CN103361578A - 一种合金含铬粉末冶金钢及其制备方法 - Google Patents
一种合金含铬粉末冶金钢及其制备方法 Download PDFInfo
- Publication number
- CN103361578A CN103361578A CN201310249115XA CN201310249115A CN103361578A CN 103361578 A CN103361578 A CN 103361578A CN 201310249115X A CN201310249115X A CN 201310249115XA CN 201310249115 A CN201310249115 A CN 201310249115A CN 103361578 A CN103361578 A CN 103361578A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- hour
- under
- condition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种合金含铬粉末冶金钢及其制备方法,其特征在于由下列重量份的原料制成:铁粉94-99、镍粉1.4-1.8、石墨粉0.6-0.8、铝粉1.2-1.4、Bi0.4-0.5、Sb0.03-0.05、Mn1.6-1.8、Be0.1-0.3、氧化硼1.2-1.4、CaO1.0-1.1、二硼化钽0.3-0.5、硼化钒0.2-0.4、硬酸酸锌2.3-2.5、微晶蜡1.2-1.5、分散剂2-3。本发明制造的工具钢硬度高,耐磨性好,法兰组织致密,微观结构良好,孔隙很少,结构刚度、硬度、耐疲劳性能、抗拉强度性能优良。而且由于采用了模压,使设备简化,降了生产成本。
Description
技术领域
本发明涉及粉末冶金领域,尤其涉及一种合金含铬粉末冶金钢及其制备方法。
背景技术
粉末冶金技术是将材料科学和金属成形技术完善的结合起来一种新型技术,因为高效、无切削加工、节材、节能、环保而被广泛使用于各种行业。
粉末冶金结构件制品材料成分不受熔炼限制,既可以加入合金成分,也可以加入其它结构组分,并且在相当大的范围内根据要求进行调整,进而在力学性能上能达到与钢件匹配的效果。
粉末冶金机械化程度高,既能减少人员,又能提高效率,进而节约成本。粉末冶金技术能取代传统的制造工艺,为广大传统企业节约成本。
所以研究各种机械零部件的粉末冶金的配方,适应不同的需要,具有重要的意义。
发明内容
本发明的目的是提供一种合金含铬粉末冶金钢及其制备方法。
本发明的技术方案如下:
一种合金含铬粉末冶金钢,其特征在于由下列重量份的原料制成:
铁粉94-99、镍粉1.4-1.8、石墨粉0.6-0.8、铝粉1.2-1.4、Bi0.4-0.5、Sb0.03-0.05、Mn1.6-1.8、Be0.1-0.3、氧化硼1.2-1.4、CaO1.0-1.1、二硼化钽0.3-0.5、硼化钒0.2-0.4、硬酸酸锌2.3-2.5、微晶蜡1.2-1.5、分散剂2-3。
所述的分散剂由下列重量份的原料制成:氨丙基三乙氧基硅烷1.5-1.8、硼化锆0.3-0.5、高耐磨炭黑0.2-0.4、氟化锆0.2-0.5、二甲基硅油2.3-2.5、微晶石蜡3-4、羧甲基纤维素2-3;
制备方法是:将各物料混合,研磨分散均匀即可。
所述的合金含铬粉末冶金钢的制备方法,其特征在于包括以下步骤:
(1)将各物料混合,在45-47℃下搅拌均匀40-50分钟后,装入模具,压制成坯;
(2)将压坯放在烧结炉中,以6-8℃/分钟速率升温至420-430℃条件下烧结2-3小时;再以9-12℃/分钟速率升温至680-710℃条件下烧结2-3小时;以16-18℃/分钟速率升温至1060-1090℃条件下烧结2-3小时;再以以9-11℃/分钟速率降温至660-690℃条件下保温2-3小时;
(3)将压坯放入0-5℃中冷却1-2小时,取出;
(4)将压坯送入蒸汽处理炉中,在炉中温度450-490℃的条件下通入蒸汽50-60分钟;再在炉中温度250-290℃的条件下通入蒸汽40-60分钟;
(5)取出即得。
本发明制造的工具钢硬度高,耐磨性好,法兰组织致密,微观结构良好,孔隙很少,结构刚度、硬度、耐疲劳性能、抗拉强度性能优良。而且由于采用了模压,使设备简化,降了生产成本。
具体实施方式
一种合金含铬粉末冶金钢,由下列重量份的原料(公斤)制成:
铁粉94、镍粉1.8、石墨粉0.8、铝粉1.2、Bi0.4、Sb0.05、Mn1.8、Be0.3、氧化硼1.2、CaO1.1、二硼化钽0.5、硼化钒0.4、硬酸酸锌2.5、微晶蜡1.2、分散剂2。
所述的分散剂由下列重量份的原料制成:氨丙基三乙氧基硅烷1.8、硼化锆0.3、高耐磨炭黑0.4、氟化锆0.5、二甲基硅油2.5、微晶石蜡3、羧甲基纤维素2;
制备方法是:将各物料混合,研磨分散均匀即可。
合金含铬粉末冶金钢的制备方法,包括以下步骤:
(1)将各物料混合,在45-47℃下搅拌均匀40-50分钟后,装入模具,压制成坯;
(2)将压坯放在烧结炉中,以6-8℃/分钟速率升温至420-430℃条件下烧结2-3小时;再以9-12℃/分钟速率升温至680-710℃条件下烧结2-3小时;以16-18℃/分钟速率升温至1060-1090℃条件下烧结2-3小时;再以以9-11℃/分钟速率降温至660-690℃条件下保温2-3小时;
(3)将压坯放入0-5℃中冷却1-2小时,取出;
(4)将压坯送入蒸汽处理炉中,在炉中温度450-490℃的条件下通入蒸汽50-60分钟;再在炉中温度250-290℃的条件下通入蒸汽40-60分钟;
(5)取出即得。
经过检测,本发明法兰的热处理硬度:HRC65 ;抗拉强度:1580MPa 。
Claims (2)
1.一种合金含铬粉末冶金钢,其特征在于由下列重量份的原料制成:
铁粉94-99、镍粉1.4-1.8、石墨粉0.6-0.8、铝粉1.2-1.4、Bi0.4-0.5、Sb0.03-0.05、Mn1.6-1.8、Be0.1-0.3、氧化硼1.2-1.4、CaO1.0-1.1、二硼化钽0.3-0.5、硼化钒0.2-0.4、硬酸酸锌2.3-2.5、微晶蜡1.2-1.5、分散剂2-3;
所述的分散剂由下列重量份的原料制成:氨丙基三乙氧基硅烷1.5-1.8、硼化锆0.3-0.5、高耐磨炭黑0.2-0.4、氟化锆0.2-0.5、二甲基硅油2.3-2.5、微晶石蜡3-4、羧甲基纤维素2-3;制备方法是:将各物料混合,研磨分散均匀即可。
2.根据权利要求1所述的合金含铬粉末冶金钢的制备方法,其特征在于包括以下步骤:
(1)将各物料混合,在45-47℃下搅拌均匀40-50分钟后,装入模具,压制成坯;
(2)将压坯放在烧结炉中,以6-8℃/分钟速率升温至420-430℃条件下烧结2-3小时;再以9-12℃/分钟速率升温至680-710℃条件下烧结2-3小时;以16-18℃/分钟速率升温至1060-1090℃条件下烧结2-3小时;再以以9-11℃/分钟速率降温至660-690℃条件下保温2-3小时;
(3)将压坯放入0-5℃中冷却1-2小时,取出;
(4)将压坯送入蒸汽处理炉中,在炉中温度450-490℃的条件下通入蒸汽50-60分钟;再在炉中温度250-290℃的条件下通入蒸汽40-60分钟;
(5)取出即得。