量份数计的如下原料：苯乙烯-丙烯酸-2-乙基己酯-丙烯酸聚合物190份、重质碳酸钙12份、碳化硅微粉15份、六偏磷酸钠1.8份、2-丁氧基乙醇15份、二甲氨基乙醇5份、三聚磷酸铝38份、辛基酚聚氧乙烯醚1份、去离子水25份。
本发明制备方法：同实施例1，质量配比如上所述，将该成品进行性能检测，检测结果见表1。
实施例3
汽车用水性耐碎落涂料，包括按照质量份数计的如下原料：苯乙烯-丙烯酸-2-乙基己酯-丙烯酸聚合物166份、重质碳酸钙10份、碳化硅微粉12.8份、六偏磷酸钠1.6份、2-丁氧基乙醇13份、二甲氨基乙醇3份、三聚磷酸铝35份、辛基酚聚氧乙烯醚0.8份、去离子水22份。
本发明制备方法：同实施例1，质量配比如上所述，将该成品进行性能检测，检测结果见表1。
将实施例1-3制备的成品进行下表各项性能测试，结果见表1：
表1 性能测试数据
| 性能 | 实施例1 | 实施例2 | 实施例3 |
| 附着力（划圈法），级 | 1 | 1 | 1 |
| 漆膜外观，级 | 2 | 2 | 2 |
| 耐盐水性（6%氯化钠溶液，24h） | 无变化 | 无变化 | 无变化 |
由上表可见，本发明涂料附着力强，漆膜外观优良，将涂层外观分为5个等级（1级最好，5级最差），本发明所得涂层外观可达到2级，对涂层进行耐碎落性能测试，耐碎等级为1级。
上述实施例仅是对本发明产品的说明，并非对本发明做出任何形式上的限制，在不脱离本发明的技术方案范围之内，任何利用上述揭示的技术内容作出简单变换的等同方案，均属本发明的保护范围。
Claims (3)
1.汽车用水性耐碎落涂料，其特征在于，包括按照质量份数计的如下原料：苯乙烯-丙烯酸-2-乙基己酯-丙烯酸聚合物180-190份、重质碳酸钙9-12份、碳化硅微粉10-15份、六偏磷酸钠0.9-1.8份、2-丁氧基乙醇10-15份、二甲氨基乙醇1-5份、三聚磷酸铝30-38份、辛基酚聚氧乙烯醚0.5-1份、去离子水18-25份。
2.根据权利要求1所述的汽车用水性耐碎落涂料，其特征在于，所述苯乙烯-丙烯酸-2-乙基己酯-丙烯酸聚合物的固含量为45-50%。
3.根据权利要求1所述的汽车用水性耐碎落涂料，其特征在于，所述碳化硅微粉的粒径为1200目。