CN103449722B - A kind of figured glass brick manufacturing process - Google Patents
A kind of figured glass brick manufacturing process Download PDFInfo
- Publication number
- CN103449722B CN103449722B CN201310417000.7A CN201310417000A CN103449722B CN 103449722 B CN103449722 B CN 103449722B CN 201310417000 A CN201310417000 A CN 201310417000A CN 103449722 B CN103449722 B CN 103449722B
- Authority
- CN
- China
- Prior art keywords
- line
- weaving
- glass
- leaf
- silk
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention provides a kind of figured glass brick manufacturing process, mainly comprise Mold Making, make Stem and leaf of Hongkong Pavetta line or hollow picture-weaving in silk line drift 1-2 block; Then preparation temperature is suitable for the melten glass liquid suppressed; Suppress half base, fusion molding again, finally anneal, obtain described Stem and leaf of Hongkong Pavetta line or hollow picture-weaving in silk line plate glass.Positively effect of the present invention is adopted to be that the figure of Stem and leaf of Hongkong Pavetta line or hollow picture-weaving in silk line plate glass product is concavo-convex alternate on the outer surface, star or as beautiful picture-weaving in silk, stereoscopic sensation is stronger, better to the visual effect of people in similar night sky.At home and abroad plate glass internal surface is shaping still belongs to the first; Cut glass compared with brick production technology with traditional colored drawing, sand, its manufacturing process level of automation is high, production efficiency and yield rate high, create an aesthetic feeling is also suitable for industrial application, and output is high, and cost reduces, yield rate, more than 85%, can meet the diversified demand in market simultaneously.
Description
Technical field
The present invention relates to a kind of finishing material manufacture method, be specifically related to a kind of figured glass brick manufacturing process.
Background technology
Existing glass brick production process, sand as traditional is cut glass brick, stained glass bricks, sand is cut glass brick, stained glass bricks production technique, need first special gummed paper to be sticked on plate glass face, according to patterning requirement carve profile, then according to the actual requirements, with the required figure of dry powder sandblast machine ejection, finally color spray rifle paint color on the pattern in plate glass face is used.This production technique has following weak point: 1, figure is opaque, and stereoscopic sensation is bad.2, manual production, level of automation is low, labour intensity is large.3, production efficiency is low.
Summary of the invention
For solving the problems of the technologies described above, the invention provides a kind of figured glass brick manufacturing process.
Production technique of the present invention mainly comprises the steps:
(1) Mold Making: designing mould Stem and leaf of Hongkong Pavetta line or hollow picture-weaving in silk print image, image Aspect Ratio presses 1:0.8-1.2, convex-concave goes out decorative pattern 3-5 millimeter, figure is carved on drift, mold and punching head adopts overall cooling, and mating die base plate and framed size make Stem and leaf of Hongkong Pavetta line or hollow picture-weaving in silk line drift 1-2 block;
(2) temperature of glass liquid controls: get sandstone 50-60 part, soda ash 15-20 part, lithium feldspar 8.5-12.5 part, rhombspar 12-17.5 part by weight, be mixed in proportion into admixtion; Admixtion, after fusing, will be decremented to 1000-1100 DEG C for 1100-1200 DEG C of temperature of glass liquid by subregion, obtain the melten glass liquid of proper temperature compacting;
(3) suppress: step (2) described molten glass gobs is dropped in forming press equipment die and suppresses, adjustment machine speed be 20-22 cut/point, the heavy 1125-1150 gram of material, carry out compacting half base;
(4) fusion molding: be fixed thereon second base by plate glass fixture, then by three groups of annular burners, double base laser heating, final fusion molding Stem and leaf of Hongkong Pavetta line or hollow picture-weaving in silk line plate glass;
(5) anneal: during annealing, annealing furnace top temperature is 560-570 DEG C, by five workspace gradually by lapse of temperature to 510-530 DEG C, when plate glass is come out of the stove the most at last, temperature controls at 120-150 DEG C, obtains described Stem and leaf of Hongkong Pavetta line or hollow picture-weaving in silk line plate glass.
Positively effect of the present invention is adopted to be that the figure of Stem and leaf of Hongkong Pavetta line or hollow picture-weaving in silk line plate glass product is concavo-convex alternate on the outer surface, star or as beautiful picture-weaving in silk, stereoscopic sensation is stronger, better to the visual effect of people in similar night sky.At home and abroad plate glass internal surface is shaping still belongs to the first; Cut glass compared with brick production technology with traditional colored drawing, sand, its manufacturing process level of automation is high, production efficiency and yield rate high, create an aesthetic feeling is also suitable for industrial application, and output is high, and cost reduces, yield rate, more than 85%, can meet the diversified demand in market simultaneously.
Embodiment
Stem and leaf of Hongkong Pavetta line plate glass and picture-weaving in silk line plate glass are as novel plate glass product a kind of in plate glass industry, its production technique is mainly on-line Full shaping in the one that plate glass internal surface is shaping, early stage is designed mould drawing as requested, carry out Mould Machining by figure, concrete manufacturing process is shown in following embodiment.
Embodiment 1
(1) Mold Making: designing mould Stem and leaf of Hongkong Pavetta print image, image Aspect Ratio presses 1:0.8, and convex-concave goes out 3 millimeters, decorative pattern, and figure is carved on drift, and mold and punching head adopts overall cooling, and mating die base plate and framed size make Stem and leaf of Hongkong Pavetta line drift 1 piece;
(2) temperature of glass liquid controls: get 50 parts, sandstone, soda ash 20 parts, lithium feldspar 12.5 parts, rhombspar 12 parts by weight, be mixed in proportion into admixtion; Admixtion, after fusing, will be that 1100 DEG C of temperature of glass liquid are decremented to 1000 DEG C by subregion, obtain the melten glass liquid of proper temperature compacting;
(3) suppress: step (2) described molten glass gobs is dropped in forming press equipment die and suppresses, adjustment machine speed be 20 to cut/point, expect heavy 1125 grams, carry out compacting half base;
(4) fusion molding: be fixed thereon second base by plate glass fixture, then by three groups of annular burners, double base laser heating, final fusion molding Stem and leaf of Hongkong Pavetta line plate glass;
(5) anneal: during annealing, annealing furnace top temperature is 560 DEG C, by five workspace gradually by lapse of temperature to 510 DEG C, when plate glass is come out of the stove the most at last, temperature controls at 120 DEG C, obtains described Stem and leaf of Hongkong Pavetta line plate glass.
Embodiment 2
(1) Mold Making: the hollow picture-weaving in silk print image of designing mould, image Aspect Ratio presses 1:1.2, and convex-concave goes out 5 millimeters, decorative pattern, and figure is carved on drift, and mold and punching head adopts overall cooling, and mating die base plate and framed size make hollow picture-weaving in silk line drift 2 pieces;
(2) temperature of glass liquid controls: get 60 parts, sandstone, soda ash 15 parts, lithium feldspar 8.5 parts, rhombspar 17.5 parts by weight, be mixed in proportion into admixtion; Admixtion, after fusing, will be that 1200 DEG C of temperature of glass liquid are decremented to 1100 DEG C by subregion, obtain the melten glass liquid of proper temperature compacting;
(3) suppress: step (2) described molten glass gobs is dropped in forming press equipment die and suppresses, adjustment machine speed be 22 to cut/point, expect heavy 1150 grams, carry out compacting half base;
(4) fusion molding: be fixed thereon second base by plate glass fixture, then by three groups of annular burners, double base laser heating, final fusion molding hollow picture-weaving in silk line plate glass;
(5) anneal: during annealing, annealing furnace top temperature is 570 DEG C, by five workspace gradually by lapse of temperature to 530 DEG C, when plate glass is come out of the stove the most at last, temperature controls at 150 DEG C, obtains described hollow picture-weaving in silk line plate glass.
Claims (1)
1. a figured glass brick manufacturing process, is characterized in that, mainly comprises the steps:
(1) Mold Making: designing mould Stem and leaf of Hongkong Pavetta line or hollow picture-weaving in silk print image, image Aspect Ratio presses 1:0.8-1.2, convex-concave goes out decorative pattern 3-5 millimeter, image carving is on drift, mold and punching head adopts overall cooling, and mating die base plate and framed size make Stem and leaf of Hongkong Pavetta line or hollow picture-weaving in silk line drift 1-2 block;
(2) temperature of glass liquid controls: get sandstone 50-60 part, soda ash 15-20 part, lithium feldspar 8.5-12.5 part, rhombspar 12-17.5 part by weight, be mixed in proportion into admixtion; Admixtion, after fusing, will be decremented to 1000-1100 DEG C for 1100-1200 DEG C of temperature of glass liquid by subregion, obtain the melten glass liquid of proper temperature compacting;
(3) suppress: described for step (2) melten glass drop is dropped in forming press equipment die and suppresses, adjustment machine speed be 20-22 cut/point, the heavy 1125-1150 gram of material, carry out compacting half base;
(4) fusion molding: be fixed thereon second base by plate glass fixture, then by three groups of annular burners, double base laser heating, final fusion molding Stem and leaf of Hongkong Pavetta line or hollow picture-weaving in silk line plate glass;
(5) anneal: during annealing, annealing furnace top temperature is 560-570 DEG C, by five workspace gradually by lapse of temperature to 510-530 DEG C, when plate glass is come out of the stove the most at last, temperature controls at 120-150 DEG C, obtains described Stem and leaf of Hongkong Pavetta line or hollow picture-weaving in silk line plate glass.