CN103357865B - 一种增强掺钛粉末冶金材料及其制备方法 - Google Patents

一种增强掺钛粉末冶金材料及其制备方法 Download PDF

Info

Publication number
CN103357865B
CN103357865B CN201310249041.XA CN201310249041A CN103357865B CN 103357865 B CN103357865 B CN 103357865B CN 201310249041 A CN201310249041 A CN 201310249041A CN 103357865 B CN103357865 B CN 103357865B
Authority
CN
China
Prior art keywords
powder
conditions
preparation
mixed
hour
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201310249041.XA
Other languages
English (en)
Other versions
CN103357865A (zh
Inventor
章功国
谢勇
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shanghai Jiasheng Automotive Parts Co ltd
Original Assignee
Anhui Jisite Intelligent Equipment Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Jisite Intelligent Equipment Co Ltd filed Critical Anhui Jisite Intelligent Equipment Co Ltd
Priority to CN201310249041.XA priority Critical patent/CN103357865B/zh
Publication of CN103357865A publication Critical patent/CN103357865A/zh
Application granted granted Critical
Publication of CN103357865B publication Critical patent/CN103357865B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种增强掺钛粉末冶金材料及其制备方法，其特征在于由下列重量份的原料制成：铁粉95‑99、铜粉0.3‑0.5、TiB1.2‑1.4、钛粉0.3‑0.5、铝粉2.4‑2.6、钼粉0.2‑0.3、Sb0.08‑0.12、Sc0.04‑0.07、NbC1‑1.3、TaC0.4‑0.7、ZrO20.4‑0.6、SiO21.2‑1.4、分散剂2‑3。本发明是一种烧结致密度高、硬度和弯曲强度高的材料，本发明的制备过程简单，成本低，可减少生产环节，降低能耗，适合于大批量生产。

Description

一种增强掺钛粉末冶金材料及其制备方法
技术领域
本发明涉及粉末冶金领域，尤其涉及一种增强掺钛粉末冶金材料及其制备方法。
背景技术
粉末冶金技术是将材料科学和金属成形技术完善的结合起来一种新型技术，因为高效、无切削加工、节材、节能、环保而被广泛使用于各种行业。
粉末冶金结构件制品材料成分不受熔炼限制，既可以加入合金成分，也可以加入其它结构组分，并且在相当大的范围内根据要求进行调整，进而在力学性能上能达到与钢件匹配的效果。
粉末冶金机械化程度高，既能减少人员，又能提高效率，进而节约成本。粉末冶金技术能取代传统的制造工艺，为广大传统企业节约成本。
所以研究各种机械零部件的粉末冶金的配方，适应不同的需要，具有重要的意义。
发明内容
本发明的目的是提供一种增强掺钛粉末冶金材料及其制备方法。
本发明的技术方案如下：
一种增强掺钛粉末冶金材料，其特征在于由下列重量份的原料制成：铁粉95-99、铜粉0.3-0.5、TiB1.2-1.4、钛粉0.3-0.5、铝粉2.4-2.6、钼粉0.2-0.3、Sb0.08-0.12、Sc0.04-0.07、NbC1-1.3、TaC0.4-0.7、ZrO20.4-0.6、SiO21.2-1.4、分散剂2-3。
所述的分散剂由下列重量份的原料制成：三聚磷酸钠2-3、丙三醇三甘油酸酯1-2、交联剂 TAC 1-2、硅烷偶联剂KH550 2-3、氮化铝粉1-2、硼化二钼0.3-0.5、微晶石蜡3-4、壳聚糖1-2；
制备方法是：将各物料混合，研磨分散均匀即可。
所述的适用于增强掺钛粉末冶金材料的制备方法，其特征在于包括以下步骤：
（1）将各物料混合，在53-56℃下搅拌均匀50-60分钟后，装入模具，压制成坯；
（2）将压坯放在烧结炉中，以4-6℃/分钟速率升温至520-540℃条件下烧结2-3小时；再以8-12℃/分钟速率升温至1050-1090℃条件下烧结3-4小时；再以8-10℃/分钟速率降温至480-550℃条件下保温2-3小时；再降温到280-290℃条件下保温2-3小时；
（3）将压坯送入蒸汽处理炉中，在炉中温度260-280℃的条件下通入蒸汽60-90分钟；
（4）将压坯放入350-390℃条件下，保温2-3小时，取出放入冷水中淬火1-2小时，取出即得。
本发明的增强掺钛粉末冶金材料是一种烧结致密度高、硬度和弯曲强度高的材料。本发明方法制备掺钛粉末冶金材料工艺过程简单，成本低，可减少生产环节，降低能耗，适合于大批量生产。
具体实施方式
一种增强掺钛粉末冶金材料，由下列重量份的原料（公斤）制成：铁粉95-99、铜粉0.5、TiB1.4、钛粉0.5、铝粉2.6、钼粉0.3、Sb0.08、Sc0.04、NbC1.3、TaC0.7、ZrO20.6、SiO21.4、分散剂3。
所述的分散剂由下列重量份的原料制成：三聚磷酸钠3、丙三醇三甘油酸酯1、交联剂 TAC 2、硅烷偶联剂KH550 3、氮化铝粉2、硼化二钼0.5、微晶石蜡4、壳聚糖2；
制备方法是：将各物料混合，研磨分散均匀即可。
增强掺钛粉末冶金材料的制备方法，包括以下步骤：
（1）将各物料混合，在53-56℃下搅拌均匀50-60分钟后，装入模具，压制成坯；
（2）将压坯放在烧结炉中，以4-6℃/分钟速率升温至520-540℃条件下烧结2-3小时；再以8-12℃/分钟速率升温至1050-1090℃条件下烧结3-4小时；再以8-10℃/分钟速率降温至480-550℃条件下保温2-3小时；再降温到280-290℃条件下保温2-3小时；
（3）将压坯送入蒸汽处理炉中，在炉中温度260-280℃的条件下通入蒸汽60-90分钟；
（4）将压坯放入350-390℃条件下，保温2-3小时，取出放入冷水中淬火1-2小时，取出即得。
经过检测，本发明法兰的热处理硬度：HRC61 ；抗拉强度：1280MPa 。

Claims (2)

1.一种增强掺钛粉末冶金材料，其特征在于由下列重量份的原料制成： 铁粉95-99、铜粉0.3-0.5、TiB1.2-1.4、钛粉0.3-0.5、铝粉2.4-2.6、钼粉0.2-0.3、Sb0.08-0.12、Sc0.04-0.07、NbC1-1.3、TaC0.4-0.7、ZrO20.4-0.6、SiO21.2-1.4、分散剂2-3； 所述的分散剂由下列重量份的原料制成：三聚磷酸钠2-3、丙三醇三甘油酸酯1-2、交联剂 TAC 1-2、硅烷偶联剂KH550 2-3、氮化铝粉1-2、硼化二钼0.3-0.5、微晶石蜡3-4、壳聚糖1-2；分散剂的制备方法是：将各物料混合，研磨分散均匀即可。
2.根据权利要求1所述的增强掺钛粉末冶金材料的制备方法，其特征在于包括以下步骤：
（1）将各物料混合，在53-56℃下搅拌均匀50-60分钟后，装入模具，压制成坯；
（2）将压坯放在烧结炉中，以4-6℃/分钟速率升温至520-540℃条件下烧结2-3小时；再以8-12℃/分钟速率升温至1050-1090℃条件下烧结3-4小时；再以8-10℃/分钟速率降温至480-550℃条件下保温2-3小时；再降温到280-290℃条件下保温2-3小时；
（3）将压坯送入蒸汽处理炉中，在炉中温度260-280℃的条件下通入蒸汽60-90分钟；
（4）将压坯放入350-390℃条件下，保温2-3小时，取出放入冷水中淬火1-2小时，取出即得。
CN201310249041.XA 2013-06-21 2013-06-21 一种增强掺钛粉末冶金材料及其制备方法 Active CN103357865B (zh)