CN103332951A - 防腐性好的加气混凝土砌块及其制备方法 - Google Patents

防腐性好的加气混凝土砌块及其制备方法 Download PDF

Info

Publication number
CN103332951A
CN103332951A CN2013102089994A CN201310208999A CN103332951A CN 103332951 A CN103332951 A CN 103332951A CN 2013102089994 A CN2013102089994 A CN 2013102089994A CN 201310208999 A CN201310208999 A CN 201310208999A CN 103332951 A CN103332951 A CN 103332951A
Authority
CN
China
Prior art keywords
parts
minute
building block
add
stirred
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2013102089994A
Other languages
English (en)
Other versions
CN103332951B (zh
Inventor
梅林�
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JIANGSU GOLDEN CUBE ENVIRONMENTAL TECHNOLOGY CO., LTD.
Original Assignee
TONGLING FENGZE BUILDING MATERIALS TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by TONGLING FENGZE BUILDING MATERIALS TECHNOLOGY Co Ltd filed Critical TONGLING FENGZE BUILDING MATERIALS TECHNOLOGY Co Ltd
Priority to CN201310208999.4A priority Critical patent/CN103332951B/zh
Publication of CN103332951A publication Critical patent/CN103332951A/zh
Application granted granted Critical
Publication of CN103332951B publication Critical patent/CN103332951B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

防腐性好的加气混凝土砌块及其制备方法。一种防腐性好的加气混凝土砌块，其特征在于由下列重量份的原料制成：水泥18-22、生石灰16-18、石膏8-15、铝粉0.3-0.4、丙二醇8-12、石英砂40-50、砖渣10-14、乌洛托品3-4、苯甲酸钠2-3、过硫酸钠3-5、油脚3-5、环氧大豆油3-5、碳酸氢钠5-7、米糠15-20。本发明中采用乌洛托品，苯甲酸钠等原料，具有较好的抗腐蚀作用，使得砌块在酸、大碱性环境中，延长使用寿命。

Description

防腐性好的加气混凝土砌块及其制备方法
技术领域
本发明属于一种建材技术，具体是一种混凝土砌块及其制备方法。
背景技术
新型墙体材料加气混凝土作为一种低能耗的、环保型的新型建筑材料，属于国家推广的建筑材料，但是由于普通加气混凝土由水泥、粉煤灰、生石灰、石膏等制成，存在干燥收缩值大、强度低、渗水、不耐腐蚀、隔热性不佳、材料来源单一等问题，因此，急需对于加气混凝土砌块技术进行进一步研究，使得更进一步满足市场的要求。
发明内容
本发明的目的是提供防腐性好的加气混凝土砌块及其制备方法，以解决目前加气混凝土砌块存在的不耐腐蚀的问题。
本发明技术方案如下：
一种防腐性好的加气混凝土砌块，其特征在于由下列重量份的原料制成：水泥18-22、生石灰16-18、石膏8-15、铝粉0.3-0.4、丙二醇8-12、石英砂40-50、砖渣10-14、乌洛托品3-4、苯甲酸钠2-3、过硫酸钠3-5、油脚3-5、环氧大豆油3-5、碳酸氢钠5-7、米糠15-20。
所述的防腐性好的加气混凝土砌块的制备方法，其特征在于包括以下步骤：
（1）、将米糠加适量水，加热至90-100℃，搅拌5-10分钟，加入油脚、丙二醇、石英砂，搅拌35-45分钟，然后加入过硫酸钠，搅拌10-15分钟后，加入环氧大豆油、碳酸氢钠搅拌20-30分钟，再加入石膏搅拌20-30分钟，搅拌成泥；
（2）、将水泥加入50-60℃热水混合5-15分钟，然后，加入步骤（1）所得的泥及生石灰、铝粉、乌洛托品、苯甲酸钠等其它物料，搅拌10-15分钟，得到含水量为30-35%的浆料；
（3）、将浆料浇注，送入40-60℃烘房中预养1.5-2.5 小时后，切割成砌块坯、在砌块坯的外壁上涂上一层二甲基硅油；
（4）、将砌块送入釜内蒸压养护。
本发明生产出来的加气混凝土砌块，其中采用油脚成分，经过引发剂改性，增加了砌块的疏水性，大大提高其渗水能力，本发明砌块在小区外墙体使用，历时3年多，没有发现墙体渗水现象，而采用传统的加气混凝土砌块，每年春季均有住户出现渗水。本发明中采用乌洛托品，苯甲酸钠等原料，具有较好的抗腐蚀作用，使得砌块在酸、大碱性环境中，延长使用寿命。
本发明生产的加气混凝土砌块具有抗压强度高、质轻、隔音、隔热、保温性好、抗冻性能及其收缩小等优点，解决了传统加气混凝土砌块强度低、易开裂的缺陷。
具体实施方式
一种防腐性好的加气混凝土砌块，其特征在于由下列重量份（公斤）的原料制成：水泥18、生石灰18、石膏8、铝粉0.3、丙二醇8、石英砂50、砖渣14、乌洛托品3、苯甲酸钠3、过硫酸钠5、油脚3、环氧大豆油5、碳酸氢钠5、米糠15。
所述的防腐性好的加气混凝土砌块的制备方法，其特征在于包括以下步骤：
（1）、将米糠加适量水，加热至90-100℃，搅拌5-10分钟，加入油脚、丙二醇、石英砂，搅拌35-45分钟，然后加入过硫酸钠，搅拌10-15分钟后，加入环氧大豆油、碳酸氢钠搅拌20-30分钟，再加入石膏搅拌20-30分钟，搅拌成泥；
（2）、将水泥加入50-60℃热水混合5-15分钟，然后，加入步骤（1）所得的泥及生石灰、铝粉、乌洛托品、苯甲酸钠等其它物料，搅拌10-15分钟，得到含水量为30-35%的浆料；
（3）、将浆料浇注，送入40-60℃烘房中预养1.5-2.5 小时后，切割成砌块坯、在砌块坯的外壁上涂上一层二甲基硅油；
（4）、将砌块送入釜内蒸压养护。
将本发明生产的空心砖切割成100mm×100mm×100mm的立方体进行性能检测，检测结果如下：抗压强度4.48Mpa，收缩值0.43mm/m，抗冻性强度损失16%。将砌块放在5%盐水中浸泡30天，强度为初始强度的91%。

Claims (2)

1.一种防腐性好的加气混凝土砌块，其特征在于由下列重量份的原料制成：水泥18-22、生石灰16-18、石膏8-15、铝粉0.3-0.4、丙二醇8-12、石英砂40-50、砖渣10-14、乌洛托品3-4、苯甲酸钠2-3、过硫酸钠3-5、油脚3-5、环氧大豆油3-5、碳酸氢钠5-7、米糠15-20。
2.根据权利要求1所述的防腐性好的加气混凝土砌块的制备方法，其特征在于包括以下步骤：
（1）、将米糠加适量水，加热至90-100℃，搅拌5-10分钟，加入油脚、丙二醇、石英砂，搅拌35-45分钟，然后加入过硫酸钠，搅拌10-15分钟后，加入环氧大豆油、碳酸氢钠搅拌20-30分钟，再加入石膏搅拌20-30分钟，搅拌成泥；
（2）、将水泥加入50-60℃热水混合5-15分钟，然后，加入步骤（1）所得的泥及生石灰、铝粉、乌洛托品、苯甲酸钠等其它物料，搅拌10-15分钟，得到含水量为30-35%的浆料；
（3）、将浆料浇注，送入40-60℃烘房中预养1.5-2.5 小时后，切割成砌块坯、在砌块坯的外壁上涂上一层二甲基硅油；
（4）、将砌块送入釜内蒸压养护。
CN201310208999.4A 2013-05-30 2013-05-30 防腐性好的加气混凝土砌块及其制备方法 Active CN103332951B (zh)