CN103362034A - 一种电子束固化的直镀喷铝纸 - Google Patents
一种电子束固化的直镀喷铝纸 Download PDFInfo
- Publication number
- CN103362034A CN103362034A CN2013102520576A CN201310252057A CN103362034A CN 103362034 A CN103362034 A CN 103362034A CN 2013102520576 A CN2013102520576 A CN 2013102520576A CN 201310252057 A CN201310252057 A CN 201310252057A CN 103362034 A CN103362034 A CN 103362034A
- Authority
- CN
- China
- Prior art keywords
- paper
- aluminium
- electronic beam
- coating
- directly plated
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种电子束固化的直镀喷铝纸,包括基纸、底涂层、铝层和面涂层,其特点是所述底涂层和面涂层为EB固化涂料经电子束固化而成,将EB固化涂料均匀涂布在基纸上经电子束固化后,在其表面直接真空喷镀铝层,然后在铝层上均匀涂布EB固化涂料后经电子束固化成直镀喷铝纸。本发明与现有技术相比产品基本无VOCs的残留,不仅具备了通常转移喷铝纸和直接镀铝喷铝纸的各种表观及理化性能,而且保证了VOCs的限量指标远低于国家和行业标准,实现了生产过程中的零排放和低能耗,产品的生产和使用更加环保、安全。
Description
技术领域
本发明涉及包装用纸技术领域,具体地说是一种无挥发性有机物(VOCs)电子束固化的直镀喷铝纸。
背景技术
目前,烟草行业的包装用纸多为转移喷铝纸,也有少量的直接镀铝喷铝纸。转移喷铝纸产品采用普通粘合剂复合,虽然可以满足特定的附着牢度要求,但受限于普通粘合剂的生产工艺及其所使用的原材料等因素,不可避免地会在粘合剂溶液中残存微量的有机溶剂,从而影响喷铝纸的VOCs限量要求。直接镀铝喷铝纸虽然大多采用水性的涂料,加工制程中的污染相对减少,但受限于目前的水性涂料在国产纸基上涂布的流平性不好,表观特征特别是亮度无法跟转移喷铝纸相比,且加工制作过程中由于要用很高的热能将涂料内的水分挥发掉,其能耗要高于转移喷铝纸的加工能耗,并且产品中还是含有少量的有机物质。
综上所述,现有技术的转移喷铝纸和直镀喷铝纸都含有少量的有机物挥发物,而且能耗要高,表观性差,尤其和我国目前创导的绿色、健康和环保的理念不相符。开发和使用绿色、环保、低碳材料是大势所趋。随着物质生活水平的改善和环境保护意识的提高,人们对包装的认识也发生了较大的变化。以往人们对包装考虑较多的是它对商品的保护性、经济性,而现在人们考虑更多的是包装的生态特征,包括包装对人类健康和社会环境的影响。目前,国内、国际都在制定相关法规,严格控制和减少挥发性有机化合物(VOCs)的排放,以及对资源能源的消耗。
发明内容
本发明的目的是针对现有技术的不足而提供的一种电子束固化的直镀喷铝纸,采用无挥发性有机物的EB涂料替代现有使用的普通粘合剂及水性或溶剂型涂料,不但满足了涂层与铝层的黏结强度要求,同时也解决了因粘合剂及涂料中残留有微量有机化合物而致使VOCs超标的问题,并能做到零排放和降低能耗,使产品的生产更加环保、经济,产品的使用更加安全、健康。
实现本发明目的的技术方案是:一种电子束固化的直镀喷铝纸,包括基纸、底涂层、铝层和面涂层,其特点是所述底涂层和面涂层为EB固化涂料经电子束固化而成,将EB固化涂料均匀涂布在基纸上经电子束固化后,在其表面直接真空喷镀铝层,然后在铝层上均匀涂布EB固化涂料后经电子束固化成直镀喷铝纸。
本发明与现有技术相比,产品基本无VOCs的残留(除了基纸本身所含的极微量的VOCs),不仅具备了通常转移喷铝纸和直接镀铝喷铝纸的各种表观及理化性能,而且保证了VOCs的限量指标远低于国家和行业标准,实现了生产过程中的零排放和低能耗,使产品的生产和使用更加环保、安全。
附图说明
图1为本发明结构示意图。
具体实施方式
参阅附图1,本发明由基纸1、底涂层2、铝层3、面涂层4组成,将无挥发性有机物的EB固化涂料均匀涂布在纸基1上,经过电子束将EB固化成底涂层2,然后在底涂层3上直接进行真空喷镀铝层3,接着再在铝层3上涂布无挥发性有机物EB固化涂料的面涂层4,面涂层4经电子束固化后,即成无挥发性有机物(VOCs)的直接镀铝喷铝纸。
以下将通过具体的实施例对本发明做进一步的阐述:
实施例1
a、底涂
以网纹辊涂布的方式,在纸基1上均匀涂布无挥发性有机物的EB固化涂料,然后经电子束将EB固化为底涂层2,涂布车速为120米/分钟。
b、真空镀铝
在10-4mbar真空条件下,在底涂层2上真空喷镀铝层3,铝层厚度大约在400Å左右。
c、面涂
在铝层3上均匀涂布无挥发性有机物的EB涂料,然后经电子束将EB固化为面涂层4,涂布车速为120米/分钟。
Claims (1)
1.一种电子束固化的直镀喷铝纸,包括基纸、底涂层、铝层和面涂层,其特征在于所述底涂层和面涂层为EB固化涂料经电子束固化而成,将EB固化涂料均匀涂布在基纸上经电子束固化后,在其表面直接真空喷镀铝层,然后在铝层上均匀涂布EB固化涂料后经电子束固化成直镀喷铝纸。