CN107755684A - 一种耐磨抗冲击性强的粉末冶金复合材料 - Google Patents

一种耐磨抗冲击性强的粉末冶金复合材料 Download PDF

Info

Publication number
CN107755684A
CN107755684A CN201710899658.4A CN201710899658A CN107755684A CN 107755684 A CN107755684 A CN 107755684A CN 201710899658 A CN201710899658 A CN 201710899658A CN 107755684 A CN107755684 A CN 107755684A
Authority
CN
China
Prior art keywords
parts
powder
powder metallurgy
strong composite
composite powder
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710899658.4A
Other languages
English (en)
Inventor
王明华
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangsu Crystal New Mstar Technology Ltd
Original Assignee
Jiangsu Crystal New Mstar Technology Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiangsu Crystal New Mstar Technology Ltd filed Critical Jiangsu Crystal New Mstar Technology Ltd
Priority to CN201710899658.4A priority Critical patent/CN107755684A/zh
Publication of CN107755684A publication Critical patent/CN107755684A/zh
Pending legal-status Critical Current

Abstract

一种耐磨抗冲击性强的粉末冶金复合材料，属于合金材料技术领域。包括以下各组份按重量份制备而成：奥氏体不锈钢50‑79份、硼化铁1‑2份、钒粉1‑6份、二氧化锰5‑8份、钴粉1‑5份、纳米二氧化硅1‑3份、石墨2‑6份、钼粉2‑5份、镍粉1‑3份、金粉1‑2份、玻璃纤维2‑8份、助剂1‑3份。本发明的耐磨性能良好、使用寿命长、生产成本低、抗压能力强，且本发明技术含量高，使用安全可靠，使用领域宽，经济效果显著。

Description

一种耐磨抗冲击性强的粉末冶金复合材料
技术领域
本发明涉及一种合金材料，尤其是一种耐磨抗冲击性强的粉末冶金复合材料，属于合金材料技术领域。
背景技术
粉末冶金是制取金属或用金属粉末作为原料，经过成形和烧结，制造金属材料、复合材料以及各种类型制品的工艺技术。由于粉末冶金技术适用范围广，能直接成型，基本不需二次加工，可降低材料成本及加工成本等优点，其已广泛应用于机械加工行业。
粉末冶金结构件制品材料成分不受熔炼限制，既可以加入合金成分，也可以加入其它结构组分，并且在相当大的范围内根据要求进行调整，进而在力学性能上能达到与钢件匹配的效果。
粉末冶金机械化程度高，既能减少人员，又能提高效率，进而节约成本。粉末冶金技术能取代传统的制造工艺，为广大传统企业节约成本。所以研究各种机械零部件的粉末冶金的配方，适应不同的需要，具有重要的意义。
发明内容
本发明的目的是针对现有技术的不足，提供一种耐磨抗冲击性强的粉末冶金复合材料。
本发明的目的是通过以下技术方案实现的：一种耐磨抗冲击性强的粉末冶金复合材料，其特征是，包括以下各组份按重量份制备而成：奥氏体不锈钢 50-79份、硼化铁1-2份、钒粉1-6份、二氧化锰5-8份、钴粉1-5份、纳米二氧化硅1-3份、石墨2-6份、钼粉2-5份、镍粉1-3份、金粉1-2 份、玻璃纤维2-8份、助剂1-3份。
所述助剂包括环烷酸铅、三聚磷酸钠、丙三醇三甘油酸酯、交联剂、硅烷偶联剂、氮化铝粉、微晶石蜡、壳聚糖。
所述奥氏体不锈钢为60-69份。
还含有抗氧化剂、耐磨剂。
所述玻璃纤维粒径为0.5-2.5mm。
奥氏体不锈钢，是指在常温下具有奥氏体组织的不锈钢。钢中含Cr约18%、Ni 8%~25%、C约0.1%时，具有稳定的奥氏体组织。奥氏体铬镍不锈钢包括著名的18Cr-8Ni钢和在此基础上增加Cr、Ni含量并加入Mo、Cu、Si、Nb、Ti等元素发展起来的高Cr-Ni系列钢。奥氏体不锈钢无磁性而且具有高韧性和塑性，但强度较低，不可能通过相变使之强化，仅能通过冷加工进行强化，如加入S，Ca，Se，Te等元素，则具有良好的易切削性。
本发明生产制造容易，使用效果良好，添加助剂，使合金粉末分散均匀，保证产品内部组织结构的纵横均匀度，使产品的疲劳寿命有所提高；本发明根据需要的不同，对材料的组成进行调整，生产的复合材料其抗拉强度、气密性高组织结构均匀，广泛适应于各环境。
本发明的耐磨性能良好、使用寿命长、生产成本低、抗压能力强，且本发明技术含量高，使用安全可靠，使用领域宽，经济效果显著。
具体实施方式
实施例1
一种耐磨抗冲击性强的粉末冶金复合材料，包括以下各组份按重量份制备而成：奥氏体不锈钢 50-79份、硼化铁1-2份、钒粉1-6份、二氧化锰5-8份、钴粉1-5份、纳米二氧化硅1-3份、石墨2-6份、钼粉2-5份、镍粉1-3份、金粉1-2 份、玻璃纤维2-8份、助剂1-3份。
助剂包括环烷酸铅、三聚磷酸钠、丙三醇三甘油酸酯、交联剂、硅烷偶联剂、氮化铝粉、微晶石蜡、壳聚糖；奥氏体不锈钢为60-69份，还含有抗氧化剂、耐磨剂，玻璃纤维粒径为0.5-2.5mm。
实施例2
一种耐磨抗冲击性强的粉末冶金复合材料，包括以下各组份按重量份制备而成：奥氏体不锈钢 79份、硼化铁2份、钒粉6份、二氧化锰8份、钴粉5份、纳米二氧化硅3份、石墨6份、钼粉5份、镍粉3份、金粉2 份、玻璃纤维8份、助剂3份。
助剂包括环烷酸铅、三聚磷酸钠、丙三醇三甘油酸酯、交联剂、硅烷偶联剂、氮化铝粉、微晶石蜡、壳聚糖；奥氏体不锈钢为60-69份，还含有抗氧化剂、耐磨剂，玻璃纤维粒径为0.5mm。
实施例3
一种耐磨抗冲击性强的粉末冶金复合材料，包括以下各组份按重量份制备而成：奥氏体不锈钢 50份、硼化铁1份、钒粉1份、二氧化锰5份、钴粉1份、纳米二氧化硅1份、石墨2份、钼粉2份、镍粉1份、金粉1份、玻璃纤维2份、助剂1份。
助剂包括环烷酸铅、三聚磷酸钠、丙三醇三甘油酸酯、交联剂、硅烷偶联剂、氮化铝粉、微晶石蜡、壳聚糖；还含有抗氧化剂、耐磨剂，玻璃纤维粒径为2.5mm。

Claims (5)

1. 一种耐磨抗冲击性强的粉末冶金复合材料，其特征是，包括以下各组份按重量份制备而成：奥氏体不锈钢 50-79份、硼化铁1-2份、钒粉1-6份、二氧化锰5-8份、钴粉1-5份、纳米二氧化硅1-3份、石墨2-6份、钼粉2-5份、镍粉1-3份、金粉1-2 份、玻璃纤维2-8份、助剂1-3份。
2.根据权利要求1所述的一种耐磨抗冲击性强的粉末冶金复合材料，其特征是，所述助剂包括环烷酸铅、三聚磷酸钠、丙三醇三甘油酸酯、交联剂、硅烷偶联剂、氮化铝粉、微晶石蜡、壳聚糖。
3.根据权利要求1所述的一种耐磨抗冲击性强的粉末冶金复合材料，其特征是，所述奥氏体不锈钢为60-69份。
4.根据权利要求1所述的一种耐磨抗冲击性强的粉末冶金复合材料，其特征是，还含有抗氧化剂、耐磨剂。
5.根据权利要求1所述的一种耐磨抗冲击性强的粉末冶金复合材料，其特征是，所述玻璃纤维粒径为0.5-2.5mm。
CN201710899658.4A 2017-09-28 2017-09-28 一种耐磨抗冲击性强的粉末冶金复合材料 Pending CN107755684A (zh)