CN103332914B - 硅藻土改性的加气混凝土砌块及其制备方法 - Google Patents

硅藻土改性的加气混凝土砌块及其制备方法 Download PDF

Info

Publication number
CN103332914B
CN103332914B CN201310208958.5A CN201310208958A CN103332914B CN 103332914 B CN103332914 B CN 103332914B CN 201310208958 A CN201310208958 A CN 201310208958A CN 103332914 B CN103332914 B CN 103332914B
Authority
CN
China
Prior art keywords
building block
stir
minute
add
diatomite
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201310208958.5A
Other languages
English (en)
Other versions
CN103332914A (zh
Inventor
梅树田
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
TONGLING FENGZE BUILDING MATERIALS TECHNOLOGY Co Ltd
Original Assignee
TONGLING FENGZE BUILDING MATERIALS TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by TONGLING FENGZE BUILDING MATERIALS TECHNOLOGY Co Ltd filed Critical TONGLING FENGZE BUILDING MATERIALS TECHNOLOGY Co Ltd
Priority to CN201310208958.5A priority Critical patent/CN103332914B/zh
Publication of CN103332914A publication Critical patent/CN103332914A/zh
Application granted granted Critical
Publication of CN103332914B publication Critical patent/CN103332914B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

硅藻土改性的加气混凝土砌块及其制备方法。硅藻土改性的加气混凝土砌块,其特征在于由下列重量份的原料制成:水泥25-30、生石灰18-22、石膏12-15、粉煤灰50-55、铝粉0.2-0.25、异噻唑啉酮1-2、氯化石蜡3-5、明胶2-3、硅藻土20-25、甲基葡萄糖苷聚氧乙烯醚2-3、过硫酸钠3-4、油脚4-6、羧甲基纤维素钠10-12。本发明中采用硅藻土改性,能增加各原料之间的粘结力,提高砌块的强度,同时,砌块有一定的吸附有毒元素的能力。

Description

硅藻土改性的加气混凝土砌块及其制备方法
技术领域
本发明属于一种建材技术,具体是一种混凝土砌块及其制备方法。
背景技术
新型墙体材料加气混凝土作为一种低能耗的、环保型的新型建筑材料,属于国家推广的建筑材料,但是由于普通加气混凝土由水泥、粉煤灰、生石灰、石膏等制成,存在干燥收缩值大、强度低、渗水、不耐腐蚀、隔热性不佳、材料来源单一等问题,因此,急需对于加气混凝土砌块技术进行进一步研究,使得更进一步满足市场的要求。
发明内容
本发明的目的是提供硅藻土改性的加气混凝土砌块及其制备方法,能提高砌块各原料之间的粘结力,提高砌块强度,同时,具有一定的吸附有毒物质的作用。
硅藻土改性的加气混凝土砌块,其特征在于由下列重量份的原料制成:水泥25-30、生石灰18-22、石膏12-15、粉煤灰50-55、铝粉0.2-0.25、异噻唑啉酮1-2、氯化石蜡3-5、明胶2-3、硅藻土20-25、甲基葡萄糖苷聚氧乙烯醚2-3、过硫酸钠3-4、油脚4-6、羧甲基纤维素钠10-12。
所述的硅藻土改性的加气混凝土砌块,其特征在于包括以下步骤:
(1)、将明胶、硅藻土加适量水,搅拌15-20分钟,加入油脚、异噻唑啉酮、甲基葡萄糖苷聚氧乙烯醚,搅拌15-25分钟,然后加入过硫酸钠,搅拌20-35分钟后,加入羧甲基纤维素钠搅拌20-30分钟,搅拌成泥;
(2)、将水泥、粉煤灰加入40-50℃热水混合20-35分钟,然后,加入步骤(1)所得的泥及铝粉、氯化石蜡等其它物料,搅拌10-15分钟,得到含水量为30-35%的浆料;
(3)、将浆料浇注,送入40-50℃烘房中预养1.5-2.5小时后,切割成砌块坯、在砌块坯的外壁上涂上一层二甲基硅油;
(4)、将砌块送入釜内蒸压养护。
本发明生产出来的加气混凝土砌块,其中采用油脚成分,经过引发剂改性,增加了砌块的疏水性,大大提高其渗水能力,本发明砌块在小区外墙体使用,历时3年多,没有发现墙体渗水现象,而采用传统的加气混凝土砌块,每年春季均有住户出现渗水。本发明中采用硅藻土改性,能增加各原料之间的粘结力,提高砌块的强度,同时,砌块有一定的吸附有毒元素的能力。
本发明生产的加气混凝土砌块具有抗压强度高、质轻、隔音、隔热、保温性好、抗冻性能及其收缩小等优点,解决了传统加气混凝土砌块强度低、易开裂的缺陷。
具体实施方式
硅藻土改性的加气混凝土砌块,其特征在于由下列重量份(公斤)的原料制成:水泥25、生石灰22、石膏12、粉煤灰50、铝粉0.25、异噻唑啉酮1、氯化石蜡3、明胶3、硅藻土20、甲基葡萄糖苷聚氧乙烯醚3、过硫酸钠4、油脚4、羧甲基纤维素钠10。
硅藻土改性的加气混凝土砌块,其特征在于包括以下步骤:
(1)、将明胶、硅藻土加适量水,搅拌15-20分钟,加入油脚、异噻唑啉酮、甲基葡萄糖苷聚氧乙烯醚,搅拌15-25分钟,然后加入过硫酸钠,搅拌20-35分钟后,加入羧甲基纤维素钠搅拌20-30分钟,搅拌成泥;
(2)、将水泥、粉煤灰加入40-50℃热水混合20-35分钟,然后,加入步骤(1)所得的泥及铝粉、氯化石蜡等其它物料,搅拌10-15分钟,得到含水量为30-35%的浆料;
(3)、将浆料浇注,送入40-50℃烘房中预养1.5-2.5小时后,切割成砌块坯、在砌块坯的外壁上涂上一层二甲基硅油;
(4)、将砌块送入釜内蒸压养护。
将本发明生产的空心砖切割成100mm×100mm×100mm的立方体进行性能检测,检测结果如下:抗压强度4.68Mpa,收缩值0.47mm/m,抗冻性强度损失20%。

Claims (2)

1.一种硅藻土改性的加气混凝土砌块,其特征在于由下列重量份的原料制成:水泥25-30、生石灰18-22、石膏12-15、粉煤灰50-55、铝粉0.2-0.25、异噻唑啉酮1-2、氯化石蜡3-5、明胶2-3、硅藻土20-25、甲基葡萄糖苷聚氧乙烯醚2-3、过硫酸钠3-4、油脚4-6、羧甲基纤维素钠10-12。
2.根据权利要求1所述的硅藻土改性的加气混凝土砌块,其特征在于包括以下步骤:
(1)、将明胶、硅藻土加适量水,搅拌15-20分钟,加入油脚、异噻唑啉酮、甲基葡萄糖苷聚氧乙烯醚,搅拌15-25分钟,然后加入过硫酸钠,搅拌20-35分钟后,加入羧甲基纤维素钠搅拌20-30分钟,搅拌成泥;
(2)、将水泥、粉煤灰加入40-50℃热水混合20-35分钟,然后,加入步骤(1)所得的泥及铝粉、氯化石蜡等其它物料,搅拌10-15分钟,得到含水量为30-35%的浆料;
(3)、将浆料浇注,送入40-50℃烘房中预养1.5-2.5小时后,切割成砌块坯、在砌块坯的外壁上涂上一层二甲基硅油;
(4)、将砌块送入釜内蒸压养护。
CN201310208958.5A 2013-05-30 2013-05-30 硅藻土改性的加气混凝土砌块及其制备方法 Active CN103332914B (zh)