CN103319211A - Gold gilding decoration process for Nixing pottery - Google Patents
Gold gilding decoration process for Nixing pottery Download PDFInfo
- Publication number
- CN103319211A CN103319211A CN2013102650298A CN201310265029A CN103319211A CN 103319211 A CN103319211 A CN 103319211A CN 2013102650298 A CN2013102650298 A CN 2013102650298A CN 201310265029 A CN201310265029 A CN 201310265029A CN 103319211 A CN103319211 A CN 103319211A
- Authority
- CN
- China
- Prior art keywords
- platinum
- decoration
- mud
- decorative pattern
- nixing pottery
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a gold gilding decoration process for Nixing pottery. The gold gilding decoration process comprises the following steps of: (1) processing platinum into a flat platinum sheet by pressing in a hammering manner; (2) manufacturing a punch die for punching a required decoration pattern on the flat platinum sheet; (3) manufacturing a ceramic product; (4) melting peach gum; (5) applying the peach gum, pasting the decoration pattern, compacting, and drying in air; (6) carrying out decoration firing for 3.0-4.0 hours at a temperature of 950-1000 DEG C under the pressure of 10-15MPa, cooling, discharging, and enabling the platinum decoration pattern to be integrally fused with an enamel layer of the Nixing pottery. By virtue of the gold gilding decoration process, the Nixing pottery adopting the decoration process is high in grade, elegant in quality, bright in color, friction-resistant, oxidation-resistant, permanently fadeless, sanitary and safe, and harmful substances such as lead and cadmium can not be dissolved out; the gold gilding decoration process is suitable for the field of the Nixing pottery, the quality level of the Nixing pottery is increased, and the increasing material and cultural life requirements of people are met.
Description
Technical field:
The present invention relates to the decoration process method of the emerging pottery of a kind of mud, relate in particular to the gold inlaying and decorating process of the emerging pottery of a kind of mud.
Background technology:
The methods such as traditional mud main colored drawing of emerging fictile surface decoration or engraving are decorated, although can play certain decorative effect, the resistance to persistence of Exterior color of products is inadequate, the time length can fade, affect decorative effect; And the chemical color that adopts has contains the harmful materials such as lead, cadmium, and the easily clear injury that goes out to cause to human body of these objectionable impuritiess affects the healthy of people; And adopt the class of the emerging fictile of mud of this decoration also not high.Along with socioeconomic fast development, improving constantly of people's living standard, people also improve constantly the requirement of the emerging pottery of mud, when requiring product to have practicality, also require product to have higher sight and aesthetic feeling, therefore, above-mentioned trailing can not satisfy the demand of the material and cultural life that people improve day by day.
Summary of the invention
For overcoming above-mentioned deficiency, the object of the present invention is to provide that a kind of class is high, rub resistance, anti-oxidant and permanent colour-fast, the gold inlaying and decorating process that also can be unclear do not go out the emerging pottery of mud of objectionable impurities, satisfy the needs of the modern material and cultural life of people.
The technical solution adopted for the present invention to solve the technical problems is: the gold inlaying and decorating process of the emerging pottery of mud may further comprise the steps:
(1) getting pure platinum presses processing to reach the platinum plain film of 0.1~0.2mm through hammer;
(2) make die cutting die according to required decorative pattern, the platinum plain film is taken out required decorative pattern after punch press is die-cut;
(3) technique is made the emerging fictile of mud routinely;
(4) get peach gum (water-soluble gum), add proper amount of clear water and treat that peach gum dissolves or dissolves through heating;
(5) coat peach gum through dissolving at the emerging fictile of mud, the platinum decorative pattern is attached on the emerging fictile of mud, compacting, after 20~24 hours peach gums were done, the platinum decorative pattern was close on the emerging fictile of the mud surface;
The emerging pottery of mud that (6) will stick the platinum decorative pattern is put in the gas pressure sintering stove decoration firing into and is burnt till, and under 10~15MPa, firing temperature is 950~1000 ℃, firing time is 3.0~4.0 hours, naturally cooling is come out of the stove, and the glaze layer of platinum decorative pattern and the emerging fictile of mud is fused into one.
Use the present invention, adopt the emerging pottery class of mud of above-mentioned decoration process method high, elegant quality, bright in luster, rub resistance, anti-oxidant and forever colour-fast, can stripping lead, the objectionable impurities such as cadmium yet, hygienic safety; The present invention is adapted to the emerging pottery of mud field, makes the emerging pottery of mud bring up to a new class, satisfies the demand of the material and cultural life that people improve day by day.
Embodiment
(1) getting pure platinum presses processing to reach the platinum plain film of 0.2mm through hammer;
(2) make die cutting die according to required decorative pattern, the platinum plain film is taken out required decorative pattern after punch press is die-cut;
(3) technique is made the emerging pottery of mud routinely;
(4) get peach gum (water-soluble gum), add proper amount of clear water and treat that peach gum dissolves;
(5) coat peach gum through dissolving in the position that the emerging pottery of mud need be decorated, the platinum decorative pattern is attached on the emerging pottery of mud, compacting, after 24 hours peach gums were done, the platinum decorative pattern was close on the emerging pottery of the mud surface;
(6) the emerging pottery of the mud decoration firing in the gas pressure sintering stove that will stick the platinum decorative pattern is burnt till, and under 10MPa, firing temperature is 1000 ℃, and firing time is 3 hours, and naturally cooling is come out of the stove, and the glaze layer of platinum decorative pattern and the emerging pottery of mud is fused into one.
Claims (1)
1. the gold inlaying and decorating process of the emerging pottery of mud is characterized in that: may further comprise the steps:
(1) getting pure platinum presses processing to reach the platinum plain film of 0.1~0.2mm through hammer;
(2) make die cutting die according to required decorative pattern, the platinum plain film is taken out required decorative pattern after punch press is die-cut;
(3) technique is made the emerging fictile of mud routinely;
(4) get peach gum, add that proper amount of clear water treats that peach gum dissolves or through heat fused;
(5) coat peach gum through dissolving or melting at ceramic, the platinum decorative pattern is attached on the ceramic, compacting, after 20~24 hours peach gums were done, the platinum decorative pattern was close on the surface of the emerging fictile of mud;
The emerging pottery of mud that (6) will stick the platinum decorative pattern is put in the gas pressure sintering stove decoration firing into and is burnt till, and under 10~15MPa, firing temperature is 950~1000 ℃, and firing time is 3.0~4.0 hours, and naturally cooling is come out of the stove.