CN103333438A - 一种含有三氟氯乙烯共聚物的抗冲击耐拉伸塑料 - Google Patents
一种含有三氟氯乙烯共聚物的抗冲击耐拉伸塑料 Download PDFInfo
- Publication number
- CN103333438A CN103333438A CN2013102763686A CN201310276368A CN103333438A CN 103333438 A CN103333438 A CN 103333438A CN 2013102763686 A CN2013102763686 A CN 2013102763686A CN 201310276368 A CN201310276368 A CN 201310276368A CN 103333438 A CN103333438 A CN 103333438A
- Authority
- CN
- China
- Prior art keywords
- parts
- stretch
- proof
- shock resistance
- plastics
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及一种含有三氟氯乙烯共聚物的抗冲击耐拉伸塑料，由以下成分按照重量比组成：三氟氯乙烯共聚物60～70份、聚间苯二甲酰间苯二胺纤维10～20份、聚亚乙基碳酸酯50～60份、1，2-聚丁二烯树脂30～40份、糠醇树脂20～30份、陶土10～20份。制成的含有三氟氯乙烯共聚物的塑料具有良好的抗冲击耐拉伸效果。
Description
技术领域
本发明涉及一种抗冲击耐拉伸塑料，特别是涉及一种含有三氟氯乙烯共聚物的抗冲击耐拉伸塑料。
背景技术
目前学者对塑料的研究也是越来越深入，研究的热点在塑料的很多性能上，如耐候性、抗老化、抗冲击、耐拉伸等。其中他们对抗冲击和耐拉伸性能研究较少，许多塑料抗冲击和耐拉伸性能也非常差，如抗冲击性能只有100J/M左右，大大限制了他们在产业上的广泛推广和应用，因此开发一种同时具有良好抗冲击耐拉伸的塑料可以扩大塑料的应用范围，具有非常庞大的市场空间。
发明内容
要解决的技术问题：常规塑料抗冲击和耐拉伸效果较差的问题。
技术方案：本发明为一种含有三氟氯乙烯共聚物的抗冲击耐拉伸塑料，由以下成分按照重量比组成：三氟氯乙烯共聚物60～70份、聚间苯二甲酰间苯二胺纤维10～20份、聚亚乙基碳酸酯50～60份、1，2-聚丁二烯树脂30～40份、糠醇树脂20～30份、陶土10～20份。在80℃下，将各种成分投入反应容器调配，搅拌均匀，加热至150℃保持8h，冷却后即可获得具有良好抗冲击耐拉伸效果的塑料。
有益效果：制备好含有三氟氯乙烯共聚物的抗冲击耐拉伸塑料后，对其抗冲击性和拉伸性能进行了实验。本发明制成的含有三氟氯乙烯共聚物的抗冲击耐拉伸塑料，抗冲击性为270～280J/M，具有良好的抗冲击性。含有三氟氯乙烯共聚物的抗冲击耐拉伸塑料拉伸性能为80～90Mpa，具有良好的耐拉伸特性。
具体实施方式
本发明塑料产品制备方法及性能测试方法如下：首先将反应罐温度调制80℃，将各种成分依次投入反应罐中，并不停搅拌，待彻底搅拌均匀后加热至150℃保持8h，冷却后获得含有三氟氯乙烯共聚物的抗冲击耐拉伸塑料。抗冲击性测试采用方法为ASTMD256标准，耐拉伸测试采用方法为GB/T1040-2006标准。
实施例1、实施例2、实施例3配方如下：
实施例1：三氟氯乙烯共聚物60kg、聚间苯二甲酰间苯二胺纤维10kg、聚亚乙基碳酸酯50kg、1，2-聚丁二烯树脂30kg、糠醇树脂20kg、陶土10kg。
实施例2：三氟氯乙烯共聚物70kg、聚间苯二甲酰间苯二胺纤维20kg、聚亚乙基碳酸酯60kg、1，2-聚丁二烯树脂40kg、糠醇树脂30kg、陶土20kg。
实施例3：三氟氯乙烯共聚物65kg、聚间苯二甲酰间苯二胺纤维15kg、聚亚乙基碳酸酯55kg、1，2-聚丁二烯树脂35kg、糠醇树脂25kg、陶土15kg。
实施例1产品的抗冲击性能为270J/M，耐拉伸性能为85Mpa。
实施例2产品的抗冲击性能为280J/M，耐拉伸性能为80Mpa。
实施例3产品的抗冲击性能为275J/M，耐拉伸性能为90Mpa。
含有三氟氯乙烯共聚物的抗冲击耐拉伸塑料都具有良好的抗冲击和耐拉伸特性。
Claims (6)
1.一种含有三氟氯乙烯共聚物的抗冲击耐拉伸塑料，其特征在于：由以下成分按照重量比组成：三氟氯乙烯共聚物60～70份、聚间苯二甲酰间苯二胺纤维10～20份、聚亚乙基碳酸酯50～60份、1，2-聚丁二烯树脂30～40份、糠醇树脂20～30份、陶土10～20份。
2.根据权利要求1所述的一种含有三氟氯乙烯共聚物的抗冲击耐拉伸塑料，其特征在于：塑料组成中三氟氯乙烯共聚物为60份。
3.根据权利要求1所述的一种含有三氟氯乙烯共聚物的抗冲击耐拉伸塑料，其特征在于：塑料组成中聚间苯二甲酰间苯二胺纤维为10份。
4.根据权利要求1所述的一种含有三氟氯乙烯共聚物的抗冲击耐拉伸塑胶，其特征在于：塑料组成中聚亚乙基碳酸酯为50份。
5.根据权利要求1所述的一种含有三氟氯乙烯共聚物的抗冲击耐拉伸塑胶，其特征在于：塑料组成中1，2-聚丁二烯树脂为30份。
6.根据权利要求1所述的一种含有三氟氯乙烯共聚物的抗冲击耐拉伸塑胶，其特征在于：塑料组成中糠醇树脂为20份。