CN104876608A - 抗热震耐火砖的制备方法 - Google Patents

抗热震耐火砖的制备方法 Download PDF

Info

Publication number
CN104876608A
CN104876608A CN201510286109.0A CN201510286109A CN104876608A CN 104876608 A CN104876608 A CN 104876608A CN 201510286109 A CN201510286109 A CN 201510286109A CN 104876608 A CN104876608 A CN 104876608A
Authority
CN
China
Prior art keywords
parts
powder
fine powder
refractory brick
shock resistant
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510286109.0A
Other languages
English (en)
Inventor
梁运富
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Liuzhou Pu Ya Trade Co Ltd
Original Assignee
Liuzhou Pu Ya Trade Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Liuzhou Pu Ya Trade Co Ltd filed Critical Liuzhou Pu Ya Trade Co Ltd
Priority to CN201510286109.0A priority Critical patent/CN104876608A/zh
Publication of CN104876608A publication Critical patent/CN104876608A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种抗热震耐火砖的制备方法，涉及耐火材料制造技术领域，包括下列重量份的原料：莫来石粉30份～40份、红柱石细粉10份～20份、硅线石细粉5份～15份、广西粘土5份～8份、硅微粉3份～5份；经过配料、混料、制坯、干燥、烧制抗热震耐火砖。与现有技术相比，本发明生产的抗热震耐火砖耐高温、耐腐蚀，抗热震性能好，荷重软化温度提高，用作工业回转窑炉耐火砖使用不易出现裂纹损坏，延长使用寿命。

Description

抗热震耐火砖的制备方法
技术领域
本发明涉及耐火材料制造技术领域，尤其是一种抗热震耐火砖的制备方法。
背景技术
工业回转窑炉用耐火砖不仅要承受高温，还要承受物料的侵蚀磨损、窑体转动产生的应力等，因此所用耐火砖要求耐高温、耐腐蚀，抗热震性能好，荷重软化温度高，而目前生产的耐火砖耐高温、耐腐蚀，但抗热震性能差，荷重软化温度较低，用作工业回转窑炉耐火砖使用容易出现裂纹损坏，使用寿命短。
发明内容
本发明所要解决的技术问题是提供一种抗热震耐火砖的制备方法，以解决目前生产的耐火砖抗热震能差，荷重软化温度较低的问题。
为了解决上述问题，本发明采用的技术方案是：这种抗热震耐火砖的制备方法，包括下列重量份的原料：莫来石粉30份～40份、红柱石细粉10份～20份、硅线石细粉5份～15份、广西粘土5份～8份、硅微粉3份～5份；
操作步骤如下：
a.按上述各原料的重量份称取莫来石粉、红柱石细粉、硅线石细粉、广西粘土、硅微粉，备用；
b.将所述莫来石粉、所述红柱石细粉、所述硅线石细粉放入混砂机混炼2min～3min，然后加入所述广西粘土和占原料总重量2%～3%的水，混炼3min～5min，再加入所述硅微粉，混炼10min～15min，得到混合料；
c.采用压砖机将步骤b所得混合料压制成砖坯；
d.所述砖坯在100℃～120℃温度下干燥1天～2天；
e.将步骤d所得砖坯放入烧成窑在1380℃～1430℃的温度下焙烧4小时～6小时，冷却至室温即得本抗热震耐火砖。
上述抗热震耐火砖的制备方法技术方案中，更具体的技术方案还可以是：所述红柱石细粉和所述硅线石细粉的颗粒直径为40μm～80μm；所述硅微粉的颗粒直径≤5μm。
所述莫来石，是铝硅酸盐在高温下生成的矿物，具有耐高温、强度高导热系数小，节能效果显著等特点，莫来石矿被用来生产高温耐火材料。
所述红柱石，是一种铝硅酸盐矿物，在常压下加热至1350℃以后，开始转化成与原晶体平行的针状莫来石，红柱石在加热转化成莫来石的过程中，可以形成良好的莫来石网络，体积膨胀约4%，具有更高的耐火性能，耐火度可达1800℃以上，且耐骤冷骤热，机械强度大，抗热冲击力强，抗渣性强，荷重转化点高，并具有极高的化学稳定性和极强的抗化学腐蚀性。
所述硅线石，是一种褐色、浅绿色、浅蓝色或白色的玻璃状硅酸盐矿物，当加热到1300℃时变为莫来石，可做高级耐火材料。
所述广西粘土，是一种可塑性好的软质耐火粘土，它的粒度极细，浸散性与粘结性也很好，烧结范围宽，含高岭石往往在70％以上，并以无序高岭石为主，可显著增加其可塑性及抗折强度，是耐火材料用的优质结合粘土。
所述硅微粉，是由天然石英或熔融石英经破碎、球磨、浮选、酸洗提纯、高纯水处理等多道工艺加工而成的微粉，具备耐温性好、耐酸碱腐蚀、导热性差、高绝缘、低膨胀、化学性能稳定、硬度大等优良的性能，被广泛用于化工、电子、涂料、高级油漆等领域。
由于采用了上述技术方案，本发明与现有技术相比具有如下有益效果：
本发明采用莫来石粉、红柱石细粉、硅线石细粉为主要原料，广西粘土和硅微粉为结合剂，经过配料、混料、制坯、干燥、烧制抗热震耐火砖，该耐火砖耐高温、耐腐蚀，抗热震性能好，荷重软化温度提高，用作工业回转窑炉耐火砖使用不易出现裂纹损坏，延长使用寿命。
具体实施方式
下面结合具体实施例对本发明作进一步详述：
实施例1
一种抗热震耐火砖的制备方法，包括下列重量份的原料：莫来石粉300公斤、红柱石细粉100公斤、硅线石细粉50公斤、广西粘土50公斤、硅微粉30公斤；本实施例的红柱石细粉和硅线石细粉的颗粒直径为40μm；硅微粉的颗粒直径为5μm。
操作步骤如下：
a.按上述各原料的重量份称取莫来石粉、红柱石细粉、硅线石细粉、广西粘土、硅微粉，备用；
b.将莫来石粉、红柱石细粉、硅线石细粉放入混砂机混炼2min，然后加入广西粘土和占原料总重量2%的水，混炼3min，再加入硅微粉，混炼10min，得到混合料；
c.采用压砖机将步骤b所得混合料压制成砖坯；
d.砖坯在100℃温度下干燥1天；
e.将步骤d所得砖坯放入烧成窑在1380℃的温度下焙烧4小时，冷却至室温即得本抗热震耐火砖。
实施例2
一种抗热震耐火砖的制备方法，包括下列重量份的原料：莫来石粉400公斤、红柱石细粉200公斤、硅线石细粉150公斤、广西粘土80公斤、硅微粉50公斤；本实施例的红柱石细粉和硅线石细粉的颗粒直径为80μm；硅微粉的颗粒直径＜5μm。
操作步骤如下：
a.按上述各原料的重量份称取莫来石粉、红柱石细粉、硅线石细粉、广西粘土、硅微粉，备用；
b.将莫来石粉、红柱石细粉、硅线石细粉放入混砂机混炼3min，然后加入广西粘土和占原料总重量3%的水，混炼5min，再加入硅微粉，混炼15min，得到混合料；
c.采用压砖机将步骤b所得混合料压制成砖坯；
d.砖坯在120℃温度下干燥2天；
e.将步骤d所得砖坯放入烧成窑在1430℃的温度下焙烧6小时，冷却至室温即得本抗热震耐火砖。

Claims (2)

1.一种抗热震耐火砖的制备方法，其特征在于包括下列重量份的原料：莫来石粉30份～40份、红柱石细粉10份～20份、硅线石细粉5份～15份、广西粘土5份～8份、硅微粉3份～5份；
操作步骤如下：
a.按上述各原料的重量份称取莫来石粉、红柱石细粉、硅线石细粉、广西粘土、硅微粉，备用；
b.将所述莫来石粉、所述红柱石细粉、所述硅线石细粉放入混砂机混炼2min～3min，然后加入所述广西粘土和占原料总重量2%～3%的水，混炼3min～5min，再加入所述硅微粉，混炼10min～15min，得到混合料；
c.采用压砖机将步骤b所得混合料压制成砖坯；
d.所述砖坯在100℃～120℃温度下干燥1天～2天；
e.将步骤d所得砖坯放入烧成窑在1380℃～1430℃的温度下焙烧4小时～6小时，冷却至室温即得本抗热震耐火砖。
2.根据权利要求1所述的抗热震耐火砖的制备方法，其特征在于：所述红柱石细粉和所述硅线石细粉的颗粒直径为40μm～80μm；所述硅微粉的颗粒直径≤5μm。
CN201510286109.0A 2015-05-29 2015-05-29 抗热震耐火砖的制备方法 Pending CN104876608A (zh)