CN101805211B - Gold inlaying and decorating process method of ceramic product - Google Patents
Gold inlaying and decorating process method of ceramic product Download PDFInfo
- Publication number
- CN101805211B CN101805211B CN2010101234357A CN201010123435A CN101805211B CN 101805211 B CN101805211 B CN 101805211B CN 2010101234357 A CN2010101234357 A CN 2010101234357A CN 201010123435 A CN201010123435 A CN 201010123435A CN 101805211 B CN101805211 B CN 101805211B
- Authority
- CN
- China
- Prior art keywords
- gold
- ceramic
- decorative pattern
- process method
- peach gum
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention provides a gold inlaying and decorating process method of a ceramic product, which comprises the following steps: (1) processing gold into a gold flat piece by hammering; (2) producing a punching die and punching the gold flat piece into a pattern to be decorated; (3) producing a ceramic product; (4) dissolving peach gum; (5) coating the peach gum, pasting the decorative pattern, compacting and airing; (6) firing decoration at the temperature of 900-950DEG C for 3.0-4.0h, cooling and discharging from a kiln so as to melt the gold decorative pattern and an enamel layer of the ceramic product into a whole; (7) carrying out surface burnishing and polishing treatment; and (8) inspecting, packaging and warehousing. The ceramic products produced by the decorating process method have the advantages of high grade and artistic value, elegant quality, splendid and magnificent vision, bright colors, friction resistance, antioxidation, permanent fastness, sanitation and safety. The invention is applied to the fields of daily and artistic ceramic and the like, improves the daily and artistic ceramic to a new grade and meets the requirement of people on increasingly-improved material and cultural life.
Description
Technical field
The present invention relates to a kind of decoration process method of ceramic, relate in particular to a kind of gold inlaying and decorating process method of ceramic.
Background technology
Traditional ceramic surface decoration mainly is to adopt methods such as decal paper or artificial colored drawing pattern color to decorate, though can play certain decorative effect, the resistance to persistence of product appearance color is not enough, and the time can fade than length, influences decorative effect; And the chemical color that is adopted has contains harmful materials such as lead, cadmium, as is used for the decorative daily-use tableware, and the clear injury that goes out to cause to human body easily of these objectionable impuritiess influences the healthy of people; And adopt the class of ceramic of this decoration also not high.Along with socioeconomic fast development; Improving constantly of people's living standard; People also improve constantly the requirement of ceramic, when requiring product to have practicality, also require product to have higher sight and aesthetic feeling; Therefore, above-mentioned trailing can not satisfy the demand of the material and cultural life that people improve day by day.
Summary of the invention
For overcoming above-mentioned deficiency, the object of the present invention is to provide a kind of class height, rub resistance, anti-oxidant and forever colour-fast, the decoration process method that also can be unclear do not go out the ceramic of objectionable impurities, satisfy the needs of the modern material and cultural life of people.
The technical solution adopted for the present invention to solve the technical problems is: a kind of gold inlaying and decorating process method of ceramic may further comprise the steps:
(1) getting the true yellow gold presses processing to reach the gold plain film of 0.1～0.22mm through hammer;
(2) make die cutting die according to required decorative pattern, the gold plain film is taken out required decorative pattern after punch press is die-cut;
(3) press common process and make ceramic;
(4) get peach gum (water-soluble gum), add proper amount of clear water and treat that peach gum dissolves or the warp heating is dissolved;
(5) on ceramic, coat peach gum, the gold decorative pattern is attached on the ceramic through dissolving, compacting, after 20～24 hours peach gums were done, the gold decorative pattern was close on the ceramic surface;
(6) the ceramic decoration firing in kiln that will stick the gold decorative pattern is burnt till, and firing temperature is 900～950 ℃, and firing time is 3.0～4.0 hours, naturally cooling, and kiln discharge fuses into one the glaze layer of gold decorative pattern and ceramic;
(7) carry out surface finish, the processing of scraping;
(8) check, packing, warehouse-in.
Use the present invention, adopt ceramic class height, elegant quality, splendid, bright in luster, the rub resistance, anti-oxidant and forever colour-fast of above-mentioned decoration process method, can stripping lead, objectionable impurities such as cadmium yet, hygienic safety; The present invention is adapted to fields such as domestic ceramics, the art pottery, makes domestic ceramics and art ceramics bring up to a new class, satisfies the demand of the material and cultural life that people improve day by day.
Embodiment
Embodiment: a kind of gold inlaying and decorating process method of domestic ceramics tableware may further comprise the steps:
(1) getting the true yellow gold presses processing to reach the gold plain film of 0.22mm through hammer;
(2) make die cutting die according to required decorative pattern, the gold plain film is taken out required decorative pattern after punch press is die-cut;
(3) press common process and make the domestic ceramics tableware;
(4) get peach gum (water-soluble gum), add proper amount of clear water and treat that peach gum dissolves;
(5) on the position that the domestic ceramics tableware need be decorated, coat peach gum, the gold decorative pattern is attached on the domestic ceramics tableware through dissolving, compacting, after 24 hours peach gums were done, the gold decorative pattern was close on the domestic ceramics tableware surface;
(6) the domestic ceramics tableware decoration firing in kiln that will stick the gold decorative pattern is burnt till, and firing temperature is 950 ℃, and firing time is 4 hours, naturally cooling, and kiln discharge fuses into one the glaze layer of gold decorative pattern and domestic ceramics tableware;
(7) carry out surface finish, the processing of scraping;
(8) check, packing, warehouse-in.
Claims (1)
1. the gold inlaying and decorating process method of a ceramic is characterized in that: may further comprise the steps:
(1) getting the true yellow gold presses processing to reach the gold plain film of 0.1～0.22mm through hammer;
(2) make die cutting die according to required decorative pattern, the gold plain film is taken out required decorative pattern after punch press is die-cut;
(3) press common process and make ceramic;
(4) get peach gum, add that proper amount of clear water treats that peach gum dissolves or through heat fused;
(5) on ceramic, coat peach gum, the gold decorative pattern is attached on the ceramic through dissolving or melting, compacting, after 20～24 hours peach gums were done, the gold decorative pattern was close on the ceramic surface;
(6) the ceramic decoration firing in kiln that will stick the gold decorative pattern is burnt till, and firing temperature is 900～950 ℃, and firing time is 3.0～4.0 hours, naturally cooling, kiln discharge;
(7) carry out surface finish, the processing of scraping;
(8) check, packing, warehouse-in.