CN104945006A - 一种绿色环保陶粒增强加气砌块 - Google Patents
一种绿色环保陶粒增强加气砌块 Download PDFInfo
- Publication number
- CN104945006A CN104945006A CN201510281745.4A CN201510281745A CN104945006A CN 104945006 A CN104945006 A CN 104945006A CN 201510281745 A CN201510281745 A CN 201510281745A CN 104945006 A CN104945006 A CN 104945006A
- Authority
- CN
- China
- Prior art keywords
- parts
- environmental protection
- haydite
- aerated block
- ceramsite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种绿色环保陶粒增强加气砌块,其特征在于,由下列重量份的原料制成:硅藻土10-12、陶粒30-50、粉煤灰15-25、聚乙烯醇0.3-0.6、生石灰10-15、水泥15-20、铝粉0.3-0.5、石膏粉2-4、氧化镁0.4-0.7、木质素磺酸钙0.3-0.5、铁粉1-3、纳米三氧化二铝3-5、炭黑2-4、无水乙醇15-20、水适量;本发明采用的工艺方法解决了陶粒在加工过程中易破碎和质轻在浆料中分布不均的问题,添加的硅藻土增强了各成分之间的粘结力,并且含有有益元素,本发明的加气砌块工艺简单,操作方便、原料来源广泛、安全环保,值得推广。
Description
技术领域
本发明涉及加气砌块领域,确切的说是一种绿色环保陶粒增强加气砌块。
背景技术
随着建筑节能要求的提出和高层化建筑的发展趋势,传统的墙体材料质量重,施工不便,不适合高层建筑。并且随着人们生活水平的日益提高,人们对绿色环保建筑也愈益重视。加气混凝土是一种具有高分散性多孔结构的新型节能墙体材料,与传统墙体材料相比,具有轻质高强、保温隔热、吸声隔音、抗震防火、施工简单等优点,能够起到节土、利废、节能的作用。由于加气混凝土具有以上优点,使其在国内外都得到了很好的应用和发展。但是目前生产的加气混凝土具有强度较低、容重大、干缩大等缺点。
陶粒是一种人造轻骨料,外壳坚硬,内部具有微多孔陶质粒状物,它具有良好的保温隔热性,耐火性优异,表面有一层隔水保气的釉层,吸水率低,抗渗抗震性好,抗冻性能和耐久性能好,具有优异的物理、化学和水力特性。为了改善上述加气混凝土的缺点,一些厂家向加气混凝土中添加陶粒,不仅增强了混凝土的骨架结构,而且能够有效地保持加气混凝土的优势,并且降低了能源的消耗,保护环境,成为新型环保高效墙材。但是,由于陶粒是一种中空的轻质骨料,在搅拌过程中,由于料浆的比重大,陶粒容易上浮,造成分布不均匀,形成产品缺陷,另一方面,由于陶粒骨料的自身强度较低,搅拌过程中易产生破损,这不仅增加了陶粒的自身吸水率,而且还降低了产品保温性能。因此,必须要对陶粒进行处理,改进加气砌块的生产工艺方法。
发明内容
本发明的目的是提供一种绿色环保陶粒增强加气砌块及其制备方法。
为了实现本发明的目的,本发明通过以下方案实施:
一种绿色环保陶粒增强加气砌块,由下列重量份的原料制成:硅藻土10-12、陶粒30-50、粉煤灰15-25、聚乙烯醇0.3-0.6、生石灰10-15、水泥15-20、铝粉0.3-0.5、石膏粉2-4、氧化镁0.4-0.7、木质素磺酸钙0.3-0.5、铁粉1-3、纳米三氧化二铝3-5、炭黑2-4、无水乙醇15-20、水适量;
本发明所述一种绿色环保陶粒增强加气砌块,由以下具体步骤制成:
(1)将铁粉、炭黑和纳米三氧化二铝加到含有0.5%硅烷偶联剂KH-550的无水乙醇中超声分散均匀,干燥后和陶粒混合加到烧结炉中,于1000-1200°C下烧结1-2小时备用;
(2)将步骤(1)制备的烧结陶粒在水池中浸泡12-24小时,再将石膏粉、聚乙烯醇和氧化镁加到2-3倍重量份的水中混合搅拌均匀,加热至20-25°C,和上述陶粒搅拌均匀备用;
(3)将粉煤灰、水泥、生石灰、硅藻土混合搅拌均匀,加入2-3倍重量份的水和木质素磺酸钙搅拌3-5分钟,再加入步骤(2)的陶粒继续搅拌3-4分钟,再将适量的水分散铝粉后加入搅拌20-40秒;
(4)将步骤(3)的产物加入浇注搅拌机内搅拌制成浆料,将浆料入模,将模具放入烘箱内静置发气2-3小时,切除超出模具的部分,脱模,再放到釜内进行蒸汽养护,蒸汽压力为1.1-1.3MPa,温度为180-190°C,蒸养时间为8-12小时。
本发明的优点是:本发明利用碳黑和铁粉反应使陶粒生成内部孔径小且比表面积大的结构,增大与浆料的接触面积,增强粘结性,利用氧化铝改性增强陶粒的强度和降低干缩系数,采用预湿处理和表面包覆的工艺方法解决了陶粒在加工过程中易破碎的问题,进一步增强与水泥砂浆的粘结性,防止在浆料中上浮分布不均,添加的硅藻土增强了各成分之间的粘结力,并且含有有益元素,提高居住环境和增强人们身体健康,本发明的加气砌块工艺简单,操作方便、原料来源广泛、安全环保,值得推广。
具体实施方案
下面通过具体实例对本发明进行详细说明。
一种绿色环保陶粒增强加气砌块,由下列重量份(公斤)的原料制成:硅藻土10、陶粒50、粉煤灰25、聚乙烯醇0.6、生石灰10、水泥20、铝粉0.5、石膏粉3、氧化镁0.6、木质素磺酸钙0.4、铁粉3、纳米三氧化二铝5、炭黑4、无水乙醇16、水适量;
本发明所述一种绿色环保陶粒增强加气砌块,由以下具体步骤制成:
(1)将铁粉、炭黑和纳米三氧化二铝加到含有0.5%硅烷偶联剂KH-550的无水乙醇中超声分散均匀,干燥后和陶粒混合加到烧结炉中,于1100°C下烧结2小时备用;
(2)将步骤(1)制备的烧结陶粒在水池中浸泡24小时,再将石膏粉、聚乙烯醇和氧化镁加到2倍重量份的水中混合搅拌均匀,加热至25°C,和上述陶粒搅拌均匀备用;
(3)将粉煤灰、水泥、生石灰、硅藻土混合搅拌均匀,加入3倍重量份的水和木质素磺酸钙搅拌5分钟,再加入步骤(2)的陶粒继续搅拌4分钟,再将适量的水分散铝粉后加入搅拌40秒;
(4)将步骤(3)的产物加入浇注搅拌机内搅拌制成浆料,将浆料入模,将模具放入烘箱内静置发气3小时,切除超出模具的部分,脱模,再放到釜内进行蒸汽养护,蒸汽压力为1.3MPa,温度为190°C,蒸养时间为8小时。
本实施例中加气砌块的性能指标如下:
抗压强度(MPa):≥4.9;
收缩值(mm/m):≤0.21;
密度(级):05;
抗冻性(15次,损失率%):≤2.2;
导热系数(W/m.k):≤ 0.16。
Claims (1)
1.一种绿色环保陶粒增强加气砌块,其特征在于,由下列重量份的原料制成:硅藻土10-12、陶粒30-50、粉煤灰15-25、聚乙烯醇0.3-0.6、生石灰10-15、水泥15-20、铝粉0.3-0.5、石膏粉2-4、氧化镁0.4-0.7、木质素磺酸钙0.3-0.5、铁粉1-3、纳米三氧化二铝3-5、炭黑2-4、无水乙醇15-20、水适量;
根据权利要求1所述一种绿色环保陶粒增强加气砌块,其特征在于,由以下具体步骤制成:
(1)将铁粉、炭黑和纳米三氧化二铝加到含有0.5%硅烷偶联剂KH-550的无水乙醇中超声分散均匀,干燥后和陶粒混合加到烧结炉中,于1000-1200°C下烧结1-2小时备用;
(2)将步骤(1)制备的烧结陶粒在水池中浸泡12-24小时,再将石膏粉、聚乙烯醇和氧化镁加到2-3倍重量份的水中混合搅拌均匀,加热至20-25°C,和上述陶粒搅拌均匀备用;
(3)将粉煤灰、水泥、生石灰、硅藻土混合搅拌均匀,加入2-3倍重量份的水和木质素磺酸钙搅拌3-5分钟,再加入步骤(2)的陶粒继续搅拌3-4分钟,再将适量的水分散铝粉后加入搅拌20-40秒;
(4)将步骤(3)的产物加入浇注搅拌机内搅拌制成浆料,将浆料入模,将模具放入烘箱内静置发气2-3小时,切除超出模具的部分,脱模,再放到釜内进行蒸汽养护,蒸汽压力为1.1-1.3MPa,温度为180-190°C,蒸养时间为8-12小时。