CN1328949A - 带装饰的酒瓶及制作工艺 - Google Patents

带装饰的酒瓶及制作工艺 Download PDF

Info

Publication number
CN1328949A
CN1328949A CN 01111422 CN01111422A CN1328949A CN 1328949 A CN1328949 A CN 1328949A CN 01111422 CN01111422 CN 01111422 CN 01111422 A CN01111422 A CN 01111422A CN 1328949 A CN1328949 A CN 1328949A
Authority
CN
China
Prior art keywords
bottle
temperature
heating furnace
decoration
wine bottle
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 01111422
Other languages
English (en)
Other versions
CN1184117C (zh
Inventor
杨肇基
黄建勇
陈小林
鲍雨
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Sichuan Quanxing Co., Ltd.
Original Assignee
CHENGDU QUANXING DISTILLERY SICHUAN PROV
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Family has litigation
First worldwide family litigation filed litigation Critical https://patents.darts-ip.com/?family=25739390&utm_source=google_patent&utm_medium=platform_link&utm_campaign=public_patent_search&patent=CN1328949(A) "Global patent litigation dataset” by Darts-ip is licensed under a Creative Commons Attribution 4.0 International License.
Application filed by CHENGDU QUANXING DISTILLERY SICHUAN PROV filed Critical CHENGDU QUANXING DISTILLERY SICHUAN PROV
Priority to CNB011114223A priority Critical patent/CN1184117C/zh
Publication of CN1328949A publication Critical patent/CN1328949A/zh
Application granted granted Critical
Publication of CN1184117C publication Critical patent/CN1184117C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

本发明公开了一种带装饰的酒瓶及制作工艺。酒瓶包括透明玻璃酒瓶本体,且酒瓶本体有瓶底向上凸立的槽座,槽座形成的凹孔的周边壁上有饰片。饰片采用烤花、印制或绘制在凹孔的周边壁上。制作工艺是将贴花纸贴在酒瓶上,加热温度为300℃－650℃,至色釉完全牢固地熔接在玻璃表面,也可以加热温度为60℃－300℃,将贴花纸表面的色釉烤结在玻璃表面。本发明的带装饰的酒瓶,可以通过饰片的变化表现各种的图案,产生美观的效果。并且结构简单,成本低。

Description

带装饰的酒瓶及制作工艺
本发明涉及一种带装饰的酒瓶及制作工艺。
目前，常见的酒瓶只是作为一种容器，其外观单一，不能给人们提供更多的美感。专利号为97200675.3的“一种玻璃酒瓶”公开了一种由透明玻璃酒瓶本体、造型饰物及底座构成，并将造型饰物放置在酒瓶本体其瓶底向上凹立的圆柱形管槽座内。这种玻璃酒瓶虽然能通过不同造型饰物提供各种带装饰的酒瓶产生美感，但不能将图案与瓶体结合在一起，且结构较为复杂，配件较多，成本增加。
本发明的目的是为了避免上述酒瓶的缺点而提供一种既能在提供美感，图案与瓶体结合在一起，又不增加多余配件的带装饰的酒瓶。本发明的目的是通过如下结构来实现的，它包括透明玻璃酒瓶本体，且酒瓶本体有瓶底向上凸立的槽座，在所述槽座形成的凹孔的周边壁或顶部上有饰片。
饰片采用烤花、印制或绘制在凹孔的周边壁上。
本发明的目的是这样达到的：将贴花纸贴在酒瓶上，送入加热炉加热，温度为300℃—650℃，加热至贴花纸表面贴花色釉熔化，同时玻璃表面开始软化，色釉完全牢固地熔接在玻璃表面为止。
上述方法加热炉的最佳温度是450℃—600℃。
本发明的目的还可以这样达到：将贴花纸贴在酒瓶上，送入加热炉加热，温度为60℃—300℃，加热至贴花纸表面贴花色釉烤结在玻璃表面为止。
上述方法加热炉的最佳温度是80℃—120℃。
以上两种带装饰的酒瓶的制作工艺，加热炉的加热温度方式是驼峰温度曲线方式，温度段分为预热、烤制、冷却。
加热炉的烤制段温度大于300℃时，温度差控制为正负20℃以内，加热炉的烤制段温度小于300℃时，温度差控制为正负10℃以内。
本发明的带装饰的酒瓶，可以通过饰片的变化表现各种的图案，产生美观的效果。并且结构简单，成本低，能为企业增加经济效益。
下面结合附图对本发明的带装饰的酒瓶作进一步详细描述。
图1是本发明带装饰的酒瓶正剖视图。
图2是图1的A-A剖视图。
图3是加热炉的驼峰温度曲线。
在图1所示中，透明玻璃酒瓶本体1的瓶底有向上凸立的槽座2。槽座2向上凸起，在其凸起部位的下部形成的凹孔4的周边壁上或其顶部，通过烤花、印制或绘制的方法将饰片3制作在将饰片3凹孔4的周边壁上或其顶部，当酒瓶在使用时，可以透过透明玻璃酒瓶看见饰片(3)上的图案。
槽座2可以是任何形状，如圆柱形、多边形等。
烤花工艺实施例一：
将贴花纸贴在酒瓶槽座2周边壁上，要求平整无气泡及残缺。加热加热炉，采用图3所示驼峰温度曲线方式设定各区间温度，整个烤花工艺分为三个阶段，即预热、烤制、冷却。将贴好贴花纸的酒瓶送入加热炉中预热至480℃时，预热过程是慢慢升温，使酒瓶不至在骤然加热时破碎。当温度达到480℃时，控制加热炉的温度进行烤花，此时，加热炉的温度差不超过正负20℃，当贴花纸表面贴花色釉熔化，同时玻璃表面开始软化，色釉完全牢固地熔接在玻璃表面时，烤制阶段完成。随后进入冷却阶段，在此阶段逐步降低温度，以防止产生和消除其残余应力，减少破碎，此阶段的时间约占整个烤花工艺的一半。
烤花工艺实施例二：
将贴花纸贴在酒瓶槽座2的周边壁上，要求平整无气泡及残缺。加热加热炉，采用图3所示驼峰温度曲线方式设定各区间温度，将贴好贴花纸的酒瓶送入加热炉中预热至590℃时，预热过程是慢慢升温，使酒瓶不至在骤然加热时破碎。当温度达到590℃时，控制加热炉的温度进行烤花，此时，加热炉的温度差不超过正负15℃，当贴花纸表面贴花色釉熔化，同时玻璃表面开始软化，色釉完全牢固地熔接在玻璃表面时，烤制阶段完成。随后进入冷却阶段，在此阶段逐步降低温度，以防止产生和消除其残余应力，减少破碎，此阶段的时间约占整个烤花工艺的一半。
烤花工艺实施例三：
将贴花纸贴在酒瓶槽座2周边壁上，要求平整无气泡及残缺。加热加热炉中，采用图3所示驼峰温度曲线方式设定各区间温度，整个烤花工艺分为三个阶段，即预热、烤制、冷却。将贴好贴花纸的酒瓶送入加热炉中预热至70℃时。当温度达到70℃时，控制加热炉的温度进行烤花，此时，加热炉的温度差不超过正负10℃，当贴花纸上的色釉烤结在玻璃表面时，烤制阶段完成。随后进入冷却阶段，在此阶段逐步降低温度，时间约占整个烤花工艺的一半。
烤花工艺实施例四：
将贴花纸贴在酒瓶槽座2的周边壁上，要求平整无气泡及残缺。加热加热炉，采用图3所示驼峰温度曲线方式设定各区间温度，将贴好贴花纸的酒瓶送入加热炉中预热至130℃时，预热过程是慢慢升温，当温度达到130℃时，控制加热炉的温度进行烤花，此时，加热炉的温度差不超过正负10℃，当贴花纸上的色釉烤结在玻璃表面时，烤制阶段完成。随后进入冷却阶段，在此阶段逐步降低温度，此阶段的时间约占整个烤花工艺的一半。
经以上实施例生产出的酒瓶，各种色釉应牢固地熔融在玻璃的表面，图案平滑，色彩鲜艳，表面富有光泽。图案完整无残缺，应力完全消除。

Claims (8)

1、一种带装饰的酒瓶，它包括透明玻璃酒瓶本体，且酒瓶本体有瓶底向上凸立的槽座，其特征在于：在所述槽座(2)形成的凹孔(4)的周边壁或顶部上有饰片(3)。
2、根据权利要求1所述的带装饰的酒瓶，其特征在于：饰片(3)采用烤花、印制或绘制在凹孔(4)的周边壁或顶部上。
3、一种带装饰的酒瓶的制作工艺，其特征在于：将贴花纸贴在酒瓶上，送入加热炉加热，温度为300℃—650℃，加热至贴花纸表面贴花色釉熔化，同时玻璃表面开始软化，色釉完全牢固地熔接在玻璃表面为止。
4、根据权利要求3所述的带装饰的酒瓶的制作工艺，其特征在于：加热炉的最佳温度是450℃—600℃。
5、一种带装饰的酒瓶的制作工艺，其特征在于：将贴花纸贴在酒瓶上，送入加热炉加热，温度为60℃—300℃，加热至贴花纸表面贴花色釉烤结在玻璃表面为止。
6、根据权利要求5所述的带装饰的酒瓶的制作工艺，其特征在于：加热炉的最佳温度是80℃—120℃。
7、根据权利要求3和权利要求5所述的带装饰的酒瓶的制作工艺，其特征在于：加热炉的加热温度方式是驼峰温度曲线方式，温度段分为预热、烤制、冷却。
8、根据权利要求7所述的带装饰的酒瓶的制作工艺，其特征在于：加热炉的烤制段温度大于300℃时，温度差控制为正负20℃以内，加热炉的烤制段温度小于300℃时，温度差控制为正负10℃以内。
CNB011114223A 2000-06-15 2001-02-28 带装饰的酒瓶及制作工艺 Expired - Fee Related CN1184117C (zh)