CN103360922A - 一种防渗透白色不饱和聚酯家具涂料 - Google Patents
一种防渗透白色不饱和聚酯家具涂料 Download PDFInfo
- Publication number
- CN103360922A CN103360922A CN201210086023XA CN201210086023A CN103360922A CN 103360922 A CN103360922 A CN 103360922A CN 201210086023X A CN201210086023X A CN 201210086023XA CN 201210086023 A CN201210086023 A CN 201210086023A CN 103360922 A CN103360922 A CN 103360922A
- Authority
- CN
- China
- Prior art keywords
- unsaturated polyester
- parts
- agent
- furniture
- impermeable
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种防渗透白色不饱和聚酯家具涂料，包括主剂A部分、包含异辛酸钴的B部分和包含过氧化甲乙酮的C部分。A部分包含以下重量份数的组份：不饱和聚酯树脂40-50份、阻聚剂0.01-0.03份、钛白粉7-10份、无机填料25-35份、硬脂酸锌3-5份、溶剂4-10份、防沉剂0.3-0.5份、消泡剂0.1-0.3份、流平剂0.2-0.5份、分散剂0.1-0.3份、硝化棉0.5-1.5份、稳定剂0.1-0.3份。本发明使用了硝化棉，解决了白色不饱和聚酯家具涂料涂装在没有封闭的密度板上容易渗透露筋的技术问题，减少了涂装的返工率。
Description
技术领域
本发明涉及一种不饱和聚酯家具涂料，特别涉及一种防渗透白色不饱和聚酯家具涂料。
背景技术
不饱和聚酯家具涂料可一次厚涂，漆膜丰满，硬度、耐溶剂性、填充性、防塌陷性好，在家具行业普遍应用。特别是目前流行的白色板式家具涂装，主要采用不饱和聚酯家具涂料做底漆、聚氨酯白色等实色漆做面漆。现在板式家具采用密度板为底材，先喷涂一道聚氨酯封闭底漆，打磨后一次厚涂白色不饱和聚酯家具涂料。如果聚氨酯封闭底漆没有完全封闭或打磨时被打穿，上面涂装白色不饱和聚酯家具涂料时容易渗透，漆膜渗透部位即会出现遮盖力差、露筋、无光泽等现象，严重影响面漆涂膜质量，造成了涂装大量返工。
发明内容
本发明所要解决的技术问题就是克服现有技术的不足，提供一种防渗透的白色不饱和聚酯家具涂料。
本发明解决其技术问题采用的技术方案为：
一种防渗透白色不饱和聚酯家具涂料，包括主剂A部分、包含异辛酸钴的B部分和包含过氧化甲乙酮的C部分，A部分包含以下重量份数的组份：
不饱和聚酯树脂40-50份、阻聚剂0.01-0.03份、钛白粉7-10份、无机填料25-35份、硬脂酸锌3-5份、溶剂4-10份、防沉剂0.3-0.5份、消泡剂0.1-0.3份、流平剂0.2-0.5份、分散剂0.1-0.3份、硝化棉0.5-1.5份、稳定剂0.1-0.3份；
所述硝化棉为用乙醇作润湿剂固含量70%的1/2s酯溶性硝化棉。
B部分包含以下重量份数的组份：异辛酸钴70-90份，异辛酸钾10-30份；C部分包含以下重量份数的组份：过氧化甲乙酮100份。
所述溶剂包含以下重量份数的组分：甲苯2-5份，醋酸乙酯2-5份。
所述不饱和聚酯树脂选用苯乙烯稀释的固含量为75%的不饱和聚酯树脂。
所述防沉剂选用气相二氧化硅；所述消泡剂选用非有机消泡剂。
所述流平剂选用氟改性丙烯酸酯类流平剂；所述阻聚剂选用对苯二酚。
所述无机填料选用滑石粉和/或重质碳酸钙；所述钛白粉选用金红石型钛白粉。
本发明还公开了防渗透白色不饱和聚酯家具涂料的生产工艺，A部分生产工艺包括如下步骤：
投入不饱和聚酯树脂→加入部分溶剂→加入阻聚剂→中速分散均匀→依次加入防沉剂、消泡剂、流平剂、分散剂、硝化棉、稳定剂→中速分散5分钟→加入钛白粉、无机填料、硬脂酸锌→中速分散30分钟至细度≤55微米→加入剩余溶剂。
所述的部分溶剂为重量份数为2-5份的甲苯；所述剩余溶剂为重量份数为2-5份的醋酸乙酯。
为了能够合理使用上述防渗透白色不饱和聚酯家具涂料进行施工，本发明还包括以下施工工艺：
施工时按A部分：B部分：C部分=100:2:2调配好搅拌均匀。
与现有技术相比，本发明取得了优越的技术效果：通过使用硝化棉制成的防渗透白色不饱和聚酯家具涂料可直接涂装在密度板上，漆膜外观、光泽均匀一致，无露筋、渗透现象，完全解决了白色不饱和聚酯家具涂料漆膜在密度板上容易渗透的技术难题。
具体实施方式
下面结合具体实施例详细描述本发明内容：
本发明涉及一种防渗透白色不饱和聚酯家具涂料，包括独立保存的三个部分，主剂A部分、包含异辛酸钴的B部分和包含过氧化甲乙酮的C部分。
A部分的配方包括：不饱和聚酯树脂、阻聚剂、钛白粉、无机填料、硬脂酸锌、溶剂、防沉剂、消泡剂、流平剂、分散剂、硝化棉和稳定剂。
所述不饱和聚酯树脂选用展辰涂料集团股份有限公司生产的用苯乙烯稀释的固含量为75%不饱和聚酯树脂，型号为JD3309；
所述阻聚剂选用法国罗地亚公司的对苯二酚；
所述无机填料为滑石粉和/或重质碳酸钙，滑石粉可以选用广州市桂华化工科技有限公司生产的TP-1250滑石粉，重质碳酸钙可以选用广州天泰化工有限公司生产的CC-1500重质碳酸钙；
所述硬脂酸锌可以选用百利合化工（中山）有限公司生产的BT1819；
所述溶剂可以选用甲苯和/或醋酸乙酯，其中甲苯可以选用茂名石化的甲苯，醋酸乙酯可以选用广州溶剂厂的醋酸乙脂；
所述防沉剂可以选用赢创德固萨公司生产的A200气相二氧化硅或美国卡博特（CABOT）公司生产的M-5气相二氧化硅；
所述消泡剂可以选用荷兰EFKA公司生产的EFKA2720非有机硅消泡剂；
所述流平剂可以选用荷兰EFKA公司生产的EFKA3777氟改性丙烯酸酯；
所述的分散剂为磷酸盐/铵化合物，可以选用泓伟公司的C-600或德国borchers 公司的 Gen ND；
所述的硝化棉可以选用四川北方硝化棉有限公司的H1/2EA硝化棉；
所述的稳定剂可以选用德谦公司的DVP粘度安定剂。
该防渗透白色不饱和聚酯家具涂料A部分的具体生产方法及各组分的重量份数如实施例1-5所述：
实施例1：
配方：不饱和聚酯树脂50份、阻聚剂0.02份、滑石粉10份、重质碳酸钙20份、钛白粉10份、硬脂酸锌3份、甲苯2份、醋酸乙酯2份、硝化棉0.5份；防沉剂：A200气相二氧化硅0.3份；消泡剂：EFKA2720非有机硅消泡剂0.3份；流平剂：EFKA3777氟改性丙烯酸酯类流平剂0.3份；分散剂：C-600 分散剂 0.3份；稳定剂：DVP安定剂0.2份。
生产方法：投入不饱和聚酯树脂→加入甲苯→加入阻聚剂→中速分散均匀→依次加入防沉剂、消泡剂、流平剂、分散剂、硝化棉、稳定剂→中速分散5分钟→加入钛白粉、滑石粉、重质碳酸钙、硬脂酸锌→中速分散30分钟至细度≤55微米→加入醋酸乙酯；
所得的不饱和聚酯家具涂料外观为：白色粘稠液体。
实施例2：
配方：不饱和聚酯树脂40份、阻聚剂0.02份、钛白粉10、滑石粉5份、重质碳酸钙30份、硬脂酸锌3份、甲苯5份、醋酸乙酯5份；防沉剂：A200气相二氧化硅0.4份；消泡剂：EFKA2720非有机硅消泡剂0.3份；流平剂：EFKA3777氟改性丙烯酸酯类流平剂0.3份；分散剂：C-600 分散剂 0.3份；硝化棉1.5份；稳定剂：DVP安定剂0.3份。
生产方法：同实施例1；
所得的不饱和聚酯家具涂料外观为：白色粘稠液体。
实施例3：
配方：不饱和聚酯树脂45份、钛白粉8份、阻聚剂0.02份、滑石粉10份、重质碳酸钙25份、硬脂酸锌3份、甲苯2份、醋酸乙酯3份；防沉剂：A200气相二氧化硅0.5份；消泡剂：EFKA2720非有机硅消泡剂0.3份；流平剂：EFKA3777氟改性丙烯酸酯类流平剂0.2份；分散剂：C-600 分散剂 0.2份；硝化棉1份；稳定剂：DVP安定剂0.3份。
生产方法：同实施例1；
所得的不饱和聚酯家具涂料外观为：白色粘稠液体。
实施例4：
配方：不饱和聚酯树脂50份、阻聚剂0.03份、钛白粉10份、重质碳酸钙35份、硬脂酸锌4份、甲苯2份、醋酸乙酯3份；防沉剂：M-5气相二氧化硅0.3份；消泡剂：EFKA2720非有机硅消泡剂0.2份；流平剂：EFKA3777氟改性丙烯酸酯类流平剂0.5份；分散剂：Gen ND分散剂 0.2份；硝化棉0.8份；稳定剂：DVP安定剂0.2份。
生产方法：投入不饱和聚酯树脂→加入甲苯→加入阻聚剂→中速分散均匀→依次加入防沉剂、消泡剂、流平剂、分散剂、硝化棉、稳定剂→中速分散5分钟→加入钛白粉、重质碳酸钙、硬脂酸锌→中速分散30分钟至细度≤55微米→加入醋酸乙酯；
所得的不饱和聚酯家具涂料外观为：白色粘稠液体。
实施例5：
配方：不饱和聚酯树脂45份、阻聚剂0.03份、钛白粉10份、滑石粉35份、硬脂酸锌5份、甲苯3份、醋酸乙酯2份；防沉剂：M-5气相二氧化硅0.4份；消泡剂：EFKA2720非有机硅消泡剂0.1份；流平剂：EFKA3777氟改性丙烯酸酯类流平剂0.2份；分散剂：Gen ND分散剂 0.1份；硝化棉1份；稳定剂：DVP安定剂0.3份。
生产方法：投入不饱和聚酯树脂→加入甲苯→加入阻聚剂→中速分散均匀→依次加入防沉剂、消泡剂、流平剂、分散剂、硝化棉、稳定剂→中速分散5分钟→加入钛白粉、滑石粉、硬脂酸锌→中速分散30分钟至细度≤55微米→加入醋酸乙酯；
所得的不饱和聚酯家具涂料外观为：白色粘稠液体。
B部分的配方包括：异辛酸钴和异辛酸钾。
所述异辛酸钴选用上海长风化工厂生产的EC-6产品，含量为6%；所述异辛酸钾选用上海长风化工厂生产的EK-10产品。
该不饱和聚酯家具涂料B部分中组份的重量份数如实施例6-8所述：
实施例6：异辛酸钴70份，异辛酸钾30份。
实施例7：异辛酸钴80份，异辛酸钾20份。
实施例8：异辛酸钴90份，异辛酸钾10份。
C部分为100份重量份数的过氧化甲乙酮。
所述的过氧化甲乙酮可以选用荷兰AKZO NOBEL公司生产的Butanox M-50产品。
施工时按A部分：B部分：C部分=100:2:2调配好搅拌均匀，加适量的稀释剂调到施工粘度，采用喷涂方法施工。喷涂施工后漆膜的表干时间≤30分钟；实干时间10h；25℃时可打磨时间≤8h，硬度≥2H；附着力：2级。
通过使用硝化棉制成的防渗漏白色不饱和聚酯家具涂料可直接涂装在密度板上，漆膜外观、光泽均匀一致，无露筋、渗透现象。加入的稳定剂解决了涂料因加入硝化棉储存变差的问题。
本发明完全解决了白色不饱和聚酯家具涂料漆膜在密度板上容易渗透的技术难题，密度板上可直接涂装白色不饱和聚酯家具涂料，无需再涂装聚氨酯封闭底漆而不影响产品质量，节约了成本，提高了功效。
Claims (10)
1.一种防渗透白色不饱和聚酯家具涂料，包括主剂A部分、包含异辛酸钴的B部分和包含过氧化甲乙酮的C部分，其特征在于，A部分包含以下重量份数的组份：
不饱和聚酯树脂40-50份、阻聚剂0.01-0.03份、钛白粉7-10份、无机填料25-35份、硬脂酸锌3-5份、溶剂4-10份、防沉剂0.3-0.5份、消泡剂0.1-0.3份、流平剂0.2-0.5份、分散剂0.1-0.3份、硝化棉0.5-1.5份、稳定剂0.1-0.3份；
所述硝化棉为用乙醇作润湿剂固含量70%的1/2s酯溶性硝化棉。
2.根据权利要求1所述的防渗透白色不饱和聚酯家具涂料，其特征在于：B部分包含以下重量份数的组份：异辛酸钴70-90份，异辛酸钾10-30份；C部分包含以下重量份数的组份：过氧化甲乙酮100份。
3.根据权利要求1所述的防渗透白色不饱和聚酯家具涂料，其特征在于：所述溶剂包含以下重量份数的组分：甲苯2-5份，醋酸乙酯2-5份。
4.根据权利要求1所述的防渗透白色不饱和聚酯家具涂料，其特征在于：所述不饱和聚酯树脂选用苯乙烯稀释的固含量为75%的不饱和聚酯树脂。
5.根据权利要求1所述的防渗透白色不饱和聚酯家具涂料，其特征在于：所述防沉剂选用气相二氧化硅；所述消泡剂选用非有机消泡剂。
6.根据权利要求1所述的防渗透白色不饱和聚酯家具涂料，其特征在于：所述流平剂选用氟改性丙烯酸酯类流平剂；所述阻聚剂选用对苯二酚。
7. 根据权利要求1所述的防渗透白色不饱和聚酯家具涂料，其特征在于：所述无机填料选用滑石粉和/或重质碳酸钙；所述钛白粉选用金红石型钛白粉。
8.一种如权利要求1所述的防渗透白色不饱和聚酯家具涂料的生产工艺，其特征在于，A部分生产工艺包括如下步骤：
投入不饱和聚酯树脂→加入部分溶剂→加入阻聚剂→中速分散均匀→依次加入防沉剂、消泡剂、流平剂、分散剂、硝化棉、稳定剂→中速分散5分钟→加入钛白粉、无机填料、硬脂酸锌→中速分散30分钟至细度≤55微米→加入剩余溶剂。
9.根据权利要求8所述的生产工艺，其特征在于：所述的部分溶剂为重量份数为2-5份的甲苯；所述剩余溶剂为重量份数为2-5份的醋酸乙酯。
10.一种如权利要求2所述的防渗透白色不饱和聚酯家具涂料的施工工艺，其特征在于：施工时按A部分：B部分：C部分=100:2:2调配好搅拌均匀。