CN103332950B - 低导热加气混凝土砌块及其制备方法 - Google Patents

低导热加气混凝土砌块及其制备方法 Download PDF

Info

Publication number
CN103332950B
CN103332950B CN201310208983.3A CN201310208983A CN103332950B CN 103332950 B CN103332950 B CN 103332950B CN 201310208983 A CN201310208983 A CN 201310208983A CN 103332950 B CN103332950 B CN 103332950B
Authority
CN
China
Prior art keywords
parts
minute
building block
aerated concrete
stir
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201310208983.3A
Other languages
English (en)
Other versions
CN103332950A (zh
Inventor
梅林�
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JIANGSU GOLDEN CUBE ENVIRONMENTAL TECHNOLOGY CO., LTD.
Original Assignee
TONGLING FENGZE BUILDING MATERIALS TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by TONGLING FENGZE BUILDING MATERIALS TECHNOLOGY Co Ltd filed Critical TONGLING FENGZE BUILDING MATERIALS TECHNOLOGY Co Ltd
Priority to CN201310208983.3A priority Critical patent/CN103332950B/zh
Publication of CN103332950A publication Critical patent/CN103332950A/zh
Application granted granted Critical
Publication of CN103332950B publication Critical patent/CN103332950B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

低导热加气混凝土砌块及其制备方法。低导热加气混凝土砌块，其特征在于由下列重量份的原料制成：水泥18-22、生石灰15-18、石膏10-15、铝粉0.25-0.4、粉煤灰20-30、漂珠15-20、废砖碎块20-25、发泡聚丙烯粒子10-15、过硫酸铵3-5、油脚6-8、氯化石蜡3-5、丙二醇5-8、丙烯酸-2- 羟基丙酯3-5、硼砂4-6。本发明中采用泡末粒子，具有质轻，隔热性的特点，在夏季情况下，采用本发明砌块的墙体的房间，室内温度比传统的加气混凝土墙体的房间低4-5度，隔热性明显提高。

Description

低导热加气混凝土砌块及其制备方法
技术领域
本发明属于一种建材技术，具体是一种混凝土砌块及其制备方法。
背景技术
新型墙体材料加气混凝土作为一种低能耗的、环保型的新型建筑材料，属于国家推广的建筑材料，但是由于普通加气混凝土由水泥、粉煤灰、生石灰、石膏等制成，存在干燥收缩值大、强度低、渗水、不耐腐蚀、隔热性不佳、材料来源单一等问题，因此，急需对于加气混凝土砌块技术进行进一步研究，使得更进一步满足市场的要求。
发明内容
本发明的目的是提供低导热加气混凝土砌块及其制备方法，以解决目前加气混凝土砌块存在的隔热性不好的问题。
本发明技术方案如下：
一种低导热加气混凝土砌块，其特征在于由下列重量份的原料制成：水泥18-22、生石灰15-18、石膏10-15、铝粉0.25-0.4、粉煤灰20-30、漂珠15-20、废砖碎块20-25、发泡聚丙烯粒子10-15、过硫酸铵3-5、油脚6-8、氯化石蜡3-5、丙二醇5-8、丙烯酸-2- 羟基丙酯3-5、硼砂4-6。
所述的低导热加气混凝土砌块的制备方法，其特征在于包括以下步骤：
（1）、将粉煤灰、漂珠加适量水，加热至80-90℃，搅拌5-10分钟，加入油脚、丙二醇，搅拌15-25分钟，然后加入过硫酸铵，搅拌30-45分钟后，加入硼砂、丙烯酸-2- 羟基丙酯、石膏搅拌30-40分钟，搅拌成泥；
（2）、将水泥加入90-100℃热水混合5-15分钟，然后，加入步骤（1）所得的泥及生石灰、铝粉、废砖碎块、氯化石蜡、发泡聚丙烯粒子等其它物料，搅拌10-15分钟，得到含水量为30-35%的浆料；
（3）、将浆料浇注，送入40-60℃烘房中预养1.5-2.5 小时后，切割成砌块坯、在砌块坯的外壁上涂上一层二甲基硅油；；
（4）、将砌块送入釜内蒸压养护，蒸汽压力1-1.3Mpa，恒压蒸养时间8-10.0h 得成品。
本发明生产出来的加气混凝土砌块，其中采用油脚成分，经过引发剂改性，增加了砌块的疏水性，大大提高其渗水能力，本发明砌块在小区外墙体使用，历时3年多，没有发现墙体渗水现象，而采用传统的加气混凝土砌块，每年春季均有住户出现渗水。本发明中采用泡末粒子，具有质轻，隔热性的特点，在夏季情况下，采用本发明砌块的墙体的房间，室内温度比传统的加气混凝土墙体的房间低4-5度，隔热性明显提高。
本发明生产的加气混凝土砌块具有抗压强度高、质轻、隔音、隔热、保温性好、抗冻性能及其收缩小等优点，解决了传统加气混凝土砌块强度低、易开裂的缺陷。
具体实施方式
一种低导热加气混凝土砌块，由下列重量份(公斤)的原料制成：水泥18、生石灰18、石膏15、铝粉0.25、粉煤灰20、漂珠20、废砖碎块20、发泡聚丙烯粒子10、过硫酸铵5、油脚6、氯化石蜡5、丙二醇5、丙烯酸-2- 羟基丙酯3、硼砂6。
低导热加气混凝土砌块的制备方法，其特征在于包括以下步骤：
（1）、将粉煤灰、漂珠加适量水，加热至80-90℃，搅拌5-10分钟，加入油脚、丙二醇，搅拌15-25分钟，然后加入过硫酸铵，搅拌30-45分钟后，加入硼砂、丙烯酸-2- 羟基丙酯、石膏搅拌30-40分钟，搅拌成泥；
（2）、将水泥加入90-100℃热水混合5-15分钟，然后，加入步骤（1）所得的泥及生石灰、铝粉、废砖碎块、氯化石蜡、发泡聚丙烯粒子等其它物料，搅拌10-15分钟，得到含水量为30-35%的浆料；
（3）、将浆料浇注，送入40-60℃烘房中预养1.5-2.5 小时后，切割成砌块坯、在砌块坯的外壁上涂上一层二甲基硅油；；
（4）、将砌块送入釜内蒸压养护，蒸汽压力1-1.3Mpa，恒压蒸养时间8-10.0h 得成品。
将本发明生产的空心砖切割成100mm×100mm×100mm的立方体进行性能检测，检测结果如下：抗压强度5.18Mpa，收缩值0.67mm/m，抗冻性强度损失21%。

Claims (1)

1.一种低导热加气混凝土砌块，其特征在于由下列重量份的原料制成：水泥18-22、生石灰15-18、石膏10-15、铝粉0.25-0.4、粉煤灰20-30、漂珠15-20、废砖碎块20-25、发泡聚丙烯粒子10-15、过硫酸铵3-5、油脚6-8、氯化石蜡3-5、丙二醇5-8、丙烯酸-2- 羟基丙酯3-5、硼砂4-6；
所述的低导热加气混凝土砌块的制备方法，包括以下步骤：
（1）、将粉煤灰、漂珠加适量水，加热至80-90℃，搅拌5-10分钟，加入油脚、丙二醇，搅拌15-25分钟，然后加入过硫酸铵，搅拌30-45分钟后，加入硼砂、丙烯酸-2- 羟基丙酯、石膏搅拌30-40分钟，搅拌成泥；
（2）、将水泥加入90-100℃热水混合5-15分钟，然后，加入步骤（1）所得的泥及生石灰、铝粉、废砖碎块、氯化石蜡、发泡聚丙烯粒子等其它物料，搅拌10-15分钟，得到含水量为30-35%的浆料；
（3）、将浆料浇注，送入40-60℃烘房中预养1.5-2.5 小时后，切割成砌块坯、在砌块坯的外壁上涂上一层二甲基硅油；；
（4）、将砌块送入釜内蒸压养护，蒸汽压力1-1.3MPa，恒压蒸养时间8-10.0h 得成品。
CN201310208983.3A 2013-05-30 2013-05-30 低导热加气混凝土砌块及其制备方法 Active CN103332950B (zh)