CN103319795A - 一种含有明矾粉末的氯化聚乙烯电缆护套料 - Google Patents
一种含有明矾粉末的氯化聚乙烯电缆护套料 Download PDFInfo
- Publication number
- CN103319795A CN103319795A CN2013101777018A CN201310177701A CN103319795A CN 103319795 A CN103319795 A CN 103319795A CN 2013101777018 A CN2013101777018 A CN 2013101777018A CN 201310177701 A CN201310177701 A CN 201310177701A CN 103319795 A CN103319795 A CN 103319795A
- Authority
- CN
- China
- Prior art keywords
- parts
- chlorinatedpolyethylene
- weight
- powder
- antioxidant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种含有明矾粉末的氯化聚乙烯电缆护套料,其是由下述重量份的原料制得:氯化聚乙烯80-90、氯丁橡胶22-25,改性氢氧化铝80-90、白炭黑5-6,三磷酸甲苯二苯酯2-4,硫磺1.5-2.3,硅烷偶联剂KH792 1.2-2.4,包膜天青石粉30-40,乙酰柠檬酸三乙酯1-2,氯化石蜡5-7,古马隆树脂3-6,明矾粉末1.3-2.2,防老剂NBC1.5-2.5、交联剂TAC0.5-1,硬酯酸锌2-4,氧化钙0.4-0.8、氧化锌1-2,抗氧剂10760.8-1.2、抗氧剂22460.3-0.5、辛基酚聚氧乙烯醚1-2,氧化镁1-2。
Description
技术领域
本发明涉及电缆料领域,确切地说是一种含有明矾粉末的氯化聚乙烯电缆护套料。
背景技术
电缆护套是电缆的最外层,如VV是聚氯乙烯绝缘,聚氯乙烯护套,外面穿的管叫保护管。电缆护套材料不仅需要有优良的物理性能,如拉伸强度、断裂伸长率等,同时还需要拥有良好的阻燃性能。
发明内容
本发明的目的在于提供一种含有明矾粉末的氯化聚乙烯电缆护套料。
上述目的通过以下方案实现:
一种含有明矾粉末的氯化聚乙烯电缆护套料,其特征在于:其是由下述重量份的原料制得:
氯化聚乙烯80-90、氯丁橡胶22-25,改性氢氧化铝80-90、白炭黑5-6,三磷酸甲苯二苯酯2-4,硫磺1.5-2.3,硅烷偶联剂KH792 1.2-2.4,包膜天青石粉30-40,乙酰柠檬酸三乙酯1-2,氯化石蜡5-7,古马隆树脂3-6,明矾粉末1.3-2.2,防老剂NBC 1.5-2.5、交联剂 TAC 0.5-1,硬酯酸锌2-4,氧化钙0.4-0.8、氧化锌1-2,抗氧剂1076 0.8-1.2、抗氧剂2246 0.3-0.5、辛基酚聚氧乙烯醚1-2,氧化镁1-2;
所述的包膜天青石粉的制备方法为:天青石粉用酒精进行球磨分散处理5-6小时,再在其中加入相当于其重量3-5%的辛基酚聚氧乙烯醚、6-8%的去离子水,于70-80℃恒温水浴中搅拌加热25-35分钟,得复混液,再在复混液里面加入相当于其重量10-15%的浓度为24-27%的Al2(SO4)3溶液,同时加入适量氨水调节pH值为8-11,搅拌30-40min后,静置3-4小时后,经过滤、洗涤、干燥处理后,在500-550℃烧结5-7小时,自然冷却至室温即得;
所述的改性氢氧化铝的制备方法为:在氢氧化铝中加入相当于其重量1-2%的丙烯酸丁酯、0.4-0.8%的马来酸二辛酯,2.8-3.5%的硅烷偶联剂A-151,放入捏合釜中,温度控制在60-65℃,充分搅拌均匀2-3h,干燥后,粉碎后即得。
所述的一种含有明矾粉末的氯化聚乙烯电缆护套料,其特征在于:制备方法包括以下步骤:
(1)将氯丁橡胶于密炼机上76-82℃下塑炼,塑炼好的氯丁橡胶冷却备用;
(2)将氯化聚乙烯于密炼机上70-80℃下塑炼,塑炼好的氯化聚乙烯冷却备用;
(3)将步骤(1)所得塑炼好的氯丁橡胶于步骤(2)所得塑炼好的氯化聚乙烯按重量份放入密炼机,于95-105℃下合炼8-12分钟;
(4)再按重量份加入其余原料,于85-95℃下混炼10-13分钟;
(5)双螺杆挤出机挤出造粒,即得。
本发明的有益效果为:改性氢氧化铝通过复合改性,可以提高其添加量,增加电缆护套材料的阻燃效果。包膜天青石粉可以增加本发明的强度和阻燃性能。
具体实施方式
一种含有明矾粉末的氯化聚乙烯电缆护套料,其是由下述重量份(kg)的原料制得:
氯化聚乙烯87、氯丁橡胶25,改性氢氧化铝80、白炭黑6,三磷酸甲苯二苯酯4,硫磺2.3,硅烷偶联剂KH792 2.4,包膜天青石粉30,乙酰柠檬酸三乙酯2,氯化石蜡7,古马隆树脂6,明矾粉末2.2,防老剂NBC 2.5、交联剂 TAC 0.7,硬酯酸锌4,氧化钙0.8、氧化锌2,抗氧剂1076 1.2、抗氧剂2246 0.4、辛基酚聚氧乙烯醚2,氧化镁1;
所述的包膜天青石粉的制备方法为:天青石粉用酒精进行球磨分散处理6小时,再在其中加入相当于其重量5%的辛基酚聚氧乙烯醚、8%的去离子水,于75℃恒温水浴中搅拌加热30分钟,得复混液,再在复混液里面加入相当于其重量12%的浓度为25%的Al2(SO4)3溶液,同时加入适量氨水调节pH值为9,搅拌35min后,静置4小时后,经过滤、洗涤、干燥处理后,在550℃烧结7小时,自然冷却至室温即得;
所述的改性氢氧化铝的制备方法为:在氢氧化铝中加入相当于其重量1%的丙烯酸丁酯、0.8%的马来酸二辛酯,3.5%的硅烷偶联剂A-151,放入捏合釜中,温度控制在65℃,充分搅拌均匀3h,干燥后,粉碎后即得。
所述的一种含有明矾粉末的氯化聚乙烯电缆护套料,制备方法包括以下步骤:
(1)将氯丁橡胶于密炼机上78℃下塑炼,塑炼好的氯丁橡胶冷却备用;
(2)将氯化聚乙烯于密炼机上80℃下塑炼,塑炼好的氯化聚乙烯冷却备用;
(3)将步骤(1)所得塑炼好的氯丁橡胶于步骤(2)所得塑炼好的氯化聚乙烯按重量份放入密炼机,于95℃下合炼12分钟;
(4)再按重量份加入其余原料,于88℃下混炼13分钟;
(5)双螺杆挤出机挤出造粒,即得。
测试本实施例材料性能,氧指数为48%,水平垂直燃烧测试中,水平燃烧达到FH-1等级,垂直燃烧达到FV-0等级。拉伸强度为14.4MPa,断裂伸长率>398%。
Claims (2)
1.一种含有明矾粉末的氯化聚乙烯电缆护套料,其特征在于:其是由下述重量份的原料制得:
氯化聚乙烯80-90、氯丁橡胶22-25,改性氢氧化铝80-90、白炭黑5-6,三磷酸甲苯二苯酯2-4,硫磺1.5-2.3,硅烷偶联剂KH792 1.2-2.4,包膜天青石粉30-40,乙酰柠檬酸三乙酯1-2,氯化石蜡5-7,古马隆树脂3-6,明矾粉末1.3-2.2,防老剂NBC 1.5-2.5、交联剂 TAC 0.5-1,硬酯酸锌2-4,氧化钙0.4-0.8、氧化锌1-2,抗氧剂1076 0.8-1.2、抗氧剂2246 0.3-0.5、辛基酚聚氧乙烯醚1-2,氧化镁1-2;
所述的包膜天青石粉的制备方法为:天青石粉用酒精进行球磨分散处理5-6小时,再在其中加入相当于其重量3-5%的辛基酚聚氧乙烯醚、6-8%的去离子水,于70-80℃恒温水浴中搅拌加热25-35分钟,得复混液,再在复混液里面加入相当于其重量10-15%的浓度为24-27%的Al2(SO4)3溶液,同时加入适量氨水调节pH值为8-11,搅拌30-40min后,静置3-4小时后,经过滤、洗涤、干燥处理后,在500-550℃烧结5-7小时,自然冷却至室温即得;
所述的改性氢氧化铝的制备方法为:在氢氧化铝中加入相当于其重量1-2%的丙烯酸丁酯、0.4-0.8%的马来酸二辛酯,2.8-3.5%的硅烷偶联剂A-151,放入捏合釜中,温度控制在60-65℃,充分搅拌均匀2-3h,干燥后,粉碎后即得。
2.根据权利要求1所述的一种含有明矾粉末的氯化聚乙烯电缆护套料,其特征在于:制备方法包括以下步骤:
(1)将氯丁橡胶于密炼机上76-82℃下塑炼,塑炼好的氯丁橡胶冷却备用;
(2)将氯化聚乙烯于密炼机上70-80℃下塑炼,塑炼好的氯化聚乙烯冷却备用;
(3)将步骤(1)所得塑炼好的氯丁橡胶于步骤(2)所得塑炼好的氯化聚乙烯按重量份放入密炼机,于95-105℃下合炼8-12分钟;
(4)再按重量份加入其余原料,于85-95℃下混炼10-13分钟;
(5)双螺杆挤出机挤出造粒,即得。