CN103342475A - 玻璃瓶喷色烤花方法 - Google Patents

玻璃瓶喷色烤花方法 Download PDF

Info

Publication number
CN103342475A
CN103342475A CN2013102782367A CN201310278236A CN103342475A CN 103342475 A CN103342475 A CN 103342475A CN 2013102782367 A CN2013102782367 A CN 2013102782367A CN 201310278236 A CN201310278236 A CN 201310278236A CN 103342475 A CN103342475 A CN 103342475A
Authority
CN
China
Prior art keywords
vial
firing method
decoration firing
baking
glass bottle
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2013102782367A
Other languages
English (en)
Inventor
赵玉忠
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN2013102782367A priority Critical patent/CN103342475A/zh
Publication of CN103342475A publication Critical patent/CN103342475A/zh
Pending legal-status Critical Current

Abstract

本发明涉及材料加工领域，具体而言，涉及玻璃瓶喷色烤花方法。该方法包括：用含有2%氢氟酸的水清洗玻璃瓶将玻璃瓶的外表面进行处理；向玻璃瓶的外表面喷涂油漆；将喷涂油漆后的玻璃瓶在150-190℃烤炉中进行第一烘烤；退温至70-80℃；将待粘贴的花纸在温水中浸泡；在室温下，将浸泡后的花纸粘贴在退温后的玻璃瓶的外表面上，自然晾干；将玻璃瓶放入160-180℃烤炉进行第二烘烤，得到喷漆并烤花的玻璃瓶。本发明提供的一种玻璃瓶喷色烤花方法，能够在透明玻璃瓶上外涂油漆再烤花纸，而且，油漆和花纸的粘贴力都大幅增强。

Description

玻璃瓶喷色烤花方法
技术领域
本发明涉及材料加工领域，具体而言，涉及玻璃瓶喷色烤花方法。
背景技术
烤花纸的瓶子广受欢迎，但是制作烤花纸的瓶子的相关技术，依然停留于在透明的玻璃瓶子上烤花纸，将温度调节在560度左右，在该高温下将花纸粘贴在透明玻璃瓶上。其中560度即可解决花纸粘贴到透明玻璃瓶上时花纸不粘贴，花纸残缺的问题。研究者为了迎合人们多样化需求，逐渐开发了在透明瓶子上外涂油漆，又粘贴花纸的烤花纸油漆瓶子，在该研究中借用现有在透明瓶子上粘贴花纸的技术会造成油漆掉落，花纸粘贴不紧的问题，因此，需要开发新的对应烤花纸油漆瓶子的制造技术。
发明内容
本发明的目的在于提供玻璃瓶喷色烤花方法，以解决上述的问题。
本发明实施例提供了一种玻璃瓶喷色烤花方法，包括：
用含有2%氢氟酸的水清洗玻璃瓶，将玻璃瓶的外表面进行处理；
向玻璃瓶的外表面喷涂油漆；
将喷涂油漆后的玻璃瓶在150-190℃烤炉中进行第一烘烤；
退温至70-80℃；
将待粘贴的花纸在温水中浸泡；
在室温下，将浸泡后的花纸粘贴在退温后的玻璃瓶的外表面上，自然晾干；
将玻璃瓶放入160-180℃烤炉进行第二烘烤，得到喷漆并烤花的玻璃瓶。
本发明实施例提供了一种玻璃瓶喷色烤花方法，用含有2%质量比的氢氟酸的水清洗玻璃瓶能改善瓶子着色力差的问题；将喷涂油漆后的玻璃瓶进行150-190℃下的第一烘烤能提高瓶子着色力，防止瓶子脱色；温水浸泡后的花纸较软，易粘贴，自然晾干后，能延长花纸与油漆的粘贴力，并防止花纸将油漆破坏；160-180℃下第二烘烤利用高温提高花纸和油漆的粘贴力，将花纸、油漆进行进一步的位置固定。
附图说明
图1示出了玻璃瓶喷色烤花方法的流程示意图。
具体实施方式
下面通过具体的实施例子并结合附图对本发明做进一步的详细描述。
实施例1：
一种玻璃瓶喷色烤花方法，包括：
用含有2%氢氟酸的水清洗玻璃瓶，将玻璃瓶的外表面进行处理；
向玻璃瓶的外表面喷涂油漆；
将喷涂油漆后的玻璃瓶在150-190℃烤炉中进行第一烘烤；
退温至70-80℃；
将待粘贴的花纸在温水中浸泡；
在室温下，将浸泡后的花纸粘贴在退温后的玻璃瓶的外表面上，自然晾干；
将玻璃瓶放入160-180℃烤炉进行第二烘烤，得到喷漆并烤花的玻璃瓶。
用含有2%质量比的氢氟酸的水清洗玻璃瓶能改善瓶子着色力差的问题，将喷涂油漆后的玻璃瓶进行150-190℃下的第一烘烤能提高瓶子着色力，防止瓶子脱色；温水浸泡后的花纸较软，易粘贴，自然晾干后，能延长花纸与油漆的粘贴力，并防止花纸将油漆破坏，160-180℃下第二烘烤利用高温提高花纸和油漆的粘贴力，将花纸、油漆进行进一步的位置固定。
实施例2：
本实施例中，玻璃瓶喷色烤花方法的流程为，如图1，所示：
步骤101，去除玻璃瓶的外表面的污渍；
除去污渍能够提高玻璃瓶与油漆的粘贴力，提高喷漆的均匀性。
通常为了便于观察，也应该将玻璃瓶的内表面尽量保持干净。
步骤102，用含有2%质量比的氢氟酸的水清洗玻璃瓶；
氢氟酸为弱酸，能与玻璃瓶表面的碱性物质进行反应，同时改变玻璃瓶表面的酸碱性，进而为后续喷漆时，油漆与玻璃瓶外表面的粘贴力更强提供前提条件。其中，2%是比较严格的控制条件，在该质量百分比浓度下，酸性的氢氟酸对玻璃瓶的外表面不会造成任何破坏，且与碱性物质的中和效果好，提高玻璃瓶外表面涂漆的均匀性。清洗时间控制在5-10分钟。
步骤103，用清水冲洗去除玻璃瓶的外表面残留的氢氟酸；
清水冲洗氢氟酸，能够调节玻璃瓶外表面的酸碱性，提高玻璃瓶外表面与油漆的粘贴力。
步骤104，在50-80℃的水中将冲洗后的玻璃瓶进行烫洗；
可以把瓶子中的氢氟酸冲洗掉。保持瓶子干净，减少水渍。
步骤105，向玻璃瓶的外表面喷涂油漆；
喷色步骤需要喷涂均匀，不能有油漆流淌，也不能有杂质。
优选采用专业喷涂人员使用通过ISO9001质量检测的油性油漆用喷枪均匀喷涂在玻璃瓶表面上。
步骤106，将喷涂油漆后的玻璃瓶在150-190℃烤炉中进行第一烘烤；
第一烘烤后能够提高油漆与玻璃瓶外表面的粘贴力。该烘烤可以选用电烤炉，第一烘烤时间控制在20-40分钟。
步骤107，退温至70-80℃；
退温的温度和时间控制得当后，能提高油漆与玻璃瓶外表面的粘贴力，到粘贴花纸步骤时，能避免花纸薄膜撕下时不会出现油漆随花纸脱落的现象。退温的方式可以采用室温自然退温或者采用风扇退温，具体退温方式可以根据情况而定。
步骤108，将待粘贴的花纸在温水中浸泡；
该步骤可以设置在以上任意步骤之前。浸泡花纸的水温不能太高，也不能太低，过高会使花纸浸泡软、粘；过低会使花纸变脆，容易粘贴不全面，用温水浸泡后的花纸粘贴在玻璃瓶上后，需要用刮板或其他专业性工具刮去花纸上和花纸周边的水份，擦干水珠，并且粘贴中不能出现气泡。温水的温度为30-40℃，粘贴的温度也非常重要，需要在室温下，室温需要在20℃以上，比如20℃-35℃。
步骤109，在室温下，将浸泡后的花纸粘贴在退温后的玻璃瓶的外表面上，自然晾干；
室温下，室温需要在20℃以上。自然晾干能延长花纸与油漆的粘贴力，并防止花纸将油漆破坏。自然晾干的时间控制在7-15小时，比如12小时，只有时间长，才能达到更好的效果。为了提高玻璃瓶烤花的效果，粘贴需要在无气泡的情况下进行。
步骤110，晾干后除去花纸的外侧薄膜；
除去的方式可以为撕下，或揭下，这个动作要轻一些，防止花纸带动油漆从玻璃瓶脱落。该步骤在其他实施例中可以不进行。
步骤111，将除去薄膜的玻璃瓶放入160-180℃下第二烘烤，得到喷漆并烤花的玻璃瓶。
将除去薄膜的玻璃瓶放入160-180℃下第二烘烤利用高温提高花纸和油漆的粘贴力，将花纸、油漆进行进一步的位置固定，第二烘烤的时间20-40分钟。
以上所述仅为本发明的优选实施例而已，并不用于限制本发明，对于本领域的技术人员来说，本发明可以有各种更改和变化。凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。

Claims (10)

1.一种玻璃瓶喷色烤花方法，其特征在于，包括：
用含有2%氢氟酸的水清洗玻璃瓶，将玻璃瓶的外表面进行处理；
向所述玻璃瓶的外表面喷涂油漆；
将喷涂油漆后的所述玻璃瓶在150-190℃烤炉中进行第一烘烤；
退温至70-80℃；
将待粘贴的花纸在温水中浸泡；
在室温下，将浸泡后的所述花纸粘贴在退温后的所述玻璃瓶的外表面上，自然晾干；
将所述玻璃瓶放入160-180℃烤炉进行第二烘烤，得到喷漆并烤花的玻璃瓶。
2.根据权利要求1所述的玻璃瓶喷色烤花方法，其特征在于，
所述用含有2%氢氟酸的水清洗玻璃瓶将玻璃瓶的外表面进行处理包括：
用含有2%质量比的氢氟酸的水清洗所述玻璃瓶；
用清水冲洗去除所述玻璃瓶的外表面残留的所述氢氟酸；
在50-80℃的水中将冲洗后的所述玻璃瓶进行烫洗。
3.根据权利要求2所述的玻璃瓶喷色烤花方法，其特征在于，
在所述用含有2%氢氟酸的水清洗玻璃瓶之前，所述用含有2%氢氟酸的水清洗玻璃瓶将玻璃瓶的外表面进行处理还包括：去除所述玻璃瓶的外表面的污渍。
4.根据权利要求2所述的玻璃瓶喷色烤花方法，其特征在于，
在所述用含有2%质量比的氢氟酸的水清洗所述玻璃瓶中，所述清洗的时间为5-10分钟。
5.根据权利要求1-4任一项所述的玻璃瓶喷色烤花方法，其特征在于，
在所述将喷涂油漆后的所述玻璃瓶在150-190℃烤炉中进行第一烘烤中，所述第一烘烤的时间为20-40分钟。
6.根据权利要求1-4任一项所述的玻璃瓶喷色烤花方法，其特征在于，
在将待粘贴的花纸在温水中浸泡中，温水的温度为30-40℃；
所述室温为20-35℃。
7.根据权利要求1-4任一项所述的玻璃瓶喷色烤花方法，其特征在于，
在所述自然晾干之后，在所述玻璃瓶放入160-180℃烤炉进行第二烘烤之前，所述玻璃瓶喷色烤花方法还包括：晾干后除去所述花纸的外侧薄膜。
8.根据权利要求7所述的玻璃瓶喷色烤花方法，其特征在于，
所述自然晾干的时间为7-15小时。
9.根据权利要求7所述的玻璃瓶喷色烤花方法，其特征在于，
所述将浸泡后的所述花纸粘贴在退温后的所述玻璃瓶的外表面上包括：在无气泡的情况下进行所述粘贴。
10.根据权利要求1所述的玻璃瓶喷色烤花方法，其特征在于，
在所述将所述玻璃瓶放入160-180℃烤炉进行第二烘烤中，所述第二烘烤的时间为20-40分钟。
CN2013102782367A 2013-07-03 2013-07-03 玻璃瓶喷色烤花方法 Pending CN103342475A (zh)