CN103360554A - 一种高性能减水剂合成方法 - Google Patents

一种高性能减水剂合成方法 Download PDF

Info

Publication number
CN103360554A
CN103360554A CN2013103005854A CN201310300585A CN103360554A CN 103360554 A CN103360554 A CN 103360554A CN 2013103005854 A CN2013103005854 A CN 2013103005854A CN 201310300585 A CN201310300585 A CN 201310300585A CN 103360554 A CN103360554 A CN 103360554A
Authority
CN
China
Prior art keywords
flask
liquid
gram
solution
reducing agent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2013103005854A
Other languages
English (en)
Inventor
张家如
傅曹辉
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI SENPU NEW MATERIALS DEVELOPMENT Co Ltd
Original Assignee
ANHUI SENPU NEW MATERIALS DEVELOPMENT Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI SENPU NEW MATERIALS DEVELOPMENT Co Ltd filed Critical ANHUI SENPU NEW MATERIALS DEVELOPMENT Co Ltd
Priority to CN2013103005854A priority Critical patent/CN103360554A/zh
Publication of CN103360554A publication Critical patent/CN103360554A/zh
Pending legal-status Critical Current

Abstract

本发明涉及减水剂技术领域，更具体的说涉及一种减水剂的合成方法。一种高性能减水剂合成方法，按照以下步骤进行：向1升的烧瓶内倒入150~200克水，在向烧瓶内加入330~370克甲基烯丙基聚氧乙烯醚，升温至60℃并充分搅拌，待甲基烯丙基聚氧乙烯醚固体完全溶解，得溶液；向上述烧瓶内的溶液中加入C液，并立即滴加A液和B液，滴加完成后，将烧瓶整体置于58~65℃环境中保温1小时；向上述保温后的烧瓶及内的溶液降温至35~45℃，向烧饼内加入碱中和，至溶液中和后，向烧瓶内加入适量水，即得聚羧酸减水剂。本发明减水剂合成方法，在反应过程中不需要进行较大的降温和升温或保温，反应过程快速简单。

Description

一种高性能减水剂合成方法
技术领域
本发明涉及减水剂技术领域，更具体的说涉及一种减水剂的合成方法。
技术背景
现有技术中减水剂的合成方法，对于环境和温度的控制要求都较高，且夏天和冬天合成过程中环境的温度又有一定的改变，且反应过程中，需要使用大量的甲醛，极易照成挥发，反应过程难以控制，且生产效率低。
发明内容
本发明要解决的技术问题是提供一种操作简单、反应过程易控的减水剂合成方法。
为解决上述技术问题，本发明提供一种高性能减水剂合成方法，按照以下步骤进行：
（1）向1升的烧瓶内倒入150~200克水，在向烧瓶内加入330~370克甲基烯丙基聚氧乙烯醚，升温至60℃并充分搅拌，待甲基烯丙基聚氧乙烯醚固体完全溶解，得溶液；
（2）向（1）中烧瓶内的溶液中加入C液，并立即滴加A液和B液，滴加完成后，将烧瓶整体置于58~65℃环境中保温1小时；
（3）将（2）中保温后的烧瓶及内的溶液降温至35~45℃，向烧饼内加入碱中和，至溶液中和后，向烧瓶内加入适量水，即得聚羧酸减水剂。
优选的，一种高性能减水剂合成方法，按照以下步骤进行：
（1）向1升的烧瓶内倒入174克水，在向烧瓶内加入355克甲基烯丙基聚氧乙烯醚，升温至60℃并充分搅拌，待甲基烯丙基聚氧乙烯醚固体完全溶解，得溶液；
（2）向（1）中烧瓶内的溶液中加入C液，并立即滴加A液和B液，滴加完成后，将烧瓶整体置于60℃环境中保温1小时；
（3）将（2）中保温后的烧瓶及内的溶液降温至40℃，向烧饼内加入碱中和，至溶液中和后，向烧瓶内加入303克水，即得聚羧酸减水剂浓度为40%。
所述A液为35克丙烯酸和25克水溶液。
所述B液为0.78克巯基乙酸和0.61克VC和55克水溶液。
所述C液为1.64克双氧水和12克水溶液。
所述双氧水浓度为27.5%。
所述A液和B液同时滴加，并控制在3小时滴加完。
采用上述技术方案的有益效果是：本发明减水剂合成方法，在反应过程中不需要进行较大的降温和升温或保温，反应过程快速简单，采用常压反应，对反应的容器要求低，降低的生产成本，同时，保证了反应过程中操作人员的工作环境安全。
具体实施方式
下面对本发明的技术方案进行说明，以便于本技术领域的技术人员理解。
一种高性能减水剂合成方法，按照以下步骤进行：
首先，向1升的烧瓶内倒入174克水，在向烧瓶内加入355克甲基烯丙基聚氧乙烯醚，升温至60℃并充分搅拌，待甲基烯丙基聚氧乙烯醚固体完全溶解，得溶液；
其次，向上述烧瓶内的溶液中加入C液，并立即滴加A液和B液，滴加完成后，将烧瓶整体置于60℃环境中保温1小时；
再次，将上述保温后的烧瓶及内的溶液降温至40℃，向烧饼内加入碱中和，至溶液中和后，向烧瓶内加入303克水，即得聚羧酸减水剂浓度为40%。
本方法合成的减水剂，能够有效的保持水泥净浆、砂浆和混凝土工作量不变而显著减少其拌和用水量，能显著提高混凝土强度，改善混凝土的抗冻性，抗渗性和减少水泥用量，而且针对夏季高温环境下混凝土的坍落度损失快有极大的改善。
上述对发明进行了示例性描述，显然本发明具体实现并不受上述方式的限制，只要采用了本发明的方法构思和技术方案进行的这种非实质改进，或未经改进将发明的构思和技术方案直接应用于其他场合的，均在本发明的保护范围之内。

Claims (7)

1.一种高性能减水剂合成方法，其特征在于，按照以下步骤进行：
（1）向1升的烧瓶内倒入150~200克水，在向烧瓶内加入330~370克甲基烯丙基聚氧乙烯醚，升温至60℃并充分搅拌，待甲基烯丙基聚氧乙烯醚固体完全溶解，得溶液；
（2）向（1）中烧瓶内的溶液中加入C液，并立即滴加A液和B液，滴加完成后，将烧瓶整体置于58~65℃环境中保温1小时；
（3）将（2）中保温后的烧瓶及内的溶液降温至35~45℃，向烧饼内加入碱中和，至溶液中和后，向烧瓶内加入适量水，即得聚羧酸减水剂。
2.根据权利要求1所述的一种高性能减水剂合成方法，其特征在于，按照以下步骤进行：
（1）向1升的烧瓶内倒入174克水，在向烧瓶内加入355克甲基烯丙基聚氧乙烯醚，升温至60℃并充分搅拌，待甲基烯丙基聚氧乙烯醚固体完全溶解，得溶液；
（2）向（1）中烧瓶内的溶液中加入C液，并立即滴加A液和B液，滴加完成后，将烧瓶整体置于60℃环境中保温1小时；
（3）将（2）中保温后的烧瓶及内的溶液降温至40℃，向烧饼内加入碱中和，至溶液中和后，向烧瓶内加入303克水，即得聚羧酸减水剂浓度为40%。
3.根据权利要求2所述的一种高性能减水剂合成方法，其特征在于：所述A液为35克丙烯酸和25克水溶液。
4.根据权利要求2所述的一种高性能减水剂合成方法，其特征在于：所述B液为0.78克巯基乙酸和0.61克VC和55克水溶液。
5.根据权利要求2所述的一种高性能减水剂合成方法，其特征在于：所述C液为1.64克双氧水和12克水溶液。
6.根据权利要求5所述的一种高性能减水剂合成方法，其特征在于：所述双氧水浓度为27.5%。
7.根据权利要求2所述的一种高性能减水剂合成方法，其特征在于：所述A液和B液同时滴加，并控制在3小时滴加完。
CN2013103005854A 2013-07-18 2013-07-18 一种高性能减水剂合成方法 Pending CN103360554A (zh)