CN102964080A - 一种混凝土用复合型发泡剂 - Google Patents

一种混凝土用复合型发泡剂 Download PDF

Info

Publication number
CN102964080A
CN102964080A CN2012104158848A CN201210415884A CN102964080A CN 102964080 A CN102964080 A CN 102964080A CN 2012104158848 A CN2012104158848 A CN 2012104158848A CN 201210415884 A CN201210415884 A CN 201210415884A CN 102964080 A CN102964080 A CN 102964080A
Authority
CN
China
Prior art keywords
parts
foaming agent
concrete
reinforcement
saponin
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2012104158848A
Other languages
English (en)
Other versions
CN102964080B (zh
Inventor
王本明
柯勇
艾勇
刘一宁
徐昌军
夏明明
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Aike Ployfoam & Plastic Products Co Ltd
Original Assignee
Anhui Aike Ployfoam & Plastic Products Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Aike Ployfoam & Plastic Products Co Ltd filed Critical Anhui Aike Ployfoam & Plastic Products Co Ltd
Priority to CN201210415884.8A priority Critical patent/CN102964080B/zh
Publication of CN102964080A publication Critical patent/CN102964080A/zh
Application granted granted Critical
Publication of CN102964080B publication Critical patent/CN102964080B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种混凝土用复合型发泡剂，由下列重量份的原料在常温下混合搅拌均匀而制成：皂素10-15份、十二烷基苯磺酸钠3-5份、十二烷基硫酸钠1-2份、聚乙二醇2-3份、明胶3-4份、改性硅藻土0.5-1份、甲基葡萄糖苷聚氧乙烯醚0.2-0.5份、聚丙烯酸树脂1-2份、水60-70份。本发明原料易得，成本较低，制备工艺简单，生产出来的发泡剂稳定性好，不易变质，发泡力好，可以减少发泡剂溶液的用量，且不影响泡沫混凝土的绝干密度以及抗压强度等指标，具有非常好的发展前途。

Description

一种混凝土用复合型发泡剂
技术领域
本发明涉及一种混凝土用复合型发泡剂，属于建筑材料领域。
背景技术
    随着国家对建筑节能材料要求的提高，泡沫混凝土受到越来越广泛的关注，泡沫混凝土是由水泥、石灰、粉煤灰、砂和外加剂等主要原料掺合均匀后浇注硬化而成的内部含有大量封闭气孔的“密孔”轻质建筑材料。发泡剂是生产泡沫混凝土的一个关键因素，它的性能直接决定着泡沫混凝土的质量。我国发泡剂应用比国外要晚得多从上世纪50年代我国开始生产应用发泡剂。常用的性价比较高的发泡剂是烷基磺酸盐系列如十二烷基苯磺酸钠，其在碱性建材中发泡力大但是泡 沫的稳定性差，消泡快，这就使得工业操作较为困难。
发明内容
本发明得目的是提供一种混凝土用复合型发泡剂，采用复合型发泡剂，即基础发泡剂加上一定量的助剂的方法来解决单一发泡剂性能不佳的现状。
本发明采用的技术方案如下：
    一种混凝土用复合型发泡剂，由下列重量份的原料在常温下混合搅拌均匀而制成：皂素10-15份、十二烷基苯磺酸钠3-5份、十二烷基硫酸钠1-2份、聚乙二醇2-3份、明胶3-4份、改性硅藻土0.5-1份、甲基葡萄糖苷聚氧乙烯醚0.2-0.5份、聚丙烯酸树脂1-2份、水60-70份。
优选地，混凝土用复合型发泡剂，由下列重量份的原料在常温下混合搅拌均匀而制成：皂素15份、十二烷基苯磺酸钠5份、十二烷基硫酸钠1.8份、聚乙二醇2.5份、明胶3份、改性硅藻土0.8份、甲基葡萄糖苷聚氧乙烯醚0.35份、聚丙烯酸树脂1.6份、水65份。
所述的改性硅藻土由以下方法制得：先用10-15%盐酸浸泡3-4小时，去离子水洗涤干净，再用10-15%氢氧化钠溶液浸泡3-4小时，再用去离子水洗涤至中性，烘干，再加入硅藻土重量2-3%的羧甲基纤维素钠、1-2%的三乙醇胺、1-2%的蔗糖，高速1200-1500转/分搅拌5-8min，得到分散液，最后将分散液烘干粉碎成超细粉末即可。
本发明的有益效果：
本发明配方中甲基葡萄糖苷聚氧乙烯醚是一种非离子表面活性剂，其本身具有良好的发泡力且稳泡效果较好，将甲基葡萄糖苷聚氧乙烯醚添加到由皂素、十二烷基苯磺酸钠、十二烷基硫酸钠、聚丙烯酸树脂等成分组成的复合型发泡剂中
能够有效地增加起泡高度，改善由于增稠剂聚丙烯酸树脂加入而导致的发泡力较差问题并且不影响泡沫的稳定性，加入明胶作为稳泡剂可以进一步改善发泡剂的稳定性。本发明中通过对硅藻土进行改性，可以有效地防止泡沫液膜厚度的衰减，同时增加了液膜中液体流失的阻力，从而达到稳泡的效果，提高泡沫的稳定性。本发明原料易得，成本较低，制备工艺简单，生产出来的发泡剂稳定性好，不易变质，发泡力好，可以减少发泡剂溶液的用量，且不影响泡沫混凝土的绝干密度以及抗压强度等指标，具有非常好的发展前途。
具体实施方式
下面结合实施例对本发明作进一步的说明。
实施例
混凝土用复合型发泡剂，由下列重量份的原料在常温下混合搅拌均匀而制成：皂素15份、十二烷基苯磺酸钠5份、十二烷基硫酸钠1.8份、聚乙二醇2.5份、明胶3份、改性硅藻土0.8份、甲基葡萄糖苷聚氧乙烯醚0.35份、聚丙烯酸树脂1.6份、水65份。
其中，所述的改性硅藻土由以下方法制得：先用15%盐酸浸泡4小时，去离子水洗涤干净，再用15%氢氧化钠溶液浸泡4小时，再用去离子水洗涤至中性，烘干，再加入硅藻土重量3%的羧甲基纤维素钠、2%的三乙醇胺、2%的蔗糖，高速1500转/分搅拌5min，得到分散液，最后将分散液烘干粉碎成超细粉末即可。
本实施例生产出来的复合发泡剂应用于泡沫混凝土试验：
选择两种发泡剂溶液：一种为普通单一发泡剂，另一种为本发明复合发泡剂，采用高速搅拌器预发泡的方法制备泡沫分别加入到1kg混凝土水泥中，制备绝干密度为800kg/cm3数量级的泡沫混凝土。结果，所需的普通单一发泡剂溶液为156ml，而所需的本发明复合发泡剂溶液92ml。
对两种泡沫混凝土的28天抗压强度进行了测试，分别为5.6MPa（普通单一发泡剂）和6.5MPa（本发明复合发泡剂）。根据泡沫混凝土砌块JC/T1062-2007建材行业标准，用本发明复合发泡剂生产出来的泡沫混凝土达到了A6.0等级。

Claims (3)

1.一种混凝土用复合型发泡剂，其特征在于，由下列重量份的原料在常温下混合搅拌均匀而制成：皂素10-15份、十二烷基苯磺酸钠3-5份、十二烷基硫酸钠1-2份、聚乙二醇2-3份、明胶3-4份、改性硅藻土0.5-1份、甲基葡萄糖苷聚氧乙烯醚0.2-0.5份、聚丙烯酸树脂1-2份、水60-70份。
2.根据权利要求1所述的混凝土用复合型发泡剂，其特征在于，由下列重量份的原料在常温下混合搅拌均匀而制成：皂素15份、十二烷基苯磺酸钠5份、十二烷基硫酸钠1.8份、聚乙二醇2.5份、明胶3份、改性硅藻土0.8份、甲基葡萄糖苷聚氧乙烯醚0.35份、聚丙烯酸树脂1.6份、水65份。
3.根据权利要求1或2所述的混凝土用复合型发泡剂，其特征在于，所述的改性硅藻土由以下方法制得：先用10-15%盐酸浸泡3-4小时，去离子水洗涤干净，再用10-15%氢氧化钠溶液浸泡3-4小时，再用去离子水洗涤至中性，烘干，再加入硅藻土重量2-3%的羧甲基纤维素钠、1-2%的三乙醇胺、1-2%的蔗糖，高速1200-1500转/分搅拌5-8min，得到分散液，最后将分散液烘干粉碎成超细粉末即可。
CN201210415884.8A 2012-10-26 2012-10-26 一种混凝土用复合型发泡剂 Expired - Fee Related CN102964080B (zh)