CN103367723A - 一种氟磷酸钙包覆镍钴锰酸锂正极材料的方法 - Google Patents
一种氟磷酸钙包覆镍钴锰酸锂正极材料的方法 Download PDFInfo
- Publication number
- CN103367723A CN103367723A CN2013103123174A CN201310312317A CN103367723A CN 103367723 A CN103367723 A CN 103367723A CN 2013103123174 A CN2013103123174 A CN 2013103123174A CN 201310312317 A CN201310312317 A CN 201310312317A CN 103367723 A CN103367723 A CN 103367723A
- Authority
- CN
- China
- Prior art keywords
- lithium manganate
- cobalt lithium
- nickel
- fluorapatite
- cathode material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
Claims (7)